CN104382268A - Method for preparing cool blended and knitted fabric - Google Patents
Method for preparing cool blended and knitted fabric Download PDFInfo
- Publication number
- CN104382268A CN104382268A CN201410800904.2A CN201410800904A CN104382268A CN 104382268 A CN104382268 A CN 104382268A CN 201410800904 A CN201410800904 A CN 201410800904A CN 104382268 A CN104382268 A CN 104382268A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fabric
- preparation
- polyester filament
- knit fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing a cool blended and knitted fabric. The method comprises the following steps: (a) raw material selection; (b) yarn spinning; (c) weaving; (d) dying; (e) after-finishing. The method has the advantages of being reasonable in arrangement of work procedures, simple and convenient in preparation process and easy to realize. The prepared fabric is thin in structure and comfortable in wearing, has good effects of heat conduction, heat dissipation and cooling, and is an ideal fabric for making summer clothes.
Description
Technical field
The present invention relates to fabric technical field, particularly relate to a kind of preparation method of cooling feeling blended knitted fabric.
Background technology
Fabric, as one of the three elements of clothes, not only can annotate style and the characteristic of clothes, directly left and right the color of clothes, moulding expression effect, also embody the development of society and people to a certain extent to the pursuit of life simultaneously.Garment material from solid endurable, the warming of the emphasis that the past is traditional to current advocate fashion freely, CRUX, Considering Environmental antipollution, health care, comfortable fittingness embody this theory invariably.
At present, along with the development of science and technology and the progress of thought of people, higher requirement be it is also proposed to the New function of garment material.During the broiling summer, merely against wear less or on clothes, output the requirement that novel hole can not meet people, from the quality performance of clothes, prepare meet summer clothes that dress requires most important.But the most of garment material structural designs in current technology are too complicated, raw material preparation is reasonable not, production technology is science not, and the functional instability causing fabric to possess, can not meet Production requirement, in addition preparation cost is high, therefore, is not easy to popularization and produces in enormous quantities.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of preparation method of cooling feeling blended knitted fabric, and can solve existing preparation section and arrange unreasonable, preparation process is complicated, and fabric performance can not meet summer clothes quality and the difficult problem of performance requirement such as feel nice and cool.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: the preparation method providing the multifunctional blended knit fabric of a kind of cool, comprises the following steps:
(a) raw material choice: choose spandex fibre, flax fiber, polyester filament and the CUP raw material as described fabric;
(b) yarn spin: by silver mixing, rove, spun yarn and twist with the fingers, yarn steaming, winder, by spandex fibre and flax fiber, polyester filament and CUP are spun into scribbled with certain proportion respectively;
C () weaves: on one side scutcher, using spandex fibre obtained in step (b) and flax fiber blended yarn as warp thread, polyester filament and copper ammonia fiber blended yarn are as weft yarn, and being woven into fabric width by plain weave is 150 ~ 180cm, and gram mass is 120 ~ 135g/m
2grey cloth;
D () is dyeed: the grey cloth of braiding in step (c) is carried out preboarding and dyeing process;
(e) Final finishing: the grey cloth after dyeing in step (c) is carried out soft finish and the sizing of light base, obtain finished product fabric.
In a preferred embodiment of the present invention, the line density of described spandex fibre, flax fiber, polyester filament and CUP is respectively 3.3 tex, 12.3tex, 10.8tex and 11.1tex.
In a preferred embodiment of the present invention, in described step (b), the spinning ratio of described spandex fibre and described flax fiber is 1:3 ~ 5; The spinning ratio of described polyester filament and described CUP is 1:2 ~ 3.
In a preferred embodiment of the present invention, in described step (c), described weaving speed is 22 r/min, and entering yarn tension is 3 ~ 5g.
In a preferred embodiment of the present invention, in described step (d), described grey cloth presetting technology is: temperature is 180 DEG C, and the boarding machine speed of a motor vehicle is 25 ~ 30m/r; Described dyeing is two bath two dyes, and wherein, a bath temperature is 120 DEG C, and two bath temperatures are 75 DEG C.
In a preferred embodiment of the present invention, in described step (e), described setting temperature is 130 ~ 138 DEG C, and the speed of a motor vehicle is 15 ~ 20m/min.
The invention has the beneficial effects as follows: the preparation method of the multifunctional blended knit fabric of a kind of cool of the present invention, this preparation method's procedure arrangement is reasonable, preparation process is easy, easy realization, not only structure is thin for prepared fabric, comfortable and easy to wear, and there is excellent heat conduction, heat radiation and nice and cool effect of lowering the temperature, be the desirable fabric preparing summer clothes.
Detailed description of the invention
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
The embodiment of the present invention comprises:
A preparation method for the multifunctional blended knit fabric of cool, comprises the following steps:
(a) raw material choice: choose line density and be respectively the spandex fibre of 3.3 tex, 12.3tex, 10.8tex and 11.1tex, flax fiber, polyester filament and CUP as raw material;
(b) yarn spin: by silver mixing, rove, spun yarn and twist with the fingers, yarn steaming, winder, spandex fibre and flax fiber are spun into scribbled with the ratio of 1:3 ~ 5, polyester filament and CUP are spun into scribbled with the ratio of 1:2 ~ 3;
C () weaves: on one side scutcher, using spandex fibre obtained in step (b) and flax fiber blended yarn as warp thread, polyester filament and copper ammonia fiber blended yarn are as weft yarn, and being woven into fabric width by plain weave is 150 ~ 180cm, and gram mass is 120 ~ 135g/m
2grey cloth; The loom speed of a motor vehicle is 22 r/min, and entering yarn tension is 3 ~ 5g;
D () is dyeed: the grey cloth of braiding in step (c) is carried out preboarding and dyeing process; Wherein, presetting technology is: temperature 180 DEG C, the boarding machine speed of a motor vehicle 25 ~ 30m/r; Described dyeing is two bath two dyes, and wherein, a bath temperature is 120 DEG C, and two bath temperatures are 75 DEG C.
(e) Final finishing: the grey cloth after dyeing in step (c) is carried out soft finish and the sizing of light base, obtain finished product fabric, wherein, setting temperature is 130 ~ 138 DEG C, and the sizing speed of a motor vehicle is 15 ~ 20m/min.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (6)
1. a preparation method for the multifunctional blended knit fabric of cool, is characterized in that, comprise the following steps:
(a) raw material choice: choose spandex fibre, flax fiber, polyester filament and the CUP raw material as described fabric;
(b) yarn spin: by silver mixing, rove, spun yarn and twist with the fingers, yarn steaming, winder, by spandex fibre and flax fiber, polyester filament and CUP are spun into scribbled with certain proportion respectively;
C () weaves: on one side scutcher, using spandex fibre obtained in step (b) and flax fiber blended yarn as warp thread, polyester filament and copper ammonia fiber blended yarn are as weft yarn, and being woven into fabric width by plain weave is 150 ~ 180cm, and gram mass is 120 ~ 135g/m
2grey cloth;
D () is dyeed: the grey cloth of braiding in step (c) is carried out preboarding and dyeing process;
(e) Final finishing: the grey cloth after dyeing in step (c) is carried out soft finish and the sizing of light base, obtain finished product fabric.
2. the preparation method of the multifunctional blended knit fabric of cool according to claim 1, is characterized in that, the line density of described spandex fibre, flax fiber, polyester filament and CUP is respectively 3.3 tex, 12.3tex, 10.8tex and 11.1tex.
3. the preparation method of the multifunctional blended knit fabric of cool according to claim 1, is characterized in that, in described step (b), the spinning ratio of described spandex fibre and described flax fiber is 1:3 ~ 5; The spinning ratio of described polyester filament and described CUP is 1:2 ~ 3.
4. the preparation method of the multifunctional blended knit fabric of cool according to claim 1, is characterized in that, in described step (c), described weaving speed is 22 r/min, and entering yarn tension is 3 ~ 5g.
5. the preparation method of the multifunctional blended knit fabric of cool according to claim 1, is characterized in that, in described step (d), described grey cloth presetting technology is: temperature is 180 DEG C, and the boarding machine speed of a motor vehicle is 25 ~ 30m/r; Described dyeing is two bath two dyes, and wherein, a bath temperature is 120 DEG C, and two bath temperatures are 75 DEG C.
6. the preparation method of the multifunctional blended knit fabric of cool according to claim 1, is characterized in that, in described step (e), described setting temperature is 130 ~ 138 DEG C, and the speed of a motor vehicle is 15 ~ 20m/min.