CN105696176A - Wool-algae fiber dual-face high-grade T-shirt fabric and technology for producing same - Google Patents
Wool-algae fiber dual-face high-grade T-shirt fabric and technology for producing same Download PDFInfo
- Publication number
- CN105696176A CN105696176A CN201410684235.7A CN201410684235A CN105696176A CN 105696176 A CN105696176 A CN 105696176A CN 201410684235 A CN201410684235 A CN 201410684235A CN 105696176 A CN105696176 A CN 105696176A
- Authority
- CN
- China
- Prior art keywords
- fabric
- grade
- wool
- yarn
- sargassum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wool-algae fiber dual-face high-grade T-shirt fabric. The fabric is of a dual-layer structure; a raw material of an inner layer of the fabric is algae/cotton fiber blended yarn, and a raw material of an outer layer of the fabric is wool yarn; and a dual-rib complex weave structure including weft plain stitch and tuck stitch is adopted. The fabric has the appearance and style of a woo knitted garment; and through the structure, the excellent performances of algae fiber and wool fiber can fully utilized, and meanwhile, a prickle feel can be effectively solved when a wool fiber garment is worn close to a skin, and the problem that the wool fiber is not suitable for internal garments can be solved.
Description
Technical field
The present invention relates to textile and production technology thereof, be specifically related to the two-sided high-grade T-shirt fabric of a kind of hair alginate fibre and production technology thereof。
Background technology
The development of social civilization, the progress of science and technology, make people that own health and living environment to be focused more on, back to nature, protection environment has become the topic that people discuss warmly, and this theory also penetrates into people in the production of clothing and choosing。Various natural fiber clothes and there are comfortable and health care clothing become the new lover of people。China's natural fiber resource-constrained, the growing demand to natural fibre product so that this natural fiber very in short supply makes the matter worse especially。Develop new natural fiber succedaneum and have become as inevitable development trend。
Alginate fibre is with alginate for raw material, adopt the fiber that wet spinning is made, not only environmental protection, have good antibiotic property, highly hygroscopic with highly-breathable, the performance such as good biocompatibility and degraded and absorbed, and the raw material resources manufacturing alginate fibre are enriched, people's demand to heath-function clothing can be met, can alleviating again natural fiber inadequate resource and the ever-increasing contradiction of people's demand to a certain extent, therefore the exploitation of alginate fibre textile has vast potential for future development。But owing to alginate fibre is with viscose glue base for carrier, it is powerful, particularly wet relatively low by force, outward appearance conformality is poor, it is impossible to meet the high-grade T-shirt fabric requirement to appearance of fabrics and Fabric Style。
Summary of the invention
It is an object of the invention to overcome the defect existed in prior art, it is provided that a kind of resistance to two-sided high-grade T-shirt fabric of the hair alginate fibre strong with anti-microbial property of soaping。
For realizing above-mentioned technique effect, the technical scheme is that the two-sided high-grade T-shirt fabric of a kind of hair alginate fibre, it is characterized in that, described fabric is double-decker, the internal layer raw material of described fabric is Sargassum/cotton fiber mixed yarn, the outer layer raw material of described fabric is wool yarn, adopts the double rib type compound structure of the change flat pin of latitude and tucked loop compound。
The present invention also aims to provide the production technology of a kind of mao of two-sided high-grade T-shirt fabric of alginate fibre, it is characterised in that comprise the steps:
S1: adopt Sargassum/silk/cotton blended yarn to carry out one side on needle-bar and be knitted to form fabric internal layer；
S2: adopt wool yarn to carry out one side on needle-bar and be knitted to form fabric outer layer；
S3: utilize polyamide staple fibre spun yarn to carry out tuck knitting on 2 needle-bars and 2 mutual disjunct single-side fabrics are coupled together in the place needed。
Wherein, the fineness of described wool yarn is not less than the fineness of Sargassum/silk/cotton blended yarn。
Wherein, the weaving ambient temperature of described fabric internal layer is 26～30 DEG C, and relative humidity is 72～76%。
Advantages of the present invention and having the beneficial effects that:
This fabric has the look and feel of knitting woollen clothing, by such structural design, alginate fibre and the respective premium properties of wool fibre is made to be fully played, simultaneously also effectively solve prodding and itching feeling when wool fibre clothing wear next to the skin, improve in wool fibre is not suitable for makeing the problem wearing clothing。The application of change latitude plain stitch, fabric is made to have good appearance retention, the formation of air layer structure, impart the plentiful outward appearance of fabric and good warmth retention property, therefore this fabric has reached the outer performance requirement wearing clothing next to the skin, makes spring and autumn top grade T-shirt with this fabric or other next to the skin outer wear clothing。
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described。Following example are only for clearly illustrating technical scheme, and can not limit the scope of the invention with this。
Embodiment 1
The two-sided high-grade T-shirt fabric of hair alginate fibre of embodiment 1, fabric is double-decker, the internal layer raw material of described fabric is Sargassum/cotton fiber mixed yarn, and the outer layer raw material of described fabric is wool yarn, adopts the double rib type compound structure of the change flat pin of latitude and tucked loop compound。
The production technology of the two-sided high-grade T-shirt fabric of hair alginate fibre, comprises the steps:
S1: adopt Sargassum/silk/cotton blended yarn to carry out one side on needle-bar and be knitted to form fabric internal layer；
S2: adopt wool yarn to carry out one side on needle-bar and be knitted to form fabric outer layer；
S3: utilize polyamide staple fibre spun yarn to carry out tuck knitting on 2 needle-bars and 2 mutual disjunct single-side fabrics are coupled together in the place needed。
Wherein, the fineness of wool yarn is equal to the fineness of Sargassum/silk/cotton blended yarn。
Wherein, the weaving ambient temperature of fabric internal layer is 26 DEG C, and relative humidity is 72%
Embodiment 2
The two-sided high-grade T-shirt fabric of hair alginate fibre of embodiment 2, it is characterized in that, described fabric is double-decker, and the internal layer raw material of described fabric is Sargassum/cotton fiber mixed yarn, the outer layer raw material of described fabric is wool yarn, adopts the double rib type compound structure of the change flat pin of latitude and tucked loop compound。
The production technology of the two-sided high-grade T-shirt fabric of hair alginate fibre, comprises the steps:
S1: adopt Sargassum/silk/cotton blended yarn to carry out one side on needle-bar and be knitted to form fabric internal layer；
S2: adopt wool yarn to carry out one side on needle-bar and be knitted to form fabric outer layer；
S3: utilize polyamide staple fibre spun yarn to carry out tuck knitting on 2 needle-bars and 2 mutual disjunct single-side fabrics are coupled together in the place needed。
Wherein, the fineness of wool yarn is equal to the fineness of Sargassum/silk/cotton blended yarn。
Wherein, the weaving ambient temperature of fabric internal layer is 30 DEG C, and relative humidity is 76%。
Embodiment 3
The two-sided high-grade T-shirt fabric of hair alginate fibre of embodiment 3, it is characterized in that, described fabric is double-decker, and the internal layer raw material of described fabric is Sargassum/cotton fiber mixed yarn, the outer layer raw material of described fabric is wool yarn, adopts the double rib type compound structure of the change flat pin of latitude and tucked loop compound。
The production technology of the two-sided high-grade T-shirt fabric of hair alginate fibre, comprises the steps:
S1: adopt Sargassum/silk/cotton blended yarn to carry out one side on needle-bar and be knitted to form fabric internal layer；
S2: adopt wool yarn to carry out one side on needle-bar and be knitted to form fabric outer layer；
S3: utilize polyamide staple fibre spun yarn to carry out tuck knitting on 2 needle-bars and 2 mutual disjunct single-side fabrics are coupled together in the place needed。
Wherein, the fineness of wool yarn is more than the fineness of Sargassum/silk/cotton blended yarn。
Wherein, the weaving ambient temperature of fabric internal layer is 28 DEG C, and relative humidity is 74%。
The fineness of wool yarn should be slightly thicker or equal thereto than Sargassum/silk/cotton blended yarn, is so conducive to improving the spreadability of wool yarn, and appearance of fabrics is plentiful, can improve the presentation quality of fabric。
The brute force of alginate fibre is relatively low, particularly wet relatively low by force。Therefore, should strictly control the humiture in workshop in process of production, it is to avoid because humidity is excessive, cause braiding process interrupt head to increase。
The internal layer of fabric only manifests Sargassum/silk/cotton blended yarn, and the outer layer of fabric only appears wool yarn, it is achieved wool yarn and Sargassum/silk/cotton blended yarn are in front and the double-decker on the contrary of fabric respectively。Such structure also can form a certain amount of air layer in fabric simultaneously, can store more still air, make the warmth retention property of fabric strengthen to some extent in air layer。Add the warmth retention property that outer layer wool fibre itself has, so that the fabric developed has good thermal property, be suitable for making spring and autumn clothing。
The above is only the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the technology of the present invention principle; can also making some improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention。
Claims (4)
1. the two-sided high-grade T-shirt fabric of hair alginate fibre, it is characterized in that, described fabric is double-decker, and the internal layer raw material of described fabric is Sargassum/cotton fiber mixed yarn, the outer layer raw material of described fabric is wool yarn, adopts the double rib type compound structure of the change flat pin of latitude and tucked loop compound。
2. the production technology of the two-sided high-grade T-shirt fabric of hair alginate fibre, it is characterised in that comprise the steps:
S1: adopt Sargassum/silk/cotton blended yarn to carry out one side on needle-bar and be knitted to form fabric internal layer；
S2: adopt wool yarn to carry out one side on needle-bar and be knitted to form fabric outer layer；
S3: utilize polyamide staple fibre spun yarn to carry out tuck knitting on 2 needle-bars and 2 mutual disjunct single-side fabrics are coupled together in the place needed。
3. the production technology of the according to claim 2 mao of two-sided high-grade T-shirt fabric of alginate fibre, it is characterised in that the fineness of described wool yarn is not less than the fineness of Sargassum/silk/cotton blended yarn。
4. the production technology of the according to claim 3 mao of two-sided high-grade T-shirt fabric of alginate fibre, it is characterised in that the weaving ambient temperature of described fabric internal layer is 26～30 DEG C, and relative humidity is 72～76%。