CN1043358C - 聚酰胺涂膜防水材料 - Google Patents

聚酰胺涂膜防水材料 Download PDF

Info

Publication number
CN1043358C
CN1043358C CN93110625A CN93110625A CN1043358C CN 1043358 C CN1043358 C CN 1043358C CN 93110625 A CN93110625 A CN 93110625A CN 93110625 A CN93110625 A CN 93110625A CN 1043358 C CN1043358 C CN 1043358C
Authority
CN
China
Prior art keywords
water
waterproof
favorable
present
polyamide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN93110625A
Other languages
English (en)
Other versions
CN1092452A (zh
Inventor
王银生
王佑先
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN93110625A priority Critical patent/CN1043358C/zh
Publication of CN1092452A publication Critical patent/CN1092452A/zh
Application granted granted Critical
Publication of CN1043358C publication Critical patent/CN1043358C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

聚酰胺涂膜防水材料属于一种建筑防水胶。本发明的聚酰胺树脂为基料,水为溶剂,改性剂与助剂等其他原料有甲醛、苯酚、酚酞、邻苯二甲酸酐、氢氧化钠与无水乙醇,基料、溶剂与助剂在防水材料中所占的重量比为14~16∶100∶1.5~2.0,在100℃左右的水中先后加入助剂、基料混合后冷却即成,生产工艺简单,无污染,产品经检测具有良好的耐候性、不透水性、耐裂性及粘结性,而且冷施工方便,成本低廉,是一种具有竞争力的新型防水材料,为防水材料开辟了一条新途径。

Description

聚酰胺涂膜防水材料
聚酰胺涂膜防水材料属于建筑防水胶。
随着建筑规模的扩大和建筑结构的变化,传统的防水材料已不能满足现代化建筑业发展的需要。目前屋面及地下工程的防水,未改性的纸胎石油沥青油毡仍占有一定的比例,防水涂料大多数是再生沥青涂料,防水密封材料基本上也是沥青基或油性低档密封材料,但由于其延伸性、低温柔性与耐老化性能差,当建筑物产生应力变化、伸缩移位时,就出现鼓泡、破裂等老化现象,导致建筑物渗漏,因此开发研究弹性和弹塑性的高分子防水材料在建筑防水工程中具有现实意义和实用价值。
80年代以来,国外建筑防水技术取得了重大进展,新材料、新工艺、新的施工技术不断出现,大大改善了建筑物的防水性能。目前日本采用高分子涂膜防水材料施工面积已占总施工面积的20%,美国占15%。我国新型高分子建筑防水材料也在积极研制、开发。如聚氨酯涂膜防水材料、氯丁乳化沥青胶、防水油膏、高分子防水卷材在防水工程中得到了广泛的应用,但有些涂料老化性能差,而有些性能好,但造价太高,难以推广。
本发明旨在研制一种性能好、生产工艺简单而成本又低的防水涂料新品种,为防水材料发展开辟一条新途径。
实施本发明任务的技术方案是:聚酰胺涂膜防水材料的主要原料成膜剂为聚酰胺,改性剂与助剂等原料有甲醛、苯酚、酚酞、邻苯二甲酸酐、氢氧化钠与无水乙醇,溶剂为水,将甲醛、苯酚、酚酞、邻苯二甲酸酐混合后,加人氢氧化钠,然后加人到无水乙醇中,再将上述改性剂与助剂加人到已升温至100℃的水中,最后在水中加入聚酰胺,助剂、水与聚酰胺配制的重量比为1.5~2.8∶100∶14~16。
下面进一步详细述本发明。
本发明的主要成膜物聚酰胺
Figure C9311062500041
是分子中包含酰胺结构的高聚物.聚酰胺具有以下优良性能。
(1)具有较好的柔软性,强度高,耐摩擦,自润滑,抗蟠变性能好;
(2)在软好时不易分解,而且能反复熔化,因此不易断裂,防止脆硬;
(3)耐腐蚀性强。
聚酰胺具有较好的牯结力,柔软性好,耐高温是做防水涂料的比较理想材料。但由于屋面防水对材料的耐水性能及耐老化性能要求较高,因此采用改性剂及助剂以提高聚酰胺高分子聚合物的防水性能及耐老化性能。选用的改性剂的原则时(1)与聚酰胺具有良好的相容性,(2)具有较好的变形性能,(3)对被粘物起架桥作用,使其与被粘物紧密结合。
本发明选用的改性剂与助剂等其他原料有甲醛、苯酚、酚酞、邻苯二甲酸酐、氢氧化钠与无水乙醇,这些原料在聚酰胺涂膜防水材料助剂中所占的重量百分比(%)分别为4.5~6.0,16~18.5,5~6.5,6.5~7.5,3.5~5,58~62。
生产聚酰胺涂膜防水材料的工艺简单方便。
按助剂、水与聚酰胺以1.5~2.0∶100∶14~16的重量比称取原料,将水加入至反应釜中,加热至100℃左右,先在水中加入已按比例配制好的改性剂与助剂,然后再加入聚酰胺树脂,待溶解后冷却再可出料装桶。
聚酰胺涂膜防水材料的特点是:
1、柔软性好,不易脆裂,抗基层变形能力强,耐老化,弹性好;
2、耐气候性,耐水性及耐腐蚀性优良;
3、粘结强度高;
4、防水层重量轻,涂膜能形成无接缝的完整防水膜;
5、施工方便,冷施工、无气味。
聚酰胺涂膜防水材料适应于屋面防水、地下工程防水及地面防潮等工程。
参照原国家建材部“关于屋面防水涂料统一鉴定质量技术要求”的方法和指标进行测试,其性能如下表:
物理性能
指标名称 国家建材部规定的指标 达到指标
耐热性 在80±2℃下恒温5h,无皱皮,起泡等现象。 无皱皮,起泡
耐碱性 20±2℃下,在饱和氢氧化钙水溶液中浸泡15d,无剥落、起泡、分层、起皱等现象。 15d浸泡。无剥落起泡、分层、起皱皮等现象。
粘结性 在20±2℃下,用8字模法测抗拉强度不小于0.2MPa。 1.78MPa
不透水性 在20±2℃水温下,动力压0.1MPa30min内涂膜不透水。 0.2MPa,30min不透水
低温柔性 在-10℃时,通过φ10mm园棒,涂膜无网纹、裂纹、剥落等现象。 -20℃涂膜无裂纹,剥落等现象
耐裂性 20±2℃下,涂膜厚0.3~0.4mm,基层裂缝不小于0.2mm时,涂膜不开裂。 涂膜不开裂
耐久性 人工加速老化试验达到四年以上。 无爆裂,膜落及粉化现象等异常现象,自然老化四年无渗漏。
聚酰胺除膜防水材料的施工方法:
1、基层平面应清扫干净,凹凸不平处应1∶2.5水泥砂浆找平,不能有积水;
2、将防水胶以1.5~2kg/m2涂刷均匀,表干后重复涂刷一次,防水层厚度为0.2~0.3cm左右;
3、在檐口、斜沟,接缝搭口等重要部位,凿5-8mm深、3-5mm宽的沟缝后,用防水胶填满沟缝,使胶与屋面板牢固粘在一起,然后再进行整个屋面的防水层施工;
4、待防水膜固化后,用1∶2.5水泥砂浆将防水层复盖,或根据屋面设计要求,做成蓄水屋面、隔热屋面、屋顶花园等;
5、防潮层施工方法与屋面施工方法大致相同。
施工注意事项:
1、施工时的气温应为0℃以上,施工期间要避免灾害性天气和其他人为因素以免损坏膜层;
2、施工时基层湿度不大于10%;
3、水泥砂浆保护层厚度应保持在2~3cm。
经近1000m2新建屋面的防水施工和3000m2左右漏水严重的旧屋面、天沟等补漏以及住房的防潮层试验都收到了满意效果,防水性能达到国家防水涂料统一鉴定的质量技术指标,竣工以来未出现任何渗漏现象或回潮现象,与其他防水材料比较,聚酰胺涂膜防水材料施工方便、无气味,涂膜不鼓泡,不生裂纹,耐水,老化性能好,而且比20~30元/m2的聚氨酯类防水材料价格低,仅10元/m2。因此聚酰胺涂膜防水材料是一种原材料来源广、工艺简单、施工无污染、不易燃、冷作业,造价低,使用寿命长的理想防水材料,具有较强的市场竞争力,值得推广。

Claims (1)

1、一种聚酰胺涂膜防水材料,其特征在于成膜剂为聚酰胺,其他原料有甲醛、苯酚、酚酞、邻苯二甲酸酐、氢氧化钠和无水乙醇,溶剂为水,将甲醛、苯酚、酚酞与邻苯二甲酸酐按重量百分比4.5~6.0、16~18.5、5~6.5、6.5~7.5混合后加入3.5~5份的氢氧化钠,再加入到58~62份无水乙醇中,然后将已溶于无水乙醇的原料加入到已升温至100℃的水中,最后在水中加入聚酰胺,助剂、水与聚酰胺配制的重量比为1.5~2.0∶100∶14~16。
CN93110625A 1993-03-16 1993-03-16 聚酰胺涂膜防水材料 Expired - Fee Related CN1043358C (zh)