CN104313580A - 一种适用于退去黄铜表面锡镍镀层的化学退镀液 - Google Patents

一种适用于退去黄铜表面锡镍镀层的化学退镀液 Download PDF

Info

Publication number
CN104313580A
CN104313580A CN201410491397.9A CN201410491397A CN104313580A CN 104313580 A CN104313580 A CN 104313580A CN 201410491397 A CN201410491397 A CN 201410491397A CN 104313580 A CN104313580 A CN 104313580A
Authority
CN
China
Prior art keywords
parts
tin
chemical
antioxidant
deplating solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410491397.9A
Other languages
English (en)
Other versions
CN104313580B (zh
Inventor
栾信清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MINGGUANG XUSHENG TECHNOLOGY Co Ltd
Original Assignee
MINGGUANG XUSHENG TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MINGGUANG XUSHENG TECHNOLOGY Co Ltd filed Critical MINGGUANG XUSHENG TECHNOLOGY Co Ltd
Priority to CN201410491397.9A priority Critical patent/CN104313580B/zh
Publication of CN104313580A publication Critical patent/CN104313580A/zh
Application granted granted Critical
Publication of CN104313580B publication Critical patent/CN104313580B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种适用于退去黄铜表面锡镍镀层的化学退镀液，其特征在于：包括以下质量份组分：甲基磺酸亚锡80-120份，甲基磺酸100-120份，硫酸锌8-12份，抗氧化剂0.5-1.5份，光亮剂5-10份，表面活性剂5-15份。本发明配方简单实用，使用甲基磺酸替代了传统的氨基三乙酸，解决了由氨基三乙酸作为退镀液处理后所带来的水体富营养化的问题，绿色环保，有效的提高了镀锡铜线上锡层的附着力和抗腐蚀能力。

Description

一种适用于退去黄铜表面锡镍镀层的化学退镀液
技术领域
本发明涉及铜线表面处理领域，具体涉及一种适用于退去黄铜表面锡镍镀层的化学退镀液。
背景技术
锡有很好的耐腐蚀能力，在空气中易钝化，能耐强碱，与盐酸和硫酸作用也较缓慢。锡的电位比铜为负，镀锡铜线上的锡层可对铜起到阳极保护层作用，因此比镀银铜线更耐腐蚀。镀锡铜线的耐温等级比镀银铜线高，可达260℃。鉴于上述原因，镀锡铜线广泛用作耐高温的航空电线及其它特种安装线的导电线芯。根据要求，制造镀锡软铜线时，必须对铜线镀锡前的进行预处理，镀锡铜线上锡层的附着力及抗腐蚀能力等性能的好坏，与铜线在镀锡前的预处理质量有关。基于此，现研究一种一种适用于退去黄铜表面锡镍镀层的化学退镀液，有效解决了这个问题。
发明内容
针对上述问题，本发明提供了一种适用于退去黄铜表面锡镍镀层的化学退镀液，环保无污染，有效的提高了镀锡铜线上锡层的附着力和抗腐蚀能力。
为了解决上述问题，本发明提供的技术方案为：
一种适用于退去黄铜表面锡镍镀层的化学退镀液，其特征在于：包括以下质量份组分：甲基磺酸亚锡80-120份，甲基磺酸100-120份，硫酸锌8-12份，抗氧化剂0.5-1.5份，光亮剂5-10份，表面活性剂5-15份。
优选的，所述各质量份组分为：甲基磺酸亚锡90-110份，甲基磺酸105-115份，硫酸锌9-11份，抗氧化剂0.75-1.25份，光亮剂7-8份，表面活性剂9-11份。
优选的，所述各质量份组分为：甲基磺酸亚锡90份，甲基磺酸105份，硫酸锌9份，抗氧化剂0.75份，光亮剂7份，表面活性剂9份。
优选的，所述各质量份组分为：甲基磺酸亚锡110份，甲基磺酸115份，硫酸锌11份，抗氧化剂1.25份，光亮剂8份，表面活性剂11份。
优选的，所述各质量份组分为：甲基磺酸亚锡100份，甲基磺酸110份，硫酸锌10份，抗氧化剂1份，光亮剂7.5份，表面活性剂10份。
本发明的有益效果为：本发明配方简单实用，使用甲基磺酸替代了传统的氨基三乙酸，解决了由氨基三乙酸作为退镀液处理后所带来的水体富营养化的问题，绿色环保，有效的提高了镀锡铜线上锡层的附着力和抗腐蚀能力。
具体实施方式
下面对本发明做进一步说明：
实施例一：
一种适用于退去黄铜表面锡镍镀层的化学退镀液，包括以下质量份组分：甲基磺酸亚锡80份，甲基磺酸100份，硫酸锌8份，抗氧化剂0.5份，光亮剂5份，表面活性剂5份。
本发明的有益效果为：本发明配方简单实用，使用甲基磺酸替代了传统的氨基三乙酸，解决了由氨基三乙酸作为退镀液处理后所带来的水体富营养化的问题，绿色环保，有效的提高了镀锡铜线上锡层的附着力和抗腐蚀能力。
实施例二：
一种适用于退去黄铜表面锡镍镀层的化学退镀液，包括以下质量份组分：甲基磺酸亚锡120份，甲基磺酸120份，硫酸锌12份，抗氧化剂1.5份，光亮剂10份，表面活性剂15份。
本发明的有益效果为：本发明配方简单实用，使用甲基磺酸替代了传统的氨基三乙酸，解决了由氨基三乙酸作为退镀液处理后所带来的水体富营养化的问题，绿色环保，有效的提高了镀锡铜线上锡层的附着力和抗腐蚀能力。
实施例三：
一种适用于退去黄铜表面锡镍镀层的化学退镀液，包括以下质量份组分：甲基磺酸亚锡100份，甲基磺酸110份，硫酸锌10份，抗氧化剂1份，光亮剂7.5份，表面活性剂10份。
本发明的有益效果为：本发明配方简单实用，使用甲基磺酸替代了传统的氨基三乙酸，解决了由氨基三乙酸作为退镀液处理后所带来的水体富营养化的问题，绿色环保，有效的提高了镀锡铜线上锡层的附着力和抗腐蚀能力。
实施例四：
一种适用于退去黄铜表面锡镍镀层的化学退镀液，包括以下质量份组分：甲基磺酸亚锡90份，甲基磺酸105份，硫酸锌9份，抗氧化剂0.75份，光亮剂7份，表面活性剂9份。
本发明的有益效果为：本发明配方简单实用，使用甲基磺酸替代了传统的氨基三乙酸，解决了由氨基三乙酸作为退镀液处理后所带来的水体富营养化的问题，绿色环保，有效的提高了镀锡铜线上锡层的附着力和抗腐蚀能力。
实施例五：
一种适用于退去黄铜表面锡镍镀层的化学退镀液，包括以下质量份组分：甲基磺酸亚锡110份，甲基磺酸115份，硫酸锌11份，抗氧化剂1.25份，光亮剂8份，表面活性剂11份。
本发明的有益效果为：本发明配方简单实用，使用甲基磺酸替代了传统的氨基三乙酸，解决了由氨基三乙酸作为退镀液处理后所带来的水体富营养化的问题，绿色环保，有效的提高了镀锡铜线上锡层的附着力和抗腐蚀能力。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (5)

1.一种适用于退去黄铜表面锡镍镀层的化学退镀液，其特征在于：包括以下质量份组分：甲基磺酸亚锡80-120份，甲基磺酸100-120份，硫酸锌8-12份，抗氧化剂0.5-1.5份，光亮剂5-10份，表面活性剂5-15份。
2.根据权利要求1所述的一种适用于退去黄铜表面锡镍镀层的化学退镀液，其特征在于：所述各质量份组分为：甲基磺酸亚锡90-110份，甲基磺酸105-115份，硫酸锌9-11份，抗氧化剂0.75-1.25份，光亮剂7-8份，表面活性剂9-11份。
3.根据权利要求1或2所述的一种适用于退去黄铜表面锡镍镀层的化学退镀液，其特征在于：所述各质量份组分为：甲基磺酸亚锡90份，甲基磺酸105份，硫酸锌9份，抗氧化剂0.75份，光亮剂7份，表面活性剂9份。
4.根据权利要求1或2所述的一种适用于退去黄铜表面锡镍镀层的化学退镀液，其特征在于：所述各质量份组分为：甲基磺酸亚锡110份，甲基磺酸115份，硫酸锌11份，抗氧化剂1.25份，光亮剂8份，表面活性剂11份。
5.根据权利要求1或2所述的一种适用于退去黄铜表面锡镍镀层的化学退镀液，其特征在于：所述各质量份组分为：甲基磺酸亚锡100份，甲基磺酸110份，硫酸锌10份，抗氧化剂1份，光亮剂7.5份，表面活性剂10份。
CN201410491397.9A 2014-09-23 2014-09-23 一种适用于退去黄铜表面锡镍镀层的化学退镀液 Active CN104313580B (zh)