CN104312253A - 一种烤漆附着力促进剂及其合成方法 - Google Patents
一种烤漆附着力促进剂及其合成方法 Download PDFInfo
- Publication number
- CN104312253A CN104312253A CN201410530003.6A CN201410530003A CN104312253A CN 104312253 A CN104312253 A CN 104312253A CN 201410530003 A CN201410530003 A CN 201410530003A CN 104312253 A CN104312253 A CN 104312253A
- Authority
- CN
- China
- Prior art keywords
- component
- adhesion promoter
- baking vanish
- propylene glycol
- monomethyl ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种烤漆附着力促进剂及其合成方法,主要由以下原料成分组成(按重量百分比):A组分(己二酸1524.7,三羟甲基丙烷1881,亚磷酸三苯酯10.7,催化剂1.5),B组分(丙二醇甲醚37.6,异丙醇745.7),将A组分物料投入放应釜中,开搅拌,并升温至140度左右出水,保温3小时后,检测酸值,加入酸值控制在70以下就可以降温,加入B组分(丙二醇甲醚37.6,异丙醇745.7),兑稀,即可。本发明附着力促进剂添加到油漆中后,使得油漆对底材具有极好的附着力,同时,制作工艺简便,制作成本低廉。
Description
技术领域
本发明涉及烤漆附着力促进剂合成制备领域,具体涉及一种烤漆附着力促进剂及其合成方法。
背景技术
附着力促进剂广泛应用于各种化纤、木材、塑料、金属、陶瓷、玻璃和PVC 等底材,大幅度提高膜层与底材的附着力,它是一种新型树脂型密着促进剂,对于涂料的防脱落性有特殊功效,可以改进多种涂料体系的附着力,如:水性涂料、水性烤漆、印花胶浆、UV 光油、塑料漆、金属烤漆等,尤其适用于水性漆,提高了附着力及韧性。
在安全线生产过程中,经常由于底材本身的质量问题,如表面不平整、表面张力低等,或者在前工序加工过程中对印刷面造成了污染,或者是烤漆本身的缺陷造成烤漆在底材上的附着牢度不够、易脱落,最终导致了成品率的下降、产品质量不稳定和生产不顺利甚至停产。
申请号为“201310017034.7”的中国专利中公开了名称为“一种附着力促进剂及其制备方法”的发明专利,该附着力促进剂包括以下重量百分比的各组分:有机溶剂65%~75%,醋酸丁酯8%~12%,环己酮4%~6%,氯化丙烯酸树脂8%~ 12%,马来酸酐树脂4%~6%,通过采用以上组分以及配比,本发明得到的该附着力促进剂能够改变PP 塑料表面密度,使热塑性丙烯酸树脂涂料能够强力的吸附在PP 塑料表面,不易脱落。但是,该发明附着力促进剂只是针对热塑性丙烯酸树脂涂料对PP料表面,具有良好的附着效果,对于添加到烤漆或施工于其他底材上时,未必具有较好的附着效果,并且,其用到的有机原料较多,工艺现对复杂,导致制造成本过高。
申请号为“201110117820.5”的中国专利中,公开了名称为“一种附着力促进剂”的发明专利,其技术方案如下:包括环氧树脂、聚氨酯树脂、表面活性剂和稀释液,所述聚氨酯树脂为聚酯型聚氨酯、聚醚型聚氨酯或聚酯- 聚醚型聚氨酯,所述表面活性剂为碳氢表面活性剂和氟表面活性剂的混合物,所述稀释剂为有机溶剂或能够与水混溶的有机溶剂与去离子水的混合物。本发明制备得到的附着力促进剂,可以显著提高油墨的附着牢度,但是,相较于本申请而言,其所应用到的有机溶剂的种类较多,导致工艺较为复杂,并且其只针对油墨而言具有极佳的附着效果,相较于烤漆而言,其未必具有良好的附着效果。
发明内容
为了解决烤漆对底材的附着力效果较差,而影响产品的质量及生产进度,本发明公开了一种烤漆附着力促进剂及其合成方法,使得油漆对底材具有极好的附着力,同时,制作工艺简便,制作成本低廉。
一种烤漆附着力促进剂,主要由以下原料成分组成(按重量百分比):A组分(己二酸1524.7,三羟甲基丙烷1881,亚磷酸三苯酯10.7,催化剂1.5),B组分(丙二醇甲醚37.6,异丙醇745.7)。
一种烤漆附着力促进剂的合成方法,包括以下工艺步骤:
(1)将A组分物料投入放应釜中,开搅拌,并升温至140度左右出水;
(2)保温3小时后,检测酸值,加入酸值控制在70以下就可以降温;
(3)加入B组分(丙二醇甲醚37.6,异丙醇745.7),兑稀,即可。
本发明的优点是:原料的使用价格比较低廉,并且其施工工艺比较简便易行,因此生产效率较高,得到的附着力促进剂添加到烤漆中的用量一般为1-3%,能够烤漆对底材具有极佳的附着效果。
具体实施方式
为了解决烤漆对底材的附着力效果较差,而影响产品的质量及生产进度,本发明公开了一种烤漆附着力促进剂及其合成方法,使得油漆对底材具有极好的附着力,同时,制作工艺简便,制作成本低廉。
下面将对本发明中的技术方案进行清楚、完整地描述,显然,所描述的仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动的前提下所获得的所有其他实施例,都属于本发明保护的范围。
以下实施例中所用到的原料均为市售,在没有特殊说明的情况下,单位均为(kg):
实施例1
工艺如下:
(1)将A组分物料投入放应釜中,开搅拌,并升温至140度左右出水;
(2)保温3小时后,检测酸值,加入酸值控制在70以下就可以降温;
(3)加入B组分(丙二醇甲醚37.6,异丙醇745.7),兑稀,即可。
本实施例中所制备得到的附着力促进剂的固体份为80%,因此,在添加到烤漆中的用量一般为1-3%即可使得烤漆对底材具有极佳的附效果。
通过以上描述可知,本发明的优点在于:原料的使用价格比较低廉,并且其施工工艺比较简便易行,因此生产效率较高,得到的附着力促进剂添加到烤漆,能够烤漆对底材具有极佳的附着效果。
以上内容是结合具体的优选实施方式对本发明所作的进一步详细说明,不能认定本发明的具体实施只局限于这些说明。对于本发明所属技术领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干简单推演或替换,都应当视为属于本发明的保护范围。
Claims (2)
1.一种烤漆附着力促进剂,其特征在于,主要由以下原料成分组成(按重量百分比):A组分(己二酸1524.7,三羟甲基丙烷1881,亚磷酸三苯酯10.7,催化剂1.5),B组分(丙二醇甲醚37.6,异丙醇745.7)。
2.根据权利要求1所述的一种烤漆附着力促进剂的合成方法,其特征在于,包括以下工艺步骤:
(1)将A组分物料投入放应釜中,开搅拌,并升温至140度左右出水;
(2)保温3小时后,检测酸值,加入酸值控制在70以下就可以降温;
(3)加入B组分(丙二醇甲醚37.6,异丙醇745.7),兑稀,即可。