CN104310402A - 农业废弃生物质制备碳化硅纳米颗粒的方法 - Google Patents

农业废弃生物质制备碳化硅纳米颗粒的方法 Download PDF

Info

Publication number
CN104310402A
CN104310402A CN201410531944.1A CN201410531944A CN104310402A CN 104310402 A CN104310402 A CN 104310402A CN 201410531944 A CN201410531944 A CN 201410531944A CN 104310402 A CN104310402 A CN 104310402A
Authority
CN
China
Prior art keywords
temperature
silicon carbide
hours
degree
carbide nanoparticles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410531944.1A
Other languages
English (en)
Other versions
CN104310402B (zh
Inventor
王冬华
付新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Weinan Normal University
Original Assignee
Weinan Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Weinan Normal University filed Critical Weinan Normal University
Priority to CN201410531944.1A priority Critical patent/CN104310402B/zh
Publication of CN104310402A publication Critical patent/CN104310402A/zh
Application granted granted Critical
Publication of CN104310402B publication Critical patent/CN104310402B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种农业废弃生物质制备碳化硅纳米颗粒的方法，将1.5g硝酸钴溶于100ml无水乙醇中，完全溶解后加入50ml正硅酸乙酯。强力搅拌下，加入8ml草酸溶液。充分搅拌24小时后，加入36g玉米苞叶粉末，待混合均匀后，加入8ml六次甲基四胺。待溶胶凝固后，将其在100度下烘箱中干燥。所得干凝胶放入高温管式炉中，氩气气氛保护下，先以每分钟10度升温速率从室温升至1000度，然后以每分钟两度升至1300度，恒温7小时。冷却至室温后，取出样品，在700度下空气中煅烧3小时，再用盐酸和氢氟酸清洗，经洗涤、过滤、干燥，最终得到产物。本发明采用简单工艺能大规模制备小尺寸且分布均匀的碳化硅纳米颗粒。

Description

农业废弃生物质制备碳化硅纳米颗粒的方法
技术领域
本发明属于化学技术领域，具体为一种农业废弃生物质制备碳化硅纳米颗粒的方法。
背景技术
碳化硅纳米材料不仅具有好的力学性能，而且具有优异的光电特性、化学惰性和生物相容性等，因而在光学器件、生物医学、纳米电子和复合材料等方面有着广泛应用前景[2，3]。碳化硅纳米颗粒比表面大，粒径尺度小，力学、光电性能优异，因此常用于高频、大功率以及条件苛刻的环境中。因此，开发一种廉价制备小尺寸且分布均匀的碳化硅纳米颗粒的技术十分重要。
目前制备碳化硅纳米材料的主要方法有：化学气相沉积法、电弧放电法、加热蒸发法、溶胶凝胶和碳热还原法等，这些技术的主要缺点是原料价格较贵，工艺流程复杂，设备复杂等。本发明目的在于利用价格低廉的农业废弃生物质，采用采用简单工艺能大规模制备小尺寸且分布均匀的碳化硅纳米颗粒。
发明内容
为了解决现有技术中存在的问题，本发明提供一种农业废弃生物质制备碳化硅纳米颗粒的方法，利用农业废弃生物质，采用简单工艺能大规模制备小尺寸且分布均匀的碳化硅纳米颗粒。其技术方案为：
一种农业废弃生物质制备碳化硅纳米颗粒的方法，包括以下步骤：
将1.5g硝酸钴溶于100ml无水乙醇中，完全溶解后加入50ml正硅酸乙酯。强力搅拌下，加入8ml草酸溶液。充分搅拌24小时后，加入36g玉米苞叶粉末，待混合均匀后，加入8ml六次甲基四胺。待溶胶凝固后，将其在100度下烘箱中干燥。所得干凝胶放入高温管式炉中，氩气气氛保护下，先以每分钟10度升温速率从室温升至1000度，然后以每分钟两度升至1300度，恒温7小时。冷却至室温后，取出样品，在700度下空气中煅烧3小时，再用盐酸和氢氟酸清洗，经洗涤、过滤、干燥，最终得到产物。
与现有技术相比，本发明的有益效果为：
本发明可以充分利用农业废弃生物质，大大降低制备碳化硅纳米材料的生产成本；工艺较为简单，形貌尺寸可控。
具体实施方式
下面结合具体实施方式对本发明的技术方案作进一步说明。
一种农业废弃生物质制备碳化硅纳米颗粒的方法，包括以下步骤：将1.5g硝酸钴溶于100ml无水乙醇中，完全溶解后加入50ml正硅酸乙酯。强力搅拌下，加入8ml草酸溶液。充分搅拌24小时后，加入36g玉米苞叶粉末，待混合均匀后，加入8ml六次甲基四胺。待溶胶凝固后，将其在100度下烘箱中干燥。所得干凝胶放入高温管式炉中，氩气气氛保护下，先以每分钟10度升温速率从室温升至1000度，然后以每分钟两度升至1300度，恒温7小时。冷却至室温后，取出样品，在700度下空气中煅烧3小时，再用盐酸和氢氟酸清洗，经洗涤、过滤、干燥，最终得到产物。
以上所述，仅为本发明较佳的具体实施方式，本发明的保护范围不限于此，任何熟悉本技术领域的技术人员，在本发明披露的技术范围内，可显而易见地得到的技术方案的简单变换或等效替换均落入本发明的保护范围内。

Claims (1)

1.一种农业废弃生物质制备碳化硅纳米颗粒的方法，其特征在于，包括以下步骤：
将1.5g硝酸钴溶于100ml无水乙醇中，完全溶解后加入50ml正硅酸乙酯；强力搅拌下，加入8ml草酸溶液；充分搅拌24小时后，加入36g玉米苞叶粉末，待混合均匀后，加入8ml六次甲基四胺；待溶胶凝固后，将其在100度下烘箱中干燥；所得干凝胶放入高温管式炉中，氩气气氛保护下，先以每分钟10度升温速率从室温升至1000度，然后以每分钟两度升至1300度，恒温7小时；冷却至室温后，取出样品，在700度下空气中煅烧3小时，再用盐酸和氢氟酸清洗，经洗涤、过滤、干燥，最终得到产物。
CN201410531944.1A 2014-09-28 2014-09-28 农业废弃生物质制备碳化硅纳米颗粒的方法 Expired - Fee Related CN104310402B (zh)