CN104308934A - Method for manufacturing fraxinus chinensis rod furniture - Google Patents
Method for manufacturing fraxinus chinensis rod furniture Download PDFInfo
- Publication number
- CN104308934A CN104308934A CN201410489560.8A CN201410489560A CN104308934A CN 104308934 A CN104308934 A CN 104308934A CN 201410489560 A CN201410489560 A CN 201410489560A CN 104308934 A CN104308934 A CN 104308934A
- Authority
- CN
- China
- Prior art keywords
- chinese wax
- bar
- wax bar
- furniture
- pressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for manufacturing fraxinus chinensis rod furniture. The method comprises the following steps: 1, peeling off at high temperature; 2, selecting a material and adjusting; 3, performing cold pressing to prevent moth; 4, designing different types of furniture; 5, performing hot-pressing formation; 6, bending and polishing; 7, milling bars and pieces; 8, assembling the furniture. The method for manufacturing fraxinus chinensis rod furniture is simple in process, the time and the labor are reduced when the furniture is manufactured, particularly the bending formation process is simple and easy in forming when fraxinus chinensis rods are manufactured, and the production efficiency of furniture is greatly improved.
Description
Technical field
The present invention relates to a kind of preparation method of furniture, especially a kind of preparation method of white wax plant furniture.
Background technology
Fraxinus is in deciduous tree, and be one of economic tree of China, Chinese wax bar is then the young growth of Chinese ash, is the shrub utilizing Chinese ash to have the strong feature of the property sprouted and be trained.
The rounded solid material shape of Chinese wax bar, texture is straight, even structure, weight and hardness are even.Fibre length is longer, and basic density is 0.56g/m, and the basic density of c. faberii is 0.334g/m
3, Manchurian ash is 0.509g/m.The parallel-to-grain compressive strength of Chinese wax bar is moderate; Tensile strength parallel to grain is higher, higher than Manchurian ash by 7.3%, higher than linden by 12.1%; Bending strength is higher, higher than c. faberii by 37.2%; Bending property is good, also higher than the bending property of elm.
" Chinese wax bar " growth of one of " Ningling Triratna " to be conquered east in Henan former Ningling County, being a kind of Shrub populations very rare both at home and abroad, for checking winds and fixing drifting sand, preventing erosion.Chinese wax bar is in the Ningling County plantation history of existing more than 300 year.Current Ningling County has become maximum Chinese wax bar production base, the whole nation, and its cultivated area, more than 200,000 mu, passes through " protection of national geography famous special product " certification.Chinese wax bar is natural green plant overgrown with bushes, and its entire body is as white as polished jade, hard and not hard, soft and do not roll over, and shaft is flexible to 180 degree of not splittings, and pliability is strong, and self fibre density is high.Due to local unique soil property, water quality and geography and climate feature, in the environment not splitting of drying, indeformable at the environment of humidity, its elasticity, toughness are that other is any wooden incomparable.Chinese wax bar belongs to green, natural, environmental protection, uniqueness, rare Ningling special product, is the desirable natural material making furniture, understands nature and become golden yellow, also known as gold bar after Chinese wax bar contacts with air.
At present in Ningling County, Shangqiu, the processing and utilization of dialogue candlestick roughly divides four kinds: sports equipment, wushu utensil, Chinese wax bar frame-type furniture and Chinese wax bar weave, wherein outstanding with furniture.Only have the existing conventional machining process of dialogue candlestick to carry out deep investigation, just can proceed from the reality, find out white wax plant furniture Problems existing and limitation, thus go to solve, go to deal with problems by the modern concepts of industrial design for problem.Through the deep investigation to Ningling ALLRED handicraft Co., Ltd, understand processing technology and flow process that Chinese wax bar a few days ago makes white wax plant furniture, for research is afterwards laid a good foundation.
Current white wax plant furniture adopts machinery to add the processing mode of traditional-handwork, processing technology and program are very complicated, make one and common leisure chaise longue is needed 104 procedures, do not measure accurately in manufacturing process, mostly by experience and the sensation behaviour of processor, make not up to standardization, and time-consuming expense material of taking a lot of work, cannot mass production be carried out.Both be unfavorable for suitability for industrialized production like this, be also not easy to Product transport, dialogue candlestick exploit the overseas market bring unfavorable very greatly.
Summary of the invention
The invention provides a kind of preparation method of white wax plant furniture, solve existing white wax plant furniture complex manufacturing process, time-consuming expense material of taking a lot of work, cannot carry out the problems such as mass production.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A preparation method for white wax plant furniture, comprises the following steps:
The first step, high temperature are removed the peel: Chinese wax bar is put into steam boiler and carries out boiling, and steam steams Chinese wax bar thoroughly removes Lao Pi;
Second step, selection adjustment: choose thin head diameter reach 1.0-3.5 centimetre and length reach the peeling of 1 meter-3 meters after Chinese wax bar carry out straightening classification bundling;
3rd step, cold pressing mothproof: the Chinese wax bar accomplishing fluently bundle is put into tank of colding pressing, tank of colding pressing seals, at cistern, mothproofing agent is mixed up, water pump is squeezed into and is colded pressing in tank, pressure is 0.4-08MPa, and cold pressing 24-36 hour, then mothproofing agent is extracted out from tank of colding pressing, open tank of colding pressing, take out Chinese wax bar and carry out airing 24-36 hour;
4th step, design category: classified by Chinese wax according to drawing, then make the Chinese wax bar pole locomotive of classification the round bar that diameter is 1.0-3.5 centimetre;
5th step, hot pressing moulding: the Chinese wax bar that car is crossed is put into steam boiler, and steam steams, then while hot according to drawing moulding, cool to room temperature after moulding;
6th step, bending polishing: Chinese wax bar good for moulding is polished at sanding machine, makes Chinese wax bar smooth;
7th step, spoke car sheet: Chinese wax bar to be got on the bus slabbing at multiple blade saw, then polishes smooth;
8th step, assembled formation: grinded Chinese wax bar is formed according to drawing, obtains white wax plant furniture.
Further, a preferred embodiment of the present invention: in the described first step, boiling temperature is 100-130 DEG C, digestion time is 3-4h.
Further, a preferred embodiment of the present invention: the temperature of colding pressing in described second step is 10-30 DEG C.
Further, a preferred embodiment of the present invention: the boiling temperature in the 5th described step is 100-130 DEG C, and digestion time is 2-3h.
Furniture prepared by the present invention comprises chair, desk sofa, toy for children etc.
Beneficial effect of the present invention:
The preparation method technique of white wax plant furniture of the present invention is simple, and it is time saving and energy saving that furniture makes, and the bending moulding technique especially in Chinese wax bar makes is simple, moulding easy, drastically increases the production efficiency of furniture.
Traditional technique and advanced technology combine by inventor, flexible for Chinese wax bar and folding constantly, have toughness and indeformable feature, dissolve in technological development, courageously take the way that high temperature is stifling, thoroughly kill dark moth of hiding, choose carefully, through remove the peel, steaming, boil, toast, the series of processes such as moulding makes household, office, leisure, the handicraft of open air and the art work, both with practical value, there is ornamental value again.
Furniture of the present invention adopts Chinese wax bar as raw material, and Chinese wax bar skin is natural Chinese medicine also known as " bark of ash ", and Long-Time Service Chinese wax bar product can clear away heart-fire improving eyesight, plays the effect of health care.
Hot pressing step of overall modelling in the present invention adopts and Chinese wax bar is fixed on steel drum outer ring hasp fastens, and can make full use of material, not waste, and avoids and Chinese wax bar is nailed moulding on timber in the past, waste time and energy, the problems such as waste timber.
Detailed description of the invention
Below in conjunction with specific embodiment, be clearly and completely described technical scheme of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
A preparation method for white wax plant furniture, comprises the following steps:
The first step, high temperature are removed the peel: Ningling Chinese wax bar is put into steam boiler and carries out boiling, and steam steams Chinese wax bar thoroughly and removes out Lao Pi, and boiling temperature is 100-130 DEG C, and digestion time is 3h;
Second step, selection adjustment: choose thin head diameter reach 1.0-3.5 centimetre and length reach the peeling of 1-3 rice after Chinese wax bar carry out straightening classification bundling;
3rd step, cold pressing mothproof: the Chinese wax bar accomplishing fluently bundle is put into tank of colding pressing, tank of colding pressing seals, at cistern, mothproofing agent is mixed up, water pump is squeezed into and is colded pressing in tank, and pressure is 0.4-08MPa, colds pressing 24 hours, then mothproofing agent is extracted out from tank of colding pressing, open tank of colding pressing, take out Chinese wax bar and carry out airing 24 hours, temperature of colding pressing is 10 DEG C;
4th step, design category: classified by Chinese wax according to drawing, then make the Chinese wax bar pole locomotive of classification the round bar that diameter is 1.0-3.5 centimetre;
5th step, hot pressing moulding: the Chinese wax bar that car is crossed is put into steam boiler, and steam steams, then while hot according to drawing moulding, cool to room temperature after moulding, boiling temperature is 100-130 DEG C, and digestion time is 2h;
6th step, bending polishing: Chinese wax bar good for moulding is polished at sanding machine, makes Chinese wax bar smooth;
7th step, spoke car sheet: Chinese wax bar to be got on the bus slabbing at multiple blade saw, then polishes smooth;
8th step, assembled formation: grinded Chinese wax bar is formed according to drawing, obtains white wax plant furniture.
Chinese wax bar is fixed on steel drum outer ring hasp and fastens by the hot pressing step of overall modelling employing in the present invention.
Embodiment 2
A preparation method for white wax plant furniture, comprises the following steps:
The first step, high temperature are removed the peel: Ningling Chinese wax bar is put into steam boiler and carries out boiling, and steam steams Chinese wax bar thoroughly and removes out Lao Pi, and boiling temperature is 100-130 DEG C, and digestion time is 4h;
Second step, selection adjustment: choose thin head diameter reach 1.0-3.5 centimetre and length reach the peeling of 1-3 rice after Chinese wax bar carry out straightening classification bundling;
3rd step, cold pressing mothproof: the Chinese wax bar accomplishing fluently bundle is put into tank of colding pressing, tank of colding pressing seals, at cistern, mothproofing agent is mixed up, water pump is squeezed into and is colded pressing in tank, and pressure is 0.4-08MPa, colds pressing 36 hours, then mothproofing agent is extracted out from tank of colding pressing, open tank of colding pressing, take out Chinese wax bar and carry out airing 36 hours, temperature of colding pressing is 30 DEG C;
4th step, design category: classified by Chinese wax according to drawing, then make the Chinese wax bar pole locomotive of classification the round bar that diameter is 1.0-3.5 centimetre;
5th step, hot pressing moulding: the Chinese wax bar that car is crossed is put into steam boiler, and steam steams, then while hot according to drawing moulding, cool to room temperature after moulding, boiling temperature is 100-130 DEG C, and digestion time is 3h;
6th step, bending polishing: Chinese wax bar good for moulding is polished at sanding machine, makes Chinese wax bar smooth;
7th step, spoke car sheet: Chinese wax bar to be got on the bus slabbing at multiple blade saw, then polishes smooth;
8th step, assembled formation: grinded Chinese wax bar is formed according to drawing, obtains white wax plant furniture.
Chinese wax bar is fixed on steel drum outer ring hasp and fastens by the hot pressing step of overall modelling employing in the present invention.
Embodiment 3
A preparation method for white wax plant furniture, comprises the following steps:
The first step, high temperature are removed the peel: Ningling Chinese wax bar is put into steam boiler and carries out boiling, and steam steams Chinese wax bar thoroughly and removes out Lao Pi, and boiling temperature is 100-130 DEG C, and digestion time is 3.5h;
Second step, selection adjustment: choose thin head diameter reach 1.0-3.5 centimetre and length reach the peeling of 1-3 rice after Chinese wax bar carry out straightening classification bundling;
3rd step, cold pressing mothproof: the Chinese wax bar accomplishing fluently bundle is put into tank of colding pressing, tank of colding pressing seals, at cistern, mothproofing agent is mixed up, water pump is squeezed into and is colded pressing in tank, and pressure is 0.4-08MPa, colds pressing 30 hours, then mothproofing agent is extracted out from tank of colding pressing, open tank of colding pressing, take out Chinese wax bar and carry out airing 28 hours, temperature of colding pressing is 20 DEG C;
4th step, design category: classified by Chinese wax according to drawing, then make the Chinese wax bar pole locomotive of classification the round bar that diameter is 1.0-3.5;
5th step, hot pressing moulding: the Chinese wax bar that car is crossed is put into steam boiler, and steam steams, then while hot according to drawing moulding, cool to room temperature after moulding, boiling temperature is 100-130 DEG C, and digestion time is 2.5h;
6th step, bending polishing: Chinese wax bar good for moulding is polished at sanding machine, makes Chinese wax bar smooth;
7th step, spoke car sheet: Chinese wax bar to be got on the bus slabbing at multiple blade saw, then polishes smooth;
8th step, assembled formation: grinded Chinese wax bar is formed according to drawing, obtains white wax plant furniture.
Chinese wax bar is fixed on steel drum outer ring hasp and fastens by the hot pressing step of overall modelling employing in the present invention.
Embodiment 4
A preparation method for white wax plant furniture, comprises the following steps:
The first step, high temperature are removed the peel: Chinese wax bar is put into steam boiler and carries out boiling, and steam steams Chinese wax bar thoroughly and removes out Lao Pi, and boiling temperature is 100-130 DEG C, and digestion time is 1h;
Second step, selection adjustment: choose thin head diameter reach 1.0-3.5 centimetre and length reach the peeling of 1-3 rice after Chinese wax bar carry out straightening classification bundling;
3rd step, cold pressing mothproof: the Chinese wax bar accomplishing fluently bundle is put into tank of colding pressing, tank of colding pressing seals, mixed up by mothproofing agent at cistern, water pump is squeezed into and is colded pressing in tank, and pressure is 0.4-08MPa, cold pressing 36 hours, then mothproofing agent is extracted out from tank of colding pressing, open tank of colding pressing, take out Chinese wax bar and carry out airing 30 hours, according to seasonal variations adjustment, temperature of colding pressing is 25 DEG C;
4th step, design category: classified by Chinese wax according to drawing, then make the Chinese wax bar pole locomotive of classification the round bar that diameter is 1.0-3.5 centimetre;
5th step, hot pressing moulding: the Chinese wax bar that car is crossed is put into steam boiler, and steam steams, then while hot according to drawing moulding, cool to room temperature after moulding, boiling temperature is 100-130 DEG C, and digestion time is 0.5h;
6th step, bending polishing: Chinese wax bar good for moulding is polished at sanding machine, makes Chinese wax bar smooth;
7th step, spoke car sheet: Chinese wax bar to be got on the bus slabbing at multiple blade saw, then polishes smooth;
8th step, assembled formation: grinded Chinese wax bar is formed according to drawing, obtains white wax plant furniture.
Chinese wax bar is fixed on steel drum outer ring hasp and fastens by the hot pressing step of overall modelling employing in the present invention.
Mothproofing agent in the present invention is any one commercially available wood treated with maring bore preservative agent or its mixture, or wood treated with maring bore preservative anticorrisive agent.
Certain hot pressing step of overall modelling also can take additive method, is not limited to the method in the present invention.
Utilize method Hepplewhite of the present invention through a large amount of practice, mothproof favorable anti-corrosion effect, handsome in appearance, appearance is bright and clean.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (4)
1. a preparation method for white wax plant furniture, is characterized in that, comprises the following steps:
The first step, high temperature are removed the peel: Chinese wax bar is put into steam boiler and carries out boiling, and steam steams Chinese wax bar thoroughly removes Lao Pi;
Second step, selection adjustment: choose thin head diameter reach 1.0-3.5 centimetre and length reach the peeling of 1.0 meters-3 meters after Chinese wax bar carry out straightening classification bundling;
3rd step, cold pressing mothproof: the Chinese wax bar accomplishing fluently bundle is put into tank of colding pressing, tank of colding pressing seals, at cistern, mothproofing agent is mixed up, water pump is squeezed into and is colded pressing in tank, pressure is 0.4-08MPa, and cold pressing 24-36 hour, then mothproofing agent is extracted out from tank of colding pressing, open tank of colding pressing, take out Chinese wax bar and carry out airing 24-36 hour; Adjust according to seasonal climate.
4th step, design category: classified by Chinese wax according to drawing, then make the Chinese wax bar pole locomotive of classification the round bar that diameter is 1.0-3.5 centimetre;
5th step, hot pressing moulding: the Chinese wax bar that car is crossed is put into steam boiler, and steam steams, then while hot according to drawing moulding, cool to room temperature after moulding;
6th step, bending polishing: Chinese wax bar good for moulding is polished at sanding machine, makes Chinese wax bar smooth;
7th step, spoke car sheet: Chinese wax bar to be got on the bus slabbing at multiple blade saw, then polishes smooth;
8th step, assembled formation: grinded Chinese wax bar is formed according to drawing, obtains white wax plant furniture.
2. the preparation method of a kind of white wax plant furniture according to claim 1, is characterized in that: in the described first step, boiling temperature is 100-130 DEG C, and digestion time is 3-4h.
3. the preparation method of a kind of white wax plant furniture according to claim 1, is characterized in that: the temperature of colding pressing in described second step is 10-30 DEG C.
4. the preparation method of a kind of white wax plant furniture according to claim 1, is characterized in that: the boiling temperature in the 5th described step is 100-130 DEG C, and digestion time is 2-3h.