CN104293218A - 一种板材用酚醛树脂胶粘剂 - Google Patents
一种板材用酚醛树脂胶粘剂 Download PDFInfo
- Publication number
- CN104293218A CN104293218A CN201410546783.3A CN201410546783A CN104293218A CN 104293218 A CN104293218 A CN 104293218A CN 201410546783 A CN201410546783 A CN 201410546783A CN 104293218 A CN104293218 A CN 104293218A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- weight
- ethyl acetate
- phenol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种板材用酚醛树脂胶粘剂,其是由下述重量份的原料制得:其是由A料和B料按照5∶2-2.1的比例混匀制得:所述的A料由下述重量份的原料制得:乙酸乙酯50-60,聚酰胺树脂20-32、环氧树脂3-5、聚苯醚0.1-0.2、月桂酰胺丙基羟磺基甜菜碱1-2、富马酸1-2、聚乙二醇0.1-0.2;所述的B料由下述重量份的原料制得:酚醛树脂10-20、1,4-丁二醇1-2、松香3-5、硬脂酰胺1-2、甲基葡萄糖聚氧乙烯醚2-3、三壬基苯基亚磷酸酯1-2、硫代硫酸钠0.1-0.2、达玛树脂2-4。
Description
技术领域
本发明属粘结剂领域,尤其涉及一种板材用酚醛树脂胶粘剂。
背景技术
用于木材胶接和木制品制造的胶黏剂。具有应力均匀、接缝弥合、胶接强度高、耐水性好能简化制品结构及实现操作机械化和自动化等特点。主要有皮胶、骨胶、酪素胶、聚醋酸乙烯酯胶黏剂、酚醛树脂胶黏剂、脲醛树脂胶粘剂、环氧树脂胶黏剂和氯丁橡胶胶黏剂等。用于板材的拼接装配和端面包边;门窗家具的榫孔胶接;地板、天棚及壁的内部装修;人造板、胶合板、夹心板、木塑复合板及木合金板等的制造;表面装饰板的黏贴等。
发明内容
本发明的目的是提供一种板材用酚醛树脂胶粘剂。
为了实现上述目的本发明采用如下技术方案:
一种板材用酚醛树脂胶粘剂,其特征在于,其是由下述重量份的原料制得:其是由A料和B料按照5:2-2.1的比例混匀制得:
所述的A料由下述重量份的原料制得:乙酸乙酯50-60,聚酰胺树脂20-32、环氧树脂3-5、聚苯醚0.1-0.2、月桂酰胺丙基羟磺基甜菜碱1-2、富马酸1-2、聚乙二醇0.1-0.2;
所述的B料由下述重量份的原料制得:酚醛树脂10-20、1,4-丁二醇1-2、松香3-5、硬脂酰胺1-2、甲基葡萄糖聚氧乙烯醚2-3、三壬基苯基亚磷酸酯1-2、硫代硫酸钠0.1-0.2、达玛树脂2-4。
所述的一种板材用酚醛树脂胶粘剂,其特征在于:制备方法包括以下步骤:
(1)按重量份取A料除乙酸乙酯各原料混匀后,于180-190℃下捏合20-30min,取出冷却后加入乙酸乙酯混匀后,得A料;
(2)按重量份取B料各原料混匀后,于170-180℃下捏合30-40min,取出冷却得B料;
(3)按重量份将B料与A料混匀后,于40-50℃下搅拌20-30min,取出冷却即得。
本发明的有益效果:
本发明配方合理,所得原料粘结性好,使用寿命长,不容易开裂。
具体实施方式、
一种板材用酚醛树脂胶粘剂,其是由下述重量kg的原料制得:其是由A料和B料按照5:2的比例混匀制得:
所述的A料由下述重量kg的原料制得:乙酸乙酯50,聚酰胺树脂20、环氧树脂5、聚苯醚0.2、月桂酰胺丙基羟磺基甜菜碱1、富马酸1、聚乙二醇0.2;
所述的B料由下述重量kg的原料制得:酚醛树脂20、1,4-丁二醇2、松香3、硬脂酰胺2、甲基葡萄糖聚氧乙烯醚2、三壬基苯基亚磷酸酯2、硫代硫酸钠0.2、达玛树脂4。
所述的一种板材用酚醛树脂胶粘剂,制备方法包括以下步骤:
(1)按重量份取A料除乙酸乙酯各原料混匀后,于182℃下捏合30min,取出冷却后加入乙酸乙酯混匀后,得A料;
(2)按重量份取B料各原料混匀后,于173℃下捏合40min,取出冷却得B料;
(3)按重量份将B料与A料混匀后,于40℃下搅拌30min,取出冷却即得。
将所得胶黏剂按涂胶量70g/m2涂布到纤维板上,然后再贴上厚度为0.3mm橡木薄木,在1.1Mpa作用下,经110℃热压成板材成品。成品中贴面板材的表面胶合强度为1.0MPa。
Claims (2)
1.一种板材用酚醛树脂胶粘剂,其特征在于,其是由下述重量份的原料制得:其是由A料和B料按照5:2-2.1的比例混匀制得:
所述的A料由下述重量份的原料制得:乙酸乙酯50-60,聚酰胺树脂20-32、环氧树脂3-5、聚苯醚0.1-0.2、月桂酰胺丙基羟磺基甜菜碱1-2、富马酸1-2、聚乙二醇0.1-0.2;
所述的B料由下述重量份的原料制得:酚醛树脂10-20、1,4-丁二醇1-2、松香3-5、硬脂酰胺1-2、甲基葡萄糖聚氧乙烯醚2-3、三壬基苯基亚磷酸酯1-2、硫代硫酸钠0.1-0.2、达玛树脂2-4。
2.根据权利要求1所述的一种板材用酚醛树脂胶粘剂,其特征在于:制备方法包括以下步骤:
(1)按重量份取A料除乙酸乙酯各原料混匀后,于180-190℃下捏合20-30min,取出冷却后加入乙酸乙酯混匀后,得A料;
(2)按重量份取B料各原料混匀后,于170-180℃下捏合30-40min,取出冷却得B料;
(3)按重量份将B料与A料混匀后,于40-50℃下搅拌20-30min,取出冷却即得。