CN104277647A - Water-resistant magnesite waterproof paint - Google Patents
Water-resistant magnesite waterproof paint Download PDFInfo
- Publication number
- CN104277647A CN104277647A CN201410451810.9A CN201410451810A CN104277647A CN 104277647 A CN104277647 A CN 104277647A CN 201410451810 A CN201410451810 A CN 201410451810A CN 104277647 A CN104277647 A CN 104277647A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- waterproof paint
- deionized water
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-resistant magnesite waterproof paint which is prepared from the following raw materials in parts by weight: 70-80 parts of silicone-acrylic emulsion, 2-4 parts of fused magnesite, 1-2 parts of sodium carboxymethyl starch, 2-3 parts of calcium fluoride, 2-3 polyoxypropylene diol, 1-1.5 parts of acrylic acid, 1-2 parts of fatty acid acetal amide, 3-4 parts of dioctyl sebacate, 0.4-0.7 part of tributyltritin chloride, 1-2 parts of 2-thiobenzimidazole, 1-1.6 parts of trimethylolpropane, 0.1-0.3 part of aluminum powder, 10-13 parts of kieselguhr, 5-7 parts of film formation assistant and 5-20 parts of deionized water. The fused magnesite added into the waterproof paint has favorable water-resistant effect, and can enhance the permeation resistance of the coating; and the coated film has the advantages of favorable flexibility, high water resistance and enduring protection for the substrate.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of water resistant magnesia waterproof paint.
Background technology
Along with development and the refinement of domestic coating industry, market is also more and more outstanding to the requirement with special functional coating, wherein anti-aging, water-fast, acid-alkali-corrosive-resisting, the performance requriements such as fire-retardant are more increased, existing water-proof material protect light, tint retention poor, not ageing-resistant, easy to crack, easily turn yellow, and have to human body, also there is certain harm, the feature of environmental protection is poor, therefore in order to meet the requirement of every profession and trade to waterproof paint, production high-performance, widely used waterproof paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of water resistant magnesia waterproof paint.
The present invention is achieved by the following technical solutions:
A kind of water resistant magnesia waterproof paint, it is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 70-80, electrosmelted magnesite clinker 2-4, sodium starch glycolate 1-2, Calcium Fluoride (Fluorspan) 2-3, polyoxypropyleneglycol 2-3, vinylformic acid 1-1.5, fatty diglycollic amide 1-2, dioctyl sebacate 3-4, tributyl tin trichloride 0.4-0.7,2-thiol group benzimidazolyl 1-2, TriMethylolPropane(TMP) 1-1.6, aluminium powder 0.1-0.3, diatomite 10-13, film coalescence aid 5-7, deionized water 5-20;
Described film coalescence aid is made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 30-40, Aloe gel 2-3,10,10'-oxos two phenoxazine arsenic 0.2-0.3, sal enixum 1-2, short and long-chain acyl triglyceride molecules 2-4, trimethyl benzyl ammonia chloride 1-2, tetramethylolmethane 2-3, deionized water 60-70;
Short and long-chain acyl triglyceride molecules is mixed with tetramethylolmethane, adds the 30-40% of above-mentioned deionized water weight, at 70-75 DEG C, be uniformly mixed 4-6 minute, stir, obtain lime set;
Trimethyl benzyl ammonia chloride is joined in remaining deionized water, above-mentioned lime set, Aloe gel is added after stirring, 5-7 minute is uniformly mixed at 30-40 DEG C, add 10,10'-oxo two phenoxazine arsenic, sal enixum, be stirred to normal temperature, adds each raw material of residue, 500-600 rev/min of dispersed with stirring 20-30 minute, obtains described film coalescence aid.
A preparation method for water resistant magnesia waterproof paint, comprises the following steps:
By Calcium Fluoride (Fluorspan), aluminium powder, diatomite mixing and ball milling evenly, add dioctyl sebacate, at 60-70 DEG C, be uniformly mixed 3-5 minute, add deionized water, sodium starch glycolate, 50-70 rev/min of dispersed with stirring 10-20 minute;
By electrosmelted magnesite clinker, vinylformic acid, polyoxypropyleneglycol mixing, heating raised temperature is 50-60 DEG C, adds TriMethylolPropane(TMP), 70-100 rev/min of dispersed with stirring 5-10 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1100 rev/min of dispersed with stirring 20-30 minute, obtains described water resistant magnesia waterproof paint.
Advantage of the present invention is:
The electrosmelted magnesite clinker that waterproof paint of the present invention adds has good water resistant effect, can strengthen the leakage resistance of coating, and the snappiness of film is good, and water-repellancy is strong, lasting to the protectiveness of base material.
Embodiment
Embodiment 1
A kind of water resistant magnesia waterproof paint, it is made up of the raw material of following weight parts (kilogram):
Organosilicon crylic acid latex 80, electrosmelted magnesite clinker 2, sodium starch glycolate 2, Calcium Fluoride (Fluorspan) 3, polyoxypropyleneglycol 2, vinylformic acid 1.5, fatty diglycollic amide 1, dioctyl sebacate 4, tributyl tin trichloride 0.7,2-thiol group benzimidazolyl 2, TriMethylolPropane(TMP) 1.6, aluminium powder 0.3, diatomite 13, film coalescence aid 5, deionized water 20;
Described film coalescence aid is made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 40, Aloe gel 2,10,10'-oxo two phenoxazine arsenic 0.3, sal enixum 1-2, short and long-chain acyl triglyceride molecules 4, trimethyl benzyl ammonia chloride 2, tetramethylolmethane 2, deionized water 70;
Short and long-chain acyl triglyceride molecules is mixed with tetramethylolmethane, adds 40% of above-mentioned deionized water weight, at 75 DEG C, be uniformly mixed 4 minutes, stir, obtain lime set;
Trimethyl benzyl ammonia chloride is joined in remaining deionized water, above-mentioned lime set, Aloe gel is added after stirring, 7 minutes are uniformly mixed at 30 DEG C, add 10,10'-oxo two phenoxazine arsenic, sal enixum, be stirred to normal temperature, adds each raw material of residue, 600 revs/min of dispersed with stirring 20-30 minute, obtain described film coalescence aid.
A preparation method for water resistant magnesia waterproof paint, comprises the following steps:
Calcium Fluoride (Fluorspan), aluminium powder, diatomite mixing and ball milling is even, add dioctyl sebacate, at 70 DEG C, be uniformly mixed 5 minutes, add deionized water, sodium starch glycolate, 70 revs/min of dispersed with stirring 20 minutes;
By electrosmelted magnesite clinker, vinylformic acid, polyoxypropyleneglycol mixing, heating raised temperature is 60 DEG C, adds TriMethylolPropane(TMP), 100 revs/min of dispersed with stirring 10 minutes;
Mixed with each raw material of residue by each raw material after above-mentioned process, 1100 revs/min of dispersed with stirring 30 minutes, obtain described water resistant magnesia waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. a water resistant magnesia waterproof paint, is characterized in that what it was made up of the raw material of following weight parts:
Organosilicon crylic acid latex 70-80, electrosmelted magnesite clinker 2-4, sodium starch glycolate 1-2, Calcium Fluoride (Fluorspan) 2-3, polyoxypropyleneglycol 2-3, vinylformic acid 1-1.5, fatty diglycollic amide 1-2, dioctyl sebacate 3-4, tributyl tin trichloride 0.4-0.7,2-thiol group benzimidazolyl 1-2, TriMethylolPropane(TMP) 1-1.6, aluminium powder 0.1-0.3, diatomite 10-13, film coalescence aid 5-7, deionized water 5-20;
Described film coalescence aid is made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 30-40, Aloe gel 2-3,10,10'-oxos two phenoxazine arsenic 0.2-0.3, sal enixum 1-2, short and long-chain acyl triglyceride molecules 2-4, trimethyl benzyl ammonia chloride 1-2, tetramethylolmethane 2-3, deionized water 60-70;
Short and long-chain acyl triglyceride molecules is mixed with tetramethylolmethane, adds the 30-40% of above-mentioned deionized water weight, at 70-75 DEG C, be uniformly mixed 4-6 minute, stir, obtain lime set;
Trimethyl benzyl ammonia chloride is joined in remaining deionized water, above-mentioned lime set, Aloe gel is added after stirring, 5-7 minute is uniformly mixed at 30-40 DEG C, add 10,10'-oxo two phenoxazine arsenic, sal enixum, be stirred to normal temperature, adds each raw material of residue, 500-600 rev/min of dispersed with stirring 20-30 minute, obtains described film coalescence aid.
2. a preparation method for water resistant magnesia waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
By Calcium Fluoride (Fluorspan), aluminium powder, diatomite mixing and ball milling evenly, add dioctyl sebacate, at 60-70 DEG C, be uniformly mixed 3-5 minute, add deionized water, sodium starch glycolate, 50-70 rev/min of dispersed with stirring 10-20 minute;
By electrosmelted magnesite clinker, vinylformic acid, polyoxypropyleneglycol mixing, heating raised temperature is 50-60 DEG C, adds TriMethylolPropane(TMP), 70-100 rev/min of dispersed with stirring 5-10 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1100 rev/min of dispersed with stirring 20-30 minute, obtains described water resistant magnesia waterproof paint.