CN104263032A - Waterproof paint for exterior wall decoration - Google Patents
Waterproof paint for exterior wall decoration Download PDFInfo
- Publication number
- CN104263032A CN104263032A CN201410451990.0A CN201410451990A CN104263032A CN 104263032 A CN104263032 A CN 104263032A CN 201410451990 A CN201410451990 A CN 201410451990A CN 104263032 A CN104263032 A CN 104263032A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof paint
- stirring
- raw material
- exterior wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses waterproof paint for exterior wall decoration. The waterproof paint is prepared from the following raw materials in parts by weight: 72-80 parts of silicone-acrylic emulsion, 1-2 parts of triallyl isocyanurate, 1-2 parts of guanidine sulfamate, 1-2 parts of diacetone alcohol, 2-3 parts of ammonium octamolybdate, 10-13 parts of expanded perlite, 3-4 parts of magnesium carbonate, 1-2 parts of 1,4-butanediol dimethacrylate, 0.1-0.2 part of dibasic lead phosphate, 1-2 parts of phosphite ester, 0.7-1 part of hydrogenated castor oil, 0.1-0.4 part of cuprous chloride, 1-2 parts of polyacrylamide, 4-6 parts of a coalescing agent and 12-20 parts of deionized water. The waterproof paint has a good decoration effect, is convenient to use, and has very high adhesion, water resistance and waterproofing property; meanwhile, a film cannot easily crack, has good seepage resistance and scratch resistance, does not generate harmful volatile substances, and is safe and environmentally friendly.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of decoration of exterior wall waterproof paint.
Background technology
Along with development and the refinement of domestic coating industry, market is also more and more outstanding to the requirement with special functional coating, wherein anti-aging, water-fast, acid-alkali-corrosive-resisting, the performance requriements such as fire-retardant are more increased, light protected by existing water-proof material, tint retention is poor, not decoration of exterior wall, easy to crack, easily turn yellow, and have to human body, also there is certain harm, the feature of environmental protection is poor, therefore in order to meet the requirement of every profession and trade to waterproof paint, production high-performance, widely used waterproof paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of decoration of exterior wall waterproof paint.
The present invention is achieved by the following technical solutions:
A kind of decoration of exterior wall waterproof paint, it is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 72-80, cyanacrylate 1-2, Guanidine Sulfamate 99 1-2, diacetone alcohol 1-2, ammonium octamolybdate 2-3, pearlstone 10-13, magnesiumcarbonate 3-4, dimethacrylate BDO ester 1-2, dibasic lead phosphite 0.1-0.2, phosphorous acid ester 1-2, hydrogenated castor oil 0.7-1, cuprous chloride 0.1-0.4, polyacrylamide 1-2, film coalescence aid 4-6, deionized water 12-20;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 40-46, oxystearic acid 2-3, alpha-bromo-cinnamaldehyde 0.4-1, plant sterol 1-2, calcium lactate 2-3, clorafin 2-3, ammonium polyphosphate 0.6-1, Xylo-Mucine 0.3-1, deionized water 70-80;
By ammonium polyphosphate, calcium lactate mixing, ball milling is even, adds oxystearic acid, is uniformly mixed 2-3 minute, obtains Preblend at 50-60 DEG C;
Xylo-Mucine is joined in above-mentioned deionized water, Terpineol 350, plant sterol, alpha-bromo-cinnamaldehyde is added after stirring, 10-20 minute is uniformly mixed at 40-50 DEG C, add above-mentioned Preblend, be stirred to normal temperature, add each raw material of residue, 300-400 rev/min of dispersed with stirring 30-40 minute, obtains described film coalescence aid.
A preparation method for decoration of exterior wall waterproof paint, is characterized in that comprising the following steps:
By pearlstone, ammonium octamolybdate mixing, ball milling is even, adds polyacrylamide, joins in deionized water, add cyanacrylate after stirring, 70-80 rev/min of dispersed with stirring 3-5 minute;
Guanidine Sulfamate 99 is mixed with dimethacrylate BDO ester, hydrogenated castor oil, adds magnesiumcarbonate after stirring, stir;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1100 rev/min of dispersed with stirring 20-30 minute, obtains described decoration of exterior wall waterproof paint.
Advantage of the present invention is:
Waterproof paint good decorating effect of the present invention, easy to use, have very high cementability, water tolerance and water-repellancy, film is not easy to crack simultaneously, anti-leakage resistance to marring is good, does not have unwanted volatile matter composition, safety and environmental protection.
Embodiment
Embodiment 1
A kind of decoration of exterior wall waterproof paint, it is made up of the raw material of following weight parts (kilogram):
Organosilicon crylic acid latex 80, cyanacrylate 2, Guanidine Sulfamate 99 1, diacetone alcohol 2, ammonium octamolybdate 2, pearlstone 13, magnesiumcarbonate 4, dimethacrylate BDO ester 1, dibasic lead phosphite 0.2, phosphorous acid ester 1, hydrogenated castor oil 0.7, cuprous chloride 0.4, polyacrylamide 2, film coalescence aid 4, deionized water 20;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 46, oxystearic acid 2, alpha-bromo-cinnamaldehyde 0.4, plant sterol 2, calcium lactate 3, clorafin 3, ammonium polyphosphate 0.6, Xylo-Mucine 0.3, deionized water 80;
By ammonium polyphosphate, calcium lactate mixing, ball milling is even, adds oxystearic acid, is uniformly mixed 3 minutes, obtains Preblend at 60 DEG C;
Xylo-Mucine is joined in above-mentioned deionized water, Terpineol 350, plant sterol, alpha-bromo-cinnamaldehyde is added after stirring, 20 minutes are uniformly mixed at 50 DEG C, add above-mentioned Preblend, be stirred to normal temperature, add each raw material of residue, 400 revs/min of dispersed with stirring 40 minutes, obtain described film coalescence aid.
A preparation method for decoration of exterior wall waterproof paint, is characterized in that comprising the following steps:
By pearlstone, ammonium octamolybdate mixing, ball milling is even, adds polyacrylamide, joins in deionized water, add cyanacrylate after stirring, 80 revs/min of dispersed with stirring 3 minutes;
Guanidine Sulfamate 99 is mixed with dimethacrylate BDO ester, hydrogenated castor oil, adds magnesiumcarbonate after stirring, stir;
Mixed with each raw material of residue by each raw material after above-mentioned process, 1100 revs/min of dispersed with stirring 30 minutes, obtain described decoration of exterior wall waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. a decoration of exterior wall waterproof paint, is characterized in that what it was made up of the raw material of following weight parts:
Organosilicon crylic acid latex 72-80, cyanacrylate 1-2, Guanidine Sulfamate 99 1-2, diacetone alcohol 1-2, ammonium octamolybdate 2-3, pearlstone 10-13, magnesiumcarbonate 3-4, dimethacrylate BDO ester 1-2, dibasic lead phosphite 0.1-0.2, phosphorous acid ester 1-2, hydrogenated castor oil 0.7-1, cuprous chloride 0.1-0.4, polyacrylamide 1-2, film coalescence aid 4-6, deionized water 12-20;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 40-46, oxystearic acid 2-3, alpha-bromo-cinnamaldehyde 0.4-1, plant sterol 1-2, calcium lactate 2-3, clorafin 2-3, ammonium polyphosphate 0.6-1, Xylo-Mucine 0.3-1, deionized water 70-80;
By ammonium polyphosphate, calcium lactate mixing, ball milling is even, adds oxystearic acid, is uniformly mixed 2-3 minute, obtains Preblend at 50-60 DEG C;
Xylo-Mucine is joined in above-mentioned deionized water, Terpineol 350, plant sterol, alpha-bromo-cinnamaldehyde is added after stirring, 10-20 minute is uniformly mixed at 40-50 DEG C, add above-mentioned Preblend, be stirred to normal temperature, add each raw material of residue, 300-400 rev/min of dispersed with stirring 30-40 minute, obtains described film coalescence aid.
2. a preparation method for decoration of exterior wall waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
By pearlstone, ammonium octamolybdate mixing, ball milling is even, adds polyacrylamide, joins in deionized water, add cyanacrylate after stirring, 70-80 rev/min of dispersed with stirring 3-5 minute;
Guanidine Sulfamate 99 is mixed with dimethacrylate BDO ester, hydrogenated castor oil, adds magnesiumcarbonate after stirring, stir;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1100 rev/min of dispersed with stirring 20-30 minute, obtains described decoration of exterior wall waterproof paint.