CN104263168A - Water-in-water multicolor paint and preparation method thereof - Google Patents
Water-in-water multicolor paint and preparation method thereof Download PDFInfo
- Publication number
- CN104263168A CN104263168A CN201410339831.1A CN201410339831A CN104263168A CN 104263168 A CN104263168 A CN 104263168A CN 201410339831 A CN201410339831 A CN 201410339831A CN 104263168 A CN104263168 A CN 104263168A
- Authority
- CN
- China
- Prior art keywords
- water
- colorful
- powder
- rotating speed
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-in-water multicolor paint and a preparation method thereof. The water-in-water multicolor paint is prepared from a protective glue solution including 2-3 parts of sodium pyrophosphate, 1.5-2.5 parts of sodium carboxymethyl starch, 1-2 parts of hydroxypropyl xanthan gum, 20-30 parts of multicolor protective glue RT-1 and 450-500 parts of water; a basic paint; and externally-coated water. The multicolor paint provided by the invention has high weather resistance, washing resistance, acid rain resistance, waterproofness and self-cleaning capacity, is highly cost-effective and is relatively light. A service life of the multicolor paint can reach over 10 years; and the multicolor paint is water-based, environment-friendly, energy-saving and non-toxic.
Description
Technical field
The present invention relates to a kind of water-water multi-color lacquer and preparation method thereof, belong to building coating technical field.
Background technology
Water-water multi-color lacquer is a kind of artificial granite, beautifies the water-borne coatings of building wall.The academic name of water-water multi-color lacquer is called liquid grouan.Being commonly called as in general industry is water-water multi-color lacquer.Refine the jellied hydrate colour particle of parcel by the water-base resin of liquid state, and be suspended in specific water-based emulsion equably, finally defining the multipolymer of colourful, that granular size is random polymer liquid colloidal, is the product of a kind of water-based, nuisanceless, rich flower hilllock texture, polymer element structure.There is weathering resistance difference in most water-water multi-color lacquer in the market, and the shortcoming that work-ing life is short limits its use range.
Summary of the invention
Object of the present invention, in order to solve the defect existed in prior art, provides a kind of high durable, resistance toly to do the wash, water-water multi-color lacquer that acid rain resistant, long service life, cost performance are high and preparation method thereof.
In order to achieve the above object, the present invention adopts following technical scheme:
A kind of water-water multi-color lacquer, comprises the raw material of following weight part:
Protection glue: trisodium phosphate 2-3, sodium starch glycolate 1.5-2.5, hydroxypropyl xanthan gum 1-2, colorful protecting glue RT-120-30, water 450-500;
Base paint: wetting agent PE-1001.5-2.5, dispersion agent HT-50402-4, elasticity defoamer HT-6071.5-2.5, colorful Mierocrystalline cellulose HM-304-8, mould inhibitor DE0.5-1.5, film coalescence aid TEXANOL3-4, elastic emulsion RS-9389150-200, elastic emulsion RS-6733100-150, multifunctional assistant AMP-952-3, sanitas DF1-2, thickening material MS-24-6, forging white powder 3-6, rutile titanium white powder 5-10, composite nano powder 80-100, water 350-450;
Outsourcing water: organosilicon crylic acid latex 200-300, defoamer HT-6100.5-1, multifunctional assistant AMP-951-2, film coalescence aid TEXANOL6-12, ethylene glycol 10-15, sanitas DF1.5-2.5, thickening material MS-23-5, water 60-70;
The preparation method of described composite nano powder is as follows: first take kaolin by weight 4-8:3-5:2-3, tuff and sepiolite, mixing and being placed on concentration is in the hydrochloric acid soln of 1-2mol/L, heating in water bath is to 70-80 DEG C, insulation 1-2h, filter, filter residue is washed with distilled water to neutrality, dry, 750-800 DEG C of calcining 2-3h, be cooled to room temperature, pulverize, cross 2000-3000 mesh sieve, then the powder after sieving is added water and make the slurries that concentration is 50-60%, add the lauryl glucosyl being equivalent to slurry weight 3-6% again, the Vltra tears of 4-8%, the lauric monoethanolamide sodium sulfate of 2-3%, the cocamidopropyl propyl amide amine oxide of 2-3%, speed lapping slurry particle diameter is to 100-150nm, be spray dried to powder, add in the most backward powder obtained be equivalent to powder weight 5-10% Sucrose acetoisobutyrate, the three red oil of 4-6%, the cuprous sulfide of 2-3%, the basic lead chromate of 1-2%, high speed dispersion 15-20min, dries, pulverizing, porphyrize,
Described wetting agent PE-100 is produced by German Ke Ning chemical company;
Described film coalescence aid TEXANOL is produced by Eastman Chem Co. of the U.S.;
Described multifunctional assistant AMP-95 is produced by Dow Chemical company;
Described colorful protecting glue RT-1 and colorful Mierocrystalline cellulose HM-30 produces by Shanghai Yu Zhu Industrial Co., Ltd.;
Described wetting agent PE-100, dispersion agent HT-5040, elasticity defoamer HT-607, mould inhibitor DE, sanitas DF, thickening material MS-2 and defoamer HT-610 produce by Nantong Han Tai Chemical Co., Ltd.;
Described elastic emulsion RS-9389 and elastic emulsion RS-6733 produces by the rich Industrial Co., Ltd. of Shanghai Ahmedabad.
The preparation method of water-water multi-color lacquer of the present invention, comprises the following steps:
(1) preparation of glue is protected
Under 800-1000r/min rotating speed, add trisodium phosphate, hydroxypropyl xanthan gum, sodium starch glycolate, colorful protecting glue RT-1, water successively, then rotating speed bring up to 1500-2000r/min again high-speed stirring dissolve completely to mentioned component, obtain protection glue;
(2) preparation of base paint
Water is added successively by base paint formulation proportioning, dispersion agent HT-5040, wetting agent PE-100, elasticity defoamer HT-607, 3-6min is stirred under 300-400r/min rotating speed, and then add forging white powder, rutile titanium white powder, composite nano powder, colorful Mierocrystalline cellulose HM-30, 15-20min is stirred under 800-1000r/min rotating speed, finally add elastic emulsion RS-9389 successively, elastic emulsion RS-6733, mould inhibitor DE, film coalescence aid TEXANOL, multifunctional assistant AMP-95, sanitas DF, thickening material MS-2, 5-10min is stirred under 1000-1500r/min rotating speed, obtain base paint,
(3) granulation
The weight such as above-mentioned obtained base paint and protection glue are mixed, with screen cloth or dispersion impeller granulation after standing 3-5min, obtains colorful particle;
(4) colorful lacquering
Organosilicon crylic acid latex is weighed up by outsourcing water formulation ratio, ethylene glycol, defoamer HT-610, multifunctional assistant AMP-95, film coalescence aid TEXANOL, sanitas DF, water is added successively under 400-600r/min rotating speed, above-mentioned obtained colorful mix particles is added even after stirring 5-10min, then thickening material MS-2 is added, 10-15min is stirred under 2000-3000r/min rotating speed, finally viscosity is adjusted to 60-80KU, obtain water-water multi-color lacquer of the present invention.
Beneficial effect of the present invention:
Water-water multi-color lacquer high durable of the present invention, resistance toly to do the wash, acid rain resistant, waterproof be self-cleaning, work-ing life can reach more than 10 years, cost performance is high, and compared with natural granite, cost is about 20% of natural granite, material is lighter, significantly reduce load than natural granite to body of wall, be more suitable for exterior-wall heat insulation, and Water-borne modification environmental protection and energy saving are nontoxic, alternative day by day rare natural granite, meets the energy-conserving and environment-protective requirement of country.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1
A kind of water-water multi-color lacquer, comprises the raw material of following weight part:
Protection glue: trisodium phosphate 2.5, sodium starch glycolate 2, hydroxypropyl xanthan gum 1.5, colorful protecting glue RT-125, water 469;
Base paint: wetting agent PE-1002, dispersion agent HT-50403, elasticity defoamer HT-6072, colorful Mierocrystalline cellulose HM-307, mould inhibitor DE1, film coalescence aid TEXANOL3, elastic emulsion RS-9389150, elastic emulsion RS-6733150, multifunctional assistant AMP-952, sanitas DF1, thickening material MS-25, forging white powder 4, rutile titanium white powder 6, composite nano powder 100, water 400;
Outsourcing water: organosilicon crylic acid latex 250, defoamer HT-6101, multifunctional assistant AMP-952, film coalescence aid TEXANOL10, ethylene glycol 15, sanitas DF2, thickening material MS-24, water 66;
The preparation method of described composite nano powder is as follows: first take kaolin by weight 6:4:3, tuff and sepiolite, mixing and being placed on concentration is in the hydrochloric acid soln of 1mol/L, heating in water bath to 80 DEG C, insulation 1h, filter, filter residue is washed with distilled water to neutrality, dry, 780 DEG C of calcining 3h, be cooled to room temperature, pulverize, cross 3000 mesh sieves, then the powder after sieving is added water and make the slurries that concentration is 55%, add the lauryl glucosyl being equivalent to slurry weight 4% again, the Vltra tears of 6%, the lauric monoethanolamide sodium sulfate of 3%, the cocamidopropyl propyl amide amine oxide of 2%, speed lapping slurry particle diameter is to 100nm, be spray dried to powder, add in the most backward powder obtained be equivalent to powder weight 8% Sucrose acetoisobutyrate, 5 three red oil, the cuprous sulfide of 2.5%, the basic lead chromate of 1.5%, high speed dispersion 16min, dries, pulverizing, porphyrize,
Described wetting agent PE-100 is produced by German Ke Ning chemical company;
Described film coalescence aid TEXANOL is produced by Eastman Chem Co. of the U.S.;
Described multifunctional assistant AMP-95 is produced by Dow Chemical company;
Described colorful protecting glue RT-1 and colorful Mierocrystalline cellulose HM-30 produces by Shanghai Yu Zhu Industrial Co., Ltd.;
Described wetting agent PE-100, dispersion agent HT-5040, elasticity defoamer HT-607, mould inhibitor DE, sanitas DF, thickening material MS-2 and defoamer HT-610 produce by Nantong Han Tai Chemical Co., Ltd.;
Described elastic emulsion RS-9389 and elastic emulsion RS-6733 produces by the rich Industrial Co., Ltd. of Shanghai Ahmedabad.
The preparation method of water-water multi-color lacquer, comprises the following steps:
(1) preparation of glue is protected
Under 1000r/min rotating speed, add trisodium phosphate, hydroxypropyl xanthan gum, sodium starch glycolate, colorful protecting glue RT-1, water successively, then rotating speed bring up to 1500r/min again high-speed stirring dissolve completely to mentioned component, obtain protection glue;
(2) preparation of base paint
Water, dispersion agent HT-5040, wetting agent PE-100, elasticity defoamer HT-607 is added successively by base paint formulation proportioning, 5min is stirred under 300r/min rotating speed, and then add forging white powder, rutile titanium white powder, composite nano powder, colorful Mierocrystalline cellulose HM-30,18min is stirred under 800r/min rotating speed, finally add elastic emulsion RS-9389, elastic emulsion RS-6733, mould inhibitor DE, film coalescence aid TEXANOL, multifunctional assistant AMP-95, sanitas DF, thickening material MS-2 successively, under 1000r/min rotating speed, stir 8min, obtain base paint;
(3) granulation
The weight such as above-mentioned obtained base paint and protection glue are mixed, with screen cloth or dispersion impeller granulation after standing 4min, obtains colorful particle;
(4) colorful lacquering
Organosilicon crylic acid latex is weighed up by outsourcing water formulation ratio, ethylene glycol, defoamer HT-610, multifunctional assistant AMP-95, film coalescence aid TEXANOL, sanitas DF, water is added successively under 5600r/min rotating speed, above-mentioned obtained colorful mix particles is added even after stirring 7min, then thickening material MS-2 is added, 12min is stirred under 2500r/min rotating speed, finally viscosity is adjusted to 70KU, obtain water-water multi-color lacquer of the present invention.
The water-water multi-color lacquer that above-described embodiment obtains meets industry service requirements, good weatherability, has good application property.The performance test results is as shown in the table:
| Test event | Test result |
| Application property | Spraying nothing difficulty, easy construction |
| Low-temperature storage stability, 3 times | Without caking, cohesion and the change of constituent |
| Water tolerance (96h) | Coating being roused without rising, ftractureing, being peeled off |
| Alkali resistance (96h) | Coating being roused without rising, ftractureing, being peeled off |
| Cohesive strength MPa (standard state) | 1.31 |
| Cohesive strength MPa (after immersion) | 1.17 |
| Shock-resistance | Coating flawless, peel off and be obviously out of shape |
Claims (2)
1. a water-water multi-color lacquer, is characterized in that, comprises the raw material of following weight part:
Protection glue: trisodium phosphate 2-3, sodium starch glycolate 1.5-2.5, hydroxypropyl xanthan gum 1-2, colorful protecting glue RT-1 20-30, water 450-500;
Base paint: wetting agent PE-100 1.5-2.5, dispersion agent HT-5040 2-4, elasticity defoamer HT-607 1.5-2.5, colorful Mierocrystalline cellulose HM-30 4-8, mould inhibitor DE 0.5-1.5, film coalescence aid TEXANOL 3-4, elastic emulsion RS-9389 150-200, elastic emulsion RS-6733 100-150, multifunctional assistant AMP-95 3-3, sanitas DF 1-2, thickening material MS-2 4-6, forging white powder 3-6, rutile titanium white powder 5-10, composite nano powder 80-100, water 120-160;
Outsourcing water: organosilicon crylic acid latex 200-300, defoamer HT-610 0.5-1, multifunctional assistant AMP-95 1-2, film coalescence aid TEXANOL 6-12, ethylene glycol 10-15, sanitas DF 1.5-2.5, thickening material MS-2 3-5, water 60-70;
The preparation method of described composite nano powder is as follows: first take kaolin by weight 4-8:3-5:2-3, tuff and sepiolite, mixing and being placed on concentration is in the hydrochloric acid soln of 1-2mol/L, heating in water bath is to 70-80 DEG C, insulation 1-2h, filter, filter residue is washed with distilled water to neutrality, dry, 750-800 DEG C of calcining 2-3h, be cooled to room temperature, pulverize, cross 2000-3000 mesh sieve, then the powder after sieving is added water and make the slurries that concentration is 50-60%, add the lauryl glucosyl being equivalent to slurry weight 3-6% again, the Vltra tears of 4-8%, the lauric monoethanolamide sodium sulfate of 2-3%, the cocamidopropyl propyl amide amine oxide of 2-3%, speed lapping slurry particle diameter is to 100-150nm, be spray dried to powder, add in the most backward powder obtained be equivalent to powder weight 5-10% Sucrose acetoisobutyrate, the three red oil of 4-6%, the cuprous sulfide of 2-3%, the basic lead chromate of 1-2%, high speed dispersion 15-20min, dries, pulverizing, porphyrize,
Described wetting agent PE-100 is produced by German Ke Ning chemical company;
Described film coalescence aid TEXANOL is produced by Eastman Chem Co. of the U.S.;
Described multifunctional assistant AMP-95 is produced by Dow Chemical company;
Described colorful protecting glue RT-1 and colorful Mierocrystalline cellulose HM-30 produces by Shanghai Yu Zhu Industrial Co., Ltd.;
Described wetting agent PE-100, dispersion agent HT-5040, elasticity defoamer HT-607, mould inhibitor DE, sanitas DF, thickening material MS-2 and defoamer HT-610 produce by Nantong Han Tai Chemical Co., Ltd.;
Described elastic emulsion RS-9389 and elastic emulsion RS-6733 produces by the rich Industrial Co., Ltd. of Shanghai Ahmedabad.
2. a preparation method for water-water multi-color lacquer as claimed in claim 1, is characterized in that comprising the following steps:
(1) preparation of glue is protected
Under 800-1000r/min rotating speed, add trisodium phosphate, hydroxypropyl xanthan gum, sodium starch glycolate, colorful protecting glue RT-1, water successively, then rotating speed bring up to 1500-2000r/min again high-speed stirring dissolve completely to mentioned component, obtain protection glue;
(2) preparation of base paint
Water is added successively by base paint formulation proportioning, dispersion agent HT-5040, wetting agent PE-100, elasticity defoamer HT-607, 3-6min is stirred under 300-400r/min rotating speed, and then add forging white powder, rutile titanium white powder, composite nano powder, colorful Mierocrystalline cellulose HM-30, 15-20min is stirred under 800-1000r/min rotating speed, finally add elastic emulsion RS-9389 successively, elastic emulsion RS-6733, mould inhibitor DE, film coalescence aid TEXANOL, multifunctional assistant AMP-95, sanitas DF, thickening material MS-2, 5-10min is stirred under 1000-1500r/min rotating speed, obtain base paint,
(3) granulation
The weight such as above-mentioned obtained base paint and protection glue are mixed, with screen cloth or dispersion impeller granulation after standing 3-5min, obtains colorful particle;
(4) colorful lacquering
Organosilicon crylic acid latex is weighed up by outsourcing water formulation ratio, ethylene glycol, defoamer HT-610, multifunctional assistant AMP-95, film coalescence aid TEXANOL, sanitas DF, water is added successively under 400-600r/min rotating speed, above-mentioned obtained colorful mix particles is added even after stirring 5-10min, then thickening material MS-2 is added, 10-15min is stirred under 2000-3000r/min rotating speed, finally viscosity is adjusted to 60-80KU, obtain water-water multi-color lacquer of the present invention.