CN109181546A - A kind of production method for the water paint that waterproofness is high - Google Patents
A kind of production method for the water paint that waterproofness is high Download PDFInfo
- Publication number
- CN109181546A CN109181546A CN201811030347.5A CN201811030347A CN109181546A CN 109181546 A CN109181546 A CN 109181546A CN 201811030347 A CN201811030347 A CN 201811030347A CN 109181546 A CN109181546 A CN 109181546A
- Authority
- CN
- China
- Prior art keywords
- base paint
- paint
- agent
- parts
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water paints that waterproofness is high, including protection glue, base paint and pure water, the protection glue include deionized water, sodium pyrophosphate and RT-1 protective glue；The base paint includes deionized water, dispersing agent, defoaming agent, wetting agent, rutile titanium white powder, calcined kaolin, colorful cellulose, inorganic bentonite, film-forming base paint, elastic emulsion, protection glue, neutralizes base paint, preservative, flatting silica, thickener, levelling agent and preservative; by being provided with rutile titanium white powder, calcined kaolin and inorganic bentonite in the present invention; reduce production cost; it is extended using the time, durability is good；By being provided with colorful cellulose and levelling agent, so that water paint has good levelling and ductility, and has color effect；By being provided with elastic emulsion and protection glue, so that water paint has excellent waterproof performance, it is convenient for marketing.
Description
Technical field
The present invention relates to water paint field, the production method of the high water paint of specifically a kind of waterproofness.
Background technique
With the continuous development of communications, the volume of traffic is increasingly increased, and bring pavement damage is also accelerating therewith, repairing damage
Bad road surface is the important link of maintenance of surface, and previous patching material mixes clay concrete using heat mostly, due to by season
With the limitation of temperature, the road surface of damage cannot be repaired at any time in time, in highway construction, often need to be bonded using waterproof
Material, type mainly have water-soluble waterproof bonding material, solvent type waterproof bonding material, response type waterproof bonding material.Wherein,
Water-soluble waterproof bonding material, the waterproofness of solvent type waterproof bonding material, cementability and durability are poor, response type waterproof
Although adhesives has the advantages that cementability, durability are good, because it has at high cost, waterproofness is bad, cementability and durable
Property is poor, and water paint does not have color effect during use, and the levelability and ductility of water paint are poor,
Middle waterproof performance is bad.Therefore, those skilled in the art provide a kind of production method of water paint that waterproofness is high, with solution
Certainly the problems mentioned above in the background art.
Summary of the invention
The purpose of the present invention is to provide a kind of production methods of water paint that waterproofness is high, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the invention provides the following technical scheme:
A kind of water paint that waterproofness is high, including protection glue, base paint and pure water, the protection glue includes deionization
Water, sodium pyrophosphate and RT-1 protective glue；The base paint includes deionized water, dispersing agent, defoaming agent, wetting agent, rutile titanium
White powder, colorful cellulose, inorganic bentonite, film-forming base paint, elastic emulsion, protection glue, neutralizes basis at calcined kaolin
Paint, preservative, flatting silica, thickener and levelling agent.
As the present invention further scheme: the protection glue is prepared by the component of following parts by weight: go from
80~90 parts of sub- water, 1~3 part of sodium pyrophosphate, 3~8 parts of RT-1 protective glue.
As further scheme of the invention: the base paint is prepared by the component of following parts by weight: deionization
30~50 parts of water, 1~3 part of dispersing agent, 2~3 parts of defoaming agent, 1~2 part of wetting agent, 1~3 part of rutile titanium white powder, calcining kaolinite
10~20 parts of soil, 1~2 part of colorful cellulose, 0.5~2.5 part of inorganic bentonite, 0.5~3.5 part of film-forming base paint, elasticity cream
30~40 parts of liquid, 10~25 parts of glue of protection, 0.2~0.5 part of base paint of neutralization, 0.4~0.8 part of preservative, flatting silica 0.3~
0.5 part, 0.1~0.3 part of thickener, 0.1~0.2 part of levelling agent.
As further scheme of the invention: the production method comprises the steps of:
A, production protection glue: according to the ratio of optimization, deionized water, sodium pyrophosphate and RT-1 protective glue being mixed, first with
The clockwise direction of 500~600rd/h of agitating paddle stirs 5~10 minutes, then stops 5~10 minutes, then again with agitating paddle 500
The speed of~600rd/h stirs 5~10 minutes counterclockwise, then stops stirring 5~10 minutes.
B, base paint is made: according to the ratio of optimization, by deionized water, dispersing agent, defoaming agent, wetting agent, rutile
Titanium dioxide, colorful cellulose, inorganic bentonite, film-forming base paint, elastic emulsion, protection glue, neutralizes basis at calcined kaolin
Paint, preservative, flatting silica, thickener and levelling agent mixing, successively add raw materials into sequence, first with agitating paddle 700~
The clockwise direction of 800rd/h stirs or so half an hour, then stops half an hour or so, then again with agitating paddle 700~
The speed of 800rd/h stirs or so half an hour counterclockwise, then stops stirring or so half an hour.
C, it is granulated: 300 parts of base paint that mix up color is added in 300 part 5% of protection glue, standing 3~use after five minutes
Sieve or dispersion impeller are granulated, and viscosity are please such as accomplished 130KU or more with pelletizer granulation, to form colorful particle.
D, it is stirred: being 800rd/h, following raw material of successively readjusting prices in sequence: colorful particle, the third cream of silicon in speed
Liquid, deionized water, defoaming agent, neutralizer, ethylene glycol, film-forming base paint and thickener, then speed improves to 2000rd/h and exists
High-speed stirred, mixing time are 60 minutes, are sequentially added in order, revolving speed 300rd/h, and the duration is 5 minutes；Sufficiently disappear
After bubble removing, protection glue is added and persistently stirs half an hour in the state of 500rd/h；Then thickener is added to adjust
Viscosity, mixing speed 800rd/h, duration are half an hour.
As further scheme of the invention: the wetting agent uses anion or non-ionic.
Compared with prior art, the beneficial effects of the present invention are: by being provided with rutile titanium white powder, calcining in the present invention
Kaolin and inorganic bentonite, reduce production cost, extend it using the time, durability is good；It is colorful by being provided with
Cellulose and levelling agent so that water paint has good levelling and ductility, and have color effect；By being provided with bullet
Property lotion and protection glue so that water paint has excellent waterproof performance, convenient for marketing.
Detailed description of the invention
Fig. 1 is a kind of structural schematic diagram of the production method of water paint that waterproofness is high.
Specific embodiment
Referring to Fig. 1, in the embodiment of the present invention, a kind of water paint that waterproofness is high, including protection glue, base paint with
And pure water, protection glue includes deionized water, sodium pyrophosphate and RT-1 protective glue；Base paint includes deionized water, dispersing agent, disappears
Infusion, wetting agent, rutile titanium white powder, calcined kaolin, colorful cellulose, inorganic bentonite, film-forming base paint, elasticity cream
Liquid, neutralizes base paint, preservative, flatting silica, thickener and levelling agent at protection glue.
Preferably, protection glue is prepared by the component of following parts by weight: 80~90 parts of deionized water, sodium pyrophosphate 1
~3 parts, 3~8 parts of RT-1 protective glue.
Preferably, base paint is prepared by the component of following parts by weight: 30~50 parts of deionized water, dispersing agent 1~3
Part, 2~3 parts of defoaming agent, 1~2 part of wetting agent, 1~3 part of rutile titanium white powder, 10~20 parts of calcined kaolin, colorful cellulose
1~2 part, 0.5~2.5 part of inorganic bentonite, 0.5~3.5 part of film-forming base paint, 30~40 parts of elastic emulsion, protection glue 10
~25 parts, neutralize 0.2~0.5 part of base paint, 0.4~0.8 part of preservative, 0.3~0.5 part of flatting silica, thickener 0.1~0.3
Part, 0.1~0.2 part of levelling agent.
Preferably, which comprises the steps of:
A, production protection glue: according to the ratio of optimization, deionized water, sodium pyrophosphate and RT-1 protective glue being mixed, first with
The clockwise direction of 500~600rd/h of agitating paddle stirs 5~10 minutes, then stops 5~10 minutes, then again with agitating paddle 500
The speed of~600rd/h stirs 5~10 minutes counterclockwise, then stops stirring 5~10 minutes.
B, base paint is made: according to the ratio of optimization, by deionized water, dispersing agent, defoaming agent, wetting agent, rutile
Titanium dioxide, colorful cellulose, inorganic bentonite, film-forming base paint, elastic emulsion, protection glue, neutralizes basis at calcined kaolin
Paint, preservative, flatting silica, thickener and levelling agent mixing, successively add raw materials into sequence, first with agitating paddle 700~
The clockwise direction of 800rd/h stirs or so half an hour, then stops half an hour or so, then again with agitating paddle 700~
The speed of 800rd/h stirs or so half an hour counterclockwise, then stops stirring or so half an hour.
C, it is granulated: 300 parts of base paint that mix up color is added in 300 part 5% of protection glue, standing 3~use after five minutes
Sieve or dispersion impeller are granulated, and viscosity are please such as accomplished 130KU or more with pelletizer granulation, to form colorful particle.
D, it is stirred: being 800rd/h, following raw material of successively readjusting prices in sequence: colorful particle, the third cream of silicon in speed
Liquid, deionized water, defoaming agent, neutralizer, ethylene glycol, film-forming base paint and thickener, then speed improves to 2000rd/h and exists
High-speed stirred, mixing time are 60 minutes, are sequentially added in order, revolving speed 300rd/h, and the duration is 5 minutes；Sufficiently disappear
After bubble removing, protection glue is added and persistently stirs half an hour in the state of 500rd/h；Then thickener is added to adjust
Viscosity, mixing speed 800rd/h, duration are half an hour.
Preferably, wetting agent uses anion or non-ionic.
It is above-described, it is merely preferred embodiments of the present invention, but protection scope of the present invention is not limited to
This, anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention
And its inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (5)
1. a kind of water paint that waterproofness is high, including protection glue, base paint and pure water, which is characterized in that the protection
Glue includes deionized water, sodium pyrophosphate and RT-1 protective glue；The base paint includes deionized water, dispersing agent, defoaming agent, profit
Humectant, rutile titanium white powder, calcined kaolin, colorful cellulose, inorganic bentonite, film-forming base paint, elastic emulsion, protective glue
Liquid neutralizes base paint, preservative, flatting silica, thickener and levelling agent.
2. a kind of high water paint of waterproofness according to claim 1, which is characterized in that the protection glue is by as follows
The component of parts by weight is prepared: 80~90 parts of deionized water, 1~3 part of sodium pyrophosphate, 3~8 parts of RT-1 protective glue.
3. a kind of high water paint of waterproofness according to claim 1, which is characterized in that the base paint by weighing as follows
The component of amount part is prepared: 30~50 parts of deionized water, 1~3 part of dispersing agent, 2~3 parts of defoaming agent, 1~2 part of wetting agent, gold
1~3 part of red stone titanium dioxide, 10~20 parts of calcined kaolin, 1~2 part of colorful cellulose, 0.5~2.5 part of inorganic bentonite, at
0.5~3.5 part of film base paint, 10~25 parts of glue of protection, neutralizes 0.2~0.5 part of base paint, is anti-30~40 parts of elastic emulsion
0.4~0.8 part of rotten agent, 0.3~0.5 part of flatting silica, 0.1~0.3 part of thickener, 0.1~0.2 part of levelling agent.
4. a kind of production method of the high water paint of waterproofness according to claims 1 to 3, which is characterized in that the system
It is comprised the steps of as method:
A, production protection glue: according to the ratio of optimization, deionized water, sodium pyrophosphate and RT-1 protective glue being mixed, first with
The clockwise direction of 500~600rd/h of agitating paddle stirs 5~10 minutes, then stops 5~10 minutes, then again with agitating paddle 500
The speed of~600rd/h stirs 5~10 minutes counterclockwise, then stops stirring 5~10 minutes；
B, base paint is made: according to the ratio of optimization, by deionized water, dispersing agent, defoaming agent, wetting agent, rutile titanium white
Powder, calcined kaolin, colorful cellulose, inorganic bentonite, film-forming base paint, elastic emulsion, protection glue, neutralize base paint,
Preservative, flatting silica, thickener and levelling agent mixing, successively add raw materials into, in sequence first with 700~800rd/ of agitating paddle
The clockwise direction of h stirs or so half an hour, then stop half an hour or so, then again with 700~800rd/h's of agitating paddle
Speed stirs or so half an hour counterclockwise, then stops stirring or so half an hour；
C, it is granulated: 300 parts of base paint that mix up color is added in 300 part 5% of protection glue, standing 3~use sieve after five minutes
Or dispersion impeller is granulated, and viscosity is please such as accomplished 130KU or more with pelletizer granulation, to form colorful particle；
D, it is stirred: being 800rd/h in speed, following raw material of successively readjusting prices in sequence: colorful particle, is gone silicone acrylic emulsion
Ionized water, defoaming agent, neutralizer, ethylene glycol, film-forming base paint and thickener, then speed is improved to 2000rd/h in high-speed stirring
It mixes, mixing time is 60 minutes, is sequentially added in order, revolving speed 300rd/h, and the duration is 5 minutes；Sufficiently eliminate bubble
Afterwards, protection glue is added and persistently stirs half an hour in the state of 500rd/h；Then addition thickener adjusts viscosity,
Mixing speed is 800rd/h, and the duration is half an hour.
5. a kind of production method of the high water paint of waterproofness according to claim 1, which is characterized in that the wetting
Agent uses anion or non-ionic.