CN104261773A - 耐水性水泥基自流平材料 - Google Patents
耐水性水泥基自流平材料 Download PDFInfo
- Publication number
- CN104261773A CN104261773A CN201410479647.7A CN201410479647A CN104261773A CN 104261773 A CN104261773 A CN 104261773A CN 201410479647 A CN201410479647 A CN 201410479647A CN 104261773 A CN104261773 A CN 104261773A
- Authority
- CN
- China
- Prior art keywords
- water
- component
- based self
- leveling material
- water resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种耐水性水泥基自流平材料,由A组份和B组份按质量比100:20-30制成,A组份按质量百分比计由以下原料制成:P052.5水泥25-40%、硫铝酸盐水泥10-25%、50-100目河砂30-40%、重钙5-10%、减水剂0.1-0.2%、碳酸理0.1-0.3%、缓凝剂0.1-0.3%、纤维素醚0.1-0.3%;B组份按质量百分比计由以下原料制成:丙烯酸丁酯30-40%、苯乙烯1-3%、甲基丙烯酸甲酯10-20%、醇酯-125-10%、交联剂1-2%、偶联剂5-10%、引发剂2-3%、水35-46%;本发明具有经常泡水后不剥落、无变色、无气泡、且做厚不开裂、易推广、易推广的优点,适合在潮湿和室外环境使用。
Description
技术领域
本发明涉及建筑领域,尤其涉及一种耐水性水泥基自流平材料。
背景技术
随着人们生活水平的提高,对建筑材料的要求越来越高,同时也就对地坪材料的要求提高了,各种新型的地坪装饰材料都相继问世,比如PVC地板,橡胶地板,水性聚氨酯地坪等等。诸如此类的装饰材料都需要有个非常平整的地面作为基础,毛胚房的基层一般是混凝土基层,混凝土是有水泥、砂、石头和水混合而成,因为它含有大颗粒,其表面非常不平整,强度低,容易起灰,不美观,脚感也极其不舒服。自流平具有良好的流动性、稳定性以及流平层厚度薄、强度高和施工简便等优点。水泥基自流平的诞生不但使找平的费用大大降低了,更使找平的房子上下空间节省了,同时地坪养护时间也缩短了,可以说是省时、省力、省心。
现有水泥基自流平的配方一般由普灰水泥、特种水泥、沙子、石膏、一些精细助剂所组成。而其中石膏是必不可缺的,这是由于自流平干燥过程中会干缩,需要石膏防止干缩开裂,防止干缩粉化,防止干缩起壳。
目前,建筑上使用的石膏制品有一个共同的弱点就是其耐水性(抗水性)差并且当其处于水饱和状态时抗压强度差,例如,石膏制品在干燥状况时,其抗压强度为6-10MPa,而当它处于水饱和状态时,其强度损失可达70%,甚至更大。
因此传统水泥基自流平的耐水性差是一个普遍缺点。也正是如此,传统水泥基自流平不可以用在室外或是潮湿的基层上。如果把传统水泥基自流平做在室外或是容易有水冲洗(滴落)环境(菜场地坪、浴室)下、或是潮湿基层上,很容易起鼓、粉化没强度等等。
再则,当传统水泥基自流平厚度做到4-5毫米,很容易开裂。一般传统水泥基自流平只能做到2-3毫米,一旦客户需要厚度做到4-5毫米,传统水泥基自流平是很难达到的。
所以,传统水泥基自流平材料存在耐水性差以及自流平厚度做到一定厚度后易开裂的缺陷,现有的水泥基自流平材料配方在技术上还没有能够实现在室外或潮湿的基层上使用,使得应用领域就受到了很大的限制。
发明内容
有鉴于此,本发明所要解决的技术问题是:提供一种高耐水性、高抗裂性的耐水性水泥基自流平材料,克服现有的水泥基自流平材料耐水性差以及自流平厚度做到一定厚度后易开裂,水泥基自流平材料配方在技术上还没有能够实现在室外或潮湿的基层上使用的缺陷。
为了达到上述目的,本发明采用如下技术方案来实现的:
一种耐水性水泥基自流平材料,由A组份和B组份制成,
所述A组份按质量百分比计由以下原料制成:
P052.5水泥25-40%、硫铝酸盐水泥10-25%、50-100目河砂30-40%、重钙5-10%、减水剂0.1-0.2%、碳酸理0.1-0.3%、缓凝剂0.1-0.3%、纤维素醚0.1-0.3%;
所述B组份按质量百分比计由以下原料制成:
丙烯酸丁酯30-40%、苯乙烯1-3%、甲基丙烯酸甲酯10-20%、醇酯-125-10%、交联剂1-2%、偶联剂5-10%、引发剂2-3%、水35-46%;
所述A组份和B组份按100:20-30的质量比混合后搅拌配置而成耐水性水泥基自流平材料。
本发明的解决方案中所述重钙可采用325目双灰粉。
本发明的解决方案中所述减水剂可采用聚羧酸减水剂。
本发明的解决方案中所述缓凝剂可采用柠檬酸。
本发明的解决方案中所述纤维素醚可采用甲基纤维素醚。
本发明的解决方案中所述交联剂可采用双丙酮丙烯酰胺。
本发明的解决方案中所述偶联剂可采用硅烷偶联剂。
本发明的解决方案中所述引发剂可采用偶氮类引发剂。
所述耐水性水泥基自流平材料的制造工艺包括以下步骤:
制作A组份:按质量配比将P052.5水泥、硫铝酸盐水泥、50-100目河砂、重钙、减水剂、碳酸理、缓凝剂、纤维素醚混合搅拌8-15分钟,检测合格后出料包装;
制作B组份:按质量配比将水、丙烯酸丁酯、苯乙烯、甲基丙烯酸甲酯、醇酯-12、交联剂、偶联剂、引发剂混合后,在氮气保护下高速剪切搅拌10-15分钟之后在高速剪切条件下辐照50-80分钟进行接枝聚合反应,反应完成并冷却后进行检测,合格后包装,制得耐水乳液(B组份)。
所述的辐射是指通过钴60伽马射线或电子束辐射,使得制作B组份过程中产生大分子过氧化自由基或过氧化物引发接枝聚合反应。
本发明的解决方案中所述接枝聚合反应的温度为75-95℃。
本发明的解决方案中所述剪切转速为800-1500转/分钟,在高速剪切搅拌条件下形成稳定的高分散体系,充分快速的进行接枝聚合反应。
本发明工程试验表明,该水泥基自流平材料在耐水性和较高厚度的抗裂性上优于传统的水泥基自流平材料,表1为本发明试验测试数据表。
抗压强度、抗折强度、拉伸粘结强度、流动度按JC/T985-2005《地面用水泥基自流平砂浆》检验方法进行检测;
B组份的耐水性按GB/T 22374-2008《地坪涂装材料》的检测方法进行,表1中的耐水性是指A组份和B组份按计量比混合搅拌后制得的水泥基自流平材料的耐水性。
表1 为本发明试验测试数据表
由上述技术方案可在,本发明的有益效果是:
与现有技术相比,本发明通过将水、丙烯酸丁酯、苯乙烯、甲基丙烯酸甲酯、醇酯-12、交联剂、偶联剂、引发剂按一定质量比进行接枝聚合反应制成耐水性乳液(B组份)并与A组份按特定质量比进行混合搅拌制成的耐水性水泥基自流平材料克服了传统水泥基自流平耐水性差不能在潮湿和室外环境下使用以及自流平厚度达到一定程度后易开裂的缺陷,实现了在潮湿基层和室外环境下的使用,具有不气泡、不剥落、无变色、且做厚不开裂的优点,有着非常高的推广性和实用性。
具体实施方式
为了使本领域技术人员能更进一步了解本发明结合具体实施例进行说明。
实施例1
A组份:
P052.5水泥300kg、硫铝酸盐水泥200kg、50-100目河砂394kg、325目双灰粉100kg、聚羧酸减水剂2kg、碳酸理1kg、柠檬酸1kg、甲基纤维素醚2kg;投入搅拌锅内搅拌10分钟。
B组份:
水80kg、丙烯酸丁酯64kg、苯乙烯4kg、甲基丙烯酸甲酯24kg、醇酯-12 12kg、双丙酮丙烯酰胺2kg、硅烷偶联剂10kg、偶氮类引发剂4kg混合后,于反应釜内在氮气保护下1000转/分钟剪切搅拌12分钟之后在高速剪切条件下通过钴60伽马射线辐照60分钟进行接枝聚合反应,反应温度维持在90℃,反应完成并冷却制得耐水乳液(B组份)。
施工时将A组份和B组份混合后搅拌均匀后即可使用(配比:A:B=100:20)。
实施例2
A组份:
P052.5水泥400kg、硫铝酸盐水泥160kg、50-100目河砂360kg、325目双灰粉73kg、聚羧酸减水剂1.3kg、碳酸理2kg、柠檬酸1.7kg、甲基纤维素醚2kg;投入搅拌锅内搅拌15分钟。
B组份:
水98kg、丙烯酸丁酯92.4kg、苯乙烯8.4kg、甲基丙烯酸甲酯30.8kg、醇酯-1221kg、双丙酮丙烯酰胺4.2kg、硅烷偶联剂16.8kg、偶氮类引发剂8.4kg混合后,于反应釜内在氮气保护下1000转/分钟剪切搅拌12分钟之后在高速剪切条件下通过钴60伽马射线辐照80分钟进行接枝聚合反应,反应温度维持在75℃,反应完成并制得耐水乳液(B组份)。
施工时将A组份和B组份混合后搅拌均匀后即可使用(配比:A:B=100:28)。
Claims (10)
1.一种耐水性水泥基自流平材料,由A组份和B组份制成,其特征在于:所述A组份按质量百分比计由以下原料制成:
P052.5水泥25-40%、硫铝酸盐水泥10-25%、50-100目河砂30-40%、重钙5-10%、减水剂0.1-0.2%、碳酸理0.1-0.3%、缓凝剂0.1-0.3%、纤维素醚0.1-0.3%;
所述B组份按质量百分比计由以下原料制成:
丙烯酸丁酯30-40%、苯乙烯1-3%、甲基丙烯酸甲酯10-20%、醇酯-125-10%、交联剂1-2%、偶联剂5-10%、引发剂2-3%、水35-46%;
所述A组份和B组份按100:20-30的质量比混合后搅拌配置而成耐水性水泥基自流平材料。
2.如权利要求1所述的耐水性水泥基自流平材料,其特征在于:所述重钙为325目双灰粉。
3.如权利要求1所述的耐水性水泥基自流平材料,其特征在于:所述减水剂为聚羧酸减水剂。
4.如权利要求1所述的耐水性水泥基自流平材料,其特征在于:所述缓凝剂为柠檬酸。
5.如权利要求1所述的耐水性水泥基自流平材料,其特征在于:所述纤维素醚为甲基纤维素醚。
6.如权利要求1所述的耐水性水泥基自流平材料,其特征在于:所述交联剂为双丙酮丙烯酰胺。
7.如权利要求1所述的耐水性水泥基自流平材料,其特征在于:所述偶联剂为硅烷偶联剂,所述引发剂为偶氮类引发剂。
8.如权利要求1-7中任一所述的耐水性水泥基自流平材料,其特征在于:所述耐水性水泥基自流平材料中的A组份和B组份通过以下方法制得:
制作A组份:按质量配比将P052.5水泥、硫铝酸盐水泥、50-100目河砂、重钙、减水剂、碳酸理、缓凝剂、纤维素醚混合搅拌8-15分钟,检测合格后出料包装;
制作B组份:按质量配比将水、丙烯酸丁酯、苯乙烯、甲基丙烯酸甲酯、醇酯-12、交联剂、偶联剂、引发剂混合后,在氮气保护下高速剪切搅拌10-15分钟之后在高速剪切条件下辐照50-80分钟进行接枝聚合反应,反应完成并冷却后进行检测,合格后包装。
9.如权利要求8所述的耐水性水泥基自流平材料,其特征在于:所述接枝聚合反应的温度为75-95℃。
10.如权利要求8-9中任一所述的耐水性水泥基自流平材料,其特征在于:所述剪切转速为800-1500转/分钟。