CN104213160A - 一种五金件电镀工艺 - Google Patents

一种五金件电镀工艺 Download PDF

Info

Publication number
CN104213160A
CN104213160A CN201410414763.0A CN201410414763A CN104213160A CN 104213160 A CN104213160 A CN 104213160A CN 201410414763 A CN201410414763 A CN 201410414763A CN 104213160 A CN104213160 A CN 104213160A
Authority
CN
China
Prior art keywords
electroplating
handware
hardware
solution contains
plating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410414763.0A
Other languages
English (en)
Inventor
王晓磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU CITY DONGBANG TOWN XUSHI HONGLEI HARDWARE MACHINERY PLANT
Original Assignee
CHANGSHU CITY DONGBANG TOWN XUSHI HONGLEI HARDWARE MACHINERY PLANT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU CITY DONGBANG TOWN XUSHI HONGLEI HARDWARE MACHINERY PLANT filed Critical CHANGSHU CITY DONGBANG TOWN XUSHI HONGLEI HARDWARE MACHINERY PLANT
Priority to CN201410414763.0A priority Critical patent/CN104213160A/zh
Publication of CN104213160A publication Critical patent/CN104213160A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种五金件电镀工艺，采用垂直旋转电镀方式，包括如下步骤：a、采用碱性溶液清洗去除五金件表面的油污：所述碱性溶液含有氢氧化钠40-50g/L、碳酸钠30-40g/L、磷酸三钠40-50g/L、OP-乳化剂2-5mL/L，所述碱性溶液的温度为80-90℃，清洗时间为15min；b、对五金件进行水洗后镀镍：电镀溶液含有氯化镍180-220g/L、盐酸120-150g/L，电镀电流密度3-4A/dm2，电镀时间10min，阳极为镍板；c、采用清水清洗电镀后的所述五金件并烘干。通过上述方式，本发明采用旋转电镀方式在五金件表面电镀金属镍层，使电镀后的五金件具有表面镀层平整、厚度均匀的特点。

Description

一种五金件电镀工艺
技术领域
本发明涉及五金机械领域，特别是涉及一种五金件电镀工艺。
背景技术
电镀是五金件生产过程中应用非常广泛的表面优化处理技术，是利用电化学的方法，在五金件的表面沉淀形成金属和合金镀层的工艺方法。所谓电镀，是把镀液中的金属离子，在外电场的作用下，经过电极反应还原成为金属原子，并在阴极上进行金属沉淀，从而在五金件表面形成了一个镀层，从而有效地改变了五金件的颜色、质感，以防止蚀变，对五金件起到装饰和延长使用寿命的作用。
随着制造业的发展，五金件的形状越来越复杂，要求及标准不断提高，特别是小型复杂的五金零部件，靠传统的挂镀加阴极移动方式，往往会造成镀层不均匀、表面有毛刺、粗糙等现象，从而使成品合格率较低。
 
发明内容
本发明主要解决的技术问题是提供一种五金件抛光工艺，采用旋转电镀方式在五金件表面电镀金属镍层，使电镀后的五金件具有表面镀层平整、厚度均匀的特点，同时使电镀后的五金件具有良好的光亮度、硬度及耐腐蚀性，并且成品合格率高。
为解决上述技术问题，本发明采用的一个技术方案是：一种五金件电镀工艺，采用垂直旋转电镀方式，包括如下步骤：a、采用碱性溶液清洗去除五金件表面的油污：所述碱性溶液含有氢氧化钠40-50g/L、碳酸钠30-40g/L、磷酸三钠40-50g/L、OP-乳化剂2-5mL/L，所述碱性溶液的温度为80-90℃，清洗时间为15min；b、对上述去除表面油污后的五金件进行水洗后镀镍：电镀溶液含有氯化镍180-220g/L、盐酸120-150g/L，电镀电流密度3-4A/dm2，电镀时间10min，阳极为镍板；c、采用清水清洗电镀后的所述五金件并烘干。
在本发明一个较佳实施例中，所述碱性溶液含有氢氧化钠45g/L、碳酸钠32g/L、磷酸三钠47g/L、OP-乳化剂3mL/L。
在本发明一个较佳实施例中，所述电镀溶液含有氯化镍200g/L、盐酸130g/L。
在本发明一个较佳实施例中，，所述电镀电流密度3.5A/dm2。
本发明的有益效果是：本发明采用旋转电镀方式在五金件表面电镀金属镍层，使电镀后的五金件具有表面镀层平整、厚度均匀的特点，同时使电镀后的五金件具有良好的光亮度、硬度及耐腐蚀性，并且成品合格率高。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括：
一种五金件电镀工艺，采用垂直旋转电镀方式，将五金件垂直吊装，旋转轴与地面垂直，这种电镀方式的优点在于槽体垂直安装，对场地面积要求小，五金件入槽定位方便，容易操作，阳极垂直布置，能很容易保证镀层的均匀性， 所述电镀工艺包括如下步骤：a、采用碱性溶液清洗去除五金件表面的油污：所述碱性溶液含有氢氧化钠40-50g/L、碳酸钠30-40g/L、磷酸三钠40-50g/L、OP-乳化剂2-5mL/L，所述碱性溶液的温度为80-90℃，清洗时间为15min；b、对上述去除表面油污后的五金件进行水洗后镀镍：电镀溶液含有氯化镍180-220g/L、盐酸120-150g/L，电镀电流密度3-4A/dm2，电镀时间10min，阳极为镍板；c、采用清水清洗电镀后的所述五金件并烘干。
其中，所述碱性溶液含有氢氧化钠45g/L、碳酸钠32g/L、磷酸三钠47g/L、OP-乳化剂3mL/L，在碱性溶液中借助皂化作用清除五金件表面油污。
所述电镀溶液含有氯化镍200g/L、盐酸130g/L，使金属镍沉积在五金件表面，形成均匀、致密、结合力良好的镀镍层。
所述电镀电流密度3.5A/dm2，电流小，使五金件镀层平整、厚度均匀。
本发明揭示了一种五金件电镀工艺，采用旋转电镀方式在五金件表面电镀金属镍层，使电镀后的五金件具有表面镀层平整、厚度均匀的特点，同时使电镀后的五金件具有良好的光亮度、硬度及耐腐蚀性，并且成品合格率高。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。 

Claims (4)

1.一种五金件电镀工艺，其特征在于，采用垂直旋转电镀方式，包括如下步骤：a、采用碱性溶液清洗去除五金件表面的油污：所述碱性溶液含有氢氧化钠40-50g/L、碳酸钠30-40g/L、磷酸三钠40-50g/L、OP-乳化剂2-5mL/L，所述碱性溶液的温度为80-90℃，清洗时间为15min；b、对上述去除表面油污后的五金件进行水洗后镀镍：电镀溶液含有氯化镍180-220g/L、盐酸120-150g/L，电镀电流密度3-4A/dm2，电镀时间10min，阳极为镍板；c、采用清水清洗电镀后的所述五金件并烘干。
2.根据权利要求1所述的五金件电镀工艺，其特征在于，所述碱性溶液含有氢氧化钠45g/L、碳酸钠32g/L、磷酸三钠47g/L、OP-乳化剂3mL/L。
3.根据权利要求1所述的五金件电镀工艺，其特征在于，所述电镀溶液含有氯化镍200g/L、盐酸130g/L。
4.根据权利要求1所述的五金件电镀工艺，其特征在于，所述电镀电流密度3.5A/dm2。
CN201410414763.0A 2014-08-22 2014-08-22 一种五金件电镀工艺 Pending CN104213160A (zh)