CN104211368B - 一种轻质空心砖及其制备方法 - Google Patents
一种轻质空心砖及其制备方法 Download PDFInfo
- Publication number
- CN104211368B CN104211368B CN201410402266.9A CN201410402266A CN104211368B CN 104211368 B CN104211368 B CN 104211368B CN 201410402266 A CN201410402266 A CN 201410402266A CN 104211368 B CN104211368 B CN 104211368B
- Authority
- CN
- China
- Prior art keywords
- brick
- light
- powder
- hollow
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种轻质空心砖,由下列重量份的原材料制成:氧化镁30-40,氯化镁8-10,复合发泡剂0.4-0.6,碳纤维2-4,自制混凝土10-15、余量为水,所述的复合发泡剂由下列重量份的组分原料混合而成:珍珠岩20-30、KMnO4?4-5、过碳酸钠20-30、聚丙烯酸钠1-2、焦磷酸钠4-6、三乙醇胺0.2-0.4、甲酸1-2、三氯丙基磷酸酯1-2、氧化锌2-3、磷酸三乙酯4-5、纳米银0.1-0.2组成,将配料进行搅拌、磨粉,混合均匀,即可。本发明的轻质空心砖,具有质量轻,孔洞大小均匀,隔音、保温效果好,同时本空心砖还具有防火、防水、防震、防腐、强度高,可锯的特点。
Description
技术领域
本发明涉及新型建材领域,具体属于一种轻质空心砖及其制备方法。
背景技术
传统的空心砖是以粘土、页岩等为主要原料,经过原料处理、成型、烧结制成,质轻、强度高、保温、隔音降噪性能好。
随着建筑业的发展,对空心砖的需求量日益增大,制造传统空心砖浪费将要浪费大量粘土等资源,成本高,烧制时污染环境。
发明内容
本发明的目的在于提供一种轻质空心砖及其制备方法,本发明的轻质空心砖掺渣利废比例高,原料来源广泛,成本低廉,使用广泛,产品综合品质稳定,同时该轻质空心砖具有耐火性高,加工工艺简单,不污染环境等优点,同时为空心砖生产提供了新的原料来源。
本发明的技术方案如下:一种轻质空心砖,其特征在于,由下列重量份的原材料制成:氧化镁30-40,氯化镁8-10,复合发泡剂0.4-0.6,碳纤维2-4,自制混凝土10-15、余量为水,所述的复合发泡剂由下列重量份的组分原料混合而成:珍珠岩20-30、KMnO44-5、过碳酸钠20-30、聚丙烯酸钠1-2、焦磷酸钠4-6、三乙醇胺0.2-0.4、甲酸1-2、三氯丙基磷酸酯1-2、氧化锌2-3、磷酸三乙酯4-5、纳米银0.1-0.2组成,将配料进行搅拌、磨粉,混合均匀,即可。所述的自制混凝土由下列方法制备而成:(1)、按重量份称取建筑垃圾破碎40-50、硫酸铝渣10-15、火山灰12-15、沸石粉2-3、粉煤灰3-4、农作物秸秆粉10-12、锯末10-12,废铝粉1-2、钨粉3-5、氧化镁2-4、松香皂化酯1-3、乙酸10-15、尿素5-8、甲基丙烯酸缩水甘油酯1-2、甲基丙烯酸酯1-2、乙二胺1-5、亚麻油0.2-0.4;(2)、将称取的建筑垃圾破碎,然后放入浓度为20-30%的纳米二氧化硅水胶体中浸泡处理6-8天,捞出,得到A料;(3)、将氧化镁、钨粉、松香皂化酯、乙酸、尿素、甲基丙烯酸缩水甘油酯、甲基丙烯酸酯、乙二胺、亚麻油加入到搅拌釜里,常温下混合充分搅拌10-15分钟,得到B料;(4)将A料、B料混合及配方中的其余物料混合,再加入适量的水,混合成浆料,再将废铝粉加入浆料中充分搅拌后,加入搅拌成型机加工成料球,自然晾干成生料球后,再经200-300℃焙烧1-小时,再粉碎成粉料即可。
所述的轻质空心砖的制备方法,其特征在于,包括以下步骤:
(1)按配方比例将氯化镁、氧化镁依次投入水中充分搅拌溶解;
(2)再加碳纤维搅拌均匀,加入三分一复合发泡剂充分搅拌后,再加入自制混凝土搅拌5-10分钟后,将剩下的发泡剂全部加入其中充分搅拌成浆料;
(3)将搅拌好的浆料灌进轻质空心砖的模具中,常温下陈化70-75小时,然后出模常温下自然养护15-20天,即可入成品库。
本发明与现有技术相比具有如下优点:
本发明的轻质空心砖,具有质量轻,孔洞大小均匀,隔音、保温效果好,同时本空心砖还具有防火、防水、防震、防腐、强度高,可锯的特点。
具体实施方式
一种轻质空心砖,由下列重量(kg)的原材料制成:环保粉粒建筑材料40、炉渣灰15、砂子13、自制混凝土9、镍铬铁合金渣26、电石渣11、高粘凹凸棒石粘土粉5、碳酸氢钠5、烷基苯磺酸钠2、二羟乙基或羟丙基甲基纤维素0.4、茶皂素0.2、氧化锑2、硼酸锌5、适量的水,
其中,自制混凝土由下列方法制备而成:(1)、按重量(kg)称取建筑垃圾45、硫酸铝渣13、火山灰14、沸石粉2.5、粉煤灰3.5、农作物秸秆粉11、锯末11,废铝粉1.5、钨粉4、氧化镁3、松香皂化酯2、乙酸14、尿素7、甲基丙烯酸缩水甘油酯1、甲基丙烯酸酯2、乙二胺4、亚麻油0.3;(2)、将称取的建筑垃圾破碎,然后放入浓度为20-30%的纳米二氧化硅水胶体中浸泡处理7天,捞出,得到A料;(3)、将氧化镁、钨粉、松香皂化酯、乙酸、尿素、甲基丙烯酸缩水甘油酯、甲基丙烯酸酯、乙二胺、亚麻油加入到搅拌釜里,常温下混合充分搅拌13分钟,得到B料;(4)将A料、B料混合及配方中的其余物料混合,再加入适量的水,混合成浆料,再将废铝粉加入浆料中充分搅拌后,加入搅拌成型机加工成料球,自然晾干成生料球后,再经250℃焙烧1小时,再粉碎成粉料即可。
轻质空心砖的制备方法,包括以下步骤:
(1)按配方比例将氯化镁、氧化镁依次投入水中充分搅拌溶解;
(2)再加碳纤维搅拌均匀,加入三分一复合发泡剂充分搅拌后,再加入自制混凝土搅拌5-10分钟后,将剩下的发泡剂全部加入其中充分搅拌成浆料;
(3)将搅拌好的浆料灌进轻质空心砖的模具中,常温下陈化70-75小时,然后出模常温下自然养护15-20天,即可入成品库。
经检测,本实施例制得的空心砖的容重、导热系数、承压能力分别为:1075kg/m3、0.349w/(m.K)、3.326Mpa。
Claims (2)
1.一种轻质空心砖,其特征在于,由下列重量份的原材料制成:氧化镁30-40、氯化镁8-10、复合发泡剂0.4-0.6、碳纤维2-4、自制混凝土10-15、适量水;所述的复合发泡剂由下列重量份的组分原料混合而成:珍珠岩20-30、KMnO44-5、过碳酸钠20-30、聚丙烯酸钠1-2、焦磷酸钠4-6、三乙醇胺0.2-0.4、甲酸1-2、三氯丙基磷酸酯1-2、氧化锌2-3、磷酸三乙酯4-5、纳米银0.1-0.2组成,将配料进行搅拌、磨粉,混合均匀,即可;
所述的自制混凝土由下列方法制备而成:(1)、按重量份称取建筑垃圾40-50、硫酸铝渣10-15、火山灰12-15、沸石粉2-3、粉煤灰3-4、农作物秸秆粉10-12、锯末10-12、废铝粉1-2、钨粉3-5、氧化镁2-4、松香皂化酯1-3、乙酸10-15、尿素5-8、甲基丙烯酸缩水甘油酯1-2、甲基丙烯酸酯1-2、乙二胺1-5、亚麻油0.2-0.4;(2)、将称取的建筑垃圾破碎,然后放入浓度为20-30%的纳米二氧化硅水胶体中浸泡处理6-8天,捞出,得到A料;(3)、将氧化镁、钨粉、松香皂化酯、乙酸、尿素、甲基丙烯酸缩水甘油酯、甲基丙烯酸酯、乙二胺、亚麻油加入到搅拌釜里,常温下混合充分搅拌10-15分钟,得到B料;(4)将A料、B料混合及配方中除废铝粉的其余物料混合,再加入适量的水,混合成浆料,再将废铝粉加入浆料中充分搅拌后,加入搅拌成型机加工成料球,自然晾干成生料球后,再经200-300℃焙烧1小时,再粉碎成粉料即可。
2.如权利要求1所述的轻质空心砖的制备方法,其特征在于,包括以下步骤:
(1)按配方比例将氯化镁、氧化镁依次投入水中充分搅拌溶解;
(2)再加碳纤维搅拌均匀,加入三分之一复合发泡剂充分搅拌后,再加入自制混凝土搅拌5-10分钟后,将剩下的发泡剂全部加入其中充分搅拌成浆料;
(3)将搅拌好的浆料灌进轻质空心砖的模具中,常温下陈化70-75小时,然后出模常温下自然养护15-20天,即可入成品库。