CN104193894A - 橡胶锤用橡胶生产工艺 - Google Patents

橡胶锤用橡胶生产工艺 Download PDF

Info

Publication number
CN104193894A
CN104193894A CN201410503675.8A CN201410503675A CN104193894A CN 104193894 A CN104193894 A CN 104193894A CN 201410503675 A CN201410503675 A CN 201410503675A CN 104193894 A CN104193894 A CN 104193894A
Authority
CN
China
Prior art keywords
rubber
latex
condensation
storage tank
production process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410503675.8A
Other languages
English (en)
Inventor
马聚龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Dongbeitang Yongfeng Rubber Plastic Factory
Original Assignee
Wuxi Dongbeitang Yongfeng Rubber Plastic Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Dongbeitang Yongfeng Rubber Plastic Factory filed Critical Wuxi Dongbeitang Yongfeng Rubber Plastic Factory
Priority to CN201410503675.8A priority Critical patent/CN104193894A/zh
Publication of CN104193894A publication Critical patent/CN104193894A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种橡胶锤用橡胶生产工艺，包括如下步骤：1）将丁烯腈、丙二烯、浓缩水和聚合剂按3:1:1:1的质量比进行物料混合；2）将混合物料进入反应釜，再往反应釜中加入剂乳液和活化剂支取胶乳；3）对经反应釜制取的胶乳进行脱气，脱气后的胶乳进入胶乳储槽中；4）将胶乳储槽中的胶乳送至凝聚釜进行凝聚；5）再将凝聚后的橡胶先用质量浓度为0.2-0.5%的烧碱溶液下清洗2-3次，再用质量浓度为0.2-0.5%的盐酸溶液在在20-40℃的温度下清洗4-5次；6）最后脱水、最后进入干燥箱干燥得橡胶。本发明操作简单，工艺巧妙，经本发明处理的橡胶具有较强的耐磨和抗腐蚀性能，使用寿命长。

Description

橡胶锤用橡胶生产工艺
技术领域
本发明涉及橡胶领域，具体地说，特别涉及到一种橡胶锤用橡胶生产工艺。
 
背景技术
在装修行业安装地板时，为了使地板砖下的水泥分布均匀不出现空洞，往往使用橡胶锤敲击地板砖。现有的橡胶锤，包括锤体和手柄，锤体内设有内芯，锤体和手柄为一体结构。现有的橡胶锤是采用的橡胶在长期使用后会出现橡胶疲劳、受损、被腐蚀等问题，影响橡胶锤的使用寿命。
发明内容
本发明的目的在于针对现有技术中的不足，提供一种橡胶锤用橡胶生产工艺，以解决上述问题。
本发明所解决的技术问题可以采用以下技术方案来实现：
橡胶锤用橡胶生产工艺，包括如下步骤：
1）将丁烯腈、丙二烯、浓缩水和聚合剂按3:1:1:1的质量比进行物料混合；
2）将混合物料进入反应釜，再往反应釜中加入剂乳液和活化剂支取胶乳；
3）对经反应釜制取的胶乳进行脱气，脱气后的胶乳进入胶乳储槽中；
4）将胶乳储槽中的胶乳送至凝聚釜进行凝聚；
5）再将凝聚后的橡胶先用质量浓度为0.2-0.5%的烧碱溶液下清洗2-3次，再用质量浓度为0.2-0.5%的盐酸溶液在在20-40℃的温度下清洗4-5次；
6）最后脱水、最后进入干燥箱干燥得橡胶。
优选的，所述步骤5）中烧碱溶液的最佳浓度为0.3%，最佳清洗次数为2次。
优选的，所述步骤5）中盐酸溶液的最佳浓度为0.3%，最佳清洗次数为2次。
与现有技术相比，本发明的有益效果如下：
操作简单，工艺巧妙，经本发明处理的橡胶具有较强的耐磨和抗腐蚀性能，使用寿命长。
 
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
实施例1
橡胶锤用橡胶生产工艺，包括如下步骤：
1）将丁烯腈、丙二烯、浓缩水和聚合剂按3:1:1:1的质量比进行物料混合；
2）将混合物料进入反应釜，再往反应釜中加入剂乳液和活化剂支取胶乳；
3）对经反应釜制取的胶乳进行脱气，脱气后的胶乳进入胶乳储槽中；
4）将胶乳储槽中的胶乳送至凝聚釜进行凝聚；
5）再将凝聚后的橡胶先用质量浓度为0.2%的烧碱溶液下清洗2次，再用质量浓度为0.2%的盐酸溶液在在20℃的温度下清洗4次；
6）最后脱水、最后进入干燥箱干燥得橡胶。
实施例2
橡胶锤用橡胶生产工艺，包括如下步骤：
1）将丁烯腈、丙二烯、浓缩水和聚合剂按3:1:1:1的质量比进行物料混合；
2）将混合物料进入反应釜，再往反应釜中加入剂乳液和活化剂支取胶乳；
3）对经反应釜制取的胶乳进行脱气，脱气后的胶乳进入胶乳储槽中；
4）将胶乳储槽中的胶乳送至凝聚釜进行凝聚；
5）再将凝聚后的橡胶先用质量浓度为0.5%的烧碱溶液下清洗3次，再用质量浓度为0.5%的盐酸溶液在在40℃的温度下清洗5次；
6）最后脱水、最后进入干燥箱干燥得橡胶。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.橡胶锤用橡胶生产工艺，其特征在于，包括如下步骤：
1）将丁烯腈、丙二烯、浓缩水和聚合剂按3:1:1:1的质量比进行物料混合；
2）将混合物料进入反应釜，再往反应釜中加入剂乳液和活化剂支取胶乳；
3）对经反应釜制取的胶乳进行脱气，脱气后的胶乳进入胶乳储槽中；
4）将胶乳储槽中的胶乳送至凝聚釜进行凝聚；
5）再将凝聚后的橡胶先用质量浓度为0.2-0.5%的烧碱溶液下清洗2-3次，再用质量浓度为0.2-0.5%的盐酸溶液在在20-40℃的温度下清洗4-5次；
6）最后脱水、最后进入干燥箱干燥得橡胶。
2.根据权利要求1所述的橡胶锤用橡胶生产工艺，其特征在于，所述步骤5）中烧碱溶液的最佳浓度为0.3%，最佳清洗次数为2次。
3.根据权利要求1所述的橡胶锤用橡胶生产工艺，其特征在于，所述步骤5）中盐酸溶液的最佳浓度为0.3%，最佳清洗次数为2次。
CN201410503675.8A 2014-09-28 2014-09-28 橡胶锤用橡胶生产工艺 Pending CN104193894A (zh)