CN104178010A - Composite coating for outdoor deck chair and preparation method thereof - Google Patents
Composite coating for outdoor deck chair and preparation method thereof Download PDFInfo
- Publication number
- CN104178010A CN104178010A CN201410431929.XA CN201410431929A CN104178010A CN 104178010 A CN104178010 A CN 104178010A CN 201410431929 A CN201410431929 A CN 201410431929A CN 104178010 A CN104178010 A CN 104178010A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite coating
- chaise longue
- agents
- outdoor chaise
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a composite coating for an outdoor deck chair. The composite coating comprises the following components in parts by weight: 30-45 parts of emulsions, 5-8 parts of anti-mildew agents, 5-18 parts of titanium dioxide, 2-5 parts of film-forming auxiliary agents, 10-15 parts of ethylene copolymer elastomers, 10-20 parts of anti-slipping agents, 0.5-1 part of anti-aging agents, 8-12 parts of lithopone, 0.2-0.3 part of defoaming agents, 5-8 parts of ammonium polyphosphate, 5-8 parts of nanometer calcium carbonate, 1-3 parts of iron powder and 30-45 parts of water. The composite coating for the outdoor deck chair, which is prepared through the interaction and intercoordination of the components by selecting the emulsions, the film-forming auxiliary agents, the anti-slipping agents and the like of a proper formula in proper proportion and using the anti-mildew agents, the anti-aging agents, the ethylene copolymer elastomers, the lithopone, the iron powder, the nanometer calcium carbonate and the like for cooperation, has the characteristics of strong light irradiation resistance, aging resistance, rainwater erosion resistance, slip resistance and the like.
Description
Technical field
The present invention relates to coating material field, particularly, relate to a kind of outdoor chaise longue composite coating and preparation method thereof.
Background technology
Along with the raising of people's living standard, people more and more like carrying out outdoor activity.Seashore is the good place to go of people's amusement and recreation, and beach chair and outdoor chair also become people and select the good place of having a rest.As the chaise longue of outdoor, not only require the people that is more suitable for of its structure design to have a rest, meanwhile, also to there is resistance to strong illumination, ageing-resistant, rain erosion resistant, anti-skidding etc. characteristic.The existing coating for chair can not meet the requirements such as resistance to strong illumination, ageing-resistant, rain erosion resistant simultaneously.
Summary of the invention
Goal of the invention: the technical problem to be solved in the present invention is to provide a kind of outdoor chaise longue composite coating, this coating colleague has resistance to strong illumination, ageing-resistant, rain erosion resistant, the characteristic such as anti-skidding.
The present invention also technical issues that need to address is to provide the preparation method of above-mentioned outdoor chaise longue with composite coating.
Technique means: for realizing above-mentioned technical purpose, the invention provides a kind of outdoor chaise longue composite coating, it comprises the component of following parts by weight: 30～45 parts, 30～45 parts of emulsions, 5～8 parts of mould inhibitors, 5～18 parts of titanium dioxides, 2～5 parts of film coalescence aid, 10～15 parts of Toughening Effect of Ethylene Copolymer Elastomers, 10～20 parts of slipproofing agents, 0.5～1 part, anti-aging agent, 8～12 parts, zinc sulfide white, 0.2～0.3 part of defoamer, 5～8 parts of polyphosphoric acid amines, 5～8 parts of nano-calcium carbonates, 1～3 part of iron powder and water.
Preferably, described outdoor chaise longue comprises the component of following parts by weight with composite coating: 40 parts, 40 parts of emulsions, 6 parts of mould inhibitors, 15 parts of titanium dioxides, 3 parts of film coalescence aid, 13 parts of Toughening Effect of Ethylene Copolymer Elastomers, 15 parts of slipproofing agents, 0.8 part, anti-aging agent, 10 parts, zinc sulfide white, 0.25 part of defoamer, 6 parts of polyphosphoric acid amines, 7 parts of nano-calcium carbonates, 2 parts of iron powders and water.
Preferably, described emulsion is any one in polyaminoester emulsion, benzene emulsion, organosilicon crylic acid latex, and wherein, the solid content of described emulsion is 45～60%.
Described mould inhibitor is any one in silicone quaternary ammonium salt, Bitertanol and dibenzoyl peroxide.
Described film coalescence aid is any one in voltalef, resol and ethylene glycol monomethyl ether.
Described slipproofing agent is any one or a few in rubber particles, hollow glass micropearl and polyurethane particles, and wherein, the particle diameter of described slipproofing agent is 200～240 orders.Be preferably hollow glass micropearl and rubber particles.Use hollow glass micropearl, when coating is constantly exposed new surface because wearing and tearing, pressurized makes surperficial bead break and forms new pit, has strengthened surperficial roughness, increases friction resistance, even skidproof effect is also fine under water hygrometric state.And rubber ion is the most frequently used anti-slip particles, not only can increase anti-skid, can also increase comfort.Functional quality can reach anti-skidding and comfortable object of trampling than the mixture that is the rubber ion of 1:1 and hollow glass micropearl as slipproofing agent simultaneously, is more conducive to anti-skidding on rainy day.
Described anti-aging agent is 4,4'-thiobis (the 6-tertiary butyl-3-methylphenol), β-(3, tri-grades of butyl-4-hydroxy phenyls of 5-) propionic acid octadecanol ester, tricresyl phosphite fat (2,4-di-tert-butyl-phenyl), any one in two (2,4-di-tert-butyl-phenyl) pentaerythritol diphosphites.
Described defoamer is silicone antifoam agent.
The invention allows for the preparation method of composite coating for above-mentioned outdoor chaise longue, it is characterized in that, comprise the steps: said components to mix, constant temperature at the uniform velocity stirs, and each component is uniformly distributed.
Preferably, the condition that described constant temperature average rate stirs is that the speed of 80～100r/min at 25～28 ℃ stirs 4～5h.
Described anti-aging agent is 4,4'-thiobis (the 6-tertiary butyl-3-methylphenol), β-(3, tri-grades of butyl-4-hydroxy phenyls of 5-) propionic acid octadecanol ester, tricresyl phosphite fat (2,4-di-tert-butyl-phenyl), any one in two (2,4-di-tert-butyl-phenyl) pentaerythritol diphosphites.By adding anti-aging agent, can improve the wearing quality of coating.Be preferably tricresyl phosphite fat (2,4-di-tert-butyl-phenyl).
The invention allows for the preparation method of composite coating for above-mentioned outdoor chaise longue, comprise the steps: said components to mix, constant temperature at the uniform velocity stirs, and each component is uniformly distributed.
Preferably, the condition that described constant temperature average rate stirs is that the speed of 80～100r/min at 25～28 ℃ stirs 4～5h.
Beneficial effect: compared with prior art, the present invention is by selecting the emulsion, film coalescence aid, slipproofing agent etc. of suitable formula and ratio, and coordinate mould inhibitor, anti-aging agent, Toughening Effect of Ethylene Copolymer Elastomer, zinc sulfide white, iron powder and nano-calcium carbonate etc. use, by interaction and the coordination of each component, prepared outdoor chaise longue can have resistance to strong illumination, ageing-resistant, rain erosion resistant, the characteristic such as anti-skidding with composite coating simultaneously.
Embodiment
According to following embodiment, the present invention may be better understood.Yet, those skilled in the art will readily understand, the described content of embodiment is only for the present invention is described, and should also can not limit the present invention described in detail in claims.
Embodiment 1
A kind of outdoor chaise longue composite coating, the component that comprises following parts by weight: 5 parts of 40 parts of polyaminoester emulsions, 6 parts of Bitertanols, 15 parts of titanium dioxides, 3 parts of film coalescence aid, 13 parts of Toughening Effect of Ethylene Copolymer Elastomers, 10 parts of hollow glass micropearls, rubber particles, 4,40 parts, 0.8 part of 4'-thiobis (the 6-tertiary butyl-3-methylphenol), 10 parts, zinc sulfide white, 0.25 part of silicone antifoam agent, 6 parts of polyphosphoric acid amines, 7 parts of nano-calcium carbonates, 2 parts of iron powders and water.Said components is mixed, and the speed with 100r/min at 25 ℃ stirs 5h, obtains.
Embodiment 2
A kind of outdoor chaise longue composite coating, the component that comprises following parts by weight: 30 parts, 30 parts of benzene emulsions, 8 parts of silicone quaternary ammonium salts, 5 parts of titanium dioxides, 5 parts of ethylene glycol monomethyl ethers, 10 parts of Toughening Effect of Ethylene Copolymer Elastomers, 10 parts of hollow glass micropearls, 10 parts of polyurethane particles, β-(tri-grades of butyl-4-hydroxy phenyls of 3,5-) 0.5 part of propionic acid octadecanol ester, 12 parts, zinc sulfide white, 0.2 part of silicone antifoam agent, 8 parts of polyphosphoric acid amines, 5 parts of nano-calcium carbonates, 3 parts of iron powders and water.Said components is mixed, and the speed with 100r/min at 28 ℃ stirs 5h, obtains.
Embodiment 3
A kind of outdoor chaise longue composite coating, the component that comprises following parts by weight: 45 parts, 45 parts of organosilicon crylic acid latexs, 5 parts of dibenzoyl peroxide, 18 parts of titanium dioxides, 2 parts of voltalef, 15 parts of Toughening Effect of Ethylene Copolymer Elastomers, 10 parts of rubber particles, 1 part, tricresyl phosphite fat (2,4-di-tert-butyl-phenyl), 8 parts, zinc sulfide white, 0.3 part of silicone antifoam agent, 5 parts of polyphosphoric acid amines, 8 parts of nano-calcium carbonates, 1 part of iron powder and water.Said components is mixed, and the speed with 100r/min at 28 ℃ stirs 5h, obtains.
Embodiment 4
A kind of outdoor chaise longue composite coating, the component that comprises following parts by weight: 38 parts, 37 parts of benzene emulsions, 6 parts of Bitertanols, 10 parts of titanium dioxides, 3 parts, resol, 11 parts of Toughening Effect of Ethylene Copolymer Elastomers, 6 parts of rubber particles, 7 parts of hollow glass micropearls, 0.7 part of two (2,4-di-tert-butyl-phenyl) pentaerythritol diphosphites, 9 parts, zinc sulfide white, 0.25 part of silicone antifoam agent, 6 parts of polyphosphoric acid amines, 7 parts of nano-calcium carbonates, 2 parts of iron powders and water.Said components is mixed, and the speed with 100r/min at 25 ℃ stirs 5h, obtains.
Embodiment 5
A kind of outdoor chaise longue composite coating, the component that comprises following parts by weight: 45 parts, 42 parts of organosilicon crylic acid latexs, 6 parts of dibenzoyl peroxide, 10 parts of titanium dioxides, 24 parts of ethylene glycol monomethyl ethers, 13 parts of Toughening Effect of Ethylene Copolymer Elastomers, 8 parts of hollow glass micropearls, 8 parts of rubber particles, 0.8 part, tricresyl phosphite fat (2,4-di-tert-butyl-phenyl), 10 parts, zinc sulfide white, 0.22 part of silicone antifoam agent, 7 parts of polyphosphoric acid amines, 6 parts of nano-calcium carbonates, 3 parts of iron powders and water.Said components is mixed, and the speed with 100r/min at 25 ℃ stirs 5h, obtains.
Embodiment 6
Outdoor chaise longue to embodiment 1～5 preparation carries out performance test with composite coating, and its result is as shown in table 1:
The outdoor chaise longue of table 1 coating property index
Note: alkali-proof evaluation is coating to be placed in to 10%NaOH solution soaking detect.
Claims (9)
1. an outdoor chaise longue composite coating, it is characterized in that, comprise the component of following parts by weight: 30～45 parts, 30～45 parts of emulsions, 5～8 parts of mould inhibitors, 5～18 parts of titanium dioxides, 2～5 parts of film coalescence aid, 10～15 parts of Toughening Effect of Ethylene Copolymer Elastomers, 10～20 parts of slipproofing agents, 0.5～1 part, anti-aging agent, 8～12 parts, zinc sulfide white, 0.2～0.3 part of defoamer, 5～8 parts of polyphosphoric acid amines, 5～8 parts of nano-calcium carbonates, 1～3 part of iron powder and water.
2. outdoor chaise longue composite coating according to claim 1, is characterized in that, described emulsion is any one in polyaminoester emulsion, benzene emulsion, organosilicon crylic acid latex, and wherein, the solid content of described emulsion is 45～60%.
3. outdoor chaise longue composite coating according to claim 1, is characterized in that, described mould inhibitor is any one in silicone quaternary ammonium salt, Bitertanol and dibenzoyl peroxide.
4. outdoor chaise longue composite coating according to claim 1, is characterized in that, described film coalescence aid is any one in voltalef, resol and ethylene glycol monomethyl ether.
5. outdoor chaise longue composite coating according to claim 1, is characterized in that, described slipproofing agent is any one or a few in rubber particles, hollow glass micropearl and polyurethane particles, and wherein, the particle diameter of described slipproofing agent is 200～240 orders.
6. outdoor chaise longue composite coating according to claim 1, it is characterized in that, described anti-aging agent is 4,4'-thiobis (the 6-tertiary butyl-3-methylphenol), β-(3, tri-grades of butyl-4-hydroxy phenyls of 5-) propionic acid octadecanol ester, tricresyl phosphite fat (2,4-di-tert-butyl-phenyl), any one in two (2,4-di-tert-butyl-phenyl) pentaerythritol diphosphites.
7. outdoor chaise longue composite coating according to claim 1, is characterized in that, described defoamer is silicone antifoam agent.
8. the preparation method of composite coating for outdoor chaise longue claimed in claim 1, is characterized in that, comprise the steps: said components to mix, constant temperature at the uniform velocity stirs, and each component is uniformly distributed.
9. preparation method according to claim 8, is characterized in that, the condition that described constant temperature average rate stirs is that the speed of 80～100r/min at 25～28 ℃ stirs 4～5h.