CN104194601A - Antiskid paint for bicycle court tracks and preparation method thereof - Google Patents
Antiskid paint for bicycle court tracks and preparation method thereof Download PDFInfo
- Publication number
- CN104194601A CN104194601A CN201410432805.3A CN201410432805A CN104194601A CN 104194601 A CN104194601 A CN 104194601A CN 201410432805 A CN201410432805 A CN 201410432805A CN 104194601 A CN104194601 A CN 104194601A
- Authority
- CN
- China
- Prior art keywords
- parts
- velodrome
- resistant coating
- skid
- runway
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antiskid paint for bicycle court tracks, which comprises the following components in parts by weight: 25-40 parts of emulsion, 5-8 parts of light calcium carbonate, 3-8 parts of titanium white, 2-5 parts of film formation assistant, 5-8 parts of talcum powder, 10-25 parts of antiskid agent, 0.5-1 part of anti-aging agent, 8-12 parts of lithopone, 0.2-0.3 part of defoaming agent and 35-45 parts of water. The invention also discloses a preparation method of the antiskid paint. By selecting the emulsion, film formation assistant, antiskid agent and the like according to the proper formula and proportion and combining the film formation assistant, talcum powder, lithopone and defoaming agent, all the components interact and are coordinated, so that the prepared antiskid paint has the characteristics of favorable antiskid effect, excellent water resistance and favorable wear resistance, and is especially suitable for bicycle court tracks.
Description
Technical field
The present invention relates to coating material field, particularly, relate to a kind of velodrome runway skid-resistant coating.
Background technology
Sports represents the economic looks of Zhe Yi state, particularly 2008 Olympic Games and the Asian Games in 2010 wins the bidding, much and will build more multi-class stadiums, wherein the construction of bicycle racing venue also obtains very large development in big or middle city in the whole nation.Venue racing track not only will be considered long-term work-ing life, also will consider the factors such as environment protection, economy and suitability simultaneously.The anti-skid of two runways is key links of the whole match of restriction, existing skid-resistant coating can not meet water tolerance and wear resistant etc. when improving anti-skid simultaneously, therefore, need to develop a kind of skid-resistant coating, when guaranteeing anti-skid, improve weathering resistance, water tolerance and the wear resistance of runway.
Summary of the invention
Goal of the invention: the technical problem to be solved in the present invention is to provide a kind of velodrome runway skid-resistant coating, this coating, when improving anti-skid, also has excellent weathering resistance, water tolerance and wear resistance.
The present invention also technical issues that need to address is to provide the preparation method of above-mentioned velodrome runway with skid-resistant coating.
Technique means: for realizing above-mentioned technical purpose, the invention provides a kind of velodrome runway skid-resistant coating, it comprises the component of following parts by weight: 35~45 parts, 25~40 parts of emulsions, 5~8 parts of light calcium carbonates, 3~8 parts of titanium dioxides, 2~5 parts of film coalescence aid, 5~8 parts of talcum powder, 10~25 parts of slipproofing agents, 0.5~1 part, anti-aging agent, 8~12 parts, zinc sulfide white, 0.2~0.3 part of defoamer and water.
Preferably, described velodrome runway comprises the component of following parts by weight with skid-resistant coating: 38~42 parts, 30~35 parts of emulsions, 6~8 parts of light calcium carbonates, 5~8 parts of titanium dioxides, 3~4 parts of film coalescence aid, 6~7 parts of talcum powder, 15~20 parts of slipproofing agents, 0.8~1 part, anti-aging agent, 10~12 parts, zinc sulfide white, 0.25~0.3 part of defoamer and water.
The most preferably, described velodrome runway comprises the component of following parts by weight with skid-resistant coating: 40 parts, 32 parts of emulsions, 7 parts of light calcium carbonates, 6 parts of titanium dioxides, 3.5 parts of film coalescence aid, 6.5 parts of talcum powder, 18 parts of slipproofing agents, 0.9 part, anti-aging agent, 11 parts, zinc sulfide white, 0.29 part of defoamer and water.
Particularly, described emulsion is any one in polyaminoester emulsion, benzene emulsion, organosilicon crylic acid latex, and wherein, the solid content of described emulsion is 45~60%.Preferably, described emulsion is polyaminoester emulsion.
Described film coalescence aid is voltalef or resol.
Described slipproofing agent is any one or a few in rubber particles, hollow glass micropearl and polyurethane particles, and wherein, the particle diameter of described slipproofing agent is 120~200 orders.Be preferably hollow glass micropearl and rubber particles.Use hollow glass micropearl, when coating, because wearing and tearing, constantly exposing new surface is that pressurized makes surperficial bead break and forms new pit, has strengthened surperficial roughness, increases friction resistance, even skidproof effect is also fine under water hygrometric state.And rubber ion is the most frequently used anti-slip particles, not only can increase anti-skid, can also increase the comfort of trampling.Functional quality can reach anti-skidding and comfortable object of trampling than the mixture that is the rubber ion of 1:1 and hollow glass micropearl as slipproofing agent simultaneously, is more conducive to anti-skidding on rainy day.
Described anti-aging agent is 4,4 '-thiobis (the 6-tertiary butyl-3-methylphenol), β-(3, tri-grades of butyl-4-hydroxy phenyls of 5-) propionic acid octadecanol ester, tricresyl phosphite fat (2,4-di-tert-butyl-phenyl), any one in two (2,4-di-tert-butyl-phenyl) pentaerythritol diphosphites.By adding anti-aging agent, can improve the wearing quality of coating.Be preferably tricresyl phosphite fat (2,4-di-tert-butyl-phenyl).
The invention allows for the preparation method of skid-resistant coating for above-mentioned velodrome runway, comprise the steps: said components to mix, constant temperature at the uniform velocity stirs, and each component is uniformly distributed.
Preferably, the condition that described constant temperature average rate stirs is that the speed of 80~100r/min at 25~28 ℃ stirs 4~5h.
Beneficial effect: compared with prior art, the present invention is by selecting the emulsion, film coalescence aid, slipproofing agent etc. of suitable formula and ratio, and coordinate the use of film coalescence aid, talcum powder, zinc sulfide white and defoamer, by interaction and the coordination of each component, prepared skid-resistant coating has good antiskid effect, water tolerance is excellent and wear resistant is good feature, is especially applicable to velodrome runway.
Embodiment
According to following embodiment, the present invention may be better understood.Yet, those skilled in the art will readily understand, the described content of embodiment is only for the present invention is described, and should also can not limit the present invention described in detail in claims.
Embodiment 1
A kind of velodrome runway skid-resistant coating, the component that comprises following parts by weight: 40 parts, 0.29 part of 32 parts of polyaminoester emulsion, 7 parts of light calcium carbonates, 6 parts of titanium dioxides, 3.5 parts, resol, 6.5 parts of talcum powder, 9 parts of hollow glass micropearls (200 order), 9 parts of rubber particles (200 order), 0.9 part, tricresyl phosphite fat (2,4-di-tert-butyl-phenyl), 11 parts, zinc sulfide white, defoamer (BYK-055) and water.Said components is mixed, and the speed with 100r/min at 25 ℃ stirs 5h, obtains.
Embodiment 2
A kind of velodrome runway skid-resistant coating, the component that comprises following parts by weight: 42 parts, 0.3 part of 30 parts of benzene emulsion, 8 parts of light calcium carbonates, 5 parts of titanium dioxides, 4 parts, resol, 6 parts of talcum powder, 20 parts of hollow glass micropearls (200 order), 1.0 parts of 4,4 '-thiobiss (the 6-tertiary butyl-3-methylphenol), 11 parts, zinc sulfide white, defoamer (BYK-055) and water.Said components is mixed, and the speed with 100r/min at 28 ℃ stirs 5h, obtains.
Embodiment 3
A kind of velodrome runway skid-resistant coating, the component that comprises following parts by weight: 38 parts, 0.25 part of 35 parts of organosilicon crylic acid latex, 6 parts of light calcium carbonates, 8 parts of titanium dioxides, 4 parts of voltalef, 7 parts of talcum powder, 20 parts of rubber particles (200 order), β-(tri-grades of butyl-4-hydroxy phenyls of 3,5-) 0.8 part of propionic acid octadecanol ester, 12 parts, zinc sulfide white, defoamer (BYK-055) and water.Said components is mixed, and the speed with 100r/min at 28 ℃ stirs 5h, obtains.
Embodiment 4
A kind of velodrome runway skid-resistant coating, the component that comprises following parts by weight: 35 parts, 0.2 part of 28 parts of polyaminoester emulsion, 8 parts of light calcium carbonates, 3 parts of titanium dioxides, 2 parts of voltalef, 8 parts of talcum powder, 10 parts of rubber particles, 10 parts of hollow glass micropearls, 0.5 part of two (2,4-di-tert-butyl-phenyl) pentaerythritol diphosphites, 8 parts, zinc sulfide white, defoamer (BYK-055) and water.Said components is mixed, and the speed with 100r/min at 25 ℃ stirs 5h, obtains.
Embodiment 5
A kind of velodrome runway skid-resistant coating, the component that comprises following parts by weight: 45 parts, 0.3 part of 40 parts of benzene emulsion, 5 parts of light calcium carbonates, 8 parts of titanium dioxides, 5 parts, resol, 5 parts of talcum powder, 12 parts of rubber particles, 7 parts of polyurethane particles, 1 part, tricresyl phosphite fat (2,4-di-tert-butyl-phenyl), 12 parts, zinc sulfide white, defoamer (BYK-055) and water.Said components is mixed, and the speed with 100r/min at 25 ℃ stirs 5h, obtains.
Embodiment 6
Velodrome runway to embodiment 1~5 preparation carries out performance test with skid-resistant coating, and its result is as shown in table 1:
Table 1 skid-resistant coating performance index
Note: alkali-proof evaluation is coating to be placed in to 10%NaOH solution soaking detect.From above-mentioned detected result, can find out, velodrome runway prepared by the present invention is good by the non-skid property of skid-resistant coating, also has excellent weathering resistance, water tolerance and wear resistance.
Claims (8)
1. a velodrome runway skid-resistant coating, it is characterized in that, comprise the component of following parts by weight: 35~45 parts, 25~40 parts of emulsions, 5~8 parts of light calcium carbonates, 3~8 parts of titanium dioxides, 2~5 parts of film coalescence aid, 5~8 parts of talcum powder, 10~25 parts of slipproofing agents, 0.5~1 part, anti-aging agent, 8~12 parts, zinc sulfide white, 0.2~0.3 part of defoamer and water.
2. velodrome runway skid-resistant coating according to claim 1, it is characterized in that, comprise the component of following parts by weight: 38~42 parts, 30~35 parts of emulsions, 6~8 parts of light calcium carbonates, 5~8 parts of titanium dioxides, 3~4 parts of film coalescence aid, 6~7 parts of talcum powder, 15~20 parts of slipproofing agents, 0.8~1 part, anti-aging agent, 10~12 parts, zinc sulfide white, 0.25~0.3 part of defoamer and water.
3. velodrome runway skid-resistant coating according to claim 1 and 2, is characterized in that, described emulsion is any one in polyaminoester emulsion, benzene emulsion, organosilicon crylic acid latex, and wherein, the solid content of described emulsion is 45~60%.
4. velodrome runway skid-resistant coating according to claim 1 and 2, is characterized in that, described film coalescence aid is voltalef or resol.
5. velodrome runway skid-resistant coating according to claim 1 and 2, it is characterized in that, described slipproofing agent is any one or a few in rubber particles, hollow glass micropearl and polyurethane particles, and wherein, the particle diameter of described slipproofing agent is 120~200 orders.
6. velodrome runway skid-resistant coating according to claim 1 and 2, it is characterized in that, described anti-aging agent is 4,4 '-thiobis (the 6-tertiary butyl-3-methylphenol), β-(3, tri-grades of butyl-4-hydroxy phenyls of 5-) propionic acid octadecanol ester, tricresyl phosphite fat (2,4-di-tert-butyl-phenyl), any one in two (2,4-di-tert-butyl-phenyl) pentaerythritol diphosphites.
7. the preparation method of skid-resistant coating for velodrome runway claimed in claim 1, is characterized in that, comprise the steps: said components to mix, constant temperature at the uniform velocity stirs, and each component is uniformly distributed.
8. preparation method according to claim 7, is characterized in that, the condition that described constant temperature average rate stirs is that the speed of 80~100r/min at 25~28 ℃ stirs 4~5h.