CN105860683A - Non-slip composition for coating stadium - Google Patents
Non-slip composition for coating stadium Download PDFInfo
- Publication number
- CN105860683A CN105860683A CN201610249411.3A CN201610249411A CN105860683A CN 105860683 A CN105860683 A CN 105860683A CN 201610249411 A CN201610249411 A CN 201610249411A CN 105860683 A CN105860683 A CN 105860683A
- Authority
- CN
- China
- Prior art keywords
- parts
- stadium
- coated
- calcium hydroxide
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a non-slip composition for coating a stadium. The non-slip composition is prepared from the following components in parts by weight: 70 to 80 parts of styrene-acrylic emulsion, 12 to 16 parts of aliphatic ester sulfate, 7 to 10 parts of polyoxypropylene glycerol ether, 5 to 8 parts of sodium dehydroacetate, 13 to 17 parts of pH (potential of hydrogen) adjuster, and 30 to 35 parts of calcium hydroxide powder. By adopting the type, the non-slip composition for coating the stadium has the advantages that the adhesion force is very good; after coating, the surface roughness of the stadium can prevent the slipping of people in the walking process; the environment-protection property is excellent, the environment-friendly property is realized, and any toxic or side effect is avoided.
Description
Technical field
The present invention relates to anti-slip material field, particularly relate to a kind of on-slip compositions being coated on stadium.
Background technology
Stadium has referred to that 400-Meter Dash road, center contain football pitch, have fixing curb, runway more than 6, and has the outdoor Track field of fixing grandstand.Stadium accommodates attendance by grandstand and is divided into: more than first class 25000 people, second class 15000-25000 people, third class 5000-15000 people, below fourth level 5000 people.There are Bird's Nest, Shanghai Stadium, stadium, Nanjing etc. in the more famous stadium of China, and stadium is the most universal in foreign country.Because to hold various match in stadium, belong to the place that artificial abortion is bigger, if having people to fall down can cause danger, it is therefore desirable to anti-slip material is laid.
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of on-slip compositions being coated on stadium, has the skidproof effect of highly significant.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide a kind of on-slip compositions being coated on stadium, including component have styrene-acrylic emulsion, fatty acid ester sulfate, polypropylene glycerol aether, sodium dehydroacetate, pH adjusting agent and calcium hydroxide powder, the described on-slip compositions being coated on stadium in parts by weight, including component have: styrene-acrylic emulsion 70-80 part, fatty acid ester sulfate 12-16 part, polypropylene glycerol aether 7-10 part, sodium dehydroacetate 5-8 part, pH adjusting agent 13-17 part, calcium hydroxide powder 30-35 part.
In a preferred embodiment of the present invention, the described on-slip compositions being coated on stadium in parts by weight, including component have: styrene-acrylic emulsion 75 parts, 14 parts of fatty acid ester sulfate, polypropylene glycerol aether 8 parts, sodium dehydroacetate 7 parts, pH adjusting agent 15 parts, calcium hydroxide powder 32 parts.
In a preferred embodiment of the present invention, described pH adjusting agent is ammonia.
In a preferred embodiment of the present invention, the mesh number of described calcium hydroxide powder is 200-250 mesh.
The invention has the beneficial effects as follows: the on-slip compositions being coated on stadium of the present invention, there is extraordinary adhesive force, the rough surface in stadium after coating, thus prevent people from slipping when walking, and there is excellent environmental-protecting performance, environmentally friendly, nonhazardous effect.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, all other embodiments that those of ordinary skill in the art are obtained under not making creative work premise, broadly fall into the scope of protection of the invention.
Embodiment one:
A kind of on-slip compositions being coated on stadium is provided, including component have styrene-acrylic emulsion, fatty acid ester sulfate, polypropylene glycerol aether, sodium dehydroacetate, pH adjusting agent and calcium hydroxide powder, the described on-slip compositions being coated on stadium in parts by weight, including component have: styrene-acrylic emulsion 75 parts, 14 parts of fatty acid ester sulfate, polypropylene glycerol aether 8 parts, sodium dehydroacetate 7 parts, pH adjusting agent 15 parts, calcium hydroxide powder 32 parts.Described pH adjusting agent is ammonia.The mesh number of described calcium hydroxide powder is 220 mesh.
Embodiment two:
A kind of on-slip compositions being coated on stadium is provided, including component have styrene-acrylic emulsion, fatty acid ester sulfate, polypropylene glycerol aether, sodium dehydroacetate, pH adjusting agent and calcium hydroxide powder, the described on-slip compositions being coated on stadium in parts by weight, including component have: styrene-acrylic emulsion 70 parts, 16 parts of fatty acid ester sulfate, polypropylene glycerol aether 7 parts, sodium dehydroacetate 8 parts, pH adjusting agent 13 parts, calcium hydroxide powder 35 parts.Described pH adjusting agent is ammonia.The mesh number of described calcium hydroxide powder is 200 mesh.
Embodiment three:
A kind of on-slip compositions being coated on stadium is provided, including component have styrene-acrylic emulsion, fatty acid ester sulfate, polypropylene glycerol aether, sodium dehydroacetate, pH adjusting agent and calcium hydroxide powder, the described on-slip compositions being coated on stadium in parts by weight, including component have: styrene-acrylic emulsion 80 parts, 12 parts of fatty acid ester sulfate, polypropylene glycerol aether 10 parts, sodium dehydroacetate 5 parts, pH adjusting agent 17 parts, calcium hydroxide powder 30 parts.Described pH adjusting agent is ammonia.The mesh number of described calcium hydroxide powder is 250 mesh.
The invention has the beneficial effects as follows:
One, the on-slip compositions being coated on described on stadium has extraordinary adhesive force, the rough surface in stadium after coating, thus prevents people from slipping when walking;
Two, the on-slip compositions being coated on described on stadium has excellent environmental-protecting performance, environmentally friendly, nonhazardous effect.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the invention content to be made or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical field, the most in like manner it is included in the scope of patent protection of the present invention.
Claims (4)
1. the on-slip compositions that a kind is coated on stadium, it is characterized in that, including component have styrene-acrylic emulsion, fatty acid ester sulfate, polypropylene glycerol aether, sodium dehydroacetate, pH adjusting agent and calcium hydroxide powder, the described on-slip compositions being coated on stadium in parts by weight, including component have: styrene-acrylic emulsion
70-80 part, fatty acid ester sulfate 12-16 part, polypropylene glycerol aether
7-10 part, sodium dehydroacetate 5-8 part, pH adjusting agent 13-17 part, calcium hydroxide powder 30-35 part.
The on-slip compositions being coated on stadium the most according to claim 1, it is characterized in that, the described on-slip compositions being coated on stadium in parts by weight, including component have: styrene-acrylic emulsion 75 parts, 14 parts of fatty acid ester sulfate, polypropylene glycerol aether 8 parts, sodium dehydroacetate 7 parts, pH adjusting agent 15 parts, calcium hydroxide powder 32 parts.
The on-slip compositions being coated on stadium the most according to claim 1, it is characterised in that described pH adjusting agent is ammonia.
The on-slip compositions being coated on stadium the most according to claim 1, it is characterised in that the mesh number of described calcium hydroxide powder is 200-250 mesh.