CN104151641A - 一种耐油密封圈 - Google Patents

一种耐油密封圈 Download PDF

Info

Publication number
CN104151641A
CN104151641A CN201410337439.3A CN201410337439A CN104151641A CN 104151641 A CN104151641 A CN 104151641A CN 201410337439 A CN201410337439 A CN 201410337439A CN 104151641 A CN104151641 A CN 104151641A
Authority
CN
China
Prior art keywords
parts
oil
aging agent
dop
zinc oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410337439.3A
Other languages
English (en)
Inventor
吴延福
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGGUO TIANYUN RUBBER PRODUCTS Co Ltd
Original Assignee
NINGGUO TIANYUN RUBBER PRODUCTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGGUO TIANYUN RUBBER PRODUCTS Co Ltd filed Critical NINGGUO TIANYUN RUBBER PRODUCTS Co Ltd
Priority to CN201410337439.3A priority Critical patent/CN104151641A/zh
Publication of CN104151641A publication Critical patent/CN104151641A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐油密封圈，由以下各成分及其重量比组成：丁腈橡胶：80—84份、防老剂RD：1.2—1.4份、防老剂IPPD：2.2—2.4份、氧化锌：4.2—4.4份、DOP：16—16.4份、硬脂酸：1.2—1.5份、炭黑：35—37份、促进剂M：1.8—2份。本发明的耐油密封圈整体性能好，拉伸强度提高20—25％，伸长率提高15—18％，耐温160—170℃，耐腐性性好，使用寿命长。

Description

一种耐油密封圈
技术领域
本发明涉及一种耐油密封圈。
背景技术
密封圈分为O型、三角型、矩型、D型、T型、方型、心型、X型、五棱型、橄榄型等。密封圈是由一个或几个零件组成的环形罩，固定在轴承的一个套圈或垫圈上，并与另一套圈或垫圈接触或形成窄的迷宫间隙，防止润滑油漏出及外物侵入；密封圈性能与以下几点有关：如拉伸强度、抗撕裂性、耐磨性、稳定性、耐热性能、抗腐蚀性等；现有技术中耐油密封圈的上述性能还没有达到很好的使用要求，需要进一步改进。
发明内容
针对上述问题，本发明提供了一种耐油密封圈，具有耐腐蚀、耐高温等特点。
为了解决上述问题，本发明提供的技术方案为：
一种耐油密封圈，由以下各成分及其重量比组成：丁腈橡胶：80—84份、防老剂RD：1.2—1.4份、防老剂IPPD：2.2—2.4份、氧化锌：4.2—4.4份、DOP：16—16.4份、硬脂酸：1.2—1.5份、炭黑：35—37份、促进剂M：1.8—2份。
优选的，由以下各成分及其重量比组成：丁腈橡胶：82—84份、防老剂RD：1.25—1.4份、防老剂IPPD：2.25—2.4份、氧化锌：4.25—4.4份、DOP：16.2—16.4份、硬脂酸：1.2—1.5份、炭黑：35.5—37份、促进剂M：1.8—2份。
优选的，由以下各成分及其重量比组成：丁腈橡胶：82.5份、防老剂RD：1.35份、防老剂IPPD：2.25份、氧化锌：4.35份、DOP：16.2份、硬脂酸：1.23份、炭黑：36.5份、促进剂M：1.85份。
优选的，由以下各成分及其重量比组成：丁腈橡胶：83.5份、防老剂RD：1.25份、防老剂IPPD：2.35份、氧化锌：4.25份、DOP：16.3份、硬脂酸：1.45份、炭黑：35.5份、促进剂M：1.96份。
丁腈橡胶是耐油、耐老化性能较好的合成橡胶，故本技术方案采用丁腈橡胶作为耐油密封圈的主体材料。
防老剂RD污染性小。
氧化锌加快硫化速度，提高硫化程度，增加胶料导热性。
DOP能够缩短混炼时间，较快速度，有助于生产加工。
硬脂酸稳定剂、活性剂。
与现有技术相比，本发明的有益效果为：
本发明的耐油密封圈整体性能好，拉伸强度提高20—25％，伸长率提高15—18％，耐温160—170℃，耐腐性性好，使用寿命长。
具体实施方式
下面对本发明做进一步说明：
实施例1：
一种耐油密封圈，由以下各成分及其重量比组成：丁腈橡胶：80份、防老剂RD：1.4份、防老剂IPPD：2.2份、氧化锌：4.4份、DOP：16份、硬脂酸：1.5份、炭黑：35份、促进剂M：2份。
丁腈橡胶是耐油、耐老化性能较好的合成橡胶，故本技术方案采用丁腈橡胶作为耐油密封圈的主体材料。
防老剂RD污染性小。
氧化锌加快硫化速度，提高硫化程度，增加胶料导热性。
DOP能够缩短混炼时间，较快速度，有助于生产加工。
硬脂酸稳定剂、活性剂。
实施例2：
一种耐油密封圈，由以下各成分及其重量比组成：丁腈橡胶：84份、防老剂RD：1.2份、防老剂IPPD：2.4份、氧化锌：4.2份、DOP：16.4份、硬脂酸：1.2份、炭黑：37份、促进剂M：1.8份。
实施例3：
一种耐油密封圈，由以下各成分及其重量比组成：丁腈橡胶：80份、防老剂RD：1.2份、防老剂IPPD：2.2份、氧化锌：4.4份、DOP：16.4份、硬脂酸：1.5份、炭黑：35份、促进剂M：2份。
实施例4：
一种耐油密封圈，由以下各成分及其重量比组成：丁腈橡胶：82.5份、防老剂RD：1.35份、防老剂IPPD：2.25份、氧化锌：4.35份、DOP：16.2份、硬脂酸：1.23份、炭黑：36.5份、促进剂M：1.85份。
实施例5：
一种耐油密封圈，由以下各成分及其重量比组成：丁腈橡胶：83.5份、防老剂RD：1.25份、防老剂IPPD：2.35份、氧化锌：4.25份、DOP：16.3份、硬脂酸：1.45份、炭黑：35.5份、促进剂M：1.96份。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (4)

1.一种耐油密封圈，其特征在于：由以下各成分及其重量比组成：丁腈橡胶：80—84份、防老剂RD：1.2—1.4份、防老剂IPPD：2.2—2.4份、氧化锌：4.2—4.4份、DOP：16—16.4份、硬脂酸：1.2—1.5份、炭黑：35—37份、促进剂M：1.8—2份。
2.根据权利要求1所述的耐油密封圈，其特征在于：由以下各成分及其重量比组成：丁腈橡胶：82—84份、防老剂RD：1.25—1.4份、防老剂IPPD：2.25—2.4份、氧化锌：4.25—4.4份、DOP：16.2—16.4份、硬脂酸：1.2—1.5份、炭黑：35.5—37份、促进剂M：1.8—2份。
3.根据权利要求1所述的耐油密封圈，其特征在于：由以下各成分及其重量比组成：丁腈橡胶：82.5份、防老剂RD：1.35份、防老剂IPPD：2.25份、氧化锌：4.35份、DOP：16.2份、硬脂酸：1.23份、炭黑：36.5份、促进剂M：1.85份。
4.根据权利要求1所述的耐油密封圈，其特征在于：由以下各成分及其重量比组成：丁腈橡胶：83.5份、防老剂RD：1.25份、防老剂IPPD：2.35份、氧化锌：4.25份、DOP：16.3份、硬脂酸：1.45份、炭黑：35.5份、促进剂M：1.96份。
CN201410337439.3A 2014-07-15 2014-07-15 一种耐油密封圈 Pending CN104151641A (zh)