CN104122129A - Zm6合金光谱标准物质的配比方法 - Google Patents
Zm6合金光谱标准物质的配比方法 Download PDFInfo
- Publication number
- CN104122129A CN104122129A CN201410359600.7A CN201410359600A CN104122129A CN 104122129 A CN104122129 A CN 104122129A CN 201410359600 A CN201410359600 A CN 201410359600A CN 104122129 A CN104122129 A CN 104122129A
- Authority
- CN
- China
- Prior art keywords
- alloy
- magnesium
- stove
- intermediate alloy
- sequence number
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种ZM6镁合金光谱标准物质的配比方法，通过配比表，根据原材料中各元素的含量及合金总重量，计算出各个梯度中原材料的重量，根据计算结果对各个梯度进行配比。本发明可以消除因原材料中各位置中元素含量不同造成的最终结果的偏差，计算的数据准确客观，经实际生产，产品完全可以满足对合金进行炉前化学快速分析的要求。
Description
技术领域
本发明涉及一种配比方法，尤其是一种ZM6合金光谱标准物质的配比方法。
背景技术
ZM6镁合金俗称为航空专用镁合金，在GB1177-91和HB964-82中对航空专用镁合金的化学成分均进行了规定。目前在航空航天工业中，随着新产品研制和生产的不断发展，ZM6镁合金越来越多地被用于制造各种类型的军用产品或其零部件，尤其是在国家重点机型和高新工程中使用。为了确保航空航天产品的质量，ZM6镁合金的质量控制工作非常重要，因此研究开发ZM6镁合金光谱标准物质的发展趋势及市场潜力无疑是巨大的。
设计合理可行的化学成分配比方案，关系到ZM6镁合金标准物质的实用性。化学成分是标准物质的重要技术指标，化学成分设计的原则在国内和国外是一致的，通常将化学成分设计成5个梯度，并涵盖合金的化学成分技术要求，其各种元素的化学成分满足仪器工作曲线的需要。ZM6镁合金光谱标准物质的化学成分亦将分成5个梯度，其成份如下表所示：
在配比时，一般采用两种方法，一是使用化学成分配制好合金锭二次重镕得到成品，对于大批生产时，很方便，但各项化学成分均靠合金锭生产厂家来保证；二是购进原材料，自己现场配料重新熔铸。ZM6镁合金光谱标准物质的5个梯度的化学成分范围非常窄，二次重镕的方式不能满足成份的要求，只能采用现场重新熔铸的方式，然而ZM6镁合金光谱标准物质为一种新的材料，需要探索一种成熟的配比方法。
发明内容
本发明的目的是提供一种ZM6镁合金光谱标准物质的配比方法，满足该物质5个梯度的化学成分的要求，以实现光谱标准物质对合金进行炉前化学快速分析。
本发明的具体技术方案是，
1.材料选择
按照下表进行原材料选择：
2.材料准备
1)将镁锭切割成不大于10mm×10mm的条状；
2)将镁锆中间合金平均切割成若干份合金小料，检验并记载每份Zr的含量；
3)将镁钕中间合金平均切割成若干份合金小料，检验并记载每份Nd的含量；
4)将锌锭重熔浇注成不大于2mm的薄片，然后切成15mm×15mm薄片；
5)将镁锆中间合金小料切割成不大于10mm×10mm规格的条状；
6)将每份镁钕中间合金小料破碎成不大于20mm×20mm×30mm的块状；
3.设定原材料配料比例
原材料的配料比例要求如下表所示，其中5个梯度用5个序号表示：
| 序号 | Zn | Zr | Nd |
| 1 | 0.10％ | 0.27％ | 1.60％ |
| 2 | 0.30％ | 0.47％ | 2.20％ |
| 3 | 0.50％ | 0.67％ | 2.50％ |
| 4 | 0.80％ | 0.85％ | 2.80％ |
| 5 | 1.10％ | 1.20％ | 3.20％ |
4.配料计算
1)镁钕中间合金重量：
Px＝T×Dx/A
其中，T：每炉合金总重量
Px：每炉镁钕中间合金重量，x表示标样的序号，分别为1、2、3、4、5
Dx：配料比例表中序号x的钕配料要求
A：镁钕中间合金中钕的含量
2)锌锭重量
Qx＝T×Nx
其中，T：每炉合金总重量
Qx：每炉锌重量，x表示标样的序号，分别为1、2、3、4、5
Nx：配料比例表中序号x的锌配料要求
3)镁锆中间合金重量：
Zx＝T×Rx/B
其中，T：每炉合金总重量
Zx：每炉镁锆中间合金，x表示标样的序号，分别为1、2、3、4、5
Rx：配料比例表中序号x的锆配料要求
B：镁锆中间合金中锆的含量
4)纯镁重量
Hx＝T-Px-Qx-Zx
其中，T：每炉合金总重量
Hx：每炉锌重量，x表示标样的序号，分别为1、2、3、4、5；
5.进行配比
按计算的结果进行5个梯度的ZM6镁合金光谱标准物质进行配比后进行标准物质的制备。
上述步骤中的配料称重使用电子天平，其精度要求：
镁锆合金：±1g；镁钕合金：±2g；锌：±0.5g；纯镁：0～5g。
所述的步骤2中，将镁锆中间合金和镁钕中间合金平均分成12份。
所述的步骤2中，使用风镐破碎镁钕中间合金小料。
所述的步骤4中，每炉合金总重量为2500克。
本发明通过配比表，根据原材料中各元素的含量及合金总重量，计算出各个梯度中原材料的重量，根据计算结果对各个梯度进行配比。在配比前将中间合金分成若干份并分别测定含量，可以消除因原材料中各位置中元素含量不同造成的最终结果的偏差。本发明采用现场熔铸的方式，计算的数据准确客观，经实际生产，产品完全可以满足对合金进行炉前化学快速分析的要求。
具体实施方式
一种ZM6镁合金光谱标准物质的配比方法，该方法包括以下步骤：
1.材料选择
按照下表进行原材料选择：
2.材料准备
1)将镁锭切割成不大于10mm×10mm的条状；
2)将镁锆中间合金平均切割成若干份合金小料，检验并记载每份Zr的含量；
3)将镁钕中间合金平均切割成若干份合金小料，检验并记载每份Nd的含量；
4)将锌锭重熔浇注成不大于2mm的薄片，然后切成15mm×15mm薄片；
5)将镁锆中间合金小料切割成不大于10mm×10mm规格的条状；
6)将每份镁钕中间合金小料破碎成不大于20mm×20mm×30mm的块状；
3.设定原材料配料比例
原材料的配料比例要求如下表所示，其中5个梯度用5个序号表示：
| 序号 | Zn | Zr | Nd |
| 1 | 0.10％ | 0.27％ | 1.60％ |
| 2 | 0.30％ | 0.47％ | 2.20％ |
| 3 | 0.50％ | 0.67％ | 2.50％ |
| 4 | 0.80％ | 0.85％ | 2.80％ |
| 5 | 1.10％ | 1.20％ | 3.20％ |
4.配料计算
1)镁钕中间合金重量：
Px＝T×Dx/A
其中，T：每炉合金总重量
Px：每炉镁钕中间合金重量，x表示标样的序号，分别为1、2、3、4、5
Dx：配料比例表中序号x的钕配料要求
A：镁钕中间合金中钕的含量
2)锌锭重量
Qx＝T×Nx
其中，T：每炉合金总重量
Qx：每炉锌重量，x表示标样的序号，分别为1、2、3、4、5
Nx：配料比例表中序号x的锌配料要求
3)镁锆中间合金重量：
Zx＝T×Rx/B
其中，T：每炉合金总重量
Zx：每炉镁锆中间合金，x表示标样的序号，分别为1、2、3、4、5
Rx：配料比例表中序号x的锆配料要求
B：镁锆中间合金中锆的含量
4)纯镁重量
Hx＝T-Px-Qx-Zx
其中，T：每炉合金总重量
Hx：每炉锌重量，x表示标样的序号，分别为1、2、3、4、5；
5.进行配比
按计算的结果进行5个梯度的ZM6镁合金光谱标准物质进行配比后进行标准物质的制备。
上述步骤中的配料称重使用电子天平，其精度要求：
镁锆合金：±1g；镁钕合金：±2g；锌：±0.5g；纯镁：0～5g。
所述的步骤2中，将镁锆中间合金和镁钕中间合金平均分成12份。
所述的步骤2中，使用风镐破碎镁钕中间合金小料。
所述的步骤4中，每炉合金总重量为2500克。
实施例
对ZM6镁合金光谱标准物质进行配比，该物质分为5个梯度，其成份如下表所示：
具体的配比方法如下：
1.材料选择
按照下表进行原材料选择：
2.材料准备
1)将镁锭切割成10mm×10mm的条状；
2)将镁锆中间合金平均切割成12份合金小料，检验并记载每份Zr的含量；
3)将镁钕中间合金平均切割成12份合金小料，检验并记载每份Nd的含量；
4)将锌锭重熔浇铸成15mm×15mm×2mm的薄片；
5)将镁锆中间合金小料用风镐切割成10mm×10mm规格的条状；
6)将每份镁钕中间合金小料破碎成不大于20mm×20mm×30mm的块状；
3.设定原材料配料比例
原材料的配料比例要求如下表所示，其中5个梯度用5个序号表示：
| 序号 | Zn | Zr | Nd |
| 1 | 0.10％ | 0.27％ | 1.60％ |
| 2 | 0.30％ | 0.47％ | 2.20％ |
| 3 | 0.50％ | 0.67％ | 2.50％ |
| 4 | 0.80％ | 0.85％ | 2.80％ |
| 5 | 1.10％ | 1.20％ | 3.20％ |
4.配料计算
1)镁钕中间合金重量：
Px＝T×Dx/A
其中，T：每炉合金总重量
Px：每炉镁钕中间合金重量，x表示标样的序号，分别为1、2、3、4、5
Dx：配料比例表中序号x的钕配料要求
A：镁钕中间合金中钕的含量
2)锌锭重量
Qx＝T×Nx
其中，T：每炉合金总重量
Qx：每炉锌重量，x表示标样的序号，分别为1、2、3、4、5
Nx：配料比例表中序号x的锌配料要求
3)镁锆中间合金重量：
Zx＝T×Rx/B
其中，T：每炉合金总重量
Zx：每炉镁锆中间合金，x表示标样的序号，分别为1、2、3、4、5
Rx：配料比例表中序号x的锆配料要求
B：镁锆中间合金中锆的含量
4)纯镁重量
Hx＝T-Px-Qx-Zx
其中，T：每炉合金总重量
Hx：每炉锌重量，x表示标样的序号，分别为1、2、3、4、5；
经计算后，所得出的5个梯度的ZM6镁合金光谱标准物质的配比如下表，其中每炉合金总重量为2500克：
5.进行配比
按计算的结果进行5个梯度的ZM6镁合金光谱标准物质进行配比后进行标准物质的制备。
Claims (5)
1.一种ZM6镁合金光谱标准物质的配比方法，其特征是,所述的方法包括以下步骤：
(1)材料选择
按照下表进行原材料选择：
(2)材料准备
a.将镁锭切割成不大于10mm×10mm的条状；
b.将镁锆中间合金平均切割成若干份合金小料，检验并记载每份Zr的含量；
c.将镁钕中间合金平均切割成若干份合金小料，检验并记载每份Nd的含量；
d.将锌锭重熔浇注成不大于2mm的薄片，然后切成15mm×15mm薄片；
e.将镁锆中间合金小料切割成不大于10mm×10mm规格的条状；
f.将每份镁钕中间合金小料破碎成不大于20mm×20mm×30mm的块状；
(3)设定原材料配料比例
原材料的配料比例要求如下表所示，其中5个梯度用5个序号表示：
(4)配料计算
a.镁钕中间合金重量：
Px＝T×Dx/A
其中，T：每炉合金总重量
Px：每炉镁钕中间合金重量，x表示标样的序号，分别为1、2、3、4、5
Dx：配料比例表中序号x的钕配料要求
A：镁钕中间合金中钕的含量
b.锌锭重量
Qx＝T×Nx
其中，T：每炉合金总重量
Qx：每炉锌重量，x表示标样的序号，分别为1、2、3、4、5
Nx：配料比例表中序号x的锌配料要求
c.镁锆中间合金重量：
Zx＝T×Rx/B
其中，T：每炉合金总重量
Zx：每炉镁锆中间合金，x表示标样的序号，分别为1、2、3、4、5
Rx：配料比例表中序号x的锆配料要求
B：镁锆中间合金中锆的含量
d.纯镁重量
Hx＝T-Px-Qx-Zx
其中，T：每炉合金总重量
Hx：每炉锌重量，x表示标样的序号，分别为1、2、3、4、5；
(5)进行配比
按计算的结果进行5个梯度的ZM6镁合金光谱标准物质进行配比后进行标准物质的制备。
2.如权利要求1所述的ZM6镁合金光谱标准物质的配比方法，其特征是,上述步骤中的配料称重使用电子天平，其精度要求：
镁锆合金：±1g；镁钕合金：±2g；锌：±0.5g；纯镁：0～5g。
3.如权利要求1所述的ZM6镁合金光谱标准物质的配比方法，其特征是，所述的步骤(2)中，将镁锆中间合金和镁钕中间合金平均分成12份。
4.如权利要求1所述的ZM6镁合金光谱标准物质的配比方法，其特征是，所述的步骤(2)中，使用风镐破碎镁钕中间合金小料。
5.如权利要求1所述的ZM6镁合金光谱标准物质的配比方法，其特征是，所述的步骤(4)中，每炉合金总重量为2500克。