CN104119758A - 一种致密抗渗漏防水涂料 - Google Patents

一种致密抗渗漏防水涂料 Download PDF

Info

Publication number
CN104119758A
CN104119758A CN201410293838.4A CN201410293838A CN104119758A CN 104119758 A CN104119758 A CN 104119758A CN 201410293838 A CN201410293838 A CN 201410293838A CN 104119758 A CN104119758 A CN 104119758A
Authority
CN
China
Prior art keywords
parts
minute
stirring
add
dispersed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410293838.4A
Other languages
English (en)
Inventor
蒋能
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Original Assignee
Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd filed Critical Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Priority to CN201410293838.4A priority Critical patent/CN104119758A/zh
Publication of CN104119758A publication Critical patent/CN104119758A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种致密抗渗漏防水涂料，它是由下述重量份的原料组成的：硅丙乳液62-70、沙蒿胶2-3、环氧氯丙烷1-2、聚四氟乙烯蜡1-2、六甲基磷酰三胺0.1-0.2、醇酯十二成膜助剂1-2、乙二胺四亚甲基叉膦酸钠1-2、偏硼酸铵2-3、双十二碳醇酯2-3、六溴环十二烷0.1-0.3、氮化铝3-4、膨润土6-10、磷酸二氢铝0.3-1、成膜助剂5-8、去离子水10-16，本发明的防水涂料具有优异的柔韧性、抗渗性、耐候性、隔热性，与基层的粘结性强，阻燃效果好，无毒、无环境污染，表面强度高，色泽均匀，手感细腻，耐擦拭性强，抗磨性好。

Description

一种致密抗渗漏防水涂料
技术领域
    本发明主要涉及一种涂料，尤其涉及一种致密抗渗漏防水涂料。
背景技术
   传统的防水材料主要有防水卷材、防水涂料、密封油膏等柔性防水材料，以及以水泥基材为主，添加药水剂及其它助剂的刚性防水材料。我国大部分防水工程均采用传统防水材料，传统防水材料存在着耐老化性能差、拉伸强度低、对温度敏感等缺点。传统防水涂料用来屋面防水，容易引起老化、干裂、变形、折断、分层等现象，用于室内防水，对于形状复杂的场所，施工困难，而对渗漏现象，质量更难以保证，人们每隔几年就要花费大量的资金和劳动力进行返修，不仅搅乱了人们的正常生活、工作和生产秩序，而且影响整幢致密抗渗漏物的使用寿命。为了满足各行业对防水涂料的要求，生产高性能，应用广泛的防水涂料很有必要。
发明内容
本发明目的就是提供一种致密抗渗漏防水涂料。
本发明是通过以下技术方案实现的：
一种致密抗渗漏防水涂料，它是由下述重量份的原料组成的：
硅丙乳液62-70、沙蒿胶2-3、环氧氯丙烷1-2、聚四氟乙烯蜡1-2、六甲基磷酰三胺0.1-0.2、醇酯十二成膜助剂1-2、乙二胺四亚甲基叉膦酸钠1-2、偏硼酸铵2-3、双十二碳醇酯2-3、六溴环十二烷0.1-0.3、氮化铝3-4、膨润土6-10、磷酸二氢铝0.3-1、成膜助剂5-8、去离子水10-16；
所述的成膜助剂是由下述重量份的原料组成的：
硅丙乳液30-35、芦荟提取液0.3-2、尼泊金乙酯1-2、氟硅酸钠0.8-1、季戊四醇2-3、二月桂酸二丁基锡0.1-0.2、微粉硅胶2-4、三甲基苄基氯化铵0.8-2、去离子水70-75；
将微粉硅胶与季戊四醇混合，在65-70℃下搅拌混合2-4分钟，加入上述去离子水重量的30-40%、三甲基苄基氯化铵，100-200转/分搅拌分散6-12分钟，得分散液；
将尼泊金乙酯与芦荟提取液混合，搅拌均匀后加入到硅丙乳液中，在35-40℃下保温搅拌10-15分钟，加入上述分散液、二月桂酸二丁基锡，搅拌至常温，加入剩余各原料，300-400转/分搅拌分散7-10分钟，即得所述成膜助剂。
一种致密抗渗漏防水涂料的制备方法，包括以下步骤：
将膨润土、氮化铝混合，加入双十二碳醇酯、聚四氟乙烯蜡，60-70℃下搅拌混合3-5分钟，加入到去离子水中，搅拌均匀，加入乙二胺四亚甲基叉膦酸钠，70-100转/分搅拌分散4-7分钟；
将环氧氯丙烷加入到硅丙乳液中，搅拌均匀后加入环氧氯丙烷、偏硼酸铵，100-200转/分搅拌分散3-6分钟；
将上述处理后的各原料与剩余各原料混合，500-600转/分搅拌分散20-30分钟，即得所述致密抗渗漏防水涂料。
本发明的优点是：
本发明的防水涂料具有优异的柔韧性、抗渗性、耐候性、隔热性，与基层的粘结性强，阻燃效果好，无毒、无环境污染，表面强度高，色泽均匀，手感细腻，耐擦拭性强，抗磨性好。
具体实施方式
实施例1
一种致密抗渗漏防水涂料，它是由下述重量份（公斤）的原料组成的：
硅丙乳液70、沙蒿胶2、环氧氯丙烷2、聚四氟乙烯蜡2、六甲基磷酰三胺0.2、醇酯十二成膜助剂1-2、乙二胺四亚甲基叉膦酸钠1、偏硼酸铵2、双十二碳醇酯3、六溴环十二烷0.3、氮化铝3、膨润土10、磷酸二氢铝0.3、成膜助剂8、去离子水16；
所述的成膜助剂是由下述重量份的原料组成的：
硅丙乳液35、芦荟提取液0.3、尼泊金乙酯2、氟硅酸钠0.8、季戊四醇2、二月桂酸二丁基锡0.1、微粉硅胶2、三甲基苄基氯化铵0.8、去离子水75；
将微粉硅胶与季戊四醇混合，在70℃下搅拌混合2分钟，加入上述去离子水重量的40%、三甲基苄基氯化铵，200转/分搅拌分散12分钟，得分散液；
将尼泊金乙酯与芦荟提取液混合，搅拌均匀后加入到硅丙乳液中，在40℃下保温搅拌15分钟，加入上述分散液、二月桂酸二丁基锡，搅拌至常温，加入剩余各原料，400转/分搅拌分散10分钟，即得所述成膜助剂。
一种致密抗渗漏防水涂料的制备方法，包括以下步骤：
将膨润土、氮化铝混合，加入双十二碳醇酯、聚四氟乙烯蜡，70℃下搅拌混合5分钟，加入到去离子水中，搅拌均匀，加入乙二胺四亚甲基叉膦酸钠，100转/分搅拌分散7分钟；
将环氧氯丙烷加入到硅丙乳液中，搅拌均匀后加入环氧氯丙烷、偏硼酸铵，200转/分搅拌分散6分钟；
将上述处理后的各原料与剩余各原料混合，600转/分搅拌分散30分钟，即得所述致密抗渗漏防水涂料。
性能测试：
延伸率：≥300％ ；
不透水性：0.3MPa( 一个小时不透水)。

Claims (2)

1.一种致密抗渗漏防水涂料，其特征在于它是由下述重量份的原料组成的：
硅丙乳液62-70、沙蒿胶2-3、环氧氯丙烷1-2、聚四氟乙烯蜡1-2、六甲基磷酰三胺0.1-0.2、醇酯十二成膜助剂1-2、乙二胺四亚甲基叉膦酸钠1-2、偏硼酸铵2-3、双十二碳醇酯2-3、六溴环十二烷0.1-0.3、氮化铝3-4、膨润土6-10、磷酸二氢铝0.3-1、成膜助剂5-8、去离子水10-16；
所述的成膜助剂是由下述重量份的原料组成的：
硅丙乳液30-35、芦荟提取液0.3-2、尼泊金乙酯1-2、氟硅酸钠0.8-1、季戊四醇2-3、二月桂酸二丁基锡0.1-0.2、微粉硅胶2-4、三甲基苄基氯化铵0.8-2、去离子水70-75；
将微粉硅胶与季戊四醇混合，在65-70℃下搅拌混合2-4分钟，加入上述去离子水重量的30-40%、三甲基苄基氯化铵，100-200转/分搅拌分散6-12分钟，得分散液；
将尼泊金乙酯与芦荟提取液混合，搅拌均匀后加入到硅丙乳液中，在35-40℃下保温搅拌10-15分钟，加入上述分散液、二月桂酸二丁基锡，搅拌至常温，加入剩余各原料，300-400转/分搅拌分散7-10分钟，即得所述成膜助剂。
2.一种如权利要求1所述的致密抗渗漏防水涂料的制备方法，其特征在于包括以下步骤：
将膨润土、氮化铝混合，加入双十二碳醇酯、聚四氟乙烯蜡，60-70℃下搅拌混合3-5分钟，加入到去离子水中，搅拌均匀，加入乙二胺四亚甲基叉膦酸钠，70-100转/分搅拌分散4-7分钟；
将环氧氯丙烷加入到硅丙乳液中，搅拌均匀后加入环氧氯丙烷、偏硼酸铵，100-200转/分搅拌分散3-6分钟；
将上述处理后的各原料与剩余各原料混合，500-600转/分搅拌分散20-30分钟，即得所述致密抗渗漏防水涂料。
CN201410293838.4A 2014-06-26 2014-06-26 一种致密抗渗漏防水涂料 Pending CN104119758A (zh)