CN106752249A - 一种高粘结性腻子材料及制备方法 - Google Patents
一种高粘结性腻子材料及制备方法 Download PDFInfo
- Publication number
- CN106752249A CN106752249A CN201710007993.9A CN201710007993A CN106752249A CN 106752249 A CN106752249 A CN 106752249A CN 201710007993 A CN201710007993 A CN 201710007993A CN 106752249 A CN106752249 A CN 106752249A
- Authority
- CN
- China
- Prior art keywords
- weight
- polyvinyl alcohol
- adhesion
- putty material
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高粘结性腻子材料及制备方法,至少由白水泥、重钙粉、纤维素醚、可再分散乳胶粉、聚乙烯醇、淀粉醚材料配制而成。本发明精选优质材料,选用优质触变润滑剂和淀粉醚作为抗流挂剂,使产品本身具有良好的抗流挂性,同时使用木质纤维和纤维素醚来增稠保水,保水率达到95%以上;同时选用可再分散乳胶粉和PVA17‑88配合作为白水泥的改性剂,使本产品标准拉伸粘结强度达到0.8MPa以上。在石膏板、水泥顶棚、金属、玻璃等光滑表面披刮都能具有良好的粘结力,拉伸粘结强度能达到0.5PMa以上。
Description
技术领域
本发明涉及建筑材料领域,特别涉及一种高粘结性腻子材料及制备方法。
背景技术
腻子是建筑装饰材料的一种,用来修补找平墙面,为下一步装饰打下良好的基础。室内天花板装修一般采用以下两种方案:
第一种方案:直接在天花板基层上披刮内墙腻子找平,然后使用内墙面层材料。因天花板基层为商品混凝土浇筑而成,天花板表面存在脱模剂等杂质,采用普通内墙腻子找平因重力和杂质的原因容易造成天花板腻子掉落,在干透后容易起壳脱层。
第二种方案:选用石膏板作为吊顶,然后披刮内墙腻子找平,再使用内墙面层材料。因石膏板本身和腻子的相容不好,造成腻子粉容易和石膏板脱层,造成腻子层整体脱落。
中国专利申请CN1908081A公开了一种防水腻子,选用白水泥、碳酸钙、灰钙粉等粉体,加入聚乙烯醇、纤维素溶液、酰胺溶液进行改性。该专利主要是为了防水,在该专利公开的防水腻子中,粘结力差,容易造成腻子层整体脱落。本发明旨在石膏板、水泥顶棚、金属、玻璃等光滑表面披刮都能具有良好的粘结力,与石膏板、水泥顶棚、金属、玻璃等介质牢牢粘结在一起。
发明内容
有鉴于此,本发明提出一种高粘结性腻子材料及制备方法,在石膏板、水泥顶棚、金属、玻璃等光滑表面披刮都能具有良好的粘结力,与石膏板、水泥顶棚、金属、玻璃等介质牢牢粘结在一起。
一方面,本发明提供了一种高粘结性腻子材料,至少由白水泥、重钙粉、纤维素醚、可再分散乳胶粉、聚乙烯醇、淀粉醚材料配制而成。
为了提高粘结力,在进一步技术方案中,聚乙烯醇选用PVA17-88型号。
为了提高粘结力,在进一步技术方案中,各材料重量配比:白水泥:10~40%,重钙粉:60~90%,纤维素醚:0.4~1%,可再分散乳胶粉:1~5%,聚乙烯醇:0.5~2%,淀粉醚:0.02~0.1%。
为了提高粘结力,在进一步技术方案中,还包括触变润滑剂、消泡剂、木质纤维。
为了提高粘结力,在进一步技术方案中,各材料重量配比:触变润滑剂:0.1~0.2%,消泡剂:0.1~0.2%,木质纤维:0.3~0.5%。
另一方面,本发明还提供了一种高粘结性腻子材料制备方法,包括以下步骤:
步骤1:在搅拌机中加入60~90份重量的重钙粉,再加入10~40份重量的白水泥,搅拌10分钟;
步骤2:再加入0.4~1份重量的纤维素醚、1~5份重量的可再分散乳胶粉、0.5~2份重量的聚乙烯醇、0.02~0.1份重量的淀粉醚、0.1~0.2份重量的触变润滑剂、0.1~0.2份重量的消泡剂、0.3~0.5份重量的木质纤维后,再搅拌20分钟,使原材料充分混合均匀。
为了提高粘结力,在进一步技术方案中,聚乙烯醇选用PVA17-88型号。
另一方面,本发明还提供了另一种高粘结性腻子材料制备方法,包括以下步骤:
步骤1:取一小桶,其中加入0.4~1份重量的纤维素醚、1~5份重量的可再分散乳胶粉、0.5~2份重量的聚乙烯醇、0.02~0.1份重量的淀粉醚、0.1~0.2份重量的触变润滑剂、0.1~0.2份重量的消泡剂、0.3~0.5份重量的木质纤维,充分搅拌后备用;
步骤2:在搅拌机中加入60~90份重量的重钙粉,再加入10~40份重量的白水泥,再加入小桶中已搅拌均匀的材料,搅拌30分钟,使原材料充分混合均匀。
为了提高粘结力,在进一步技术方案中,聚乙烯醇选用PVA17-88型号。
本发明精选优质材料,选用优质触变润滑剂和淀粉醚作为抗流挂剂,使产品本身具有良好的抗流挂性,同时使用木质纤维和纤维素醚来增稠保水,保水率达到95%以上;同时选用可再分散乳胶粉和PVA17-88配合作为白水泥的改性剂,使本产品标准拉伸粘结强度达到0.8MPa以上。在石膏板、水泥顶棚、金属、玻璃等光滑表面披刮都能具有良好的粘结力,拉伸粘结强度能达到0.5PMa以上。
具体实施方式
需要说明的是,在不冲突的情况下,本发明中的实施例及实施例中的特征可以相互组合。
本发明优选了一种高粘结性腻子材料,由以下材料配制而成,具体重量配比如下:
1、白水泥:10~40%,作为凝胶材料
2、重钙粉:60~90%,作为轻质填充材料
3、纤维素醚:0.4~1%,作为增稠、保水材料
4、可再分散乳胶粉:1~5%,作为产品稳定剂,增强粘结强度,防开裂
5、PVA17-88:0.5~1%,作为增加产品粘结力;PVA17-88是指PVA = polyvinylalcohol,意思是“聚乙烯醇”,是由聚醋酸乙烯酯经醇解而成的结晶性高分子材料。17 表示平均聚合度1700~1800,88 表示醇解度均为88%±2%。
6、淀粉醚:0.02~0.1%,增强抗流挂性
7、触变润滑剂:0.1~0.2%,增强抗流挂性
8、消泡剂:0.1~0.2%,增强材料密实性,增强整体强度
9、木质纤维:0.3~0.5%,抗裂,增强和易性好
上述1~6种材料为必须添加材料,上述7~9种材料为可增强产品性能的材料。另外,也可以增加其它材料。
本发明还提供了第一实施例的一种高粘结性腻子材料制备方法,包括以下步骤:
步骤1:在搅拌机中加入60~90份重量的重钙粉,再加入10~40份重量的白水泥,搅拌10分钟;
步骤2:再加入0.4~1份重量的纤维素醚、1~5份重量的可再分散乳胶粉、0.5~2份重量的PVA17-88、0.02~0.1份重量的淀粉醚、0.1~0.2份重量的触变润滑剂、0.1~0.2份重量的消泡剂、0.3~0.5份重量的木质纤维后,再搅拌20分钟,使原材料充分混合均匀。
本发明还提供了第二实施例的一种高粘结性腻子材料制备方法,包括以下步骤:
步骤1:取一小桶,其中加入0.4~1份重量的纤维素醚、1~5份重量的可再分散乳胶粉、0.5~2份重量的PVA17-88、0.02~0.1份重量的淀粉醚、0.1~0.2份重量的触变润滑剂、0.1~0.2份重量的消泡剂、0.3~0.5份重量的木质纤维,充分搅拌后备用;
步骤2:在搅拌机中加入60~90份重量的重钙粉,再加入10~40份重量的白水泥,再加入小桶中已搅拌均匀的材料,搅拌30分钟,使原材料充分混合均匀。
本发明上述实施例为最优实施例,精选优质材料,选用优质触变润滑剂和淀粉醚作为抗流挂剂,使产品本身具有良好的抗流挂性,同时使用木质纤维和纤维素醚来增稠保水,保水率达到95%以上;同时选用可再分散乳胶粉和PVA17-88配合作为白水泥的改性剂。采用上述配方和制备方法,经过试验测定,本产品标准拉伸粘结强度达到0.8MPa以上。在石膏板、水泥顶棚、金属、玻璃等光滑表面披刮都能具有良好的粘结力,拉伸粘结强度能达到0.5PMa以上。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围内。
Claims (9)
1.一种高粘结性腻子材料,其特征在于:至少由白水泥、重钙粉、纤维素醚、可再分散乳胶粉、聚乙烯醇、淀粉醚材料配制而成。
2.根据权利要求1所述的高粘结性腻子材料,其特征在于:聚乙烯醇选用PVA17-88型号。
3.根据权利要求1所述的高粘结性腻子材料,其特征在于:各材料重量配比:白水泥:10~40%,重钙粉:60~90%,纤维素醚:0.4~1%,可再分散乳胶粉:1~5%,聚乙烯醇:0.5~2%,淀粉醚:0.02~0.1%。
4.根据权利要求1至3任意一项所述的高粘结性腻子材料,其特征在于:还包括触变润滑剂、消泡剂、木质纤维。
5.根据权利要求4所述的高粘结性腻子材料,其特征在于:各材料重量配比:触变润滑剂:0.1~0.2%,消泡剂:0.1~0.2%,木质纤维:0.3~0.5%。
6.一种高粘结性腻子材料制备方法,其特征在于,包括以下步骤:
步骤1:在搅拌机中加入60~90份重量的重钙粉,再加入10~40份重量的白水泥,搅拌10分钟;
步骤2:再加入0.4~1份重量的纤维素醚、1~5份重量的可再分散乳胶粉、0.5~2份重量的聚乙烯醇、0.02~0.1份重量的淀粉醚、0.1~0.2份重量的触变润滑剂、0.1~0.2份重量的消泡剂、0.3~0.5份重量的木质纤维后,再搅拌20分钟,使原材料充分混合均匀。
7.根据权利要求6所述的高粘结性腻子材料制备方法,其特征在于:聚乙烯醇选用PVA17-88型号。
8.一种高粘结性腻子材料制备方法,其特征在于,包括以下步骤:
步骤1:取一小桶,其中加入0.4~1份重量的纤维素醚、1~5份重量的可再分散乳胶粉、0.5~2份重量的聚乙烯醇、0.02~0.1份重量的淀粉醚、0.1~0.2份重量的触变润滑剂、0.1~0.2份重量的消泡剂、0.3~0.5份重量的木质纤维,充分搅拌后备用;
步骤2:在搅拌机中加入60~90份重量的重钙粉,再加入10~40份重量的白水泥,再加入小桶中已搅拌均匀的材料,搅拌30分钟,使原材料充分混合均匀。
9.根据权利要求8所述的高粘结性腻子材料制备方法,其特征在于:聚乙烯醇选用PVA17-88型号。