CN104119755B - 一种抗裂防水涂料 - Google Patents
一种抗裂防水涂料 Download PDFInfo
- Publication number
- CN104119755B CN104119755B CN201410293068.3A CN201410293068A CN104119755B CN 104119755 B CN104119755 B CN 104119755B CN 201410293068 A CN201410293068 A CN 201410293068A CN 104119755 B CN104119755 B CN 104119755B
- Authority
- CN
- China
- Prior art keywords
- stirring
- add
- minutes
- raw material
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种抗裂防水涂料,它是由下述重量份的原料组成的:硅丙乳液60-64、聚双环戊二烯2-3、煅石膏粉3-6、三甘醇2-3、聚乙烯醇缩丁醛0.2-0.4、三聚磷酸铝1-2、单硬脂酸甘油单酯0.4-1、N-羟甲基丙烯酰胺1-2、沉淀硫酸钡9-12、醋酸钠0.4-1、二苯基咪唑啉0.1-0.3、硫酸亚铁0.1-0.2、成膜助剂4-6、去离子水10-14,本发明的防水涂料漆膜坚硬、耐磨性好、附着力强,并具有良好的耐水性,特别适用于内墙,外墙和房顶等涂覆;并在配料成分中加入了碳化钽、轻质碳酸钙和偏钒酸铵等,有效的提高了抗性,粘结力好,经久耐用。
Description
技术领域
本发明主要涉及一种涂料,尤其涉及一种抗裂防水涂料。
背景技术
传统的防水材料主要有防水卷材、防水涂料、密封油膏等柔性防水材料,以及以水泥基材为主,添加药水剂及其它助剂的刚性防水材料。我国大部分防水工程均采用传统防水材料,传统防水材料存在着耐老化性能差、拉伸强度低、对温度敏感等缺点。传统防水涂料用来屋面防水,容易引起老化、干裂、变形、折断、分层等现象,用于室内防水,对于形状复杂的场所,施工困难,而对渗漏现象,质量更难以保证,人们每隔几年就要花费大量的资金和劳动力进行返修,不仅搅乱了人们的正常生活、工作和生产秩序,而且影响整幢建筑物的使用寿命。为了满足各行业对防水涂料的要求,生产高性能,应用广泛的防水涂料很有必要。
发明内容
本发明目的就是提供一种抗裂防水涂料。
本发明是通过以下技术方案实现的:
一种抗裂防水涂料,它是由下述重量份的原料组成的:
硅丙乳液60-64、聚双环戊二烯2-3、煅石膏粉3-6、三甘醇2-3、聚乙烯醇缩丁醛0.2-0.4、三聚磷酸铝1-2、单硬脂酸甘油单酯0.4-1、N-羟甲基丙烯酰胺1-2、沉淀硫酸钡9-12、醋酸钠0.4-1、二苯基咪唑啉0.1-0.3、硫酸亚铁0.1-0.2、成膜助剂4-6、去离子水10-14;
所述的成膜助剂是由下述重量份的原料组成的:
醋丙乳液20-26、吡咯烷酮羟酸钠1-2、烯基琥珀酸酐0.5-1、单硬脂酸甘油酯0.3-1、山奈酚0.1-0.2、四硼酸钠2-3、聚乙烯醇3-4、阿拉伯胶1-2、乳酸钙2-3、去离子水60-70;
将乳酸钙与山奈酚混合搅拌均匀,加入上述去离子水重量的20-30%,在70-75℃下搅拌混合5-7分钟,加入阿拉伯胶,搅拌至常温,得凝胶;
将四硼酸钠与烯基琥珀酸酐混合,搅拌均匀后加入聚乙烯醇,在60-70℃下搅拌混合3-5分钟,加入到剩余的去离子水中,搅拌至常温,加入剩余各原料,400-500转/分搅拌分散10-16分钟,即得所述成膜助剂。
一种抗裂防水涂料的制备方法,包括以下步骤:
将煅石膏粉与沉淀硫酸钡混合,搅拌均匀后加入到去离子水中,加入单硬脂酸甘油单酯,在40-50℃下搅拌混合3-5分钟,加入三聚磷酸铝,50-100转/分搅拌分散6-10分钟;
将聚双环戊二烯加入到硅丙乳液中,搅拌均匀后加入三甘醇、N-羟甲基丙烯酰胺,60-80转/分搅拌分散2-4分钟,加入上述处理后的各原料与剩余各原料,500-700转/分搅拌分散20-30分钟,即得所述抗裂防水涂料。
本发明的优点是:
本发明的防水涂料漆膜坚硬、耐磨性好、附着力强,并具有良好的耐水性,特别适用于内墙,外墙和房顶等涂覆;并在配料成分中加入了碳化钽、轻质碳酸钙和偏钒酸铵等,有效的提高了抗性,粘结力好,经久耐用。
具体实施方式
实施例1
一种抗裂防水涂料,它是由下述重量份(公斤)的原料组成的:
硅丙乳液64、聚双环戊二烯3、煅石膏粉6、三甘醇2、聚乙烯醇缩丁醛0.4、三聚磷酸铝1-2、单硬脂酸甘油单酯0.4、N-羟甲基丙烯酰胺2、沉淀硫酸钡12、醋酸钠0.4、二苯基咪唑啉0.3、硫酸亚铁0.2、成膜助剂4、去离子水14;
所述的成膜助剂是由下述重量份的原料组成的:
醋丙乳液26、吡咯烷酮羟酸钠1、烯基琥珀酸酐0.5、单硬脂酸甘油酯0.3、山奈酚0.2、四硼酸钠3、聚乙烯醇3-4、阿拉伯胶2、乳酸钙2-3、去离子水70;
将乳酸钙与山奈酚混合搅拌均匀,加入上述去离子水重量的30%,在75℃下搅拌混合7分钟,加入阿拉伯胶,搅拌至常温,得凝胶;
将四硼酸钠与烯基琥珀酸酐混合,搅拌均匀后加入聚乙烯醇,在70℃下搅拌混合3分钟,加入到剩余的去离子水中,搅拌至常温,加入剩余各原料,500转/分搅拌分散16分钟,即得所述成膜助剂。
一种抗裂防水涂料的制备方法,其特征在于包括以下步骤:
将煅石膏粉与沉淀硫酸钡混合,搅拌均匀后加入到去离子水中,加入单硬脂酸甘油单酯,在50℃下搅拌混合3分钟,加入三聚磷酸铝,100转/分搅拌分散10分钟;
将聚双环戊二烯加入到硅丙乳液中,搅拌均匀后加入三甘醇、N-羟甲基丙烯酰胺,80转/分搅拌分散2分钟,加入上述处理后的各原料与剩余各原料,700转/分搅拌分散30分钟,即得所述抗裂防水涂料。
性能测试:
延伸率:≥300%;
不透水性:0.3MPa(一个小时不透水)。
Claims (2)
1.一种抗裂防水涂料,其特征在于它是由下述重量份的原料组成的:
硅丙乳液64、聚双环戊二烯3、煅石膏粉6、三甘醇2、聚乙烯醇缩丁醛0.4、三聚磷酸铝1-2、单硬脂酸甘油单酯0.4、N-羟甲基丙烯酰胺2、沉淀硫酸钡12、醋酸钠0.4、二苯基咪唑啉0.3、硫酸亚铁0.2、成膜助剂4、去离子水14;
所述的成膜助剂是由下述重量份的原料组成的:
醋丙乳液26、吡咯烷酮羟酸钠1、烯基琥珀酸酐0.5、单硬脂酸甘油酯0.3、山奈酚0.2、四硼酸钠3、聚乙烯醇3-4、阿拉伯胶2、乳酸钙2-3、去离子水70;
将乳酸钙与山奈酚混合搅拌均匀,加入上述去离子水重量的30%,在75℃下搅拌混合7分钟,加入阿拉伯胶,搅拌至常温,得凝胶;
将四硼酸钠与烯基琥珀酸酐混合,搅拌均匀后加入聚乙烯醇,在70℃下搅拌混合3分钟,加入到剩余的去离子水中,搅拌至常温,加入剩余各原料,500转/分搅拌分散16分钟,即得所述成膜助剂。
2.一种如权利要求1所述的抗裂防水涂料的制备方法,其特征在于包括以下步骤:
将煅石膏粉与沉淀硫酸钡混合,搅拌均匀后加入到去离子水中,加入单硬脂酸甘油单酯,在50℃下搅拌混合3分钟,加入三聚磷酸铝,100转/分搅拌分散10分钟;
将聚双环戊二烯加入到硅丙乳液中,搅拌均匀后加入三甘醇、N-羟甲基丙烯酰胺,80转/分搅拌分散2分钟,加入上述处理后的各原料与剩余各原料,700转/分搅拌分散30分钟,即得所述抗裂防水涂料。