CN104119716A - Self-cleaning waterproof coating - Google Patents
Self-cleaning waterproof coating Download PDFInfo
- Publication number
- CN104119716A CN104119716A CN201410293033.XA CN201410293033A CN104119716A CN 104119716 A CN104119716 A CN 104119716A CN 201410293033 A CN201410293033 A CN 201410293033A CN 104119716 A CN104119716 A CN 104119716A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- stirring
- raw material
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a self-cleaning waterproof coating which comprises the following raw materials in parts by weight: 62-70 parts of silicone acrylic emulsion, 1-2 parts of linseed oil, 1-2 parts of zinc dihydrogen phosphate, 1-2 parts of sodium lauroyl sarcosine, 2-3 parts of dimethyl glutarate, 2-3 parts of maleic anhydride grafted polypropylene, 1-2 parts of dimethyl diallyl ammonium chloride, 1-2 parts of tetrabutylammonium bromide, 1.2-2 parts of laurate dihydroxyethylamide, 1-2 parts of isopropanol, 3-5 parts of nano bauxite, 6-8.5 parts of vermiculite powder, 0.5-1 part of ascorbic acid, 6-8 parts of film-forming assistant and 10-17 parts of de-ionized water. The waterproof coating has a very good heat insulation effect, and has good wiping resistance, waterproofness, self-cleaning effect, adhesiveness, acid-base resistance, corrosion resistance and storage stability and long shelf life; the formed coating is stable.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of automatically cleaning waterproof paint.
Background technology
Traditional water-proof material mainly contains the flexible waterproof materials such as waterproof roll, waterproof paint, sealing cement, and taking cement matrix as main, adds the rigidity water-proofing material of liquid medicine agent and other auxiliary agent.The most of waterproofing work of China all adopts conventional waterproof material, conventional waterproof material exist loss of properties on aging, tensile strength low, to shortcomings such as temperature sensitives.Conventional waterproof coating is used for roof waterproof, easily cause aging, dry and cracked, be out of shape, fracture, the phenomenon such as layering, for indoor waterproof, for complex-shaped place, constructional difficulties, and to Seepage, quality is more difficult to ensure, people will spend a large amount of funds every several years and labor force reprocesses, and have not only confused people's orthobiosis, work and the production order, and affect the work-ing life of whole building self-cleaning article.In order to meet the requirement of every profession and trade to waterproof paint, production high-performance, widely used waterproof paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of automatically cleaning waterproof paint.
The present invention is achieved by the following technical solutions:
A kind of automatically cleaning waterproof paint, it is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 62-70, Semen Lini oil 1-2, primary zinc phosphate 1-2, sodium lauroyl sareosine 1-2, Methyl glutarate 2-3, maleic anhydride inoculated polypropylene 2-3, dimethyl diallyl ammonium chloride 1-2, Tetrabutyl amonium bromide 1-2, lauric acid diethyl amide 1.2-2, Virahol 1-2, nano aluminum alumina 3-5, vermiculite power 6-8.5, xitix 0.5-1, film coalescence aid 6-8, deionized water 10-17;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 30-35, extract solution from aloe 0.3-2, ethyl p-hydroxybenzoate 1-2, Sodium Silicofluoride 0.8-1, tetramethylolmethane 2-3, dibutyl tin laurate 0.1-0.2, micropowder silica gel 2-4, trimethyl benzyl ammonia chloride 0.8-2, deionized water 70-75;
Micropowder silica gel is mixed with tetramethylolmethane, at 65-70 DEG C, be uniformly mixed 2-4 minute, add 30-40%, the trimethyl benzyl ammonia chloride of above-mentioned deionized water weight, 100-200 rev/min of dispersed with stirring 6-12 minute, obtains dispersion liquid;
Ethyl p-hydroxybenzoate is mixed with extract solution from aloe, after stirring, join in organosilicon crylic acid latex, insulated and stirred 10-15 minute at 35-40 DEG C, add above-mentioned dispersion liquid, dibutyl tin laurate, be stirred to normal temperature, add the each raw material of residue, 300-400 rev/min of dispersed with stirring 7-10 minute, obtains described film coalescence aid.
A preparation method for automatically cleaning waterproof paint, comprises the following steps:
Sodium lauroyl sareosine is joined in deionized water, add dimethyl diallyl ammonium chloride, vermiculite power after stirring, 50-70 rev/min of dispersed with stirring 3-5 minute, adds Methyl glutarate, stirs;
Primary zinc phosphate, nano aluminum alumina are mixed, add lauric acid diethyl amide, Virahol, be uniformly mixed 3-5 minute at 60-70 DEG C, join in organosilicon crylic acid latex, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 500-600 rev/min of dispersed with stirring 20-30 minute, obtains described automatically cleaning waterproof paint.
Advantage of the present invention is:
Waterproof paint of the present invention has good heat insulating effect, and resistance to wiping is strong, and water-repellancy is strong, and automatically cleaning is effective, and the film of formation is stable, and cohesiveness is strong, resistance to acids and bases, good corrosion resistance, excellent storage stability, long quality-guarantee period.
Embodiment
Embodiment 1
A kind of automatically cleaning waterproof paint, it by following weight parts (kilogram) raw material form:
Organosilicon crylic acid latex 70, Semen Lini oil 2, primary zinc phosphate 1, sodium lauroyl sareosine 2, Methyl glutarate 3, maleic anhydride inoculated polypropylene 3, dimethyl diallyl ammonium chloride 1, Tetrabutyl amonium bromide 1, lauric acid diethyl amide 1.2, Virahol 2, nano aluminum alumina 3, vermiculite power 8.5, xitix 0.5, film coalescence aid 8, deionized water 17;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 30-35, extract solution from aloe 0.3, ethyl p-hydroxybenzoate 2, Sodium Silicofluoride 0.8, tetramethylolmethane 3, dibutyl tin laurate 0.2, micropowder silica gel 4, trimethyl benzyl ammonia chloride 0.8, deionized water 75;
Micropowder silica gel is mixed with tetramethylolmethane, at 70 DEG C, is uniformly mixed 2 minutes, add above-mentioned deionized water weight 40%, trimethyl benzyl ammonia chloride, 200 revs/min of dispersed with stirring 12 minutes, obtain dispersion liquid;
Ethyl p-hydroxybenzoate is mixed with extract solution from aloe, after stirring, join in organosilicon crylic acid latex, insulated and stirred 15 minutes at 40 DEG C, add above-mentioned dispersion liquid, dibutyl tin laurate, be stirred to normal temperature, add the each raw material of residue, 400 revs/min of dispersed with stirring 10 minutes, obtain described film coalescence aid.
A preparation method for automatically cleaning waterproof paint, comprises the following steps:
Sodium lauroyl sareosine is joined in deionized water, add dimethyl diallyl ammonium chloride, vermiculite power after stirring, 70 revs/min of dispersed with stirring 3-5 minute, add Methyl glutarate, stir;
Primary zinc phosphate, nano aluminum alumina are mixed, add lauric acid diethyl amide, Virahol, be uniformly mixed 5 minutes at 70 DEG C, join in organosilicon crylic acid latex, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 600 revs/min of dispersed with stirring 30 minutes, obtain described automatically cleaning waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. an automatically cleaning waterproof paint, is characterized in that what it was made up of the raw material of following weight parts:
Organosilicon crylic acid latex 62-70, Semen Lini oil 1-2, primary zinc phosphate 1-2, sodium lauroyl sareosine 1-2, Methyl glutarate 2-3, maleic anhydride inoculated polypropylene 2-3, dimethyl diallyl ammonium chloride 1-2, Tetrabutyl amonium bromide 1-2, lauric acid diethyl amide 1.2-2, Virahol 1-2, nano aluminum alumina 3-5, vermiculite power 6-8.5, xitix 0.5-1, film coalescence aid 6-8, deionized water 10-17;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 30-35, extract solution from aloe 0.3-2, ethyl p-hydroxybenzoate 1-2, Sodium Silicofluoride 0.8-1, tetramethylolmethane 2-3, dibutyl tin laurate 0.1-0.2, micropowder silica gel 2-4, trimethyl benzyl ammonia chloride 0.8-2, deionized water 70-75;
Micropowder silica gel is mixed with tetramethylolmethane, at 65-70 DEG C, be uniformly mixed 2-4 minute, add 30-40%, the trimethyl benzyl ammonia chloride of above-mentioned deionized water weight, 100-200 rev/min of dispersed with stirring 6-12 minute, obtains dispersion liquid;
Ethyl p-hydroxybenzoate is mixed with extract solution from aloe, after stirring, join in organosilicon crylic acid latex, insulated and stirred 10-15 minute at 35-40 DEG C, add above-mentioned dispersion liquid, dibutyl tin laurate, be stirred to normal temperature, add the each raw material of residue, 300-400 rev/min of dispersed with stirring 7-10 minute, obtains described film coalescence aid.
2. a preparation method for automatically cleaning waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
Sodium lauroyl sareosine is joined in deionized water, add dimethyl diallyl ammonium chloride, vermiculite power after stirring, 50-70 rev/min of dispersed with stirring 3-5 minute, adds Methyl glutarate, stirs;
Primary zinc phosphate, nano aluminum alumina are mixed, add lauric acid diethyl amide, Virahol, be uniformly mixed 3-5 minute at 60-70 DEG C, join in organosilicon crylic acid latex, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 500-600 rev/min of dispersed with stirring 20-30 minute, obtains described automatically cleaning waterproof paint.