CN1041169A - 抗静电聚醋酸乙烯醇溶树脂 - Google Patents

抗静电聚醋酸乙烯醇溶树脂 Download PDF

Info

Publication number
CN1041169A
CN1041169A CN 89107295 CN89107295A CN1041169A CN 1041169 A CN1041169 A CN 1041169A CN 89107295 CN89107295 CN 89107295 CN 89107295 A CN89107295 A CN 89107295A CN 1041169 A CN1041169 A CN 1041169A
Authority
CN
China
Prior art keywords
polyvinyl
parts
resin
acetate sol
antistatic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 89107295
Other languages
English (en)
Inventor
张�杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Antistatic Material Factory Building Engineering Co Northern Suburban Distric
Original Assignee
Antistatic Material Factory Building Engineering Co Northern Suburban Distric
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Antistatic Material Factory Building Engineering Co Northern Suburban Distric filed Critical Antistatic Material Factory Building Engineering Co Northern Suburban Distric
Priority to CN 89107295 priority Critical patent/CN1041169A/zh
Publication of CN1041169A publication Critical patent/CN1041169A/zh
Pending legal-status Critical Current

Abstract

抗静电聚醋酸乙烯醇溶树脂，属于一种抗静电粘合剂。
本发明所述的树脂主要是由聚醋酸乙烯醇溶树脂、石墨粉、乙炔黑粉、镁粉、乙醇或甲醇复配而成。其外观呈灰色粘性液体，粘度5600～6000cp，电阻值1010Ω～0，pH6～7。本发明导电性能好，常温固化初始强度高，粘接力强，特别适用于在水泥地板、木结构地板上直接粘贴PVC抗静电塑料地板砖及其它材料。

Description

本发明属于一种抗静电粘合剂。
在本发明实现以前，未发现有相同或相近似的已有技术在公开出版物上公开发表。本申请人在申请本发明专利的同时，申请了“抗静电氯丁胶”、“抗静电改性尿醛树脂”、“抗静电壁纸胶”三个发明专利，其共同特点是抗静电性能好，粘合力强，但均不适用于在水泥地板、木结构地板上直接粘贴PVC抗静电塑料地板砖。
本发明的目的就是提供一种抗静电聚醋酸乙烯醇溶树脂，从而克服了以上所述技术中存在的问题。
本发明所述的抗静电聚醋酸乙烯醇溶树脂，其组成成份是：每100份所述的树脂中，含市售的聚醋酸乙烯醇溶树脂42～52份，最好为47份，石墨粉36～40份，最好为39份，乙炔黑粉2份，镁粉1份，市售的98%（含量百分比）的乙醇也可以是甲醇6～14份。
在生产时，可以使用搪瓷或不锈钢的带有强搅拌装置的釜作为生产设备，在其中按前述比例加入所述的石墨粉、乙炔黑粉、镁粉，并在常温、强力搅拌的条件下搅拌5min，然后将所述的聚醋酸乙烯醇溶树脂按前述比例加入到上述的机器中，并搅拌10min后再按前述的比例加入所述的乙醇或甲醇，在常温下搅拌30min使其混合均匀，即可成为产品。
本发明的技术指标：
1、外观：灰黑色粘性液体。
2、粘度：5600～6000cp
3、PH：6～7
4、电阻值：1010Ω～0
5、粘合力：剪切力＞80kg/cm2，拉力＞24.5kg/cm2，
剥离力＞2kg/cm2
本发明导电性能好，单组份常温固化初始强度高，粘接力强，固化快，耐酸、碱、水，固化后阻燃。主要适用于水泥地板、木结构地板上直接粘贴pvc抗静电塑料地板砖，并适用于混凝土、毛毯、木材、纸制品、发泡聚苯乙烯墙壁等不同材料的粘贴。
实施例1：
在带有强搅拌装置的2吨搪瓷釜中加入所述的石墨粉540kg，乙炔黑30kg，镁粉15kg，在常温下强力搅拌5min，然后加入市售的聚醋酸乙烯醇溶树脂630kg，在常温的条件下强力搅拌10min，最后向釜中加入市售的98%（含量百分比）的乙醇90kg，并在常温的条件下，强力搅拌30min，使其充分混合均匀，即可得到1500kg粘度为5600cp的灰黑色粘性液体。
实施例2：
在带有强搅拌装置的不锈钢和面机内，加入所述的石墨粉39kg、乙炔黑2kg、镁粉1kg，在常温下强力搅拌5min然后加入市售的聚醋酸乙烯醇溶树脂47kg，在常温下强力搅拌10min。最后向釜中加入市售的98%（含量百分比）的甲醇11kg，在常温下强力搅拌30min，使其混合均匀，即可得到100kg粘度为5800cp的灰黑色粘性液体。
实施例3：
在带有强搅拌装置的2吨搪瓷釜中加入所述的石墨粉600kg、乙炔黑30kg、镁粉15kg，在常温下强力搅拌5min，然后加入所述的聚醋酸乙烯醇溶树脂780kg，在常温下强力搅拌10min。最后向釜中加入所述的甲醇210kg，并在常温下强力搅拌30min，使其充分混合均匀，即可得到1500kg粘度为6000cp的灰黑色粘性液体。

Claims (2)

1、一种抗静电聚醋酸乙烯醇溶树脂，其特征在于在每100份所述的树脂中含市售的聚醋酸乙烯醇溶树脂42～52份，最好为47份，石墨粉36～40份，最好为39份，乙炔黑粉2份，镁粉1份，市售的98%(含量百分比)的乙醇6～14份。
2、根据权利要求1所述的树脂，其特征在于所述的乙醇可被市售的98%（含量百分比）的甲醇等量代替。
CN 89107295 1989-10-04 1989-10-04 抗静电聚醋酸乙烯醇溶树脂 Pending CN1041169A (zh)