CN1528697A - 干粉状瓷砖粘合剂 - Google Patents

干粉状瓷砖粘合剂 Download PDF

Info

Publication number
CN1528697A
CN1528697A CNA2003101079489A CN200310107948A CN1528697A CN 1528697 A CN1528697 A CN 1528697A CN A2003101079489 A CNA2003101079489 A CN A2003101079489A CN 200310107948 A CN200310107948 A CN 200310107948A CN 1528697 A CN1528697 A CN 1528697A
Authority
CN
China
Prior art keywords
water
agent
dry powder
cement
tile adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2003101079489A
Other languages
English (en)
Other versions
CN1259273C (zh
Inventor
陆文雄
曹栋樑
刘庆
赵美丽
王超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Haili Industry & Trading Co Ltd
Shanghai University
University of Shanghai for Science and Technology
Original Assignee
Shanghai Haili Industry & Trading Co Ltd
University of Shanghai for Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Haili Industry & Trading Co Ltd, University of Shanghai for Science and Technology filed Critical Shanghai Haili Industry & Trading Co Ltd
Priority to CN 200310107948 priority Critical patent/CN1259273C/zh
Publication of CN1528697A publication Critical patent/CN1528697A/zh
Application granted granted Critical
Publication of CN1259273C publication Critical patent/CN1259273C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种以粉煤灰为主要原料的瓷砖专用粘合剂，属化学建筑材料技术领域。本发明的干粉状瓷砖粘合剂的组成成分及含量(重量百分比)如下：二级粉煤灰60－90％、激发剂3－10％、水泥6－20％、乳胶粉1－5％、保水剂0.2－1.0％、消泡剂0.05－0.15％。将上述各原料按规定的重量比分别称重后，放入搅拌釜中，经一定时间的搅拌混合均匀后，即可得干粉状瓷砖粘合剂。在使用时，根据施工要求加入一定比例的水，搅拌均匀后即可使用。该干粉状瓷砖粘合剂具有较好的施工性以及良好的粘结力或粘结强度。本发明由于以固体废弃物粉煤灰为主要原料，成本低廉，为粉煤灰的综合利用开辟了一条新的途径，因而具有较好的经济效益，社会效益和环境效益。

Description

干粉状瓷砖粘合剂
技术领域
本发明涉及一种干粉状瓷砖粘合剂，更具体地说，是涉及一种以粉煤灰为主要原料的瓷砖专用粘合剂，属化学建筑材料技术领域。
背景技术
目前，在建筑装潢行业中，作为建筑材料瓷砖铺贴用的粘合剂，传统使用的一般为聚乙烯醇缩醛胶加水泥，高分子乳液加填料，水玻璃加填料，以及高分子材料与水泥基的改性粉状产品。以上这些瓷砖粘合剂，其原料成本价格较昂贵，不宜广泛使用，而且对环境保护也不利。
发明内容
本发明的目的是提供一种以粉煤灰为主要原料的瓷砖粘合剂，为粉煤灰的综合利用开辟新途径。
本发明采用了以下技术方案来达到上述目的的。
本发明的一种干粉状瓷砖粘合剂，其特征在于以粉煤灰为主要原料，该粘合剂的组成成分及含量(重量百分比)如下：
二级粉煤灰    60-90％      激发剂    3-10％
水泥          6-20％       乳胶粉    1-5％
保水剂        0.2-1.0％    消泡剂    0.05-0.15％
其中，二级粉煤灰的细度(45μm方孔筛余量)≤20％，烧失量≤8％，需水量比≤105％，SO3含量≤3％，含水量≤1％；
水泥采用波特兰水泥，标号为42.5；
激发剂为硫酸盐、铝酸钙、硅酸钠、氧化钙；
乳胶粉：细度为200目的丁二烯-苯乙烯聚合物；
保水剂：纤维素醚；
消泡剂：是一种非离子表面活性物质和二氧化硅的混合物。
本发明的一种干粉状瓷砖粘合剂，其制备方法为：根据上述规定的重量比分别称取粉煤灰、水泥、激发剂、乳胶粉、保水剂、消泡剂，并放入搅拌釜中，经一定时间的搅拌混合均匀后，即可得干粉状瓷砖粘合剂。
本发明利用的是二级粉煤灰。粉煤灰在自身和激发剂的作用下，具有一定胶凝性。当有水存在时，能在常温下与Ca(OH)2反应生成具有胶凝性的化合物。本发明就是利用粉煤灰这一特征，将其作为一种活性填料，来制取一种优质价廉的干粉状瓷砖粘合剂。在使用时，根据施工要求加入一定比例的水，搅拌均匀后即可使用。
本发明的干粉状瓷砖粘合剂具有以下显著优点：
1.具有较好的施工性以及良好的粘结力或粘结强度。
2.以固体废弃物粉煤灰为主要原料，成本低廉，为粉煤灰的综合利用开辟了一条新的途径，因而具有较好的经济效益，社会效益和环境效益。
3.本发明的生产工艺和设备简单，有利于工业化生产和推广应用。
具体实施方式
将本发明和具体实施例叙述于后：
实施例一：本发明利用的粉煤灰的化学成分和指标如下：
化学成分   SiO2  Fe2O3   CaO  Al2O3   MgO
质量百分比(％)   53.63  6.82   6.75  27.00   1.46
细度(45um方孔筛余量)：14％
烧失量：4.74％
需水量比：98％
SO3含量：2.23％
含水量：0.5％
本发明以制备1000千克干粉状瓷砖粘合剂为例：
取800千克二级粉煤灰，加入特定的搅拌釜中，再加入75千克激发剂，110千克波特兰水泥(标号42.5)，10千克乳胶粉(细度为200目的丁二烯-苯乙烯聚合物)，4千克纤维素醚和1千克消泡剂，在搅拌釜中搅拌半小时，使均匀混合后，即可得到干粉状瓷砖粘合剂。
实施例二：本实施例利用的粉煤灰的化学成分和指标与上述实施例相同，以制备1000千克干粉状瓷砖粘合剂为例：取700公斤粉煤灰，加入搅拌釜中，再加入100公斤硫酸钙和氧化钙(重量比为2∶1)的混合物，175公斤波特兰水泥(标号为42.5)，20公斤乳胶粉(细度为200目的丁二烯-苯乙烯聚合物)，4公斤纤维素醚和1公斤消泡剂，在搅拌釜中搅拌半小时，使均匀混合后，即可得到干粉状瓷砖粘合剂。
使用时，根据施工要求，可加入一定比例的水，即干粉状瓷砖粘合剂和水按2∶1的比例进行混合，搅拌均匀后，放置10分钟即可使用。

Claims (2)

1.一种干粉状瓷砖粘合剂，其特征在于以粉煤灰为主要原料，该粘合剂的组成成分及含量(重量百分比)如下：
二级粉煤灰    60-90％      激发剂    3-10％
水泥          6-20％       乳胶粉    1-5％
保水剂        0.2-1.0％    消泡剂    0.05-0.15％
其中，二级粉煤灰的细度(45μm方孔筛余量)≤20％，烧失量≤8％，需水量比≤105％，SO3含量≤3％，含水量≤1％；
水泥采用波特兰水泥，标号为42.5；
激发剂为硫酸盐、铝酸钙、硅酸钠、氧化钙；
乳胶粉：细度为200目的丁二烯-苯乙烯聚合物；
保水剂：纤维素醚；
消泡剂：是一种非离子表面活性物质和二氧化硅的混合物。
2.根据权利要求1所述的一种干粉状瓷砖粘合剂，其特征是根据上述规定的重量比分别称取粉煤灰、水泥、激发剂、乳胶粉、保水剂、消泡剂，并放入搅拌釜中，经一定时间的搅拌混合均匀后，即可得干粉状瓷砖粘合剂。
CN 200310107948 2003-10-16 2003-10-16 干粉状瓷砖粘合剂 Expired - Fee Related CN1259273C (zh)