CN103642432A - 非石棉型混合胶黏剂的制作方法 - Google Patents
非石棉型混合胶黏剂的制作方法 Download PDFInfo
- Publication number
- CN103642432A CN103642432A CN201310643294.5A CN201310643294A CN103642432A CN 103642432 A CN103642432 A CN 103642432A CN 201310643294 A CN201310643294 A CN 201310643294A CN 103642432 A CN103642432 A CN 103642432A
- Authority
- CN
- China
- Prior art keywords
- powder
- asbestos
- polyvinyl acetate
- acetate resin
- magnesium silicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种非石棉型混合胶黏剂的制作方法,包括如下如下步骤:S1,将聚醋酸乙烯树脂与甲醇混合成糊状液体;S2,将聚醋酸乙烯树脂与甲醇混合成的糊状液体加入重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石粉末的步骤;S3,在加入重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石粉末后的糊状液体中再加入甲醇,调和均匀值得产品。本发明原料中不具有石棉,可有效代替石棉型混合胶黏剂。有效降低了石棉对人体的伤害。
Description
技术领域
本发明涉及胶黏剂领域,尤其涉及混合胶黏剂的制作方法。
背景技术
将醋酸乙烯树脂系列聚合物掺入无机填料,便能获得一种廉价的胶黏剂,以往一直采用石棉做填料,但石棉是致癌物质。
发明内容
本发明的目的是提供非石棉型混合胶黏剂的制作方法,减少石棉型混合胶黏剂对人体的伤害。
本发明提供一种非石棉型混合胶黏剂的制作方法,包括如下如下步骤:S1,将聚醋酸乙烯树脂与甲醇混合成糊状液体;S2,将聚醋酸乙烯树脂与甲醇混合成的糊状液体加入重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石粉末的步骤;S3,在加入重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石粉末后的糊状液体中再加入甲醇,调和均匀值得产品。
本发明提供了一种非石棉型混合胶黏剂的制作方法,原料中不具有石棉,可有效代替石棉型混合胶黏剂。有效降低了石棉对人体的伤害。
在一些实施方式中,聚醋酸乙烯树脂、S1中与聚醋酸乙烯树脂混合成糊状液体的甲醇、重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石以及S3中加入的甲醇的重量份数比为34:5:21:20:2:1:17。本配方不仅仅具有良好的附着力,而且耐碱腐蚀,适用于粘结氯乙烯衬瓦、发泡苯乙烯一起汽车用空气过滤器元件。
具体实施方式
本发明提供了一种非石棉型混合胶黏剂的制作方法,包括如下如下步骤:S1,将聚醋酸乙烯树脂与甲醇混合成糊状液体;S2,将聚醋酸乙烯树脂与甲醇混合成的糊状液体加入重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石粉末的步骤;S3,在加入重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石粉末后的糊状液体中再加入甲醇,调和均匀值得产品。
其中,聚醋酸乙烯树脂、S1中与聚醋酸乙烯树脂混合成糊状液体的甲醇、重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石以及S3中加入的甲醇的重量份数比为34:5:21:20:2:1:17。
本发明提供了一种非石棉型混合胶黏剂的制作方法,原料中不具有石棉,可有效代替石棉型混合胶黏剂。有效降低了石棉对人体的伤害。本配方不仅仅具有良好的附着力,而且耐碱腐蚀,适用于粘结氯乙烯衬瓦、发泡苯乙烯一起汽车用空气过滤器元件。
以上所述仅是本发明的优选方式,应当指出,对于本领域普通技术人员来说,在不脱离本发明创造构思的前提下,还可以做出若干相似的变形和改进,这些也应视为本发明的保护范围之内。
Claims (2)
1.非石棉型混合胶黏剂的制作方法,其特征在于,包括如下如下步骤:
S1,将聚醋酸乙烯树脂与甲醇混合成糊状液体;
S2,将聚醋酸乙烯树脂与甲醇混合成的糊状液体加入重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石粉末的步骤;
S3,在加入重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石粉末后的糊状液体中再加入甲醇,调和均匀值得产品。
2.根据权利要求1所述的非石棉型混合胶黏剂的制作方法,其特征在于,聚醋酸乙烯树脂、S1中与聚醋酸乙烯树脂混合成糊状液体的甲醇、重质碳酸钙、滑石粉、纤维状硅酸镁粉末、蒙脱石以及S3中加入的甲醇的重量份数比为34:5:21:20:2:1:17。