CN104099591A - 一种淡香型铝合金表面处理剂 - Google Patents

一种淡香型铝合金表面处理剂 Download PDF

Info

Publication number
CN104099591A
CN104099591A CN201410276858.0A CN201410276858A CN104099591A CN 104099591 A CN104099591 A CN 104099591A CN 201410276858 A CN201410276858 A CN 201410276858A CN 104099591 A CN104099591 A CN 104099591A
Authority
CN
China
Prior art keywords
parts
stirring
raw material
add
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410276858.0A
Other languages
English (en)
Inventor
徐泽军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ruizhan Tongling Technologies Co Ltd
Original Assignee
Ruizhan Tongling Technologies Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ruizhan Tongling Technologies Co Ltd filed Critical Ruizhan Tongling Technologies Co Ltd
Priority to CN201410276858.0A priority Critical patent/CN104099591A/zh
Publication of CN104099591A publication Critical patent/CN104099591A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种淡香型铝合金表面处理剂，它是由下述重量份的原料组成的：安息香酸0.6-1、铝酸钴0.3-1、烃基丁二酸2-3、重络酸钾2.2-4、香茅醇0.2-0.5、顺丁烯二酸酐1-2.6、甘油2-3、松焦油0.1-0.2、四丁基溴化铵0.3-1、棕榈蜡1-2、水滑石粉0.1-0.2、碳化铬0.1-0.3、成膜助剂2-4、3-氨基丙基三甲氧基硅烷16-20、去离子水110-130，本发明的表面处理剂环保性好，处理后的沉渣少，具有淡淡的清香，可以提高抗菌防腐性能，提高对工件的保护效果。

Description

一种淡香型铝合金表面处理剂
 
技术领域
    本发明主要涉及表面处理领域，尤其涉及一种淡香型铝合金表面处理剂。
背景技术
    铝合金的表面处理方法有很多，如物理法、化学法、物理化学法和综合法。现在常用的方法是阳极氧化法，通过电化学方法在铝合金表面形成转化膜，这种方法虽然可提高铝合金的淡香型性能，但是其适应环境的能力差，转化膜层不够均匀、易脱落，耐磨性能没有得到改善，而传统的磷酸盐转化和铬酸盐钝化表面处理技术虽然可以获得良好的效果，但处理过程中排出的废液中含有锌、锰、镍、铬等重金属离子和亚淡香型等致癌物质，对环境污染非常严重，而金属表面硅烷化处理技术由于不涉及危害环境的物质，生产工艺能耗低、技术应用领域广泛，被认为有望取代磷酸盐转化处理和铬酸盐钝化处理，是金属表面单独防护最新发展方向。
发明内容
本发明目的就是提供一种淡香型铝合金表面处理剂。
本发明是通过以下技术方案实现的：
一种淡香型铝合金表面处理剂，它是由下述重量份的原料组成的：
安息香酸0.6-1、铝酸钴0.3-1、烃基丁二酸2-3、重络酸钾2.2-4、香茅醇0.2-0.5、顺丁烯二酸酐1-2.6、甘油2-3、松焦油0.1-0.2、四丁基溴化铵0.3-1、棕榈蜡1-2、水滑石粉0.1-0.2、碳化铬0.1-0.3、成膜助剂2-4、3-氨基丙基三甲氧基硅烷16-20、去离子水110-130；
所述的成膜助剂是由下述重量份的原料组成的：
醋丙乳液25-30、茶皂素1-2、吡咯烷酮羟酸钠1-2、羟基硅油0.1-0.3、三亚甲基膦酸2-3、烯丙基聚乙二醇0.7-1、硬脂酸锌0.3-0.4、1,2-二甲基咪唑0.2-0.3、去离子水80-90；
将吡咯烷酮羟酸钠加入到醋丙乳液中，加入羟基硅油，100-200转/分搅拌分散3-5分钟；
将茶皂素与烯丙基聚乙二醇混合，加入上述去离子水重量的40-60%，在60-70℃下搅拌混合6-10分钟，加入硬脂酸锌，100-200转/分搅拌分散4-6分钟；
将上述处理后的各原料与剩余各原料混合，400-600转/分搅拌分散20-30分钟，即得所述成膜助剂。
一种淡香型铝合金表面处理剂的制备方法，包括以下步骤：
将安息香酸加入到甘油中，搅拌混合后加入烃基丁二酸，搅拌均匀，加入水滑石粉，70-100转/分搅拌分散3-5分钟；
将香茅醇、棕榈蜡混合，搅拌均匀后加入碳化铬，60-70℃下搅拌混合4-6分钟，冷却至常温；
将上述处理后的各原料与剩余各原料混合，500-600转/分搅拌分散1-2小时，即得所述淡香型铝合金表面处理剂。
本发明的优点是：
    本发明的表面处理剂环保性好，处理后的沉渣少，具有淡淡的清香，可以提高抗菌防腐性能，提高对工件的保护效果。
具体实施方式
实施例1
一种淡香型铝合金表面处理剂，它是由下述重量份的原料组成的：
安息香酸0.6、铝酸钴0.3、烃基丁二酸3、重络酸钾2.2、香茅醇0.5、顺丁烯二酸酐2.6、甘油2、松焦油0.2、四丁基溴化铵0.3、棕榈蜡2、水滑石粉0.2、碳化铬0.3、成膜助剂2、3-氨基丙基三甲氧基硅烷20、去离子水130；
所述的成膜助剂是由下述重量份的原料组成的：
醋丙乳液30、茶皂素1、吡咯烷酮羟酸钠2、羟基硅油0.3、三亚甲基膦酸2、烯丙基聚乙二醇0.7、硬脂酸锌0.4、1,2-二甲基咪唑0.3、去离子水90；
将吡咯烷酮羟酸钠加入到醋丙乳液中，加入羟基硅油,200转/分搅拌分散5分钟；
将茶皂素与烯丙基聚乙二醇混合，加入上述去离子水重量的60%，在70℃下搅拌混合10分钟，加入硬脂酸锌，200转/分搅拌分散6分钟；
将上述处理后的各原料与剩余各原料混合， 600转/分搅拌分散30分钟，即得所述成膜助剂。
一种淡香型铝合金表面处理剂的制备方法，包括以下步骤：
将安息香酸加入到甘油中，搅拌混合后加入烃基丁二酸，搅拌均匀，加入水滑石粉，100转/分搅拌分散3分钟；
将香茅醇、棕榈蜡混合，搅拌均匀后加入碳化铬，70℃下搅拌混合6分钟，冷却至常温；
将上述处理后的各原料与剩余各原料混合，600转/分搅拌分散2小时，即得所述淡香型铝合金表面处理剂。
使用方法：
将进行脱脂、水洗后的铝合金工件置于本发明的表面处理剂中进行浸渍，工作温度20-40℃，工作时间0.5-1min。
性能测试：
取本发明的表面处理剂处理的铝合金板材做实验，该板材的规格为80mm×100mm×4mm，将该板材横向切开，进行喷洒试验，所用试剂为浓度为5% 的氯化钠溶液，试验时间300 小时，测量在切割线一侧形成的鼓泡宽度，结果鼓泡宽度为0 ；
耐盐性：
将该板材浸泡在浓度为5% 的氯化钠溶液中，浸泡300 小时，材料表面基本无变化，浸泡300 小时，无锈斑出现；
耐酸性：
将该板材用温度为23℃的0.05mol/l硫酸进行喷淋实验，实验时间20小时，用清水洗净，在室内放置2小时，漆膜表面无变化，无起泡、无脱落、无破损；
抗剥离性：
将该板材表面涂上一层2-3mm的浆糊，放到温度为50℃，相对湿度为90-96%的密封箱中，实验时间24小时，取出后用清水洗净，漆膜表面无起泡、无脱落、无破损。

Claims (2)

1.一种淡香型铝合金表面处理剂，其特征在于它是由下述重量份的原料组成的：
安息香酸0.6-1、铝酸钴0.3-1、烃基丁二酸2-3、重络酸钾2.2-4、香茅醇0.2-0.5、顺丁烯二酸酐1-2.6、甘油2-3、松焦油0.1-0.2、四丁基溴化铵0.3-1、棕榈蜡1-2、水滑石粉0.1-0.2、碳化铬0.1-0.3、成膜助剂2-4、3-氨基丙基三甲氧基硅烷16-20、去离子水110-130；
所述的成膜助剂是由下述重量份的原料组成的：
醋丙乳液25-30、茶皂素1-2、吡咯烷酮羟酸钠1-2、羟基硅油0.1-0.3、三亚甲基膦酸2-3、烯丙基聚乙二醇0.7-1、硬脂酸锌0.3-0.4、1,2-二甲基咪唑0.2-0.3、去离子水80-90；
将吡咯烷酮羟酸钠加入到醋丙乳液中，加入羟基硅油，100-200转/分搅拌分散3-5分钟；
将茶皂素与烯丙基聚乙二醇混合，加入上述去离子水重量的40-60%，在60-70℃下搅拌混合6-10分钟，加入硬脂酸锌，100-200转/分搅拌分散4-6分钟；
将上述处理后的各原料与剩余各原料混合，400-600转/分搅拌分散20-30分钟，即得所述成膜助剂。
2.一种如权利要求1所述的淡香型铝合金表面处理剂的制备方法，其特征在于包括以下步骤：
将安息香酸加入到甘油中，搅拌混合后加入烃基丁二酸，搅拌均匀，加入水滑石粉，70-100转/分搅拌分散3-5分钟；
将香茅醇、棕榈蜡混合，搅拌均匀后加入碳化铬，60-70℃下搅拌混合4-6分钟，冷却至常温；
将上述处理后的各原料与剩余各原料混合，500-600转/分搅拌分散1-2小时，即得所述淡香型铝合金表面处理剂。
CN201410276858.0A 2014-06-19 2014-06-19 一种淡香型铝合金表面处理剂 Pending CN104099591A (zh)