CN104099017A - 一种非带锈的铝合金表面处理剂 - Google Patents

一种非带锈的铝合金表面处理剂 Download PDF

Info

Publication number
CN104099017A
CN104099017A CN201410275693.5A CN201410275693A CN104099017A CN 104099017 A CN104099017 A CN 104099017A CN 201410275693 A CN201410275693 A CN 201410275693A CN 104099017 A CN104099017 A CN 104099017A
Authority
CN
China
Prior art keywords
parts
alloy surface
stirring
raw material
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410275693.5A
Other languages
English (en)
Inventor
徐泽军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ruizhan Tongling Technologies Co Ltd
Original Assignee
Ruizhan Tongling Technologies Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ruizhan Tongling Technologies Co Ltd filed Critical Ruizhan Tongling Technologies Co Ltd
Priority to CN201410275693.5A priority Critical patent/CN104099017A/zh
Publication of CN104099017A publication Critical patent/CN104099017A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种非带锈的铝合金表面处理剂，它是由下述重量份的原料组成的：芥酸酰胺0.6-1、硫脲0.7-1、棕榈酸2-3、偏硼酸钾1-2、偏硼酸钠0.5-1、烷基磷酸酯二乙醇胺盐1-2、硫酸锰2-3、氟化钙0.3-0.6、月桂酰两性基二乙酸二钠0.8-1、亚硫酸钠1-2、蒙脱土0.2-0.4、季戊四醇4-6、成膜助剂2-4、3-氨基丙基三甲氧基硅烷11-18、去离子水100-120，本发明的表面处理剂适用于不带锈的铝合金表面，能够起到很好的防锈效果，形成的涂膜具有很好的抗酸、抗碱、抗盐雾性，耐热性好，耐候性强。

Description

一种非带锈的铝合金表面处理剂
 
技术领域
    本发明主要涉及表面处理领域，尤其涉及一种非带锈的铝合金表面处理剂。
背景技术
    铝合金的表面处理方法有很多，如物理法、化学法、物理化学法和综合法。现在常用的方法是阳极氧化法，通过电化学方法在铝合金表面形成转化膜，这种方法虽然可提高铝合金的非带锈的性能，但是其适应环境的能力差，转化膜层不够均匀、易脱落，耐磨性能没有得到改善，而传统的磷酸盐转化和铬酸盐钝化表面处理技术虽然可以获得良好的效果，但处理过程中排出的废液中含有锌、锰、镍、铬等重金属离子和亚非带锈的等致癌物质，对环境污染非常严重，而金属表面硅烷化处理技术由于不涉及危害环境的物质，生产工艺能耗低、技术应用领域广泛，被认为有望取代磷酸盐转化处理和铬酸盐钝化处理，是金属表面单独防护最新发展方向。
发明内容
本发明目的就是提供一种非带锈的铝合金表面处理剂。
本发明是通过以下技术方案实现的：
一种非带锈的铝合金表面处理剂，它是由下述重量份的原料组成的：
芥酸酰胺0.6-1、硫脲0.7-1、棕榈酸2-3、偏硼酸钾1-2、偏硼酸钠0.5-1、烷基磷酸酯二乙醇胺盐1-2、硫酸锰2-3、氟化钙0.3-0.6、月桂酰两性基二乙酸二钠0.8-1、亚硫酸钠1-2、蒙脱土0.2-0.4、季戊四醇4-6、成膜助剂2-4、3-氨基丙基三甲氧基硅烷11-18、去离子水100-120；
所述的成膜助剂是由下述重量份的原料组成的：
醋丙乳液25-30、茶皂素1-2、吡咯烷酮羟酸钠1-2、羟基硅油0.1-0.3、三亚甲基膦酸2-3、烯丙基聚乙二醇0.7-1、硬脂酸锌0.3-0.4、1,2-二甲基咪唑0.2-0.3、去离子水80-90；
将吡咯烷酮羟酸钠加入到醋丙乳液中，加入羟基硅油，100-200转/分搅拌分散3-5分钟；
将茶皂素与烯丙基聚乙二醇混合，加入上述去离子水重量的40-60%，在60-70℃下搅拌混合6-10分钟，加入硬脂酸锌，100-200转/分搅拌分散4-6分钟；
将上述处理后的各原料与剩余各原料混合，400-600转/分搅拌分散20-30分钟，即得所述成膜助剂。
一种非带锈的铝合金表面处理剂的制备方法，包括以下步骤：
将硫酸锰、氟化钙、蒙脱土混合，球磨至细度为60-100μm，搅拌均匀后加入到季戊四醇中，60-80℃下搅拌混合4-10分钟，加入棕榈酸，搅拌至常温，加入到去离子水中，加入剩余各原料，400-600转/分搅拌分散1-2小时，即得所述非带锈的铝合金表面处理剂。
本发明的优点是：
    本发明的表面处理剂适用于不带锈的铝合金表面，能够起到很好的防锈效果，形成的涂膜具有很好的抗酸、抗碱、抗盐雾性，耐热性好，耐候性强。
具体实施方式
实施例1
一种非带锈的铝合金表面处理剂，它是由下述重量份的原料组成的：
芥酸酰胺0.6、硫脲0.7、棕榈酸2、偏硼酸钾2、偏硼酸钠0.5、烷基磷酸酯二乙醇胺盐1、硫酸锰2、氟化钙0.6、月桂酰两性基二乙酸二钠0.8、亚硫酸钠1、蒙脱土0.4、季戊四醇6、成膜助剂2、3-氨基丙基三甲氧基硅烷18、去离子水120；
所述的成膜助剂是由下述重量份的原料组成的：
醋丙乳液30、茶皂素1、吡咯烷酮羟酸钠2、羟基硅油 0.3、三亚甲基膦酸3、烯丙基聚乙二醇0.7、硬脂酸锌0.3、1,2-二甲基咪唑0.3、去离子水90；
将吡咯烷酮羟酸钠加入到醋丙乳液中，加入羟基硅油，200转/分搅拌分散5分钟；
将茶皂素与烯丙基聚乙二醇混合，加入上述去离子水重量的60%，在70℃下搅拌混合6分钟，加入硬脂酸锌，100转/分搅拌分散6分钟；
将上述处理后的各原料与剩余各原料混合，400转/分搅拌分散30分钟，即得所述成膜助剂。
一种非带锈的铝合金表面处理剂的制备方法，包括以下步骤：
将硫酸锰、氟化钙、蒙脱土混合，球磨至细度为100μm，搅拌均匀后加入到季戊四醇中，80℃下搅拌混合10分钟，加入棕榈酸，搅拌至常温，加入到去离子水中，加入剩余各原料，600转/分搅拌分散2小时，即得所述非带锈的铝合金表面处理剂。
使用方法：
将进行脱脂、水洗后的铝合金工件置于本发明的表面处理剂中进行浸渍，工作温度20-40℃，工作时间0.5-1min。
性能测试：
取本发明的表面处理剂处理的铝合金板材做实验，该板材的规格为80mm×100mm×4mm，将该板材横向切开，进行喷洒试验，所用试剂为浓度为5% 的氯化钠溶液，试验时间300 小时，测量在切割线一侧形成的鼓泡宽度，结果鼓泡宽度为0 ；
耐盐性：
将该板材浸泡在浓度为5% 的氯化钠溶液中，浸泡300 小时，材料表面基本无变化，浸泡300 小时，无锈斑出现；
耐酸性：
将该板材用温度为23℃的0.05mol/l硫酸进行喷淋实验，实验时间20小时，用清水洗净，在室内放置2小时，漆膜表面无变化，无起泡、无脱落、无破损；
抗剥离性：
将该板材表面涂上一层2-3mm的浆糊，放到温度为50℃，相对湿度为90-96%的密封箱中，实验时间24小时，取出后用清水洗净，漆膜表面无起泡、无脱落、无破损。

Claims (2)

1.一种非带锈的铝合金表面处理剂，其特征在于它是由下述重量份的原料组成的：
芥酸酰胺0.6-1、硫脲0.7-1、棕榈酸2-3、偏硼酸钾1-2、偏硼酸钠0.5-1、烷基磷酸酯二乙醇胺盐1-2、硫酸锰2-3、氟化钙0.3-0.6、月桂酰两性基二乙酸二钠0.8-1、亚硫酸钠1-2、蒙脱土0.2-0.4、季戊四醇4-6、成膜助剂2-4、3-氨基丙基三甲氧基硅烷11-18、去离子水100-120；
所述的成膜助剂是由下述重量份的原料组成的：
醋丙乳液25-30、茶皂素1-2、吡咯烷酮羟酸钠1-2、羟基硅油0.1-0.3、三亚甲基膦酸2-3、烯丙基聚乙二醇0.7-1、硬脂酸锌0.3-0.4、1,2-二甲基咪唑0.2-0.3、去离子水80-90；
将吡咯烷酮羟酸钠加入到醋丙乳液中，加入羟基硅油，100-200转/分搅拌分散3-5分钟；
将茶皂素与烯丙基聚乙二醇混合，加入上述去离子水重量的40-60%，在60-70℃下搅拌混合6-10分钟，加入硬脂酸锌，100-200转/分搅拌分散4-6分钟；
将上述处理后的各原料与剩余各原料混合，400-600转/分搅拌分散20-30分钟，即得所述成膜助剂。
2.一种如权利要求1所述的非带锈的铝合金表面处理剂的制备方法，其特征在于包括以下步骤：
将硫酸锰、氟化钙、蒙脱土混合，球磨至细度为60-100μm，搅拌均匀后加入到季戊四醇中，60-80℃下搅拌混合4-10分钟，加入棕榈酸，搅拌至常温，加入到去离子水中，加入剩余各原料，400-600转/分搅拌分散1-2小时，即得所述非带锈的铝合金表面处理剂。
CN201410275693.5A 2014-06-19 2014-06-19 一种非带锈的铝合金表面处理剂 Pending CN104099017A (zh)