CN104313592A - 一种水基电镀防锈剂及其制备方法 - Google Patents
一种水基电镀防锈剂及其制备方法 Download PDFInfo
- Publication number
- CN104313592A CN104313592A CN201410622246.2A CN201410622246A CN104313592A CN 104313592 A CN104313592 A CN 104313592A CN 201410622246 A CN201410622246 A CN 201410622246A CN 104313592 A CN104313592 A CN 104313592A
- Authority
- CN
- China
- Prior art keywords
- water
- add
- parts
- antirust agent
- 30min
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水基电镀防锈剂,其特征是由下述重量份的原料制得:氨基硅油0.5-1,羧甲基淀粉钠2-4,乙基麦芽酚0.5-1,聚乙二醇月桂酸酯1-2,改性助剂6-8,L-半胱氨酸0.2-0.4,水性蜡乳液4-6,辛烯基琥珀酸淀粉酯1-2,月桂酰胺丙基羟磺基甜菜碱0.3-0.5,季戊四醇油酸酯0.3-0.5,硫代硫酸钠1-2,羟基乙叉二膦酸二钠0.1-0.2,水30-40。本发明的防锈剂在金属表面形成的膜层具有极强的防腐蚀﹑防变色、防静电、防锈和耐盐雾能力,不易燃烧,环保无毒,使用方便,易于操作,处理后的工件光泽度好。
Description
技术领域
本发明涉及金属处理领域,具体涉及一种水基电镀防锈剂及其制备方法。
背景技术
金属工件在生产加工及运输的过程中,很容易生锈,而一旦生锈,将对成品的外观和性能产生不良影响,锈蚀严重的甚至会造成钢材报废。钢铁生锈给国民经济造成巨大损失,因此需要使用防锈剂对金属进行保护。防锈剂的作用方式是通过在金属表面形成一层薄膜来防止金属发生锈蚀。常用防锈剂大部分为油性,其在生产、使用的过程中使用大量有机溶剂,对环境造成污染,因此水基防锈剂的研究具有重要的意义。
传统的金属水基防锈剂大多数都含有亚硝酸盐,其具有价廉、效果良好及使用方便、易去除等优势,但是由于亚硝酸盐能转化成致癌物,其使用和排放已经受到严格限制。目前,新型环保水基防锈剂的研究开始得到广泛的关注,成为一种开发趋势。
发明内容
本发明的目的是提供一种水基电镀防锈剂。
本发明是通过以下技术方案实现的:
一种水基电镀防锈剂,其特征在于,其是由下述重量份的原料制得:
氨基硅油0.5-1,羧甲基淀粉钠2-4,乙基麦芽酚0.5-1,聚乙二醇月桂酸酯1-2,改性助剂6-8,L-半胱氨酸0.2-0.4,水性蜡乳液4-6,辛烯基琥珀酸淀粉酯1-2,月桂酰胺丙基羟磺基甜菜碱0.3-0.5,季戊四醇油酸酯0.3-0.5,硫代硫酸钠1-2,羟基乙叉二膦酸二钠0.1-0.2,水30-40;
其中改性助剂由下列重量份的原料制成:
纳米蒙脱土10-20,有机硅季铵盐3-5,聚乙二醇2-4,苹果酸0.5-1,单宁酸0.1-0.2,绿原酸0.05-0.1,三聚磷酸钠1-2;
改性助剂的制备方法是:
将纳米蒙脱土与苹果酸、三聚磷酸钠加入适量水中超声分散15-30min,过滤后干燥,加入聚乙二醇、单宁酸、绿原酸和适量乙醇超声分散5-10min再一并加入反应容器,加入有机硅季铵盐,在氮气保护下加热搅拌回流反应8-12h,过滤并用乙醇洗涤数次,真空干燥完全,即得。
一种水基电镀防锈剂的制备方法,其特征在于,包括以下步骤:
(1)将聚乙二醇月桂酸酯、辛烯基琥珀酸淀粉酯和月桂酰胺丙基羟磺基甜菜碱加入1/3-1/2量的水中,800-1000r/min搅拌10-15min,再加入季戊四醇油酸酯和氨基硅油,60-80℃、800-1000r/min下搅拌15-30min,得组分A;
(2)将水性蜡乳液和改性助剂加入余量的水中,先超声分散5-10min,再加入羧甲基淀粉钠,8000-10000r/min高速匀浆15-30min,得组分B;
(3)将组分A、组分B与其余原料混合后400-600r/min搅拌15-30min,分装后即得。
其中水性蜡乳液选用水性巴西棕榈蜡乳液。
本发明的优点是:
1. 本发明的防锈剂在金属表面形成的膜层具有极强的防腐蚀﹑防变色、防锈和耐盐雾能力,不易燃烧,环保无毒,使用方便,易操作,处理后的工件光泽度好;
2. 通过添加改性助剂,使防锈剂在金属表面形成牢固、致密、耐腐蚀的膜层,同时还有防静电、抗菌防霉、易去污等效应。
具体实施方式
本发明非限定实施例如下:
一种水基电镀防锈剂,由下列重量(kg)的组分原料制备而成:
氨基硅油0.8,羧甲基淀粉钠3,乙基麦芽酚0.8,聚乙二醇月桂酸酯1.5,改性助剂7,L-半胱氨酸0.3,水性蜡乳液5,辛烯基琥珀酸淀粉酯1.5,月桂酰胺丙基羟磺基甜菜碱0.4,季戊四醇油酸酯0.4,硫代硫酸钠1.5,羟基乙叉二膦酸二钠0.15,水35;
其中,改性助剂由下列重量(kg)的原料制成:
纳米蒙脱土15,有机硅季铵盐4,聚乙二醇3,苹果酸0.8,单宁酸0.15,绿原酸0.08,三聚磷酸钠1.5;
改性助剂的制备方法:
将纳米蒙脱土与苹果酸、三聚磷酸钠加入适量水中超声分散30min,过滤后干燥,加入聚乙二醇、单宁酸、绿原酸和适量乙醇超声分散10min再一并加入反应容器,加入有机硅季铵盐,在氮气保护下加热搅拌回流反应10h,过滤并用乙醇洗涤数次,真空干燥完全,即得。
水基电镀防锈剂的制备方法包括以下步骤:
(1)将聚乙二醇月桂酸酯、辛烯基琥珀酸淀粉酯和月桂酰胺丙基羟磺基甜菜碱加入1/2量的水中,1000r/min搅拌15min,再加入季戊四醇油酸酯和氨基硅油,80℃、1000r/min下搅拌30min,得组分A;
(2)将水性蜡乳液和改性助剂加入余量的水中,先超声分散5min,再加入羧甲基淀粉钠,10000r/min高速匀浆15min,得组分B;
(3)将组分A、组分B与其余原料混合后600r/min搅拌15min,分装后即得。
经检验,湿热试验45#钢片20天合格,盐雾试验45#钢片7天合格。
Claims (2)
1.一种水基电镀防锈剂,其特征在于,其是由下述重量份的原料制得:
氨基硅油0.5-1,羧甲基淀粉钠2-4,乙基麦芽酚0.5-1,聚乙二醇月桂酸酯1-2,改性助剂6-8,L-半胱氨酸0.2-0.4,水性蜡乳液4-6,辛烯基琥珀酸淀粉酯1-2,月桂酰胺丙基羟磺基甜菜碱0.3-0.5,季戊四醇油酸酯0.3-0.5,硫代硫酸钠1-2,羟基乙叉二膦酸二钠0.1-0.2,水30-40;
所述改性助剂由下列重量份的原料制成:
纳米蒙脱土10-20,有机硅季铵盐3-5,聚乙二醇2-4,苹果酸0.5-1,单宁酸0.1-0.2,绿原酸0.05-0.1,三聚磷酸钠1-2;
所述改性助剂的制备方法是:
将纳米蒙脱土与苹果酸、三聚磷酸钠加入适量水中超声分散15-30min,过滤后干燥,加入聚乙二醇、单宁酸、绿原酸和适量乙醇超声分散5-10min再一并加入反应容器,加入有机硅季铵盐,在氮气保护下加热搅拌回流反应8-12h,过滤并用乙醇洗涤数次,真空干燥完全,即得。
2.根据权利要求1所述的一种水基电镀防锈剂的制备方法,其特征在于,包括以下步骤:
(1)将聚乙二醇月桂酸酯、辛烯基琥珀酸淀粉酯和月桂酰胺丙基羟磺基甜菜碱加入1/3-1/2量的水中,800-1000r/min搅拌10-15min,再加入季戊四醇油酸酯和氨基硅油,60-80℃、800-1000r/min下搅拌15-30min,得组分A;
(2)将水性蜡乳液和改性助剂加入余量的水中,先超声分散5-10min,再加入羧甲基淀粉钠,8000-10000r/min高速匀浆15-30min,得组分B;
(3)将组分A、组分B与其余原料混合后400-600r/min搅拌15-30min,分装后即得。