CN104087242A - 一种沥青废橡胶防水油膏的制备方法 - Google Patents
一种沥青废橡胶防水油膏的制备方法 Download PDFInfo
- Publication number
- CN104087242A CN104087242A CN201410280678.XA CN201410280678A CN104087242A CN 104087242 A CN104087242 A CN 104087242A CN 201410280678 A CN201410280678 A CN 201410280678A CN 104087242 A CN104087242 A CN 104087242A
- Authority
- CN
- China
- Prior art keywords
- waste rubber
- raw material
- pitch
- formula ratio
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种沥青废橡胶防水油膏的制备方法，涉及化工技术领域，由以下组分的原料组成，石油沥青95-105份、废橡胶粉10-20份、硫磺粉10-20份、机油35.0-35.2份、重松节油32.0-32.2份、松焦油17.0-17.2份、无机填料81-83份。本发明的有益效果是：本发明制备方便简单，原料易得，设备投资少，便于操作，制备的沥青废橡胶防水油膏，环保无污染，纯度高，使用效果好，耐高温性强，安全可靠。
Description
技术领域
本发明涉及化工技术领域，具体涉及一种沥青废橡胶防水油膏的制备方法。
背景技术
建筑密封材料是嵌入建筑物缝隙、门窗四周、玻璃镶嵌部位以及由于开裂产生的裂缝，能承受位移且能达到气密、水密的目的的材料，又称嵌缝材料。建筑密封材料中，使用最为广泛的一种材料即为建筑密封膏，建筑密封膏主要由于其防水效果好，施工方便，高温不流淌，黏结性能好，低温不脆裂等优点，广泛的使用在各种工业厂房与民用建筑屋面工程等一些低温技术领域的接缝密封，防水油膏在生产时候的由于在生产的技术匮乏，因此可选度很低，生产的方法与生产时候所产生的污染无法保证。
发明内容
本发明所要解决的技术问题在于提供一种无毒环保，制备工艺简单的沥青废橡胶防水油膏的制备方法。
本发明所要解决的技术问题采用以下技术方案来实现：
一种沥青废橡胶防水油膏，其特征在于，由以下组分的原料组成：
各原料的优选组分为：
所述的无机填充料有两种，分别为石棉绒和滑石粉，所述的石棉绒：滑石粉为20：21。
本发明的另一目的是制备本发明沥青废橡胶防水油膏的制备方法，其特征在于：包括以下工艺步骤，
a.选取一反应釜，按照配方量将原料中的沥青和松焦油加入其中，加热脱水，然后将温度控制在200℃，按照配方量加入原料中的废橡胶粉，持续搅拌。
b.在不断搅拌步骤a中釜内的混合物时，将温度升至200-230℃，进行脱硫反应，而后得到再生橡胶沥青。
c.将步骤b中釜内的反应物进行降温，降至160℃后，按照配方量将原料中的硫磺粉加入其中，保温反应30min。
d.待上述步骤c反应结束后，再次将内部的温度降至140℃，然后按照配方量将原料中的机油加入其中，在继续降温至100℃，按照配方量将原料中的重松节油和无机填料加入其中，搅拌均匀后，得到的产物即为本发明所要制备的沥青废橡胶防水油膏成品，包装入库。
本发明的有益效果是：本发明制备方便简单，原料易得，设备投资少，便于操作，制备的沥青废橡胶防水油膏，环保无污染，纯度高，使用效果好，耐高温性强，安全可靠。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
本发明所要解决的技术问题采用以下技术方案来实现：
一种沥青废橡胶防水油膏，由以下组分的原料组成：
制备本发明沥青废橡胶防水油膏的的方法，包括以下工艺步骤：
a.选取一反应釜，按照配方量将原料中的沥青和松焦油加入其中，加热脱水，然后将温度控制在200℃，按照配方量加入原料中的废橡胶粉，持续搅拌。
b.在不断搅拌步骤a中釜内的混合物时，将温度升至200-230℃，进行脱硫反应，而后得到再生橡胶沥青。
c.将步骤b中釜内的反应物进行降温，降至160℃后，按照配方量将原料中的硫磺粉加入其中，保温反应30min。
d.待上述步骤c反应结束后，再次将内部的温度降至140℃，然后按照配方量将原料中的机油加入其中，在继续降温至100℃，按照配方量将原料中的重松节油、石棉绒和滑石粉加入其中，搅拌均匀后，得到的产物即为本发明所要制备的沥青废橡胶防水油膏成品，包装入库。
实施例2
一种沥青废橡胶防水油膏，由以下组分的原料组成：
制备本发明沥青废橡胶防水油膏的的方法，包括以下工艺步骤：
a.选取一反应釜，按照配方量将原料中的沥青和松焦油加入其中，加热脱水，然后将温度控制在200℃，按照配方量加入原料中的废橡胶粉，持续搅拌。
b.在不断搅拌步骤a中釜内的混合物时，将温度升至200-230℃，进行脱硫反应，而后得到再生橡胶沥青。
c.将步骤b中釜内的反应物进行降温，降至160℃后，按照配方量将原料中的硫磺粉加入其中，保温反应30min。
d.待上述步骤c反应结束后，再次将内部的温度降至140℃，然后按照配方量将原料中的机油加入其中，在继续降温至100℃，按照配方量将原料中的重松节油、石棉绒和滑石粉加入其中，搅拌均匀后，得到的产物即为本发明所要制备的沥青废橡胶防水油膏成品，包装入库。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种沥青废橡胶防水油膏，其特征在于，由以下组分的原料组成：
。
2.根据权利要求1所述的一种沥青废橡胶防水油膏，其特征在于：优选的原料组分为：
。
3.根据权利要求1所述的一种沥青废橡胶防水油膏，其特征在于：所述的无机填充料有两种，分别为石棉绒和滑石粉，所述的石棉绒：滑石粉为20：21。
4.根据权利要求1-2所述的一种沥青废橡胶防水油膏的制备方法，其特征在于：包括以下步骤，
a.选取一反应釜，按照配方量将原料中的沥青和松焦油加入其中，加热脱水，然后将温度控制在200℃，按照配方量加入原料中的废橡胶粉，持续搅拌。
b.在不断搅拌步骤a中釜内的混合物时，将温度升至200-230℃，进行脱硫反应，而后得到再生橡胶沥青。
c.将步骤b中釜内的反应物进行降温，降至160℃后，按照配方量将原料 中的硫磺粉加入其中，保温反应30min。
d.待上述步骤c反应结束后，再次将内部的温度降至140℃，然后按照配方量将原料中的机油加入其中，在继续降温至100℃，按照配方量将原料中的重松节油和无机填料加入其中，搅拌均匀后，得到的产物即为本发明所要制备的沥青废橡胶防水油膏成品，包装入库。