CN103664083B - 高强度铁矿渣粉保温砂浆及其制备方法 - Google Patents

高强度铁矿渣粉保温砂浆及其制备方法 Download PDF

Info

Publication number
CN103664083B
CN103664083B CN201310605231.0A CN201310605231A CN103664083B CN 103664083 B CN103664083 B CN 103664083B CN 201310605231 A CN201310605231 A CN 201310605231A CN 103664083 B CN103664083 B CN 103664083B
Authority
CN
China
Prior art keywords
powder
slag
thermal insulation
insulation mortar
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310605231.0A
Other languages
English (en)
Other versions
CN103664083A (zh
Inventor
许正贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu Tian Wangyuxu Articles For Use Co Ltd
Original Assignee
Bengbu Tian Wangyuxu Articles For Use Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Tian Wangyuxu Articles For Use Co Ltd filed Critical Bengbu Tian Wangyuxu Articles For Use Co Ltd
Priority to CN201310605231.0A priority Critical patent/CN103664083B/zh
Publication of CN103664083A publication Critical patent/CN103664083A/zh
Application granted granted Critical
Publication of CN103664083B publication Critical patent/CN103664083B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高强度铁矿渣粉保温砂浆，其特征在于由下列重量份的原料制成：水泥300-340、水泥路渣粉末50-55、铁矿渣粉20-24、鳞片状石墨粉8-10、钠基膨润土粉14-18、羧甲基纤维素钠5-8、海泡石粉20-25、高岭土粉50-56、石膏粉10-15、羟丙基田菁胶粉4-6、黄原胶5-8、丙烯酰胺1-2、硼砂3-4、改性纳米碳粉4-6、水600-650；本发明采用铁矿渣粉的保温砂浆具有容重轻、导热系数低、抗开裂、抗老化、粘结力强、具有良好的和易性和施工性能、使用方便，同时具有防水抗渗、抗压强度高、贮存和运输方便、不污染环境等优点。

Description

高强度铁矿渣粉保温砂浆及其制备方法
技术领域
本发明属于建筑材料领域，具体涉及一种高强度铁矿渣粉保温砂浆及其制备方法。
背景技术
我国外墙保温包括有机保温体系和无机保温体系和有机和无机复合保温材料三类。其中，主要为有机类保温材料，生产和施工技术已经很成熟，但是不能防火，污染环境，易老化。无机类保温砂浆材料由于其成品低，强度高，保温，防火，耐候性等优点受到广泛的关注，但是仍存在成本较高、材料来源有限等缺点，仍然具有改进的空间。
随着建筑绿色施工的发展废弃的混凝土块、标准砖块及（空心）加气混凝土砌块等建筑固体废弃物的使用已成为节能要求而普遍使用的材料，但由于其体积较大，强度相对较低，故在搬运过程中由于操作不当很容易产生棱掉角的破坏，此部分砌块将不能用于主体工程之上。这些破坏的固体废弃物往往是运回厂家重新加气或者当建筑垃圾而扔掉。利用这些建筑垃圾作为砂浆材料，可以废物利用，具有环境效益。
发明内容
本发明的目的是提供一种高强度铁矿渣粉保温砂浆及其制备方法。
本发明的技术方案如下：
一种高强度铁矿渣粉保温砂浆，其特征在于由下列重量份的原料制成：水泥300-340、水泥路渣粉末50-55、铁矿渣粉20-24、鳞片状石墨粉8-10、钠基膨润土粉14-18、羧甲基纤维素钠5-8、海泡石粉20-25、高岭土粉50-56、石膏粉10-15、羟丙基田菁胶粉4-6、黄原胶5-8、丙烯酰胺1-2、硼砂3-4、改性纳米碳粉4-6、水600-650；所述的改性纳米碳粉由下列重量份的原料制成：纳米碳10-11、玉石粉20-24、苯甲酸钠1-2、当归油1-2、阳起石粉2-3、硅烷偶联剂KH5501-2、亚硒酸钠1-2、绞股蓝粉1-2；将各原料成分混合，研磨分散均匀即得。
所述的高强度铁矿渣粉保温砂浆的制备方法，其特征在于是将除水泥以后的其它成分混合，加热至60-70℃，搅拌20-30分钟，成浆料，然后加入水泥混合成膏体即得。
本发明采用铁矿渣粉的保温砂浆具有容重轻、导热系数低、抗开裂、抗老化、粘结力强、具有良好的和易性和施工性能、使用方便，同时具有防水抗渗、抗压强度高、贮存和运输方便、不污染环境等优点。
具体实施方式
一种高强度铁矿渣粉保温砂浆，由下列重量份（公斤）的原料制成：水泥300、水泥路渣粉末50、铁矿渣粉24、鳞片状石墨粉8、钠基膨润土粉14、羧甲基纤维素钠5、海泡石粉20、高岭土粉56、石膏粉10、羟丙基田菁胶粉4、黄原胶8、丙烯酰胺2、硼砂3、改性纳米碳粉6、水600；
所述的高强度铁矿渣粉保温砂浆的制备方法，其特征在于是将除水泥以后的其它成分混合，加热至60-70℃，搅拌20-30分钟，成浆料，然后加入水泥混合成膏体即得。
所述的改性纳米碳粉由下列重量份（公斤）的原料制成：纳米碳10、玉石粉24、苯甲酸钠1、当归油1、阳起石粉3、硅烷偶联剂KH5502、亚硒酸钠1、绞股蓝粉1；将各原料成分混合，研磨分散均匀即得。
本发明砂浆各项性能为：导热系数0.064W/m.k，抗冻性符合要求（15次无变化），28d抗压强度：0.24Mpa，防火等级为A级。

Claims (1)

1.一种高强度铁矿渣粉保温砂浆，其特征在于由下列重量份的原料制成：水泥300-340、水泥路渣粉末50-55、铁矿渣粉20-24、鳞片状石墨粉8-10、钠基膨润土粉14-18、羧甲基纤维素钠5-8、海泡石粉20-25、高岭土粉50-56、石膏粉10-15、羟丙基田菁胶粉4-6、黄原胶5-8、丙烯酰胺1-2、硼砂3-4、改性纳米碳粉4-6、水600-650；所述的改性纳米碳粉由下列重量份的原料制成：纳米碳10-11、玉石粉20-24、苯甲酸钠1-2、当归油1-2、阳起石粉2-3、硅烷偶联剂KH5501-2、亚硒酸钠1-2、绞股蓝粉1-2；将各原料成分混合，研磨分散均匀即得；
所述的高强度铁矿渣粉保温砂浆的制备方法是将除水泥以后的其它成分混合，加热至60-70℃，搅拌20-30分钟，成浆料，然后加入水泥混合成膏体即得。
CN201310605231.0A 2013-11-26 2013-11-26 高强度铁矿渣粉保温砂浆及其制备方法 Expired - Fee Related CN103664083B (zh)