CN105236855A - 高防水保温砂浆及其制备方法 - Google Patents

高防水保温砂浆及其制备方法 Download PDF

Info

Publication number
CN105236855A
CN105236855A CN201510562007.7A CN201510562007A CN105236855A CN 105236855 A CN105236855 A CN 105236855A CN 201510562007 A CN201510562007 A CN 201510562007A CN 105236855 A CN105236855 A CN 105236855A
Authority
CN
China
Prior art keywords
parts
powder
water
insulation mortar
magnesium oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510562007.7A
Other languages
English (en)
Inventor
朱安会
马洪章
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Xin Run Type Material Co Ltd
Original Assignee
Anhui Xin Run Type Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Xin Run Type Material Co Ltd filed Critical Anhui Xin Run Type Material Co Ltd
Priority to CN201510562007.7A priority Critical patent/CN105236855A/zh
Publication of CN105236855A publication Critical patent/CN105236855A/zh
Pending legal-status Critical Current

Abstract

一种高防水保温砂浆，其特征在于由下列重量份的原料制成：水泥300-340、氧化镁20-24、硅藻土粉30-35、粉煤灰50-55、聚丙烯纤维20-24、聚羧酸减水剂10-12、石膏粉21-25、石英砂粉5-8、木质素磺酸钙3-5、扩散剂MF2-3、聚乙烯醇12-15、EDTA四钠2-3、明矾粉2-3、碳酸钠1-2、氧化钙2-3、氧化镁5-8、硫酸铝渣10-16、改性纳米碳粉4-6、水600-650；本保温砂浆能够快速凝结硬化。防水性好，与基材产生较强的粘结能力，体积稳定性好，凝结硬化时产生体积微膨胀，不开裂、不空鼓，耐水性强，抗老化，使用寿命长。

Description

高防水保温砂浆及其制备方法
技术领域
本发明属于建筑材料领域，具体涉及一种高防水保温砂浆及其制备方法。
背景技术
我国外墙保温包括有机保温体系和无机保温体系和有机和无机复合保温材料三类。其中，主要为有机类保温材料，生产和施工技术已经很成熟，但是不能防火，污染环境，易老化。无机类保温砂浆材料由于其成品低，强度高，保温，防火，耐候性等优点受到广泛的关注，但是仍存在成本较高、材料来源有限等缺点，仍然具有改进的空间。
发明内容
本发明的目的是提供一种高防水保温砂浆及其制备方法。
本发明的技术方案如下：
一种高防水保温砂浆，其特征在于由下列重量份的原料制成：水泥300-340、氧化镁20-24、硅藻土粉30-35、粉煤灰50-55、聚丙烯纤维20-24、聚羧酸减水剂10-12、石膏粉21-25、石英砂粉5-8、木质素磺酸钙3-5、扩散剂MF2-3、聚乙烯醇12-15、EDTA四钠2-3、明矾粉2-3、碳酸钠1-2、氧化钙2-3、氧化镁5-8、硫酸铝渣10-16、改性纳米碳粉4-6、水600-650；所述的改性纳米碳粉由下列重量份的原料制成：纳米碳10-11、明矾5-6、铁矿渣粉1-2、玉石粉4-5、硅烷偶联剂KH-5501-2、当归油1-2、磁石粉1-2、碳化硅4-5、醇酯十二1-2、茶多酚1-2、老鹰茶粉1-2；将各原料成分混合，研磨分散均匀即得。
所述的高防水保温砂浆的制备方法，其特征在于是将除水泥以后的其它成分混合，加热至60-70℃，搅拌20-30分钟，成浆料，然后加入水泥混合成膏体即得。
本保温砂浆能够快速凝结硬化。防水性好，与基材产生较强的粘结能力，体积稳定性好，凝结硬化时产生体积微膨胀，不开裂、不空鼓，耐水性强，抗老化，使用寿命长。
具体实施方式
一种高防水保温砂浆，由下列重量份（公斤）的原料制成：水泥300、氧化镁20、硅藻土粉30、粉煤灰50、聚丙烯纤维20、聚羧酸减水剂12、石膏粉21、石英砂粉5、木质素磺酸钙5、扩散剂MF2、聚乙烯醇12、EDTA四钠3、明矾粉3、碳酸钠2、氧化钙2、氧化镁8、硫酸铝渣16、改性纳米碳粉4、水600；
所述的高防水保温砂浆的制备方法，其特征在于是将除水泥以后的其它成分混合，加热至60-70℃，搅拌20-30分钟，成浆料，然后加入水泥混合成膏体即得。
所述的改性纳米碳粉由下列重量份（公斤）的原料制成：纳米碳10、明矾5、铁矿渣粉1、玉石粉4、硅烷偶联剂KH-5502、当归油2、磁石粉2、碳化硅5、醇酯十二1、茶多酚2、老鹰茶粉1；将各原料成分混合，研磨分散均匀即得。
本发明砂浆各项性能为：导热系数0.041W/m.k，抗冻性符合要求（15次无变化），28d抗压强度：0.35Mpa，防火等级为A级。

Claims (2)

1.一种高防水保温砂浆，其特征在于由下列重量份的原料制成：水泥300-340、氧化镁20-24、硅藻土粉30-35、粉煤灰50-55、聚丙烯纤维20-24、聚羧酸减水剂10-12、石膏粉21-25、石英砂粉5-8、木质素磺酸钙3-5、扩散剂MF2-3、聚乙烯醇12-15、EDTA四钠2-3、明矾粉2-3、碳酸钠1-2、氧化钙2-3、氧化镁5-8、硫酸铝渣10-16、改性纳米碳粉4-6、水600-650；所述的改性纳米碳粉由下列重量份的原料制成：纳米碳10-11、明矾5-6、铁矿渣粉1-2、玉石粉4-5、硅烷偶联剂KH-5501-2、当归油1-2、磁石粉1-2、碳化硅4-5、醇酯十二1-2、茶多酚1-2、老鹰茶粉1-2；将各原料成分混合，研磨分散均匀即得。
2.根据以权利要求1所述的高防水保温砂浆的制备方法，其特征在于是将除水泥以后的其它成分混合，加热至60-70℃，搅拌20-30分钟，成浆料，然后加入水泥混合成膏体即得。
CN201510562007.7A 2015-09-07 2015-09-07 高防水保温砂浆及其制备方法 Pending CN105236855A (zh)