CN104087201B - 一种乙烯-醋酸乙烯热熔胶 - Google Patents

一种乙烯-醋酸乙烯热熔胶 Download PDF

Info

Publication number
CN104087201B
CN104087201B CN201410293067.9A CN201410293067A CN104087201B CN 104087201 B CN104087201 B CN 104087201B CN 201410293067 A CN201410293067 A CN 201410293067A CN 104087201 B CN104087201 B CN 104087201B
Authority
CN
China
Prior art keywords
add
vinyl acetate
ethene
atoleine
adhesive aid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410293067.9A
Other languages
English (en)
Other versions
CN104087201A (zh
Inventor
李勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chuzhou City Guang Wei Chemical Co Ltd
Original Assignee
Chuzhou City Guang Wei Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chuzhou City Guang Wei Chemical Co Ltd filed Critical Chuzhou City Guang Wei Chemical Co Ltd
Priority to CN201410293067.9A priority Critical patent/CN104087201B/zh
Publication of CN104087201A publication Critical patent/CN104087201A/zh
Application granted granted Critical
Publication of CN104087201B publication Critical patent/CN104087201B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种乙烯-醋酸乙烯热熔胶，它是由下述重量份的原料组成的：乙烯-醋酸乙烯共聚物64-71、三萜皂苷1-2、磷酸钠0.1-0.3、甲苯基二苯基磷酸酯1-2、蓖麻油酸锌0.2-0.4、聚马来酸酐1-2、钼酸铵1-2、液体石蜡10-13、甘油聚氧乙烯醚椰油酸酯0.3-1、双巯基乙酸异辛酯二正辛基锡0.1-0.2、双十二碳醇酯2-3、粘结助剂7-10；本发明制备的热熔胶基本没有污染和挥发物，具有适中的弹性、良好的耐油迁移、间隔后易剥离、易喷胶等优点。

Description

一种乙烯-醋酸乙烯热熔胶
技术领域
本发明主要涉及一种热熔胶粉末，尤其涉及一种乙烯-醋酸乙烯热熔胶。
背景技术
热熔胶是一种可塑性的粘合剂，在一定温度范围内其物理状态随温度改变而改变，而化学特性不变，其无毒无味，属环保型化学产品。
发明内容
本发明目的就是提供一种乙烯-醋酸乙烯热熔胶。
本发明是通过以下技术方案实现的：
一种乙烯-醋酸乙烯热熔胶，它是由下述重量份的原料组成的：
乙烯-醋酸乙烯共聚物64-71、三萜皂苷1-2、磷酸钠0.1-0.3、甲苯基二苯基磷酸酯1-2、蓖麻油酸锌0.2-0.4、聚马来酸酐1-2、钼酸铵1-2、液体石蜡10-13、甘油聚氧乙烯醚椰油酸酯0.3-1、双巯基乙酸异辛酯二正辛基锡0.1-0.2、双十二碳醇酯2-3、粘结助剂7-10；
所述的增粘结助剂是由下述重量份的原料组成的：
液体石蜡24-30、亚麻籽胶2-3、氟化石墨1-2、EVA树脂4-5、马来酸二丁酯3-4、油酸钾皂0.6-2、丙基三甲氧基硅烷0.2-0.5；
将EVA树脂加热软化，加入马来酸二丁酯，搅拌均匀，加入丙基三甲氧基硅烷，在50-60℃下保温搅拌10-15分钟，加入到液体石蜡中，搅拌均匀，得粘结液；
将亚麻籽胶与油酸钾皂混合，搅拌均匀后加入氟化石墨，球磨均匀，加入到上述粘结液中，60-80转/分搅拌分散3-4分钟，即得所述粘结助剂。
一种乙烯-醋酸乙烯热熔胶的制备方法，其特征在于包括以下步骤：
将钼酸铵、蓖麻油酸锌混合加入到液体石蜡中，搅拌均匀后加入三萜皂苷，100-120转/分搅拌混合5-10分钟，加入甲苯基二苯基磷酸酯、双巯基乙酸异辛酯二正辛基锡，在50-60℃下搅拌混合10-16分钟，加入双十二碳醇酯，搅拌至常温，加入除了粘结助剂以外的各原料，在25-30℃下保温静置1-2小时，加入粘结助剂，送入混炼机，加热升温至90-100℃，混炼20-30min；将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机，挤出产物经冷却、造粒，即得所述乙烯-醋酸乙烯热熔胶。
本发明的优点是：
本发明制备的热熔胶基本没有污染和挥发物，具有适中的弹性、良好的耐油迁移、间隔后易剥离、易喷胶等优点。
具体实施方式
实施例1
一种乙烯-醋酸乙烯热熔胶，它是由下述重量份（公斤）的原料组成的：
乙烯-醋酸乙烯共聚物71、三萜皂苷1、磷酸钠0.3、甲苯基二苯基磷酸酯1、蓖麻油酸锌0.2、聚马来酸酐2、钼酸铵2、液体石蜡13、甘油聚氧乙烯醚椰油酸酯0.3、双巯基乙酸异辛酯二正辛基锡0.2、双十二碳醇酯3、粘结助剂10；
所述的增粘结助剂是由下述重量份的原料组成的：
液体石蜡30、亚麻籽胶2、氟化石墨1、EVA树脂4、马来酸二丁酯4、油酸钾皂0.6、丙基三甲氧基硅烷0.5；
将EVA树脂加热软化，加入马来酸二丁酯，搅拌均匀，加入丙基三甲氧基硅烷，在60℃下保温搅拌15分钟，加入到液体石蜡中，搅拌均匀，得粘结液；
将亚麻籽胶与油酸钾皂混合，搅拌均匀后加入氟化石墨，球磨均匀，加入到上述粘结液中，80转/分搅拌分散4分钟，即得所述粘结助剂。
一种乙烯-醋酸乙烯热熔胶的制备方法，包括以下步骤：
将钼酸铵、蓖麻油酸锌混合加入到液体石蜡中，搅拌均匀后加入三萜皂苷，120转/分搅拌混合10分钟，加入甲苯基二苯基磷酸酯、双巯基乙酸异辛酯二正辛基锡，在60℃下搅拌混合16分钟，加入双十二碳醇酯，搅拌至常温，加入除了粘结助剂以外的各原料，在30℃下保温静置2小时，加入粘结助剂，送入混炼机，加热升温至100℃，混炼30min；将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机，挤出产物经冷却、造粒，即得所述乙烯-醋酸乙烯热熔胶。
性能测试
软化点94℃；
剥离强度：92N/25mm。

Claims (2)

1.一种乙烯-醋酸乙烯热熔胶，其特征在于它是由下述重量份的原料制成的：乙烯-醋酸乙烯共聚物64-71、三萜皂苷1-2、磷酸钠0.1-0.3、甲苯基二苯基磷酸酯1-2、蓖麻油酸锌0.2-0.4、聚马来酸酐1-2、钼酸铵1-2、液体石蜡10-13、甘油聚氧乙烯醚椰油酸酯0.3-1、双巯基乙酸异辛酯二正辛基锡0.1-0.2、双十二碳醇酯2-3、粘结助剂7-10；所述的粘结助剂是由下述重量份的原料组成的：液体石蜡24-30、亚麻籽胶2-3、氟化石墨1-2、EVA树脂4-5、马来酸二丁酯3-4、油酸钾皂0.6-2、丙基三甲氧基硅烷0.2-0.5；将EVA树脂加热软化，加入马来酸二丁酯，搅拌均匀，加入丙基三甲氧基硅烷，在50-60℃下保温搅拌10-15分钟，加入到液体石蜡中，搅拌均匀，得粘结液；将亚麻籽胶与油酸钾皂混合，搅拌均匀后加入氟化石墨，球磨均匀，加入到上述粘结液中，60-80转/分搅拌分散3-4分钟，即得所述粘结助剂。
2.一种如权利要求1所述的乙烯-醋酸乙烯热熔胶的制备方法，其特征在于包括以下步骤：将钼酸铵、蓖麻油酸锌混合加入到液体石蜡中，搅拌均匀后加入三萜皂苷，100-120转/分搅拌混合5-10分钟，加入甲苯基二苯基磷酸酯、双巯基乙酸异辛酯二正辛基锡，在50-60℃下搅拌混合10-16分钟，加入双十二碳醇酯，搅拌至常温，加入除了粘结助剂以外的各原料，在25-30℃下保温静置1-2小时，加入粘结助剂，送入混炼机，加热升温至90-100℃，混炼20-30min；将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机，挤出产物经冷却、造粒，即得所述乙烯-醋酸乙烯热熔胶。
CN201410293067.9A 2014-06-26 2014-06-26 一种乙烯-醋酸乙烯热熔胶 Active CN104087201B (zh)