CN104087208B - 一种用于板材的高粘结热熔胶 - Google Patents

一种用于板材的高粘结热熔胶 Download PDF

Info

Publication number
CN104087208B
CN104087208B CN201410293113.5A CN201410293113A CN104087208B CN 104087208 B CN104087208 B CN 104087208B CN 201410293113 A CN201410293113 A CN 201410293113A CN 104087208 B CN104087208 B CN 104087208B
Authority
CN
China
Prior art keywords
add
pur
fluorographite
adhesive aid
sheet material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410293113.5A
Other languages
English (en)
Other versions
CN104087208A (zh
Inventor
李勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chuzhou City Guang Wei Chemical Co Ltd
Original Assignee
Chuzhou City Guang Wei Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chuzhou City Guang Wei Chemical Co Ltd filed Critical Chuzhou City Guang Wei Chemical Co Ltd
Priority to CN201410293113.5A priority Critical patent/CN104087208B/zh
Publication of CN104087208A publication Critical patent/CN104087208A/zh
Application granted granted Critical
Publication of CN104087208B publication Critical patent/CN104087208B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于板材的高粘结热熔胶，它是由下述重量份的原料组成的：乙烯-醋酸乙烯共聚物70-76、骨炭1-2、醋酸乙烯酯3-4、β-羟烷基酰胺1-2、烯丙基聚乙二醇1-2、抗氧剂168？0.6-1、1，2-苯并异噻唑啉-3-酮0.7-1、三硬脂酸甘油酯2-4、C5石油树脂10-13、聚乙烯0.3-0.5、氟化石墨2-3、双飞粉1-2、粘结助剂8-13；本发明制备的热熔胶中加入聚乙烯，可以降低熔融粘度，改善操作性能，提高抗剥离强度，本发明的原料来源丰富，降低了生产成本，加入的氟化石墨可以使得各组分间分散均匀，有利于提高热熔胶的稳定性。

Description

一种用于板材的高粘结热熔胶
技术领域
本发明主要涉及一种热熔胶粉末，尤其涉及一种用于板材的高粘结热熔胶。
背景技术
热熔胶是一种可塑性的粘合剂，在一定温度范围内其物理状态随温度改变而改变，而化学特性不变，其无毒无味，属环保型化学产品。
发明内容
本发明目的就是提供一种用于板材的高粘结热熔胶。
本发明是通过以下技术方案实现的：
一种用于板材的高粘结热熔胶，它是由下述重量份的原料组成的：
乙烯-醋酸乙烯共聚物70-76、骨炭1-2、醋酸乙烯酯3-4、β-羟烷基酰胺1-2、烯丙基聚乙二醇1-2、抗氧剂1680.6-1、1，2-苯并异噻唑啉-3-酮0.7-1、三硬脂酸甘油酯2-4、C5石油树脂10-13、聚乙烯0.3-0.5、氟化石墨2-3、双飞粉1-2、粘结助剂8-13；
所述的增粘结助剂是由下述重量份的原料组成的：
液体石蜡24-30、亚麻籽胶2-3、氟化石墨1-2、EVA树脂4-5、马来酸二丁酯3-4、油酸钾皂0.6-2、丙基三甲氧基硅烷0.2-0.5；
将EVA树脂加热软化，加入马来酸二丁酯，搅拌均匀，加入丙基三甲氧基硅烷，在50-60℃下保温搅拌10-15分钟，加入到液体石蜡中，搅拌均匀，得粘结液；
将亚麻籽胶与油酸钾皂混合，搅拌均匀后加入氟化石墨，球磨均匀，加入到上述粘结液中，60-80转/分搅拌分散3-4分钟，即得所述粘结助剂。
一种用于板材的高粘结热熔胶的制备方法，包括以下步骤：
将上述骨炭、氟化石墨、聚乙烯混合，球磨均匀后加入三硬脂酸甘油酯、烯丙基聚乙二醇，60-70℃下搅拌混合10-14分钟，加入除了粘结助剂以外的各原料，在25-30℃下保温静置1-2小时，加入粘结助剂，送入混炼机，加热升温至90-100℃，混炼20-30min；将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机，挤出产物经冷却、造粒，即得所述用于板材的高粘结热熔胶。
本发明的优点是：
本发明制备的热熔胶中加入聚乙烯，可以降低熔融粘度，改善操作性能，提高抗剥离强度，本发明的原料来源丰富，降低了生产成本，加入的氟化石墨可以使得各组分间分散均匀，有利于提高热熔胶的稳定性。
具体实施方式
实施例1
一种用于板材的高粘结热熔胶，它是由下述重量份（公斤）的原料组成的：
乙烯-醋酸乙烯共聚物76、骨炭2、醋酸乙烯酯4、β-羟烷基酰胺1、烯丙基聚乙二醇1、抗氧剂1680.6、1，2-苯并异噻唑啉-3-酮0.7、三硬脂酸甘油酯2、C5石油树脂13、聚乙烯0.5、氟化石墨2、双飞粉2、粘结助剂13；
所述的增粘结助剂是由下述重量份的原料组成的：
液体石蜡30、亚麻籽胶2、氟化石墨1、EVA树脂4、马来酸二丁酯3、油酸钾皂0.6、丙基三甲氧基硅烷0.5；
将EVA树脂加热软化，加入马来酸二丁酯，搅拌均匀，加入丙基三甲氧基硅烷，在50-60℃下保温搅拌15分钟，加入到液体石蜡中，搅拌均匀，得粘结液；
将亚麻籽胶与油酸钾皂混合，搅拌均匀后加入氟化石墨，球磨均匀，加入到上述粘结液中，80转/分搅拌分散4分钟，即得所述粘结助剂。
一种用于板材的高粘结热熔胶的制备方法，其特征在于包括以下步骤：
将上述骨炭、氟化石墨、聚乙烯混合，球磨均匀后加入三硬脂酸甘油酯、烯丙基聚乙二醇，70℃下搅拌混合14分钟，加入除了粘结助剂以外的各原料，在30℃下保温静置2小时，加入粘结助剂，送入混炼机，加热升温至90-100℃，混炼30min；将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机，挤出产物经冷却、造粒，即得所述用于板材的高粘结热熔胶。
性能测试
软化点91℃；
剥离强度：93N/25mm。

Claims (2)

1.一种用于板材的高粘结热熔胶，其特征在于它是由下述重量份的原料组成的：乙烯-醋酸乙烯共聚物70-76、骨炭1-2、醋酸乙烯酯3-4、β-羟烷基酰胺1-2、烯丙基聚乙二醇1-2、抗氧剂1680.6-1、1，2-苯并异噻唑啉-3-酮0.7-1、三硬脂酸甘油酯2-4、C5石油树脂10-13、聚乙烯0.3-0.5、氟化石墨2-3、双飞粉1-2、粘结助剂8-13；所述的粘结助剂是由下述重量份的原料组成的：液体石蜡24-30、亚麻籽胶2-3、氟化石墨1-2、EVA树脂4-5、马来酸二丁酯3-4、油酸钾皂0.6-2、丙基三甲氧基硅烷0.2-0.5；将EVA树脂加热软化，加入马来酸二丁酯，搅拌均匀，加入丙基三甲氧基硅烷，在50-60℃下保温搅拌10-15分钟，加入到液体石蜡中，搅拌均匀，得粘结液；将亚麻籽胶与油酸钾皂混合，搅拌均匀后加入氟化石墨，球磨均匀，加入到上述粘结液中，60-80转/分搅拌分散3-4分钟，即得所述粘结助剂。
2.一种如权利要求1所述的用于板材的高粘结热熔胶的制备方法，其特征在于包括以下步骤：将上述骨炭、氟化石墨、聚乙烯混合，球磨均匀后加入三硬脂酸甘油酯、烯丙基聚乙二醇，60-70℃下搅拌混合10-14分钟，加入除了粘结助剂以外的各原料，在25-30℃下保温静置1-2小时，加入粘结助剂，送入混炼机，加热升温至90-100℃，混炼20-30min；将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机，挤出产物经冷却、造粒，即得所述用于板材的高粘结热熔胶。
CN201410293113.5A 2014-06-26 2014-06-26 一种用于板材的高粘结热熔胶 Active CN104087208B (zh)