CN104559835A - 聚乙烯醇改性淀粉胶 - Google Patents
聚乙烯醇改性淀粉胶 Download PDFInfo
- Publication number
- CN104559835A CN104559835A CN201310493863.2A CN201310493863A CN104559835A CN 104559835 A CN104559835 A CN 104559835A CN 201310493863 A CN201310493863 A CN 201310493863A CN 104559835 A CN104559835 A CN 104559835A
- Authority
- CN
- China
- Prior art keywords
- adds
- percent
- solution
- polyvinyl alcohol
- polyethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚乙烯醇改性淀粉胶,按质量比包括以下组分:玉米淀粉10%~14%;氢氧化钠(30%溶液)4%~8%;双氧水(30%溶液)1.5%~3%;硼砂0.2%~0.8%;磷酸三丁酯0.05%~0.2%;脲醛树脂2%~6%;水加至100%。本发本发明在氧化法制胶的基础上,添加适量聚乙烯醇改性,从而达到提高淀粉胶的粘合性能的目的。
Description
技术领域
本发明涉及化工领域,尤其涉及一种聚乙烯醇改性淀粉胶的制造。
背景技术
淀粉是由葡萄糖单元以α-糖苷的形式,通过1,4结合而成的一种非还原性多羟基物质,分子式为C6H10O5,为无色无臭的白色粉末,淀粉及其水解物葡萄糖也是重要的工业原料,能生产醇、醛、酮、酸、酯及醚等有机化合物,其中许多为重要的化工原料。
淀粉资源丰富,价格便宜,使用方便,又可用其他材料进行改性。按职务品种的来源,淀粉可以分为玉米淀粉、土豆淀粉、木薯淀粉、地瓜淀粉、大米淀粉等,它们的形态、组成、颗粒大小、聚合度和糊化温度都有所不同。淀粉主要是由直链淀粉及支链淀粉两部分组成。直链淀粉是线型结构,在淀粉中含量约为10%~30%,能溶于水而不成糊状,遇碘呈蓝色。支链淀粉高度支化,在冷水中不溶,与热水作用泽膨胀而成糊状,遇碘呈紫红色。
目前,淀粉胶粘合剂多数采用氧化法制备,氧化法一般分为一步法及两步法。一步法是淀粉直接氧化、糊化、交联而成,两步法是先制成氧化淀粉,然后再加糊化剂与交联剂配成。这两种方法的原理,是先从结构上将淀粉链断裂,然后加入适量交联剂使其成为网状结构,以克服直链淀粉因氢键结合易于形成刚性胶冻的性能,尽管如此,单纯用氧化法制取的淀粉胶在快干及防冻上仍不是十分理想。为此,有的制备方法是采用添加催干剂、稳定剂的方法赖提高粘合性能。
发明内容
本发明实施例所要解决的技术问题在于,提供一种聚乙烯醇改性淀粉胶,按质量比包括以下组分:
玉米淀粉 13%~17%
氢氧化钠(30%溶液) 5%~8%
双氧水(30%溶液) 1.5%~3%
硼砂 0.2%~0.8%
尿素 0. 5%~2%
催干剂 1.2%~4.8%
水 加至100% 。
为了解决上述技术问题,本发明实施例提供了一种制备所述聚乙烯醇改性淀粉胶的工艺,包括以下步骤:
(a)在带搅拌器的反应釜中先加入总水量的1/5聚乙脲醛树脂和磷酸三丁酯;
(b)搅拌使水与淀粉完全混合均匀同时加热至80~95℃;
(c)使聚乙烯醇完全溶解后,冷却至60~70℃待用;
(d)继续搅拌的同时加入配方量为1/2的双氧水,反应30分钟;
(e)加入剩余氢氧化钠溶液,使淀粉糊化;
(f)加入预先溶解好的硼砂持续搅拌30分钟;
(g)加入催干剂充分搅匀制得成品。
实施本发明,具有如下有益效果:
本发明在氧化法制胶的基础上,添加适量聚乙烯醇改性,从而达到提高淀粉胶的粘合性能的目的。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚,下面将对本发明作进一步地详细描述。
实施例
玉米淀粉 15g
氢氧化钠(30%溶液) 6g
双氧水(30%溶液) 2g
硼砂 0.8g
尿素 1.1g
催干剂 3.1g
水 加至100% 。
在带搅拌器的反应釜中先加入水及玉米淀粉;
搅拌使水与淀粉完全混合均匀后加热至50~80℃;
加入适量氢氧化钠溶液,将溶液的PH值调节为9.5~10;
继续搅拌的同时加入配方量为1/2的双氧水,反应30分钟;
加入剩余氢氧化钠溶液,使淀粉糊化;
加入预先溶解好的硼砂及尿素持续搅拌30分钟;
加入催干剂充分搅匀制得成品。
以上所揭露的仅为本发明一种较佳实施例而已,当然不能以此来限定本发明之权利范围,因此依本发明权利要求所作的等同变化,仍属本发明所涵盖的范围。
Claims (2)
1.一种聚乙烯醇改性淀粉胶,其特征在于,按质量比包括以下组分:
玉米淀粉 10%~14%
氢氧化钠(30%溶液) 4%~8%
双氧水(30%溶液) 1.5%~3%
硼砂 0.2%~0.8%
磷酸三丁酯 0. 05%~0.2%
脲醛树脂 2%~6%
水 加至100% 。
2.一种制备权利要求1所述聚乙烯醇改性淀粉胶的工艺,其特征在于,包括以下步骤:
(a)在带搅拌器的反应釜中先加入总水量的1/5聚乙脲醛树脂和磷酸三丁酯;
(b)搅拌使水与淀粉完全混合均匀同时加热至80~95℃;
(c)使聚乙烯醇完全溶解后,冷却至60~70℃待用;
(d)继续搅拌的同时加入配方量为1/2的双氧水,反应30分钟;
(e)加入剩余氢氧化钠溶液,使淀粉糊化;
(f)加入预先溶解好的硼砂持续搅拌30分钟;
(g)加入催干剂充分搅匀制得成品。