CN104084521B - 一种铸造型砂用添加剂及其制备方法和使用方法 - Google Patents

一种铸造型砂用添加剂及其制备方法和使用方法 Download PDF

Info

Publication number
CN104084521B
CN104084521B CN201410261186.6A CN201410261186A CN104084521B CN 104084521 B CN104084521 B CN 104084521B CN 201410261186 A CN201410261186 A CN 201410261186A CN 104084521 B CN104084521 B CN 104084521B
Authority
CN
China
Prior art keywords
additive
sand
titanium dioxide
sodium
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410261186.6A
Other languages
English (en)
Other versions
CN104084521A (zh
Inventor
浦巧生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Shunjin Metal Casting Co ltd
Original Assignee
Wujiang Hydraulic Components Foundry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wujiang Hydraulic Components Foundry Co Ltd filed Critical Wujiang Hydraulic Components Foundry Co Ltd
Priority to CN201410261186.6A priority Critical patent/CN104084521B/zh
Publication of CN104084521A publication Critical patent/CN104084521A/zh
Application granted granted Critical
Publication of CN104084521B publication Critical patent/CN104084521B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种铸造型砂用添加剂及其制备方法和使用方法。添加剂由偏硅酸钠、二氧化钛、聚酰亚胺和六偏磷酸钠组成。制备方法为：将偏硅酸钠、聚酰亚胺和六偏磷酸钠分别粉碎，过120目筛；然后再与二氧化钛混合，球磨混合，烘干后破碎，过200目筛得到粉状添加剂。将添加剂与水按照重量比1：3‑5的比例混合，充分混合后，再加入到原砂中，混合即可得到铸造型砂。本发明配方合理，聚酰亚胺属于耐高温的有机高分子材料且无毒，二氧化钛属于热稳定性好的氧化物，六偏磷酸钠可以作为分散剂，各成分互相配合且绿色无污染。本发明的添加剂添加量小，普通硅砂添加本发明的添加剂后即可作为型砂使用，型砂耐高温性能好、易溃散、易清理。

Description

一种铸造型砂用添加剂及其制备方法和使用方法
技术领域
本发明涉及一种铸造型砂用添加剂及其制备方法和使用方法，属于铸造工业技术领域。
背景技术
型砂在铸造中用来造型的材料。型砂一般由铸造用原砂、型砂粘结剂和辅加物等造型材料按一定的比例混合而成。
申请号为201310034038.6《铸钢用水玻璃石英砂防粘砂添加剂及其使用方法》公开了一种水玻璃石英砂的添加剂，添加剂包括括 Al2O3、SiO2、Cr2O3和 Fe2O3。该发明解决了铸件表面不易粘砂的问题，但是添加剂加入之后的型砂溃散性差，旧砂再生困难。不利于重复利用。
发明内容
本发明的目的在于提供一种铸造型砂用添加剂及其制备方法和使用方法。
本发明是通过以下技术方案来实现的：
一种铸造型砂用添加剂，以重量份数计，由偏硅酸钠20-30份、二氧化钛15-25份、聚酰亚胺10-16份和六偏磷酸钠3-5份组成；其中，二氧化钛的粒度为120目。
其中，所述二氧化钛与六偏磷酸钠的重量比为5:1，所述偏硅酸钠是五水偏硅酸钠。
所述的一种铸造型砂用添加剂，以重量份数计，由偏硅酸钠26份、二氧化钛20份、聚酰亚胺15份和六偏磷酸钠4份组成。
所述的一种铸造型砂用添加剂的制备方法，将偏硅酸钠、聚酰亚胺和六偏磷酸钠分别粉碎，过120目筛；然后再与二氧化钛混合，球磨混合，60-80℃烘干后破碎，过200目筛得到粉状添加剂。
所述的一种铸造型砂用添加剂的使用方法，将添加剂与水按照重量比1：3-5的比例混合，充分混合后，再加入到原砂中，混合即可得到铸造型砂；其中，添加剂和水混合后的总重量为原砂重量的6-10%，原砂中硅砂的含量大于96%。
本发明所达到的有益效果：
本发明配方合理，聚酰亚胺属于耐高温的有机高分子材料且无毒，二氧化钛属于热稳定性好的氧化物，六偏磷酸钠可以作为分散剂，各成分互相配合且绿色无污染。本发明的添加剂添加量小，普通硅砂添加本发明的添加剂后即可作为型砂使用，得到的型砂耐高温性能好、易溃散、易清理，可重复使用。
具体实施方式
下面结合实施例对本发明作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例1
本实施例中，一种铸造型砂用添加剂，以重量份数计，由五水偏硅酸钠26份、二氧化钛20份、聚酰亚胺15份和六偏磷酸钠4份组成；其中，二氧化钛的粒度为120目。
所述的一种铸造型砂用添加剂的制备方法，将偏硅酸钠、聚酰亚胺和六偏磷酸钠分别粉碎，过120目筛；然后再与二氧化钛混合，球磨混合，60℃烘干后破碎，过200目筛得到粉状添加剂。
使用时，将添加剂与水按照重量比1：3的比例混合，充分混合后，再加入到原砂中，混合即可得到铸造型砂；其中，添加剂和水混合后的总重量为原砂重量的10%，原砂中硅砂的含量为98%。按照GB/T 2684-2009，测得型砂紧实率为38%，按照GB/T 2684-2009，测得型砂湿压强度0.1MPa。
实施例2
本实施例中，一种铸造型砂用添加剂，以重量份数计，由偏硅酸钠20份、二氧化钛25份、聚酰亚胺10份和六偏磷酸钠5份组成；其中，二氧化钛的粒度为120目。
所述的一种铸造型砂用添加剂的制备方法，将偏硅酸钠、聚酰亚胺和六偏磷酸钠分别粉碎，过120目筛；然后再与二氧化钛混合，球磨混合，80℃烘干后破碎，过200目筛得到粉状添加剂。
使用时，将添加剂与水按照重量比1：5的比例混合，充分混合后，再加入到原砂中，混合即可得到铸造型砂；其中，添加剂和水混合后的总重量为原砂重量的10%，原砂中硅砂的含量为96%。按照GB/T 2684-2009，测得型砂紧实率为40%，按照GB/T 2684-2009，测得型砂湿压强度0.15MPa。
实施例3
本实施例中，一种铸造型砂用添加剂，以重量份数计，由偏硅酸钠30份、二氧化钛15份、聚酰亚胺16份和六偏磷酸钠3份组成；其中，二氧化钛的粒度为120目。
所述的一种铸造型砂用添加剂的制备方法，将偏硅酸钠、聚酰亚胺和六偏磷酸钠分别粉碎，过120目筛；然后再与二氧化钛混合，球磨混合，80℃烘干后破碎，过200目筛得到粉状添加剂。
使用时，将添加剂与水按照重量比1：4的比例混合，充分混合后，再加入到原砂中，混合即可得到铸造型砂；其中，添加剂和水混合后的总重量为原砂重量的6%，原砂中硅砂的含量为99%。按照GB/T 2684-2009，测得型砂紧实率为43%，按照GB/T 2684-2009，测得型砂湿压强度0.12MPa。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变形，这些改进和变形也应视为本发明的保护范围。

Claims (5)

1.一种铸造型砂用添加剂，其特征是，以重量份数计，由偏硅酸钠 20-30 份、二氧化钛15-25 份、聚酰亚胺 10-16 份和六偏磷酸钠 3-5 份组成 ；其中，二氧化钛的粒度为 120目；所述添加剂的使用方法是，将添加剂与水按照重量比 1 ：3-5 的比例混合，充分混合后，再加入到原砂中，混合即可得到铸造型砂 ；其中，添加剂和水混合后的总重量为原砂重量的 6-10%，原砂中硅砂的含量大于 96%。
2.根据权利要求 1 所述的一种铸造型砂用添加剂，其特征是，所述二氧化钛与六偏磷酸钠的重量比为 5 ：1。
3.根据权利要求 1 所述的一种铸造型砂用添加剂，其特征是，所述偏硅酸钠是五水偏硅酸钠。
4.根据权利要求 1 所述的一种铸造型砂用添加剂，其特征是，以重量份数计，由偏硅酸钠 26 份、二氧化钛 20 份、聚酰亚胺 15 份和六偏磷酸钠 4 份组成。
5.根据权利要求 1 所述的一种铸造型砂用添加剂的制备方法，其特征是，将偏硅酸钠、聚酰亚胺和六偏磷酸钠分别粉碎，过 120 目筛 ；然后再与二氧化钛混合，球磨混合，60-80℃烘干后破碎，过 200 目筛得到粉状添加剂。
CN201410261186.6A 2014-06-13 2014-06-13 一种铸造型砂用添加剂及其制备方法和使用方法 Expired - Fee Related CN104084521B (zh)