CN104003659A - 掺杂玻璃碴的空心砖 - Google Patents
掺杂玻璃碴的空心砖 Download PDFInfo
- Publication number
- CN104003659A CN104003659A CN201410206421.XA CN201410206421A CN104003659A CN 104003659 A CN104003659 A CN 104003659A CN 201410206421 A CN201410206421 A CN 201410206421A CN 104003659 A CN104003659 A CN 104003659A
- Authority
- CN
- China
- Prior art keywords
- hollow brick
- parts
- glass
- ageing
- crusher
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种掺杂玻璃碴的空心砖，有以下重量份的原料组成，玻璃碴42份、水泥22份、膨润土11份、凹凸棒土5份、改性高炉渣渣砂4、稻壳11、纤维素醚2份，减水剂3.5份，本发明以废弃物为原料制成的空心砖，旨在解决现有空心砖由水泥及粘土制成消耗资源大、成本高的问题。
Description
技术领域
本发明涉及空心砖技术领域，具体涉及一种掺杂玻璃碴的空心砖。
背景技术
空心砖是近年内建筑行业常用的墙体主材，由于质轻、消耗原材少等优势，已经成为国家建筑部门首先推荐的产品。空心砖和实心砖相比，可节省大量的土地用土和烧砖燃料，减轻运输重量；减轻制砖和砌筑时的劳动强度，加快施工进度；减轻建筑物自重，加高建筑层数，降低造价；同时空心砖具有质轻、强度高、保温、隔音降噪性能好以及环保、无污染的特点，因而成为框架结构建筑物的理想填充材料。
空心砖一般是由粘土和水泥制成，通过制砖机压制出来后的成型空心砖，需要经过一段的时间的养护后即可作为建筑材料使用。随着建筑业的发展，对空心砖的需求越来越大，由于制造空心砖会消耗大量的资源，如粘土和水泥，成本高，不符合资源节约的原则，日益不能适应社会的需求。
发明内容
本发明的目的是提供一种掺杂玻璃碴的空心砖，提供一种以废弃物为原料制成的空心砖，旨在解决现有空心砖由水泥及粘土制成消耗资源大、成本高的问题。
本发明的技术方案如下：
掺杂玻璃碴的空心砖，有以下重量份的原料组成，玻璃碴40-45份、水泥20-25份、膨润土10-12份、凹凸棒土4-6份、改性高炉渣渣砂3-5、稻壳10-12、纤维素醚1.5-2.5份，减水剂3-4份，其具体制备步骤如下：
(1)分别采用细碎颚式破碎机、锤式破碎机、细碎对辊机对玻璃碴、改性高炉渣渣砂、稻壳的混合物进行破碎处理，得到轻骨料，细碎颚式破碎机初破后粒度为20mm-25mm，锤式破碎机破碎后粒径应小于4mm，通过细碎对辊机后粒度应小于2mm；
(2)将步骤(1)得到的轻骨料、剩余原料以及适量的水均匀混合，在150-200r/min转速下搅拌1-2小时，均匀成混合泥料；
(3)将步骤(2)得到的混合料输入陈化库，先将室内温度保持14-16℃、室内相对空气湿度80-85％，陈化21-25h，最后将室内温度保持22-25℃、室内相对空气湿度90-95％，陈化40-50h；
(4)经过陈化、干燥、烧制得到空心砖成品。
本发明通过由玻璃碴及稻壳等原料制作空心砖，不但解决了建筑行业对空心砖的大量需求的问题，降低了空心砖的制作成本，减少了水泥的使用量，而且使得废弃物料得以回收利用，减少了环境污染，具有重要的生产实践意义。
具体实施方式
掺杂玻璃碴的空心砖，有以下重量份的原料组成，玻璃碴42份、水泥22份、膨润土11份、凹凸棒土5份、改性高炉渣渣砂4、稻壳11、纤维素醚2份，减水剂3.5份，其具体制备步骤如下：
(1)分别采用细碎颚式破碎机、锤式破碎机、细碎对辊机对玻璃碴、改性高炉渣渣砂、稻壳的混合物进行破碎处理，得到轻骨料，细碎颚式破碎机初破后粒度为20mm-25mm，锤式破碎机破碎后粒径应小于4mm，通过细碎对辊机后粒度应小于2mm；
(2)将步骤(1)得到的轻骨料、剩余原料以及适量的水均匀混合，在150-200r/min转速下搅拌1-2小时，均匀成混合泥料；
(3)将步骤(2)得到的混合料输入陈化库，先将室内温度保持14-16℃、室内相对空气湿度80-85％，陈化21-25h，最后将室内温度保持22-25℃、室内相对空气湿度90-95％，陈化40-50h；
(4)经过陈化、干燥、烧制得到空心砖成品。
Claims (1)
1.掺杂玻璃碴的空心砖，其特征在于，有以下重量份的原料组成，玻璃碴40-45份、水泥20-25份、膨润土10-12份、凹凸棒土4-6份、改性高炉渣渣砂3-5、稻壳10-12、纤维素醚1.5-2.5份，减水剂3-4份，其具体制备步骤如下：
(1)分别采用细碎颚式破碎机、锤式破碎机、细碎对辊机对玻璃碴、改性高炉渣渣砂、稻壳的混合物进行破碎处理，得到轻骨料，细碎颚式破碎机初破后粒度为20mm-25mm，锤式破碎机破碎后粒径应小于4mm，通过细碎对辊机后粒度应小于2mm；
(2)将步骤(1)得到的轻骨料、剩余原料以及适量的水均匀混合，在150-200r/min转速下搅拌1-2小时，均匀成混合泥料；
(3)将步骤(2)得到的混合料输入陈化库，先将室内温度保持14-16℃、室内相对空气湿度80-85％，陈化21-25h，最后将室内温度保持22-25℃、室内相对空气湿度90-95％，陈化40-50h；
(4)经过陈化、干燥、烧制得到空心砖成品。