CN102875066B - 一种铬渣加气砖及其制备方法 - Google Patents

一种铬渣加气砖及其制备方法 Download PDF

Info

Publication number
CN102875066B
CN102875066B CN201210304872.8A CN201210304872A CN102875066B CN 102875066 B CN102875066 B CN 102875066B CN 201210304872 A CN201210304872 A CN 201210304872A CN 102875066 B CN102875066 B CN 102875066B
Authority
CN
China
Prior art keywords
weight
weight parts
slag
powder
brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210304872.8A
Other languages
English (en)
Other versions
CN102875066A (zh
Inventor
晋元龙
陈德全
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ma'an Mountain Bao Long Building Material Co Ltd
Original Assignee
Ma'an Mountain Bao Long Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ma'an Mountain Bao Long Building Material Co Ltd filed Critical Ma'an Mountain Bao Long Building Material Co Ltd
Priority to CN201210304872.8A priority Critical patent/CN102875066B/zh
Publication of CN102875066A publication Critical patent/CN102875066A/zh
Application granted granted Critical
Publication of CN102875066B publication Critical patent/CN102875066B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种铬渣加气砖,其由下列重量份的原材料加工制成:铬渣20-30、粉煤灰25-30、水泥5-10、改性凹凸棒土4-6、碳酸钡渣5-10、陶瓷厂废料5-10、轻钙粉5-10、石灰10-15、三乙醇胺石灰重量的0.1-0.3%、石膏4-5、铝粉0.02-0.08、氧化石蜡皂 加量为铝粉重量的3-5%、碳酸氢钙0.01-0.02、火山岩2-3、木质纤维素1-2、水玻璃0.3-0.5、硼砂0.03-0.05、六偏磷酸钠1-2、羟丙基甲基纤维素钠1-2、超细聚乙烯醇1-2。本发明将铬渣添加到加气砖的原材料中,同时添加其他常规助剂和改性纳米助剂,采用合适的工艺加工出的加气砖,具有成本低,性能好,实现了变废为宝的循环经济效果,减少了污染,加工出的加气砖具有容重轻、保温性能高、吸音效果好,强度高的特点,可以作为非承重墙体或称重墙体使用。

Description

一种铬渣加气砖及其制备方法
技术领域
[0001] 本发明涉及建筑材料领域,具体涉及一种铬渣加气砖及其制备方法。
背景技术
[0002] 加气混凝土砌块以水泥、矿渣、砂、石灰等为主要原料,加入发气剂,经搅拌成型、蒸压养护而成的实心砌块,加气混凝土按用途,可分为非承重砌块、承重砌块、保温块、墙板与屋面板五种。
[0003] 加气砖具有容重轻、保温性能高、吸音效果好,具有一定的强度和可加工性等优点,是我国推广应用最早,使用最广泛的轻质墙体材料之一。
[0004] 在全世界能源和自然资源保护日益重要的背景下,随着产业政策的调整和环境保护意识的提高,其他工业废弃物的利用也呈现上升趋势,大多数国家对工业废弃物在施工过程中具有的经济、环境和技术方面的优势表现出积极的兴趣,许多工业废弃物被证明可以被循环利用,成为发展循环经济和可持续发展的动力。
[0005] 人类社会工业及经济的发展和人类生活水平的提高及其多样化的结果,则形成了大生产化、高消耗化和多废弃化的社会体系。特别是大量的城市垃圾,不得不采用焚烧减容无害化和填埋处理。但是占用土地及环境污染仍是最大的社会问题。解决这个日益深刻化问题的最有力的对策是推行垃圾及工业废弃物再资源化。
[0006] 将各种工业废弃物或城市建设废弃物作为原材料添加到加气砖的的生产中,起到节省天然资源,利废环保等效果,成为发展循环经济和可持续发展的动力。
[0007] 本发明将铬渣作为原材料添加到加气砖中实现了废物的循环利用,减少了对环境的污染,符合可持续发展战略要求。
发明内容
[0008] 本发明提供了一种铬渣加气砖及其加工方法,本发明的加气砖具有容重轻、保温性能高、吸音效果好,强度高的特点,可以作为非承重墙体或称重墙体使用。
[0009] 本发明的技术方案如下:
[0010] 一种铬渣加气砖的制备方法,其特征在于,包括以下步骤:
[0011] (I)对凹凸棒土进行改性处理:先用15-20%盐酸浸泡凹凸棒土 1-2小时,静置,澄清,离心,固体用水洗至中性,烘干后,加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀,烘干,研磨成纳米粉末;
[0012] (2)将配方比例的铬渣和碳酸钡渣混合加水35-45%,在球磨机内湿磨,得到铬钡渣混合浆料;
[0013] (3)按配方比例称取其余的原材料,将块状物料投入球磨机中磨粉,粉料过180-200 目筛;
[0014] (4)将磨好的粉料、助剂、铬钡渣混合浆料混合到一起,投入搅拌机里,再加入适量的水搅拌成浆料;[0015] (5)将搅拌好的混合浆料注入模具;
[0016] (6)然后放入静养室在50_60°C密封保温,静养时间1.5-2小时,得到静养好的还体;(7)将静养好的坯体放到切割机上加工成砖块;(8)将砖块放入到高压蒸压釜中进行蒸压养护6-8小时,蒸养温度为180-195°C,蒸养压力10-11兆帕;
[0017] (9)对蒸压釜中的砖块进行撤压、降温、出爸,得到产品,
[0018] 其中,其各原材料按下列重量份的进行配制:
[0019] 铬渣20-30、粉煤灰25-30、水泥5-10、改性纳米凹凸棒土 4-6、碳酸钡渣5-10、陶瓷厂废料5_10、轻钙粉5_10、石灰10-15、二乙醇胺石灰重量的0.1-0.3%、石骨1-3、招粉0.02-0.08、氧化石蜡皂加量为铝粉重量的3-5%、碳酸氢钙0.01-0.02、火山岩2_3、木质纤维素1-2、水玻璃0.3-0.5、六偏磷酸钠1-2、羟丙基甲基纤维素钠1-2、超细聚乙烯醇1_2、硼砂 0.03-0.05,
[0020] 所述的一种铬渣加气砖的制备方法,其特征在于,其由下列重量份的原材料加工制成:
[0021] 铬渣25、水泥56、改性凹凸棒土 5、碳酸钡渣8、陶瓷厂废料6、轻钙粉12、石灰14、三乙醇胺加量为石灰重量的0.1-0.3%、石骨2、招粉0.05、氧化石腊阜加量为招粉重量的4%、碳酸氢钙0.01、火山岩3、木质纤维素1.5、水玻璃0.4、六偏磷酸钠1、轻丙基甲基纤维素钠2、硼砂0.04、超细聚乙烯醇I。
[0022] 本发明的有益效果:
[0023] 本发明通过采用铬渣作为加气砖的成分,有效的减少了环境污染,变废为宝,保护了环境;本发明通过添加纳米粉末矿粉,减轻了砖的容重,同时,减少了能源消耗;本发明砖隔热与隔音性能均好,较现有加气砖有明显提高。同时本发明通过优化配方用料,本发明的强度、抗冻性有了明显提高。所制得的加气砖既可以作为非承重墙体使用,也可以作承重墙体使用。
具体实施方式
[0024] 实施例1
[0025] 称取下列重量份的原材料:铬渣20-30、粉煤灰25-30、水泥5-10、改性纳米凹凸棒土 4-6、碳酸钡渣5-10、陶瓷厂废料5-10、轻钙粉5-10、石灰10-15、三乙醇胺石灰重量的0.1-0.3%、石骨1-3、招粉0.02-0.08、氧化石腊阜加量为招粉重量的3_5%、碳酸氢钙0.01-0.02、火山岩2-3、木质纤维素1-2、水玻璃0.3-0.5、六偏磷酸钠1_2、硼砂
0.03-0.05、羟丙基甲基纤维素钠1-2、超细聚乙烯醇1-2,
[0026] 其中,对凹凸棒土进行改性处理:先用15-20%盐酸浸泡凹凸棒土 1-2小时,静置,澄清,离心,固体用水洗 至中性,烘干后,加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀,烘干,研磨成纳米粉末,
[0027] 将称量好的上述物质按下列方法加工成加气砖成品,具体步骤:
[0028] (1)对凹凸棒土进行改性处理:先用15-20%盐酸浸泡凹凸棒土 1-2小时,静置,澄清,离心,固体用水洗至中性,烘干后,加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀,烘干,研磨成纳米粉末;
[0029] (2)将配方比例的铬渣和碳酸钡渣混合加水35-45%,在球磨机内湿磨,得到铬钡渣混合浆料;
[0030] (3)按配方比例称取其余的原材料,将块状物料投入球磨机中磨粉,粉料过180-200 目筛;
[0031] (3)将磨好的粉料、助剂、铬钡渣混合浆料混合到一起,投入搅拌机里,再加入适量的水搅拌成浆料;
[0032] (4)将搅拌好的混合浆料注入模具;
[0033] (5)然后放入静养室在50_60°C密封保温 ,静养时间1.5-2小时,得到静养好的还体;(6)将静养好的坯体放到切割机上加工成砖块;(7)将砖块放入到高压蒸压釜中进行蒸压养护6-8小时,蒸养温度为180-195°C,蒸养压力10-11兆帕;
[0034] (8)对蒸压釜中的砖块进行撤压、降温、出釜,得到产品。
[0035] 实施例2
[0036] 称取下列重量份的原材料:铬渣25、水泥56、改性纳米凹凸棒土 5、碳酸钡渣8、陶瓷厂废料6、轻钙粉12、石灰14、三乙醇胺石灰重量的0.1-0.3%、石膏2、铝粉0.05、氧化石蜡皂加量为铝粉重量的4%、碳酸氢钙0.01、火山岩3、木质纤维素1.5、水玻璃0.4、六偏磷酸钠1、硼砂0.04、羟丙基甲基纤维素钠2、超细聚乙烯醇1,其中,改性凹凸棒土由下列方法制得:先用15 %盐酸浸泡海泡石1-2小时,静置,澄清,离心,固体用水洗至中性,烘干后,加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀,烘干,粉碎成粉末,
[0037] 将称量好的上述物质按下列方法加工成加气砖成品,具体步骤:
[0038] (I)对凹凸棒土进行改性处理:先用15-20%盐酸浸泡凹凸棒土 1-2小时,静置,澄清,离心,固体用水洗至中性,烘干后,加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀,烘干,研磨成纳米粉末;
[0039] (2)将配方比例的铬渣和碳酸钡渣混合加水35-45%,在球磨机内湿磨,得到铬钡渣混合浆料;
[0040] (3)按配方比例称取其余的原材料,将块状物料投入球磨机中磨粉,粉料过180-200 目筛;
[0041] (3)将磨好的粉料、助剂、铬钡渣混合浆料混合到一起,投入搅拌机里,再加入适量的水搅拌成浆料;
[0042] (4)将搅拌好的混合浆料注入模具;
[0043] (5)然后放入静养室在50_60°C密封保温,静养时间1.5-2小时,得到静养好的还体;(6)将静养好的坯体放到切割机上加工成砖块;(7)将砖块放入到高压蒸压釜中进行蒸压养护6-8小时,蒸养温度为180-195°C,蒸养压力10-11兆帕;
[0044] (8)对蒸压釜中的砖块进行撤压、降温、出釜,得到产品。
[0045] 对实施例2的加气砖的性能检测结果见下表:
[0046]
Figure CN102875066BD00061

Claims (1)

1.一种铬渣加气砖的制备方法,其特征在于,包括以下步骤: (1)对凹凸棒土进行改性处理:先用15-20%盐酸浸泡凹凸棒土 1-2小时,静置,澄清,离心,固体用水洗至中性,烘干后,加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀,烘干,研磨成纳米粉末; (2)将配方比例的铬渣和碳酸钡渣混合加水35-45%,在球磨机内湿磨,得到铬钡渣混合浆料; (3)按配方比例称取其余的原材料,将块状物料投入球磨机中磨粉,粉料过180-200目筛; (4)将磨好的粉料、助剂、铬钡渣混合浆料混合到一起,投入搅拌机里,再加入适量的水搅拌成浆料; (5)将搅拌好的混合浆料注入模具; (6)然后放入静养室在50-60°C密封保温,静养时间1.5-2小时,得到静养好的还体;(7)将静养好的坯体放到切割机上加工成砖块;(8)将砖块放入到高压蒸压釜中进行蒸压养护6-8小时,蒸养温度为180-195°C,蒸养压力10-11兆帕; (9)对蒸压釜中的砖块进行撤压、降温、出釜,得到产品, 其中,其各原材 料按下列重量份的进行配制: 铬渣20-30、粉煤灰25-30、水泥5-10、改性纳米凹凸棒土 4_6、碳酸钡渣5_10、陶瓷厂废料5-10、轻钙粉5-10、石灰10-15、三乙醇胺石灰重量的0.1-0.3%、石膏1_3、铝粉.0.02-0.08、氧化石蜡皂加量为铝粉重量的3-5%、碳酸氢钙0.01-0.02、火山岩2_3、木质纤维素1-2、水玻璃0.3-0.5、六偏磷酸钠1-2、羟丙基甲基纤维素钠1-2、超细聚乙烯醇1_2、硼砂 0.03-0.05。
CN201210304872.8A 2012-08-25 2012-08-25 一种铬渣加气砖及其制备方法 Active CN102875066B (zh)