CN103980448A - 一种三聚氰胺树脂改性剂 - Google Patents
一种三聚氰胺树脂改性剂 Download PDFInfo
- Publication number
- CN103980448A CN103980448A CN201410237065.8A CN201410237065A CN103980448A CN 103980448 A CN103980448 A CN 103980448A CN 201410237065 A CN201410237065 A CN 201410237065A CN 103980448 A CN103980448 A CN 103980448A
- Authority
- CN
- China
- Prior art keywords
- melamine resin
- correcting agent
- properties
- polyoxyethylene
- diethanolamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种高定性和韧性的三聚氰胺树脂改性剂。由下述质量百分比组分制成：脂肪酸酰胺30%-50%；聚乙二醇 20%-40%；烷基酚聚氧乙烯醚10%-20%；水10-30%。按所述配方将各组分置于一个适当的容器中，缓慢加热升温至50-80℃，搅拌均匀，待全溶解后冷却至室温，即得到三聚氰胺树脂的改性剂。本发明能有效延长三聚氰胺甲醛树脂的聚合时间，增加其存储周期，改善树脂的韧性。
Description
技术领域
本发明涉及三聚氰胺树脂的改性剂及制备方法，可用于优化三聚氰胺树脂的使用效果，尤其用于三聚氰胺浸渍纸的制备。
背景技术
三聚氰胺甲醛树脂是一种热固性树脂，能形成耐水、耐热、耐磨、耐污染腐蚀、富有光泽的树脂保护膜，被广泛应用于家具行业多用于三聚氰胺浸渍纸的制备。目前，国内三聚氰胺浸渍纸质量参差不齐，主要是因为三聚氰胺树脂改性剂的使用水平差别很大，导致三聚氰胺甲醛树脂固化后表面易脆裂、储存稳定性差。常用的改性剂有二甘醇、氨基葡萄糖、己内酰胺等。随着社会的发展，三聚氰胺甲醛树脂浸渍纸市场需求越来越大，要求也越来越高，因此需要研究出一种高定性和韧性的三聚氰胺甲醛树脂改性剂来满足市场的需求。
发明内容
本发明目的是提供一种高韧性的三聚氰胺树脂改性剂。
采用的技术方案如下：
一种三聚氰胺树脂改性剂，其特征在于，它是由下述质量百分比组分制成：
脂肪酸酰胺 30%-50%；
聚乙二醇 20%-40%；
烷基酚聚氧乙烯醚 10%-20%；
水 10-30%。
所述的脂肪酸酰胺为油酰二乙醇胺、亚油酰二乙醇胺、硬脂酰二乙醇胺或者椰油酰二乙醇胺中的一种或者几种组合。
所述的聚乙二醇分子量200-2000之间。
所述的烷基酚聚氧乙烯醚为壬基酚聚氧乙烯醚（n为4、5、6、7或8）、辛基酚聚氧乙烯醚（n为4、5、6、7或8）或十二烷基酚聚氧乙烯醚（n为4、5、6、7或8）中的一种或者几种组合。
本发明还提供一种三聚氰胺树脂的改性剂制备方法，其特征在于包括以下步骤：按所述配方将各组分置于一个适当的容器中，缓慢加热升温至50-80℃，搅拌均匀，待全溶解后冷却至室温，即得到三聚氰胺树脂的改性剂。
本发明有益效果：
本发明能有效延长三聚氰胺甲醛树脂的聚合时间，增加其存储周期，改善树脂的韧性。脂肪酸酰胺、聚乙二醇 、烷基酚聚氧乙烯醚中都含有1个或者多个活泼反应基团，能参与树脂的共缩聚反应改变树脂结构，使交联密度下降，降低浸渍纸脆性，改善装饰层质量，使其富有弹性，增加其稳定性。
具体实施方式
下面结合实施例对发明进一步说明。
实施例1：
油酰二乙醇胺3公斤，聚乙二醇-400 2公斤，壬基酚聚氧乙烯醚（n=4）1公斤，水2公斤，放置于容器中，搅拌均匀，即得到三聚氰胺树脂的改性剂。
实施例2
选取亚油酰二乙醇胺4公斤，聚乙二醇-400 3公斤，辛基酚聚氧乙烯醚（n为5）1.5公斤，水2.5公斤，将各组分置于一个适当的容器中，缓慢加热升温至60℃，搅拌均匀，待全溶解后冷却至室温，即得到三聚氰胺树脂的改性剂。
实施例3
选取硬脂酰二乙醇胺5公斤，聚乙二醇-800 4公斤，十二烷基酚聚氧乙烯醚（n为6）2公斤，水3公斤，将各组分置于一个适当的容器中，缓慢加热升温至80℃，搅拌均匀，待全溶解后冷却至室温，即得到三聚氰胺树脂的改性剂。
实施例4
油酰二乙醇胺2公斤，硬脂酰二乙醇胺1公斤，椰油酰二乙醇胺2公斤，聚乙二醇-400 4公斤，壬基酚聚氧乙烯醚（n=4）1公斤，十二烷基酚聚氧乙烯醚（n=4）1公斤，水3公斤，放置于容器中，搅拌均匀，缓慢加热升温至70℃即得到三聚氰胺树脂的改性剂。
实施例5
三聚氰胺甲醛树脂参照GB/T14732-2006《木材工业胶黏剂用脲醛、酚醛、三聚氰胺甲醛树脂》进行制备，反应结束后添加2%的该类改性剂。
添加该类改性剂后的，三聚氰胺甲醛树脂性能如下：
缩聚时间由原来60分钟延长至155分钟，存储期由原来的4天延长至20天，添加改性剂后饰面刨花板均未发生龟裂现象。
由以上可见，使用该类活性剂，显著提高三聚氰胺甲醛树脂的稳定性和韧性。
上述讨论和实施案例仅供说明本发明具体实施方案，绝非限制其实际范围。本发明的保护范围以权利要求保护范围为准。
Claims (5)
1.一种三聚氰胺树脂改性剂，其特征在于：它是由下述质量百分比组分制成：
脂肪酸酰胺 30%-50%；
聚乙二醇 20%-40%；
烷基酚聚氧乙烯醚 10%-20%；
水 10-30%。
2.根据权利要求1所述的三聚氰胺树脂改性剂，其特征在于：所述的脂肪酸酰胺为油酰二乙醇胺、亚油酰二乙醇胺、硬脂酰二乙醇胺或者椰油酰二乙醇胺中的一种或者几种组合。
3.根据权利要求1所述的三聚氰胺树脂改性剂，其特征在于：所述的聚乙二醇分子量200-2000之间。
4.根据权利要求1所述的三聚氰胺树脂改性剂，其特征在于：所述的烷基酚聚氧乙烯醚为壬基酚聚氧乙烯醚（n为4、5、6、7或者8）、辛基酚聚氧乙烯醚（n为4、5、6、7或者8）或者十二烷基酚聚氧乙烯醚（n为4、5、6、7或者8）中的一种或者几种组合。
5.制备权利要求1-4任一所述三聚氰胺树脂改性剂的制备方法，其特征在于：包括以下步骤，按所述配比将各组分分置于适当的容器中，缓慢加热升温至50-80℃，搅拌均匀，待全溶解后冷却至室温，即得到三聚氰胺树脂的改性剂。