CN104277192A - 一种高柔韧性的改性三聚氰胺甲醛树脂 - Google Patents

一种高柔韧性的改性三聚氰胺甲醛树脂 Download PDF

Info

Publication number
CN104277192A
CN104277192A CN201410611034.4A CN201410611034A CN104277192A CN 104277192 A CN104277192 A CN 104277192A CN 201410611034 A CN201410611034 A CN 201410611034A CN 104277192 A CN104277192 A CN 104277192A
Authority
CN
China
Prior art keywords
parts
formaldehyde resin
modified melamine
resin
melamine formaldehyde
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410611034.4A
Other languages
English (en)
Inventor
黄帅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHONGZHOU HERUI TECHNOLOGY Co Ltd
Original Assignee
CHONGZHOU HERUI TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHONGZHOU HERUI TECHNOLOGY Co Ltd filed Critical CHONGZHOU HERUI TECHNOLOGY Co Ltd
Priority to CN201410611034.4A priority Critical patent/CN104277192A/zh
Publication of CN104277192A publication Critical patent/CN104277192A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种高柔韧性的改性三聚氰胺甲醛树脂，由下述按重量份计的原料制成：三聚氰胺：100份；甲醛：160~220份；异氰脲酸酯：10~20份；脂肪酸酰胺：5~10份；聚乙二醇：5~8份；烷基酚聚氧乙烯醚：3~6份；氢氧化钠：2~5份；酒精：40~60份；水：20~30份。本发明能有效延长改性三聚氰胺甲醛树脂的聚合时间，增加其存储周期，改善树脂的韧性。本发明所含树脂改性成分，能参与树脂的共缩聚反应改变树脂结构，使交联密度下降，从而使泡沫强度增加，增加韧性和降低脆性，使其富有弹性，增加其稳定性。

Description

一种高柔韧性的改性三聚氰胺甲醛树脂
技术领域
本发明涉及三聚氰胺树脂生产领域，尤其是一种高柔韧性的改性三聚氰胺甲醛树脂。
背景技术
三聚氰胺甲醛树脂是一种热固性树脂，能形成耐水、耐热、耐磨、耐污染腐蚀、富有光泽的树脂保护膜，被广泛应用于家具行业多用于三聚氰胺浸渍纸的制备。三聚氰胺树脂由于其独特的三嗪环结构以及羟甲基化合物较强的反应活性，从而导致其存在一些不足，如柔韧性较差。因此根据不同的要求，为改善三聚氰胺树脂固有的性能缺陷，往往通过将树脂进行改性的手段来实现。
发明内容
本发明目的是提供一种高柔韧性的改性三聚氰胺甲醛树脂。
采用的技术方案如下：
一种高柔韧性的改性三聚氰胺甲醛树脂，其特征在于，它是由下述按重量份计的原料制成：
三聚氰胺：100份；
甲醛：160~220份；
异氰脲酸酯：10~20份；
脂肪酸酰胺：5~10份；
聚乙二醇：5~8份；
烷基酚聚氧乙烯醚：3~6份；
氢氧化钠：2~5份；
酒精：40~60份；
水：20~30份。
所述的脂肪酸酰胺为油酰二乙醇胺、亚油酰二乙醇胺、硬脂酰二乙醇胺或者椰油酰二乙醇胺中的一种或者几种组合。
所述的聚乙二醇分子量200-2000之间。
所述的烷基酚聚氧乙烯醚为壬基酚聚氧乙烯醚（n为4、5、6、7或8）、辛基酚聚氧乙烯醚（n为4、5、6、7或8）或十二烷基酚聚氧乙烯醚（n为4、5、6、7或8）中的一种或者几种组合。
本发明还提供一种高柔韧性的改性三聚氰胺甲醛树脂制备方法，其特征在于包括以下步骤：依次将三聚氰胺、甲醛、氢氧化钠、酒精和水混合，加热到70~80℃搅拌10~20min后，加入异氰脲酸酯，继续搅拌1~2h后，加入脂肪酸酰胺、聚乙二醇、烷基酚聚氧乙烯醚，控制温度为50~80℃，搅拌均匀，待全溶解后冷却至室温，即得到改性三聚氰胺甲醛树脂。 
本发明有益效果：
本发明能有效延长改性三聚氰胺甲醛树脂的聚合时间，增加其存储周期，改善树脂的韧性。异氰脲酸酯、脂肪酸酰胺、聚乙二醇、烷基酚聚氧乙烯醚中都含有1个或者多个活泼反应基团，能参与树脂的共缩聚反应改变树脂结构，使交联密度下降，从而使泡沫强度增加，增加韧性和降低脆性，使其富有弹性，增加其稳定性。
具体实施方式
下面结合实施例对发明进一步说明。
实施例1：
总计共100公斤的原料，它是由下述按重量份计的原料制成：
三聚氰胺：100份；
甲醛：180份；
异氰脲酸酯：12份；
油酰二乙醇胺：6份；
聚乙二醇：6份；
壬基酚聚氧乙烯醚（n=4）：4份；
氢氧化钠：3份；
酒精：45份；
水：25份。
依次将三聚氰胺、甲醛、氢氧化钠、酒精和水混合，加热到80℃搅拌10min后，加入异氰脲酸酯，继续搅拌1后，加入油酰二乙醇胺、聚乙二醇、壬基酚聚氧乙烯醚（n=4），控制温度为80℃，搅拌均匀，待全溶解后冷却至室温，即得到改性三聚氰胺甲醛树脂。
实施例2
总计共100公斤的原料，它是由下述按重量份计的原料制成：
三聚氰胺：100份；
甲醛：200份；
异氰脲酸酯：16份；
亚油酰二乙醇胺：8份；
聚乙二醇：8份；
辛基酚聚氧乙烯醚（n=5）：5份；
氢氧化钠：4份；
酒精：50份；
水：30份。
依次将三聚氰胺、甲醛、氢氧化钠、酒精和水混合，加热到70℃搅拌10后，加入异氰脲酸酯，继续搅拌2h后，加入亚油酰二乙醇胺、聚乙二醇、辛基酚聚氧乙烯醚（n=5），控制温度为60℃，搅拌均匀，待全溶解后冷却至室温，即得到改性三聚氰胺甲醛树脂。

Claims (5)

1. 一种高柔韧性的改性三聚氰胺甲醛树脂，其特征在于，它是由下述按重量份计的原料制成：
三聚氰胺：100份；
甲醛：160~220份；
异氰脲酸酯：10~20份；
脂肪酸酰胺：5~10份；
聚乙二醇：5~8份；
烷基酚聚氧乙烯醚：3~6份；
氢氧化钠：2~5份；
酒精：40~60份；
水：20~30份。
2. 根据权利要求1所述的一种高柔韧性的改性三聚氰胺甲醛树脂，其特征在于：脂肪酸酰胺为油酰二乙醇胺、亚油酰二乙醇胺、硬脂酰二乙醇胺或者椰油酰二乙醇胺中的一种或者几种组合。
3. 根据权利要求1所述的一种高柔韧性的改性三聚氰胺甲醛树脂，其特征在于：所述的聚乙二醇分子量200-2000之间。
4. 根据权利要求1所述的一种高柔韧性的改性三聚氰胺甲醛树脂，其特征在于：所述的烷基酚聚氧乙烯醚为壬基酚聚氧乙烯醚（n为4、5、6、7或8）、辛基酚聚氧乙烯醚（n为4、5、6、7或8）或十二烷基酚聚氧乙烯醚（n为4、5、6、7或8）中的一种或者几种组合。
5. 根据权利要求1所述的一种高柔韧性的改性三聚氰胺甲醛树脂，其特征在于：所述一种高柔韧性的改性三聚氰胺甲醛树脂制备方法，其特征在于包括以下步骤：依次将三聚氰胺、甲醛、氢氧化钠、酒精和水混合，加热到70~80℃搅拌10~20min后，加入异氰脲酸酯，继续搅拌1~2h后，加入脂肪酸酰胺、聚乙二醇、烷基酚聚氧乙烯醚，控制温度为50~80℃，搅拌均匀，待全溶解后冷却至室温，即得到改性三聚氰胺甲醛树脂。
CN201410611034.4A 2014-11-04 2014-11-04 一种高柔韧性的改性三聚氰胺甲醛树脂 Pending CN104277192A (zh)