CN103978762A - 一种环保型半遮光植绒窗帘布的制作工艺 - Google Patents
一种环保型半遮光植绒窗帘布的制作工艺 Download PDFInfo
- Publication number
- CN103978762A CN103978762A CN201410229980.2A CN201410229980A CN103978762A CN 103978762 A CN103978762 A CN 103978762A CN 201410229980 A CN201410229980 A CN 201410229980A CN 103978762 A CN103978762 A CN 103978762A
- Authority
- CN
- China
- Prior art keywords
- flocking
- environment
- friendly type
- shading
- per minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于窗帘布用具技术领域，尤其涉及一种环保型半遮光植绒窗帘布的制作工艺。本发明公开了一种环保型半遮光植绒窗帘布的制作工艺，所述的制作工艺步骤如下：A：把提花错花布经防水层浸轧；B：把经过步骤1后的提花错花布经打底防渗白浆浸轧；C：在把经过步骤2后的提花错花布经植绒面浆浸轧；D：植绒，步骤3完成后进行植绒；E：焙烘扫毛，对完成步骤4后的产品进行刷毛后得成品窗帘布。本发明可以得到色彩丰富，质地厚实，柔软，保暖遮光避阳且具有吸音防潮功能的窗帘布。
Description
技术领域
本发明属于窗帘布用具技术领域，尤其涉及一种环保型半遮光植绒窗帘布的制作工艺。
背景技术
现代窗帘各式各样，种类繁多，但绝对大多数吸引消费者眼球的窗帘是鲜艳的色彩搭配和图案，而不是窗帘本身的功能。也就是说，人们大多数时候的选择是受到外观的影响，而非事物的本质。但随着绿色健康、低碳环保生活意识的推广，人们也逐渐的由外观转移到功能上，而目前市场上可供选择的多功能窗帘却并不能满足人们的需求。植绒在家纺用品上有着特别广阔的市场。植绒窗帘色彩丰富，质地厚实，柔软，保暖遮光避阳。植绒窗还有项很特别的功能吸音防潮功能。可以减少外界噪音对人们生活工作环境的干扰，提高了人们的生活品质。但是，目前的窗帘布的植绒并不能达到上述的效果，从而带来了工艺制作的难度。
发明内容
本发明的目的在于解决以上所述的技术问题，提供一种可以得到色彩丰富，质地厚实，柔软，保暖遮光避阳且具有吸音防潮功能的窗帘布的环保型半遮光植绒窗帘布的制作工艺，其技术方案如下：
一种环保型半遮光植绒窗帘布的制作工艺，其特征在于，所述的制作工艺步骤如下：
A：把提花错花布经防水层浸轧，浸轧气压为0.3-0.45mpa；防水层的材料是用进口环保型氟系防水剂与水配比而成，其配比为：纯净水97-99%进口环保型氟系防水剂1-3%；
B：把经过步骤1后的提花错花布经打底防渗白浆浸轧，生产涂刀角度为90度，刀距为55-65s，发泡比为43-47g，轧辊气压为0.25-0.4mpa，速度每分钟16-22m；打底防渗白浆主要用到是环保型软胶水，稳泡剂，发泡剂，二氧化钛分散体，氨水配比而成，粘度为2200-2500cps，ph值为9.8-10；
C：在把经过步骤2后的提花错花布经植绒面浆浸轧，生产操作涂刀角度为90度，刀距60-70s，发泡比为45-49g，轧辊气压在0.35-0.4mpa，速度每分钟14-18m；植绒面浆采用环保型软胶水，稳泡剂，发泡剂，二氧化钛分散体，氨水配置而成, ph值为9.8-10，粘度为2200-2500cps；
D：植绒，步骤3完成后进行植绒，把细绒与植绒面结合，计量为每平方3.5-4.7g，毛刷频率为45-50.2，静电电压30kv，速度每分钟14-18m；
E：焙烘扫毛，对完成步骤4后的产品进行刷毛后得成品窗帘布，刷毛频率7-10，拍打频率7.9-10.9，速度每分钟15-25m。
本发明提供的环保型半遮光植绒窗帘布的制作工艺，窗帘布经过染整、涂层植绒工艺处理后，具有色彩丰富，质地厚实，柔软等优点，布面具涤纶丝光泽和棉质感观效应。1.防水层为防止水泼溅布面上而导致布面水印；2.打底防渗白浆层是经过发泡机发泡比例调整防止在各层浆料复合的时候防止相互渗漏；3.二层结构的植绒面浆层经过植绒箱，由于经过一定电着在静电场作用下产生极化和驻极而带电，带电绒毛经转动，振动，平动等复杂运动，最后做直立定向运动依靠电场力而植入植绒面浆中。4.经过植绒后需焙烘扫毛，因在植绒过焙烘后使绒毛，发泡涂层面和基布牢固结合，经过植绒过后有些浮绒，依靠扫毛设备进行一次刷毛清理，经过机械拍打与吹风处理后效果更佳。
具体实施方式
下面具体说明实施例：
实施例1：
一种环保型半遮光植绒窗帘布的制作工艺，所述的制作工艺步骤如下：
A：把提花错花布经防水层浸轧，浸轧气压为0.3mpa；防水层的材料是用进口环保型氟系防水剂与水配比而成，其配比为：纯净水97-99%进口环保型氟系防水剂1-3%；
B：把经过步骤1后的提花错花布经打底防渗白浆浸轧，生产涂刀角度为90度，刀距为55s，发泡比为43g，轧辊气压为0.25mpa，速度每分钟16m；打底防渗白浆主要用到是环保型软胶水，稳泡剂，发泡剂，二氧化钛分散体，氨水配比而成，粘度为2200cps，ph值为9.8；
C：在把经过步骤2后的提花错花布经植绒面浆浸轧，生产操作涂刀角度为90度，刀距60s，发泡比为45g，轧辊气压在0.35mpa，速度每分钟14m；植绒面浆采用环保型软胶水，稳泡剂，发泡剂，二氧化钛分散体，氨水配置而成, ph值为9.8，粘度为2200cps；
D：植绒，步骤3完成后进行植绒，把细绒与植绒面结合，计量为每平方3.5g，毛刷频率为45次/秒，静电电压30kv，速度每分钟14m；
E：焙烘扫毛，对完成步骤4后的产品进行刷毛后得成品窗帘布，刷毛频率7次/秒，拍打频率8次/秒，速度每分钟15m。
实施例2：
一种环保型半遮光植绒窗帘布的制作工艺，其特征在于，所述的制作工艺步骤如下：
A：把提花错花布经防水层浸轧，浸轧气压为0.45mpa；防水层的材料是用进口环保型氟系防水剂与水配比而成，其配比为：纯净水97-99%进口环保型氟系防水剂1-3%；
B：把经过步骤1后的提花错花布经打底防渗白浆浸轧，生产涂刀角度为90度，刀距为65s，发泡比为47g，轧辊气压为0.4mpa，速度每分钟22m；打底防渗白浆主要用到是环保型软胶水，稳泡剂，发泡剂，二氧化钛分散体，氨水配比而成，粘度为2500cps，ph值为10；
C：在把经过步骤2后的提花错花布经植绒面浆浸轧，生产操作涂刀角度为90度，刀距70s，发泡比为49g，轧辊气压在0.4mpa，速度每分钟18m；植绒面浆采用环保型软胶水，稳泡剂，发泡剂，二氧化钛分散体，氨水配置而成, ph值为10，粘度为2500cps；
D：植绒，步骤3完成后进行植绒，把细绒与植绒面结合，计量为每平方4.7g，毛刷频率为50.2次/秒，静电电压30kv，速度每分钟18m；
E：焙烘扫毛，对完成步骤4后的产品进行刷毛后得成品窗帘布，刷毛频率10次/秒，拍打频率10.9次/秒，速度每分钟15-25m。
Claims (1)
1.一种环保型半遮光植绒窗帘布的制作工艺，其特征在于，所述的制作工艺步骤如下：
A：把提花错花布经防水层浸轧，浸轧气压为0.3-0.45mpa；防水层的材料是用进口环保型氟系防水剂与水配比而成，其配比为：纯净水97-99%进口环保型氟系防水剂1-3%；
B：把经过步骤1后的提花错花布经打底防渗白浆浸轧，生产涂刀角度为90度，刀距为55-65s，发泡比为43-47g，轧辊气压为0.25-0.4mpa，速度每分钟16-22m；打底防渗白浆主要用到是环保型软胶水，稳泡剂，发泡剂，二氧化钛分散体，氨水配比而成，粘度为2200-2500cps，ph值为9.8-10；
C：在把经过步骤2后的提花错花布经植绒面浆浸轧，生产操作涂刀角度为90度，刀距60-70s，发泡比为45-49g，轧辊气压在0.35-0.4mpa，速度每分钟14-18m；植绒面浆采用环保型软胶水，稳泡剂，发泡剂，二氧化钛分散体，氨水配置而成, ph值为9.8-10，粘度为2200-2500cps；
D：植绒，步骤3完成后进行植绒，把细绒与植绒面结合，计量为每平方3.5-4.7g，毛刷频率为45-50.2，静电电压30kv，速度每分钟14-18m；
E：焙烘扫毛，对完成步骤4后的产品进行刷毛后得成品窗帘布，刷毛频率7-10，拍打频率7.9-10.9，速度每分钟15-25m。