CN103966905B - 仿竹叶抗紫外线抗菌离型纸及其制备方法 - Google Patents
仿竹叶抗紫外线抗菌离型纸及其制备方法 Download PDFInfo
- Publication number
- CN103966905B CN103966905B CN201410194371.8A CN201410194371A CN103966905B CN 103966905 B CN103966905 B CN 103966905B CN 201410194371 A CN201410194371 A CN 201410194371A CN 103966905 B CN103966905 B CN 103966905B
- Authority
- CN
- China
- Prior art keywords
- release paper
- folium bambusae
- imitative
- antibacterial
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种仿竹叶抗紫外线抗菌离型纸的制备方法，包括以下步骤：将离型纸原纸的双面印制竹叶图案，进行电晕预处理，将离型剂涂布在印制有竹叶图案的离型纸原纸上得到仿竹叶离型纸，在仿竹叶离型纸表面涂布一层抗菌剂得到抗菌层，在抗菌层表面涂布一层PET薄膜层，并将抗菌层在20~25℃下晾干即得仿竹叶抗紫外线抗菌离型纸。本发明通过采用钯碳酸钙做催化剂，生产效率更高。本发明制备的仿竹叶抗紫外线抗菌离型纸表面涂布了有机抗菌剂不仅可以抗菌防止化工产品的腐败，而且可长时间保存，由于添加了PET薄膜层能够更好的抵御紫外线的侵袭，防止紫外线照射破坏被包装的产品，抗紫外线的能力达到了100%，抗菌率达到了100%。
Description
技术领域
本发明涉及离型纸的制备方法，具体涉及仿竹叶抗紫外线抗菌离型纸及其制备方法。
背景技术
竹叶为自然种植作物，产量有限，为了美观实用而且目前有很多产品要用到竹叶进行包装，而随着使用竹叶的量越来越大，目前种植根本无法满足需求，另外，由于竹叶无法长时间保存，包装产品后也容易破裂，另外由于没有防紫外线、防霉、防菌措施，导致一些化工产品容易在短时间内被紫外线强光照射使得产品变质，在没有抗菌措施的情况下产品也容易霉变、变质，造成极大损失。
发明内容
发明目的：针对现有技术的不足，本发明的目的是提供一种仿竹叶抗紫外线抗菌离型纸及其制备方法。本发明制备的一种仿竹叶抗紫外线抗菌离型纸容易储藏、运输，抗紫外线能力和抗菌能力极高，能防止化工产品变质或腐败。
技术方案：为了解决上述问题，本发明的技术方案是提供一种仿竹叶抗紫外线抗菌离型纸的制备方法，包括以下步骤：将离型纸原纸的双面印制竹叶图案，并进行电晕预处理，然后将离型剂涂布在印制有竹叶图案的离型纸原纸上得到仿竹叶离型纸，然后在仿竹叶离型纸表面涂布一层有机抗菌剂得到抗菌层，最后在抗菌层表面涂布一层PET薄膜层，在20～25℃下晾干即得仿竹叶抗紫外线抗菌离型纸。
其中，上述离型纸原纸的定量为70～80g/m2。
其中，上述电晕预处理电压到达8000-14000V/m2。
其中，上述离型剂包括2～5重量份的硅油、1～2重量份的钯碳酸钙、5～15重量份的棕榈油。
其中，上述有机抗菌剂为香草醛或乙基香草醛。
其中，上述PET薄膜层由以下原料制成：PET切片100～150份、VAE乳液10～20份、助剂2～10份。
其中，上述助剂为防刮伤、防粘连添加剂，所述防刮伤、防粘连添加剂为二氧化硅、高岭土、氧化钛中的任意一种或几种混合而成。
其中，上述离型剂的涂布量为0.35～0.55g/m2。
其中，上述抗菌层的涂布量为0.15～0.25g/m2。
上述的制备方法制备得到的仿竹叶抗紫外线抗菌离型纸。
有益效果：本发明的制备方法简单可行，通过采用钯碳酸钙做催化剂，生产效率更高，而且没有毒副作用，相比贵金属催化剂更有利。另外本发明制备的仿竹叶抗紫外线抗菌离型纸表面涂布了有机抗菌剂不仅可以抗菌防止化工产品的腐败，而且可长时间保存，由于添加了PET薄膜层能够更好的抵御紫外线的侵袭，防止紫外线照射破坏被包装的产品，抗紫外线的能力达到了100％，抗菌率达到了100％。
具体实施方式
下面结合具体实施方式，进一步阐述本发明。
实施例1：仿竹叶抗紫外线抗菌离型纸的制备
将离型纸原纸的双面印制竹叶图案并进行电晕预处理，离型纸原纸的定量为70g/m2，电晕预处理电压到达8000V/m2，然后将离型剂涂布在印制有竹叶图案的离型纸原纸上得到仿竹叶离型纸，离型剂的涂布量为0.35g/m2，离型剂包括2重量份的硅油、1重量份的钯碳酸钙、5重量份的棕榈油；然后在仿竹叶离型纸表面涂布一层有机抗菌剂得到抗菌层，有机抗菌剂为香草醛；抗菌层的涂布量为0.15g/m2，最后在抗菌层表面涂布一层PET薄膜层，PET薄膜层由以下原料制成：PET切片100份、VAE乳液10份、助剂2份。PET薄膜层的制备方法与现有技术中的PET薄膜制备方法一样；其中助剂为防刮伤、防粘连添加剂，所述防刮伤、防粘连添加剂为二氧化硅；最后在20℃下晾干即得仿竹叶抗紫外线抗菌离型纸。
实施例2
将离型纸原纸的双面印制竹叶图案并进行电晕预处理，离型纸原纸的定量为80g/m2，电晕预处理电压到达14000V/m2，然后将离型剂涂布在印制有竹叶图案的离型纸原纸上得到仿竹叶离型纸，离型剂的涂布量为0.55g/m2，离型剂包括5重量份的硅油、2重量份的钯碳酸钙、15重量份的棕榈油；然后在仿竹叶离型纸表面涂布一层有机抗菌剂得到抗菌层，有机抗菌剂为乙基香草醛；抗菌层的涂布量为0.25g/m2，最后在抗菌层表面涂布一层PET薄膜层，PET薄膜层由以下原料制成：PET切片150份、VAE乳液20份、助剂10份。PET薄膜层的制备方法与现有技术中的PET薄膜制备方法一样；其中助剂为防刮伤、防粘连添加剂，所述防刮伤、防粘连添加剂为高岭土；最后在25℃下晾干即得仿竹叶抗紫外线抗菌离型纸。
实施例3
将离型纸原纸的双面印制竹叶图案并进行电晕预处理，离型纸原纸的定量为75g/m2，电晕预处理电压到达11000V/m2，然后将离型剂涂布在印制有竹叶图案的离型纸原纸上得到仿竹叶离型纸，离型剂的涂布量为0.45g/m2，离型剂包括3重量份的硅油、1.5重量份的钯碳酸钙、10重量份的棕榈油；然后在仿竹叶离型纸表面涂布一层有机抗菌剂得到抗菌层，有机抗菌剂为乙基香草醛；抗菌层的涂布量为0.2g/m2，最后在抗菌层表面涂布一层PET薄膜层，PET薄膜层由以下原料制成：PET切片125份、VAE乳液15份、助剂6份。PET薄膜层的制备方法与现有技术中的PET薄膜制备方法一样；其中助剂为防刮伤、防粘连添加剂，所述防刮伤、防粘连添加剂为氧化钛；最后在23℃下晾干即得仿竹叶抗紫外线抗菌离型纸。
实施例1～3制备得到的仿竹叶抗紫外线抗菌离型纸的检测参数：
以上所述仅是本发明的优选实施方式，应当指出：对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (2)
1.一种仿竹叶抗紫外线抗菌离型纸的制备方法，其特征在于，包括以下步骤：将离型纸原纸的双面印制竹叶图案，并进行电晕预处理，然后将离型剂涂布在印制有竹叶图案的离型纸原纸上得到仿竹叶离型纸，然后在仿竹叶离型纸表面涂布一层有机抗菌剂得到抗菌层，最后在抗菌层表面涂布一层PET薄膜层，在20~25℃下晾干即得仿竹叶抗紫外线抗菌离型纸，所述离型纸原纸的定量为70~80g/m2，所述电晕预处理电压到达8000-14000V/m2，所述离型剂包括2~5重量份的硅油、1~2重量份的钯碳酸钙、5~15重量份的棕榈油，所述有机抗菌剂为香草醛或乙基香草醛，所述PET薄膜层由以下原料制成：PET切片100~150份、VAE乳液10~20份、助剂2~10份，所述助剂为防刮伤、防粘连添加剂，所述防刮伤、防粘连添加剂为二氧化硅、高岭土、氧化钛中的任意一种或几种混合而成，所述离型剂的涂布量为0.35~0.55g/m2，所述抗菌层的涂布量为0.15~0.25g/m2。
2.权利要求1所述的制备方法制备得到的仿竹叶抗紫外线抗菌离型纸。