CN103952028B - A kind of production method of environment-friendly type inner wall putty - Google Patents
A kind of production method of environment-friendly type inner wall putty Download PDFInfo
- Publication number
- CN103952028B CN103952028B CN201410150958.9A CN201410150958A CN103952028B CN 103952028 B CN103952028 B CN 103952028B CN 201410150958 A CN201410150958 A CN 201410150958A CN 103952028 B CN103952028 B CN 103952028B
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- conveyer
- powder
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to architectural decoration material field, production method particularly to a kind of environment-friendly type inner wall putty, it is characterized in that, its concrete production stage is as follows: 1) each raw material ratio by weight got the raw materials ready, wherein rubber powder 1.2～3.5 parts, fine aggregate 50～70 parts, blending stock 30～35 parts, reinforcing agent 15～25 parts, thickening agent 0.5～2.0 parts；2) by conveyer, each raw material mix is uniformly entered finished product bin；3) exported by conveyer, measure, pack, entered warehouse for finished product；4) product inspection, certified products dispatch from the factory.Described blending stock is trade waste carbide slurry.Compared with prior art, the medicine have the advantages that and utilize trade waste carbide slurry to produce environment-friendly type inner wall putty, there is scrubbing resistance ＞ 50 times, comprcssive strength >=0.06Pa, water absorption rate≤30%, nontoxic, the advantage of environmental protection, product has sharp useless, the advantage of energy-saving and environmental protection in process of production simultaneously.
Description
Technical field
The present invention relates to architectural decoration material field, particularly to the production method of a kind of environment-friendly type inner wall putty.
Background technology
At present in the production process of inner wall putty, mainly use Corn Starch Glue, Tapioca adhesive, vegetable protein starch
Glue, animal proteinum rubber powder, water-soluble phenolic resin adhesive powder, polyethylene vinyl acetate redispersable latex powder, polypropylene-the third
Olefin(e) acid redispersable latex powder, allyl resin redispersable latex powder, hydroxylated cellulose, lignocellulose, dicalcium powder, light
The raw materials such as calcium powder, Pulvis Talci, antifungus agent, preservative, product universal comprcssive strength ＜ 0.05MPa, airtight, water absorption rate
＞ 50%, mouldy when metope be full of cracks, decortication, rainy day high humidity often occur, return halogen, release is gone mouldy abnormal smells from the patient.Trace it to its cause
It is that selected raw material majority contains formaldehyde, phenol, cyanamide, sodium tripolyphosphate, formaldehyde condensation owing to production technology falls behind
The harmful and noxious substances such as thing, the most in use can discharge free formaldehyde, benzene, phenol, sodium phosphate even cyanamide etc. free
Molecule.Can volatilize when ambient temperature higher (＞ 10 DEG C), humidity relatively big (>=30%), produce toxic gas, harm people
Body is healthy.The most traditional inner wall putty can not meet environmental protection and the mankind demand to living environment；In waste resource, life
While producing cost height, pollute to production environment again, be one of this industrial workers's key factor suffering actual bodily harm；
Industrial workers remains high because of environmental pollution prevalence, especially the most in the majority with pulmonary carcinoma and hepatocarcinoma.
Summary of the invention
It is an object of the invention to provide the production method of a kind of environment-friendly type inner wall putty, it is achieved product is nontoxic, improve it and resist
Compressive Strength, raising breathability, reduce water absorption rate, meet mankind's ecological requirements to living environment, make industrial production
Environment is nontoxic, cost of material consumption to be reduced, energy resource consumption so that enterprise profit maximizes.
For achieving the above object, the present invention is achieved through the following technical solutions:
A kind of production method of environment-friendly type inner wall putty, its concrete production stage is as follows:
1) each raw material ratio by weight is got the raw materials ready, wherein rubber powder 1.2～3.5 parts, fine aggregate 50～70 parts, blending stock 30～35
Part, reinforcing agent 15～25 parts, thickening agent 0.5～2.0 parts, wherein:
Rubber powder is modified vinyl acetate, second the-the third multi-component copolymer, polyvinyl acetate, vinyl acetate, polyvinyl acetate, gathers
Ethene-vinyl acetate polymer can divide one or both in rubber powder again；
Fine aggregate is one or both in dry powder, dicalcium powder, light calcium carbonate powder, Pulvis Talci, calcium-magnesium powder；
Blending stock is trade waste carbide slurry, its Ca (OH)2Content >=90%, granularity is 0.01～0.3mm；
Reinforcing agent is the one in 32.5MPa or 42.5MPa Portland cement；
Thickening agent is the one in polyvinyl alcohol, guar gum；
2) by conveyer, each raw material mix is uniformly entered finished product bin；
3) exported by conveyer, measure, pack, entered warehouse for finished product；
4) product inspection, certified products dispatch from the factory.
Compared with prior art, the medicine have the advantages that
Utilize trade waste carbide slurry to produce environment-friendly type inner wall putty, have that water resistance is good, intensity is high, water absorption rate is low
Advantage, reach scrubbing resistance ＞ 50 times, comprcssive strength >=0.06Pa, water absorption rate≤30%, nontoxic, the advantage of environmental protection, with
Time product have that profit is useless, the advantage of energy-saving and environmental protection in process of production, country be correlated with preferential policy support under, it is achieved
Enterprise profit maximizes.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A kind of production method of environment-friendly type inner wall putty, its concrete production stage is as follows:
1) each raw material ratio by weight is got the raw materials ready, wherein rubber powder 1.2, fine aggregate 50, blending stock 30, reinforcing agent 18,
Thickening agent 0.5；
2) by conveyer, each raw material mix is uniformly entered finished product bin；
3) exported by conveyer, measure, pack, entered warehouse for finished product；
4) product inspection, certified products dispatch from the factory.
Embodiment 2
A kind of production method of environment-friendly type inner wall putty, its concrete production stage is as follows:
1) each raw material ratio by weight is got the raw materials ready, wherein rubber powder 2.5, fine aggregate 70, blending stock 32, reinforcing agent 25,
Thickening agent 0.8；
2) by conveyer, each raw material mix is uniformly entered finished product bin；
3) exported by conveyer, measure, pack, entered warehouse for finished product；
4) product inspection, certified products dispatch from the factory.
Embodiment 3
A kind of production method of environment-friendly type inner wall putty, its concrete production stage is as follows:
1) each raw material ratio by weight is got the raw materials ready, wherein rubber powder 3.5, fine aggregate 60, blending stock 35, reinforcing agent 15,
Thickening agent 1.2；
2) by conveyer, each raw material mix is uniformly entered finished product bin；
3) exported by conveyer, measure, pack, entered warehouse for finished product；
4) product inspection, certified products dispatch from the factory.
Embodiment 4
A kind of production method of environment-friendly type inner wall putty, its concrete production stage is as follows:
1) each raw material ratio by weight is got the raw materials ready, wherein rubber powder 3.0, fine aggregate 65, blending stock 35, reinforcing agent 20,
Thickening agent 2.0；
2) by conveyer, each raw material mix is uniformly entered finished product bin；
3) exported by conveyer, measure, pack, entered warehouse for finished product；
4) product inspection, certified products dispatch from the factory.
In above-described embodiment, rubber powder be modified vinyl acetate, second the-the third multi-component copolymer, polyvinyl acetate, vinyl acetate,
Polyvinyl acetate, polyethylene vinyl acetate polymer can divide one or both in rubber powder again；Fine aggregate is dry powder, triple superphosphate
One or both in powder, light calcium carbonate powder, Pulvis Talci, calcium-magnesium powder；Blending stock is trade waste carbide slurry, its Ca (OH)2
Content >=90%, granularity is 0.01～0.3mm；Reinforcing agent is in 32.5MPa or 42.5MPa Portland cement
Kind；Thickening agent is the one in polyvinyl alcohol, guar gum.Above-described embodiment product all can meet scrubbing resistance ＞ 50 times, resistance to compression
Intensity >=0.06Pa, the performance requirement of water absorption rate≤30%.
Claims (1)
1. the production method of an environment-friendly type inner wall putty, it is characterised in that its concrete production stage is as follows:
1) each raw material ratio by weight is got the raw materials ready, wherein rubber powder 1.2～3.5 parts, fine aggregate 50～70 parts, blending stock 30～35
Part, reinforcing agent 15～25 parts, thickening agent 0.5～2.0 parts, wherein:
Rubber powder is modified vinyl acetate, second the-the third multi-component copolymer, polyvinyl acetate, vinyl acetate, polyethylene-acetic acid second
Alkene polymer can divide one or both in rubber powder again；
Fine aggregate is one or both in dicalcium powder, light calcium carbonate powder, Pulvis Talci, calcium-magnesium powder；
Blending stock is trade waste carbide slurry, its Ca (OH)2Content >=90%, granularity is 0.01～0.3mm；
Reinforcing agent is the one in 32.5MPa or 42.5MPa Portland cement；
Thickening agent is the one in polyvinyl alcohol, guar gum；
2) by conveyer, each raw material mix is uniformly entered finished product bin；
3) exported by conveyer, measure, pack, entered warehouse for finished product；
4) product inspection, certified products dispatch from the factory.