CN1557885A - Taibai putty for internal wall - Google Patents
Taibai putty for internal wall Download PDFInfo
- Publication number
- CN1557885A CN1557885A CNA2004100217791A CN200410021779A CN1557885A CN 1557885 A CN1557885 A CN 1557885A CN A2004100217791 A CNA2004100217791 A CN A2004100217791A CN 200410021779 A CN200410021779 A CN 200410021779A CN 1557885 A CN1557885 A CN 1557885A
- Authority
- CN
- China
- Prior art keywords
- putty
- kilograms
- powder
- water
- taibai
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The white inner wall putty consists of dispersive polymer or powdered PVA 0.7-0.8 wt%, hydroxypropyl cellulose ether 0.8-10 wt%, coarse whiting 50-65 wt%, light calcium carbonate 7-8 wt%, sierozem 10-15 wt%, bentonite 2-5 wt% and talcum powder 5-8 wt%. The white inner wall putty has non-toxic and smell-less powder and volatile gas, raised water tolerance and strength, and raised wall surface quality.
Description
Technical field
The invention belongs to building wall adhesion layer material technology field
Background technology
For a long time, the finishing of all kinds of architecture indoor surface of wall, generally all be to adopt polyvinyl alcohol place formaldehyde to boil 107 glue to mix dry powder and make main finishing material, and boil glue with naked lights such as coal, bavins at the construction field (site) often, mix dry powder and be mixed with the putty use, both caused atmospheric pollution, can not guarantee quality product again, and the putty proportioning of this formulated is low, intensity is not high, poor water resistance owing to contain harmful formaldehyde material in the glue, influences all to the house occupant still to the constructor that it is healthy.
Summary of the invention
The weak point that purpose of the present invention exists at above-mentioned prior art just and a kind of prescription that water does not add all good too white putty of interior wall special use of glue, nontoxic, tasteless, environmental protection, safe, easy to use, intensity and water tolerance that adds is provided.
The objective of the invention is to be achieved through the following technical solutions.
The too white putty of a kind of interior wall of the present invention, its component and weight percent are: redispersible polymer (SK3000) or dry powder polyvinyl alcohol 0.7～0.8%, hydroxypropylcelluloether ether 0.8～10%, water-ground limestone 50～65%, light calcium carbonate 7～8%, ash calcium 10～15%, wilkinite 2～5%, talcum powder 5～8%.
The present invention with white inorganic coagulation material and redispersible polymer and multiple nontoxic admixture as main raw material formulated be the thin sprills of a kind of white, belong to aqueous putty, during use, after about 2: 1 ratio of putty powder and water is in harmonious proportion and stirs by weight percentage, promptly can be used for the interior wall body and be coated with and scrape construction.After no matter the present invention still lived when construction, its powder and volatilization 2 gases were all nontoxic, tasteless, very environmental protection, and, also strengthened the quality of surface of wall greatly owing to improved its water tolerance and intensity.
Embodiment
Embodiment one: get 0.7 kilogram of redispersible polymer, 10 kilograms of hydroxypropylcelluloether ethers, 62 kilograms of water-ground limestones (being dry powder), 12 kilograms of grey calcium, 5 kilograms of wilkinites, 5.3 kilograms of talcum powder, 7 kilograms of light calcium carbonates, be stirred into powder after mixing.
Embodiment two: get 0.8 kilogram of redispersible polymer, 5 kilograms of hydroxypropylcelluloether ethers, 60 kilograms of water-ground limestones (being dry powder), 15 kilograms of grey calcium, 2 kilograms of wilkinites, 7.2 kilograms of talcum powder, 8 kilograms of light calcium carbonates, be stirred into powder after mixing.
Embodiment three: get 0.8 kilogram of dry powder polyethylene, 5 kilograms of hydroxypropylcelluloether ethers, 60 kilograms of water-ground limestones (being dry powder), 15 kilograms of grey calcium, 2 kilograms of wilkinites, 7.2 kilograms of talcum powder, 8 kilograms of light calcium carbonates, be stirred into powder after mixing.
Claims (1)
1, the too white putty of a kind of interior wall, relate to and be used for the adhesion layer material of smooth and smooth metope, it is characterized in that, its component and weight percent are: redispersible polymer (SK3000) or dry powder polyvinyl alcohol 0.7～0.8%, hydroxypropylcelluloether ether 0.8～10%, water-ground limestone 50～65%, light calcium carbonate 7～8%, ash calcium 10～15%, wilkinite 2～5%, talcum powder 5～8%.