KR102157314B1 - Cement compositions using putty and the putty comprising thereof - Google Patents
Cement compositions using putty and the putty comprising thereof Download PDFInfo
- Publication number
- KR102157314B1 KR102157314B1 KR1020190113825A KR20190113825A KR102157314B1 KR 102157314 B1 KR102157314 B1 KR 102157314B1 KR 1020190113825 A KR1020190113825 A KR 1020190113825A KR 20190113825 A KR20190113825 A KR 20190113825A KR 102157314 B1 KR102157314 B1 KR 102157314B1
- Authority
- KR
- South Korea
- Prior art keywords
- putty
- cement
- weight
- composition
- equation
- Prior art date
Abstract
Description
본 발명은 퍼티용 시멘트 조성물 및 이를 포함하는 퍼티에 대한 것이다.The present invention relates to a cement composition for putty and a putty comprising the same.
구체적으로, 본 발명은 내외부 퍼티 및 에폭시 퍼티와 유사한 물리적 강도 및 가사시간을 가지면서 흙손 시공 작업성이 우수하고 백화 현상에 대한 저항성이 뛰어나며, 동시에 폐기 예정인 수성 폐페인트를 활용함으로써 제품 단가 절감을 유도할 수 있는 퍼티용 시멘트 조성물 및 이를 포함하는 퍼티에 대한 것이다. Specifically, the present invention has a similar physical strength and pot life as internal and external putty and epoxy putty, has excellent trowel construction workability, excellent resistance to whitening, and at the same time induces product cost reduction by utilizing water-based waste paint scheduled to be discarded. It relates to a cement composition for putty and putty comprising the same.
페인트(Paint, 도료)는 유동성의 물질로 물체의 표면에 넓게 도포되어 얇은 피막층을 형성하고, 시간의 경과에 따라 건조 경화됨으로써 물체의 표면을 보호할 뿐 아니라 미감을 증대시키는 기능을 갖는다.Paint is a fluid material that is widely applied to the surface of an object to form a thin film layer, and it has a function of not only protecting the surface of the object but also increasing the aesthetics by drying and curing it over time.
이러한 페인트는 특히 건축물 등과 같은 각종 구조물에 도포되어 구조물의 외관을 미려하게 할 뿐 아니라, 부식 등과 같은 손상을 방지하여 내구성을 향상시키는데 많이 이용된다.These paints are particularly applied to various structures such as buildings to enhance the appearance of the structure and are often used to improve durability by preventing damage such as corrosion.
이러한 페인트는 수성 페인트 및 유성 페인트로 구분되고, 각 페인트는 소정 규격의 캔에 보관되어 유통 및 판매되는데, 페인트 캔을 개봉한 후 사용하다 남은 잔존 페인트의 함량이 6mm 미만일 경우 일반 폐기물로 분류되지만 그 잔존량이 6mm를 초과하는 경우 지정 폐기물로 분류되어 관련 법규에 따라 처리하여야 하는 번거로움이 있다.These paints are divided into water-based paints and oil-based paints, and each paint is stored in cans of a predetermined size, distributed and sold.If the amount of residual paint remaining after opening the paint can is less than 6 mm, it is classified as general waste. If the residual amount exceeds 6mm, it is classified as a designated waste, and there is a trouble of disposing of it according to the relevant laws and regulations.
한편, 퍼티(putty)는 페인트 작업할 곳의 파임, 균열, 구멍 등의 결합을 메워 도장재가 매끈하게 마감되도록 하는 도료로서, 적용 부위에 따라 내부 퍼티 혹은 외부 퍼티로 구분할 수 있고, 수지 타입에 따라 에폭시 퍼티, 우레탄 퍼티, 폴리에스테르 퍼티, 아연 퍼티 또는 핸드코트 등으로 구분할 수도 있다.On the other hand, putty is a paint that fills the bonds of dents, cracks, and holes in the area to be painted so that the paint finishes smoothly, and can be classified into internal putty or external putty depending on the application site. It can also be classified into epoxy putty, urethane putty, polyester putty, zinc putty, or hand coat.
이와 같은 퍼티(putty)의 제조에 있어 기술적 과제는 적정 가사시간 및 물리적 강도를 가지면서 흙손 시공에 있어서의 작업성 및 백화 현상 방지 능력을 향상시키는 소재를 선택하는 것에 있고, 더불어 기존의 폐기물 등을 적정 범위로 조합하여 제조 단가를 낮추고 환경적으로도 이로운 소재를 개발하는 것에 있다.The technical task in manufacturing such putty is to select a material that improves workability and ability to prevent whitening in trowel construction while having adequate pot life and physical strength. The goal is to reduce the manufacturing cost and develop environmentally beneficial materials by combining them in an appropriate range.
이에, 일반적으로 요구되는 퍼티(putty)의 가사시간 및 물리적 강도를 만족하고, 흙손 시공 작업성 및 백화 현상 저항성이 뛰어나며, 친환경적이면서 제조단가가 저감된 퍼티용 조성물에 대한 연구개발이 필요한 실정이다. Accordingly, there is a need for research and development on a composition for putty that satisfies the generally required pot life and physical strength of putty, has excellent trowel construction workability and whitening resistance, is environmentally friendly and has a reduced manufacturing cost.
본 발명은 적정 가사시간 및 내외부 퍼티 및 에폭시 퍼티에서 요구하는 물리적 강도를 가지면서 흙손 시공 작업성 및 백화 현상 저항성이 뛰어난 퍼티용 시멘트 조성물을 제공한다.The present invention provides a cement composition for putty excellent in trowel construction workability and whitening resistance, while having an appropriate pot life and physical strength required by both inner and outer putty and epoxy putty.
본 발명은 또한, 폐기 예정인 수성 폐페인트를 활용함으로써 제품 단가 절감을 유도할 수 있고, 환경 친화적인 퍼티용 시멘트 조성물을 제공한다.The present invention also provides a cement composition for putty that can induce product cost reduction by utilizing an aqueous waste paint scheduled to be discarded, and is environmentally friendly.
본 발명은 더욱이, 적정 가사시간 및 내외부 퍼티 및 에폭시 퍼티에서 요구하는 물리적 강도를 가지면서 흙손 시공 작업성 및 백화 현상 저항성이 뛰어난 퍼티를 제공한다. The present invention further provides a putty excellent in trowel construction workability and whitening resistance while having an appropriate pot life and physical strength required by the inner and outer putty and the epoxy putty.
본 발명은, 상기 과제를 해결하기 위해 안출된 것으로써, 퍼티용 시멘트 조성물 및 이를 포함하는 퍼티에 대한 것이다.The present invention relates to a cement composition for putty and a putty including the same, as conceived to solve the above problems.
상기 퍼티용 시멘트 조성물은 SiO2를 주성분으로 함유하는 규사; 및 포틀랜드 시멘트, 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 및 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트로부터 선택되는 2종 이상의 시멘트 성분을 포함한다. 또한, 수성 페인트와 혼화되어 상기 수성 페인트를 응고시킴으로써 상기 수성 페인트와 함께 하기 수식 1을 만족하는 퍼티를 형성한다.The cement composition for putty is silica sand containing SiO 2 as a main component; And Portland cement, a first cement comprising aluminum oxide in a range of 30 to 70% by weight, and a second cement comprising calcium sulfoaluminate in a range of 25 to 45% by weight. . In addition, it is mixed with the water-based paint to solidify the water-based paint, thereby forming a putty that satisfies the following formula (1) together with the water-based paint.
[수식 1][Equation 1]
3 N/mm2 ≤ Cs ≤ 10 N/mm2 3 N/mm 2 ≤ Cs ≤ 10 N/mm 2
상기 수식 1에서, Cs는 KS L ISO 679법에 의해 측정한 상기 퍼티의 1일 양생 후 압축 강도를 의미한다. In Equation 1, Cs refers to the compressive strength of the putty measured by the KS L ISO 679 method after 1 day curing.
하나의 예시에서, 상기 퍼티용 시멘트 조성물은 SiO2를 주성분으로 함유하는 규사를 주성분으로 포함하고, 상기 시멘트 성분은 상기 포틀랜드 시멘트, 상기 제 1 시멘트 및 상기 제 2 시멘트를 포함할 수 있다.In one example, the cement composition for putty includes silica sand containing SiO 2 as a main component as a main component, and the cement component may include the Portland cement, the first cement, and the second cement.
하나의 예시에서, 상기 규사는 제 1 입도를 가지는 제 1 인조 규사; 및 상기 제 1 인조 규사의 제 1 입도와 상이한 제 2 입도를 가지는 제 2 인조 규사를 포함할 수 있다.In one example, the silica sand is a first artificial silica sand having a first particle size; And it may include a second artificial silica having a second particle size different from the first particle size of the first artificial silica.
하나의 예시에서, 상기 규사는 60 내지 80 메쉬 범위 내의 입도를 가지는 제 1 인조 규사; 및 80 내지 120 메쉬 범위 내의 입도를 가지는 제 2 인조 규사를 포함할 수 있다. In one example, the silica sand first artificial silica having a particle size in the range of 60 to 80 mesh; And it may include a second artificial silica having a particle size in the range of 80 to 120 mesh.
본 발명에 따른 퍼티용 시멘트 조성물은, 예를 들면 SiO2를 주성분으로 함유하는 규사 50 내지 70 중량부; 포틀랜드 시멘트 5 내지 20 중량부; 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 5 내지 15 중량부; 및 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트 5 내지 15 중량부를 포함할 수 있다. The cement composition for putty according to the present invention includes, for example, 50 to 70 parts by weight of silica sand containing SiO 2 as a main component; 5 to 20 parts by weight of Portland cement; 5 to 15 parts by weight of the first cement containing aluminum oxide in the range of 30 to 70% by weight; And 5 to 15 parts by weight of a second cement containing calcium sulfoaluminate in the range of 25 to 45% by weight.
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 60 내지 80 메쉬 범위 내의 입도를 가지는 제 1 인조 규사 20 내지 45 중량부; 80 내지 120 메쉬 범위 내의 입도를 가지는 제 2 인조 규사 30 내지 45 중량부; 포틀랜드 시멘트 10 내지 20 중량부; 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 5 내지 15 중량부; 및 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트 5 내지 15 중량부를 포함할 수 있다. 이 때, 퍼티용 시멘트 조성물은 하기 수식 2를 만족할 수 있다. The cement composition for putty according to the present invention may further include 20 to 45 parts by weight of the first artificial silica sand having a particle size in the range of 60 to 80 mesh; 30 to 45 parts by weight of the second artificial silica sand having a particle size in the range of 80 to 120 mesh; Portland cement 10 to 20 parts by weight; 5 to 15 parts by weight of the first cement containing aluminum oxide in the range of 30 to 70% by weight; And 5 to 15 parts by weight of a second cement containing calcium sulfoaluminate in the range of 25 to 45% by weight. At this time, the cement composition for putty may satisfy Equation 2 below.
[수식 2][Equation 2]
A<B<CA<B<C
상기 수식 2에서 A는 상기 제 1 시멘트 혹은 상기 제 2 시멘트의 조성물 내 함량(g)이고, B는 상기 포틀랜드 시멘트의 조성물 내 함량(g)이며, C는 제 1 시멘트 및 제 2 시멘트의 조성물 내 함량(g)의 합이다.In Equation 2, A is the content (g) in the composition of the first cement or the second cement, B is the content (g) in the composition of the Portland cement, and C is the composition of the first cement and the second cement. It is the sum of the content (g).
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 하기 수식 3을 만족할 수 있다.The cement composition for putty according to the present invention may also satisfy Equation 3 below.
[수식 3][Equation 3]
D<E<FD<E<F
상기 수식 3에서 D는 상기 제 1 시멘트의 조성물 내 함량(g)이고, E는 상기 제 2 시멘트의 조성물 내 함량(g)이며, F는 상기 포틀랜드 시멘트의 조성물 내 함량(g)이다.In Equation 3, D is the content in the composition of the first cement (g), E is the content in the composition of the second cement (g), and F is the content in the composition of Portland cement (g).
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 석고 5 내지 10 중량부를 더 포함할 수 있다.The cement composition for putty according to the present invention may further include 5 to 10 parts by weight of gypsum.
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 타타르산, 말산, 락트산, 시트르산 및 숙신산으로 이루어진 군에서 선택되는 어느 하나의 유기산을 포함하는 산화 방지제 0.01 내지 0.5 중량부를 더 포함할 수 있다.The cement composition for putty according to the present invention may further include 0.01 to 0.5 parts by weight of an antioxidant containing any one organic acid selected from the group consisting of tartaric acid, malic acid, lactic acid, citric acid and succinic acid.
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 소포제 0.001 내지 0.1 중량부를 더 포함할 수 있다.The cement composition for putty according to the present invention may further include 0.001 to 0.1 parts by weight of a defoaming agent.
본 발명에 따른 퍼티용 시멘트 조성물은 또한, Li2CO3 0.01 내지 0.1 중량부를 더 포함할 수 있다.The cement composition for putty according to the present invention may further include 0.01 to 0.1 parts by weight of Li 2 CO 3 .
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 면사, 아크릴사, 유리섬유사 또는 탄소섬유사 0.1 내지 0.5 중량부를 더 포함할 수 있다.The cement composition for putty according to the present invention may further include 0.1 to 0.5 parts by weight of cotton yarn, acrylic yarn, glass fiber yarn, or carbon fiber yarn.
본 발명은 더욱이, 상기 퍼티용 시멘트 조성물을 포함하는 퍼티에 대한 것이다.The present invention further relates to a putty comprising the cement composition for putty.
상기 퍼티는 상기 퍼티용 시멘트 조성물 40 내지 60 중량부; 및 수성 페인트 40 내지 60 중량부를 포함하고, 하기 수식 4 및 5를 만족한다.The putty is 40 to 60 parts by weight of the cement composition for putty; And 40 to 60 parts by weight of a water-based paint, and satisfy Equations 4 and 5 below.
[수식 4][Equation 4]
3 N/mm2 ≤ Cs ≤ 10 N/mm2 3 N/mm 2 ≤ Cs ≤ 10 N/mm 2
[수식 5][Equation 5]
20 min ≤ Pf ≤ 40 min20 min ≤ P f ≤ 40 min
상기 수식 4에서, Cs는 KS L ISO 679법에 의해 측정한 상기 퍼티의 1일 양생 후 압축 강도(N/mm2)를 의미하고, 상기 수식 5에서 Pf는 상기 퍼티의 가사시간(min)을 의미한다.In Equation 4, Cs refers to the compressive strength (N/mm 2 ) of the putty measured by the KS L ISO 679 method after 1 day curing, and in Equation 5, P f is the pot life of the putty (min) Means.
상기 퍼티는 또한, 하기 수식 6을 만족할 수 있다.The putty may also satisfy Equation 6 below.
[수식 6][Equation 6]
90g ≤ G ≤ 130g90g ≤ G ≤ 130g
상기 수식 6에서, G는 상기 퍼티에 포함되는 퍼티용 시멘트 조성물 100g 대비 수성 페인트의 중량(g)을 의미한다. In Equation 6, G means the weight (g) of the water-based paint relative to 100 g of the cement composition for putty contained in the putty.
상기 퍼티는 또한, 상기 수식 6에서 G가 120g 인 것 일 수 있다. The putty may also have a G of 120 g in Equation 6 above.
본 발명에 따른 퍼티용 시멘트 조성물은 적정 가사시간 및 내외부 퍼티 및 에폭시 퍼티에서 요구하는 물리적 강도를 가지면서 흙손 시공 작업성 및 백화 현상 저항성이 뛰어난 퍼티를 제조하는데 효과적이다. The cement composition for putty according to the present invention is effective in producing a putty excellent in trowel construction workability and whitening resistance while having an appropriate pot life and physical strength required by the inner and outer putty and the epoxy putty.
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 폐기 예정인 수성 폐페인트를 활용함으로써 제품 단가 절감을 유도할 수 있고 친환경적이며 수성 폐페인트를 별도 비용으로 폐기하여야 하는 곤란함을 개선할 수 있다.In addition, the cement composition for putty according to the present invention can induce product cost reduction by using an aqueous waste paint scheduled to be discarded, and is environmentally friendly and can improve the difficulty of disposing of the aqueous waste paint at a separate cost.
물론, 본 발명의 효과가 상기 언급한 범위 내로 제한되는 것은 아니다. Of course, the effect of the present invention is not limited within the above-mentioned range.
도 1 및 2는 본 발명의 실험예에 따른 퍼티의 흙손 시공 결과를 도시한 것이다. 1 and 2 show the results of construction of a trowel of putty according to an experimental example of the present invention.
이하, 본 발명에 대하여, 보다 구체적으로 설명한다.Hereinafter, the present invention will be described in more detail.
본 명세서에서 사용되는 용어는, 본 발명에서의 기능을 고려하면서 가능한 현재 널리 사용되는 일반적인 용어들을 선택하였으나, 이는 당 분야에 종사하는 기술자의 의도 또는 판례, 새로운 기술의 출현 등에 따라 달라질 수 있다. 또한, 특정한 경우는 출원인이 임의로 선정한 용어도 있으며, 이 경우 해당되는 발명의 설명 부분에서 상세히 그 의미를 기재할 것이다. 따라서 본 발명에서 사용되는 용어는 단순한 용어의 명칭이 아닌, 그 용어가 가지는 의미와 본 발명의 전반에 걸친 내용을 토대로 정의되어야 한다. The terms used in the present specification have selected general terms that are currently widely used as possible while considering functions in the present invention, but this may vary according to the intention or precedent of a technician working in the field, the emergence of new technologies, and the like. In addition, in certain cases, there are terms arbitrarily selected by the applicant, and in this case, the meaning of the terms will be described in detail in the description of the corresponding invention. Therefore, the terms used in the present invention should be defined based on the meaning of the term and the overall contents of the present invention, not a simple name of the term.
본 발명은 발명의 주요 기술적 사상을 벗어나지 아니하는 범위 내에서 다양한 변환을 가할 수 있고 여러 가지 실시예를 가질 수 있는바, 특정 실시예들을 도면에 예시하고 상세한 설명에 상세하게 설명하고자 한다. 그러나, 이는 특정한 실시 형태에 대해 범위를 한정하려는 것이 아니며, 발명의 사상 및 기술 범위에 포함되는 모든 변환, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 실시예들을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.In the present invention, various transformations may be applied within the scope of the main technical idea of the present invention and various embodiments may be provided. Specific embodiments are illustrated in the drawings and described in detail in the detailed description. However, this is not intended to limit the scope of the specific embodiment, it should be understood to include all the conversions, equivalents, or substitutes included in the spirit and scope of the invention. In describing the embodiments, when it is determined that a detailed description of a related known technology may obscure the subject matter, the detailed description thereof will be omitted.
본 명세서에서, "포함하다" 또는 "구성되다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.In the present specification, terms such as "comprise" or "consist" are intended to designate the presence of features, numbers, steps, actions, components, parts, or combinations thereof described in the specification, but one or more other It is to be understood that the presence or addition of features, numbers, steps, actions, components, parts, or combinations thereof, does not preclude in advance the possibility of being excluded.
본 명세서에서, "이루어지다 혹은 이루어지는" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것만으로 존재한다는 것을 명확히 하기 위한 것으로, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 배제하는 것으로 이해되어야 한다. In the present specification, terms such as "consisting of or consisting of" are used to clarify that there are only features, numbers, steps, actions, components, parts, or combinations thereof described in the specification, and one or more other features It is to be understood as excluding the possibility of the presence or addition of elements or numbers, steps, actions, components, parts, or combinations thereof.
본 명세서에서 용어 "중량부"는 달리 설명하지 아니하는 한 각 성분 사이의 중량 비율을 의미한다. In the present specification, the term "parts by weight" means a weight ratio between each component unless otherwise stated.
본 명세서에서는 용어 "응고"과 용어 "응결"을 달리 구분하여 사용하지 아니하며, 페인트를 고상화시키는 기능, 단계 및 해당 단계의 결과물을 의미하는 것으로 이해하여야 한다.In the present specification, the term "coagulation" and the term "condensation" are not used separately, and should be understood to mean a function, a step, and a result of the step of solidifying the paint.
본 명세서에서 용어 "수성 폐페인트"는 페인트 캔에 잔존하여 폐기물로 버려져야 하는 수성 페인트를 의미하는 것으로, 본 명세서 및 실시예 등에서 언급되는 "수성 폐페인트"는 수성 페인트와 그 구성 성분에 있어 차이는 없다. In the present specification, the term "water-based waste paint" refers to a water-based paint that remains in the paint can and must be discarded as waste, and the "water-based waste paint" referred to in the present specification and examples is the difference between the water-based paint and its components. There is no.
본 발명은 퍼티용 시멘트 조성물에 대한 것이다.The present invention relates to a cement composition for putty.
본 발명자는 폐인트 캔에 잔존하는 미량의 수성 페인트(수성 폐페인트)를 활용하여 내외부 퍼티 및 에폭시 퍼티와 유사한 물성 및 가사시간을 가지는 퍼티를 형성하기 위한 조성물을 개발하던 중, SiO2를 주성분으로 함유하는 규사와 함께 포틀랜드 시멘트, 산화알루미늄 함유 시멘트 및 칼슘 설포알루미네이트 함유 시멘트를 적정 비율로 포함하는 시멘트 조성물을 수성 페인트와 소정 비율로 혼합시키는 경우, 상기 수성 페인트와 시멘트 조성물의 혼화에 따라 퍼티 제품과 유사한 물성 및 가사시간을 가지면서 흙손 시공 작업성이 우수하고 백화 현상에 대한 저항성이 뛰어난 퍼티가 제조됨을 확인하여 본 발명을 완성하기에 이르렀다.The present inventor was developing a composition for forming a putty having physical properties and pot life similar to internal and external putty and epoxy putty by using a trace amount of water-based paint (water-based waste paint) remaining in the waste paint can, while SiO 2 was used as a main component. When a cement composition containing Portland cement, aluminum oxide-containing cement, and calcium sulfoaluminate-containing cement in an appropriate ratio is mixed with a water-based paint in a predetermined ratio, a putty product according to the mixing of the water-based paint and the cement composition It has been confirmed that a putty having excellent trowel construction workability and excellent resistance to whitening is produced while having physical properties and pot life similar to those of, thereby completing the present invention.
본 발명에 따른 퍼티용 시멘트 조성물은 SiO2를 주성분으로 함유하는 규사; 및 포틀랜드 시멘트, 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 및 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트로부터 선택되는 2종 이상의 시멘트 성분을 포함한다. 또한, 상기 퍼티용 시멘트 조성물은 수성 페인트와 혼화되어 상기 수성 페인트를 응고시킴으로써 상기 수성 페인트와 함께 하기 수식 1을 만족하는 퍼티를 형성한다. The cement composition for putty according to the present invention includes silica sand containing SiO 2 as a main component; And Portland cement, a first cement comprising aluminum oxide in a range of 30 to 70% by weight, and a second cement comprising calcium sulfoaluminate in a range of 25 to 45% by weight. . In addition, the cement composition for putty is mixed with a water-based paint to solidify the water-based paint to form a putty that satisfies Equation 1 below with the water-based paint.
[수식 1][Equation 1]
3 N/mm2 ≤ Cs ≤ 10 N/mm2 3 N/mm 2 ≤ Cs ≤ 10 N/mm 2
상기 수식 1에서, Cs는 KS L ISO 679법에 의해 측정한 상기 퍼티의 1일 양생 후 압축 강도(N/mm2)를 의미한다. In Equation 1, Cs refers to the compressive strength (N/mm 2 ) of the putty measured by the KS L ISO 679 method after 1 day curing.
본 발명에 따른 퍼티용 시멘트 조성물은 수성 페인트와 적정 비율로 혼화 및 응고되어 소정의 가사시간 및 물리적 강도를 가지는 퍼티를 형성할 수 있는데, 상기 수식 1은 본 발명에 따른 퍼티용 시멘트 조성물이 수성 페인트와 혼화 및 응고되어 최종 형성된 퍼티의 압축 강도가 3N/mm2 내지 10 N/mm2의 범위 내에 있다는 것을 의미한다. The cement composition for putty according to the present invention can be mixed and solidified in an appropriate ratio with water-based paint to form a putty having a predetermined pot life and physical strength, wherein Equation 1 is the cement composition for putty according to the present invention. It means that the compressive strength of the finally formed putty by mixing and solidifying with is in the range of 3N/mm 2 to 10 N/mm 2 .
본 발명에 따른 퍼티용 시멘트 조성물과 혼화되어 퍼티를 형성하는 수성 페인트의 종류는 특별히 제한되는 것은 아니고, 국내외에 시판되고 있는 내외부용 수성페인트로서 아크릴 에멀젼 수지 함유 수성 페인트, 수용성 우레탄 수지 함유 수성 페인트, EVA 수지 함유 수성 페인트, 아크릴 라텍스 함유 수성 페인트 또는 아크릴 공중합체 함유 수성 페인트 등이 예시될 수 있으나 이에 제한되는 것은 아니다.The type of water-based paint that is mixed with the cement composition for putty according to the present invention to form putty is not particularly limited, and as a water-based paint for interior and exterior marketed at home and abroad, a water-based paint containing an acrylic emulsion resin, a water-based paint containing a water-soluble urethane resin, EVA resin-containing water-based paint, acrylic latex-containing water-based paint or acrylic copolymer-containing water-based paint may be exemplified, but is not limited thereto.
본 발명에 따른 퍼티용 시멘트 조성물은 SiO2를 주성분으로 함유하는 규사; 및 포틀랜드 시멘트, 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 및 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트로부터 선택되는 2종 이상의 시멘트 성분을 포함한다.The cement composition for putty according to the present invention includes silica sand containing SiO 2 as a main component; And Portland cement, a first cement comprising aluminum oxide in a range of 30 to 70% by weight, and a second cement comprising calcium sulfoaluminate in a range of 25 to 45% by weight. .
상기 규사는, SiO2를 주성분으로 함유한다. 상기에서 용어 "주성분으로 함유한다"는 것은 SiO2를 규사에 포함되는 성분 중 가장 많은 비율로 함유한다는 것은 의미하고, 예를 들면 상기 규사는 SiO2를 80% 중량 이상, 90% 중량 이상 또는 99% 중량 이상의 비율로 함유할 수 있다.The silica sand contains SiO 2 as a main component. In the above, the term "contains as a main component" means that SiO 2 is contained in the largest proportion of the components included in the silica sand, for example, the silica sand contains 80% or more, 90% or more by weight of SiO 2 or 99 It may contain in a ratio of% by weight or more.
상기 규사는, 예를 들면 강암류, 화강편마암류 등 석영을 많이 함유하고 있는 암석이 풍화되어 형성된 천연 규사이거나 혹은 페그마타이트에 함유되어 있는 석영만을 선별 분쇄하여 모래 상으로 만든 인조 규사 일 수 있고, 바람직하게는 인조 규사 일 수 있다. The silica sand may be natural silica sand formed by weathering rocks containing a lot of quartz, such as, for example, hard rock, granite gneiss, or artificial silica sand made into sand by selectively crushing only the quartz contained in pegmatite. It may be artificial silica sand.
본 발명에 따른 퍼티용 시멘트 조성물은 가장 많은 함량으로 상기 규사를 포함할 수 있다. The cement composition for putty according to the present invention may contain the silica sand in the largest amount.
하나의 예시에서, 본 발명에 따른 퍼티용 시멘트 조성물은 SiO2를 주성분으로 함유하는 규사를 주성분으로 포함할 수 있다. 상기에서 용어 "주성분으로 포함한다"는 것은 규사를 퍼티용 시멘트 조성물에 포함되는 성분 중 가장 많은 비율로 함유한다는 것은 의미하고, 예를 들면 상기 조성물은 상기 규사를 50 중량% 이상, 55 중량% 이상, 60 중량% 이상의 비율로 포함할 수 있다. 상기 규사 함량의 상한값은, 예를 들면 80 중량% 이하, 75 중량% 이하 또는 70 중량% 이하일 수 있다.In one example, the cement composition for putty according to the present invention may include silica sand containing SiO 2 as a main component as a main component. In the above, the term "included as a main component" means that the silica sand is contained in the largest proportion of the components included in the cement composition for putty, for example, the composition contains 50% by weight or more and 55% by weight or more of the silica sand. , It may be included in a ratio of 60% by weight or more. The upper limit of the silica sand content may be, for example, 80% by weight or less, 75% by weight or less, or 70% by weight or less.
본 발명에 따른 퍼티용 시멘트 조성물은, 상기 규사를 포함하되 상기 규사는 입도가 상이한 2종의 인조 규사를 포함할 수 있다.The cement composition for putty according to the present invention includes the silica sand, but the silica sand may include two types of artificial silica sand having different particle sizes.
하나의 예시에서, 본 발명에 따른 퍼티용 시멘트 조성물은 상기 규사는 제 1 입도를 가지는 제 1 인조 규사; 및 상기 제 1 인조 규사의 제 1 입도와 상이한 제 2 입도를 가지는 제 2 인조 규사를 포함할 수 있다.In one example, the cement composition for putty according to the present invention comprises: a first artificial silica sand having a first particle size of the silica sand; And it may include a second artificial silica having a second particle size different from the first particle size of the first artificial silica.
인조 규사의 종류는 색상, 성분, 입도 등에 따라 구분될 수 있는데, 본 발명에 따른 퍼티 분말은 입도가 상이한 2종의 인조 규사를 포함하는 것을 특징으로 할 수 있다. 2종의 인조 규사를 포함하는 경우, 본 발명에 따른 퍼티용 시멘트 조성물로부터 형성된 퍼티의 가사 시간 및 물리적 강도 등 물성 조절의 용이성을 확보할 수 있다.The type of artificial silica may be classified according to color, component, particle size, etc., and the putty powder according to the present invention may be characterized by including two types of artificial silica having different particle sizes. In the case of including two kinds of artificial silica sand, it is possible to ensure the ease of controlling physical properties such as pot life and physical strength of the putty formed from the cement composition for putty according to the present invention.
구체적인 예시에서, 본 발명에 따른 퍼티용 시멘트 조성물의 상기 규사는, 60 내지 80 메쉬 범위 내의 입도를 가지는 제 1 인조 규사; 및 80 내지 120 메쉬 범위 내의 입도를 가지는 제 2 인조 규사를 포함할 수 있다. 상기에서 용어 "메쉬"는 체의 구멍이나 입자의 크기를 나타내는 단위로 타일러 표준체(Tyler Standard Sieve)에서는 1 inch(인치) 길이 안에 들어 있는 눈금의 수로 나타내는 수치이고, 메쉬의 크기가 클수록 입도는 작아진다. In a specific example, the silica sand of the cement composition for putty according to the present invention, the first artificial silica sand having a particle size in the range of 60 to 80 mesh; And it may include a second artificial silica having a particle size in the range of 80 to 120 mesh. In the above, the term "mesh" is a unit representing the size of a sieve's pores or particles, and in the Tyler Standard Sieve, it is a value expressed by the number of scales within 1 inch (inch) length, and the larger the mesh size, the smaller the particle size. Lose.
보다 더 구체적인 예시에서, 본 발명에 따른 퍼티용 시멘트 조성물의 상기 규사는 메쉬 넘버 #7의 인조 규사 및 메쉬 넘버 #8의 인조 규사를 포함할 수 있다.In a more specific example, the silica sand of the cement composition for putty according to the present invention may include artificial silica sand of mesh number #7 and artificial silica sand of mesh number #8.
본 발명에 따른 퍼티용 시멘트 조성물은, 상기 규사와 함께 시멘트 성분을 포함한다.The cement composition for putty according to the present invention contains a cement component together with the silica sand.
상기 시멘트 성분은, 포틀랜드 시멘트, 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 및 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트로부터 선택되는 2종 이상 이다.The cement component is at least two selected from Portland cement, a first cement containing aluminum oxide in a range of 30 to 70% by weight, and a second cement containing calcium sulfoaluminate in a range of 25 to 45% by weight. .
상기 포틀랜드 시멘트는 소위 1종 시멘트로 불리는 것으로서, 산화칼슘(CaO), 이산화규소(SiO2), 산화알루미늄(Al2O3) 및 산화철(Fe2O3)을 함유하는 원료를 적당한 비율로 충분히 혼합하여, 그 일부가 용융하여 소결된 클링커에 적당량의 석고를 가하여 분말로 하여 제조한 시멘트를 의미한다.The Portland cement is a so-called class 1 cement, and a raw material containing calcium oxide (CaO), silicon dioxide (SiO 2 ), aluminum oxide (Al 2 O 3 ) and iron oxide (Fe 2 O 3 ) is sufficiently It refers to a cement produced by adding an appropriate amount of gypsum to a clinker that is mixed and partially melted and sintered to form a powder.
상기 제 1 시멘트는 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 것으로 업계에서 소위 알루미나 시멘트라 불리는 것일 수 있다. The first cement contains aluminum oxide in the range of 30 to 70% by weight, and may be so-called alumina cement in the industry.
구체적으로, 상기 알루미나 시멘트는 칼슘 알루미네이트를 주성분으로 함유하는 것으로서, 알루미나와 칼슘계 물질을 적정비율로 하여 용융 또는 소성시킨 후 얻어진 클링커를 미분쇄하여 분말형태로 만들어진 시멘트를 의미한다. 상기 알루미나 시멘트는 포틀랜드 시멘트의 촉진 결합제 역할을 수행하는 것으로써 최종 퍼티 제품의 목적하는 가사시간 및 압축강도 등을 조절하기 위해 채택된 구성이다. 또한, 상기 알루미나 시멘트는 화학적 저항성이 우수하며, 산성 분위기 하에서 사용할 수 있는 장점이 있는 것으로 알려져 있어, 퍼티의 백화 현상 저항성 향상에도 기여할 수 있다.Specifically, the alumina cement contains calcium aluminate as a main component, and refers to a cement made into a powder form by pulverizing the obtained clinker after melting or firing the alumina and calcium-based material in an appropriate ratio. The alumina cement serves as an accelerating binder for Portland cement, and is a configuration adopted to control the desired pot life and compressive strength of the final putty product. In addition, the alumina cement has excellent chemical resistance and is known to have an advantage of being able to be used in an acidic atmosphere, and thus it may contribute to improving the resistance to whitening of putty.
상기 제 1 시멘트의 산화알루미늄 함량은, 30 내지 70 중량%의 범위 내에서 조절될 수 있는데, 예를 들면 상기 제 1 시멘트는 산화알루미늄을 30 내지 60 중량% 또는 30 내지 50 중량%의 범위 내로 포함할 수 있다. The aluminum oxide content of the first cement may be adjusted within the range of 30 to 70% by weight, for example, the first cement contains aluminum oxide in the range of 30 to 60% by weight or 30 to 50% by weight can do.
상기 제 2 시멘트는 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함한다. 상기 칼슘 설포알루미네이트는 3CaO·3Al2O3·CaSO4 과 같은 화학식을 가지는 무기질계 초속경 재료로서 물과 접촉할 때 순식간에 물과 반응하여 에트린가이트(Ettringite) 수화물을 생성함으로써, 시멘트와 혼합할 때 수일 혹은 수 십일에 얻어지는 일반 포틀랜드 시멘트의 압축강도를 수 시간 내에 얻을 수 있게 하는 역할을 수행하는 것으로 알려져 있다. The second cement contains calcium sulfoaluminate in the range of 25 to 45% by weight. The calcium sulfoaluminate is an inorganic ultrafast hard material having the same formula as 3CaO·3Al 2 O 3 ·CaSO 4 and reacts with water in an instant when it comes into contact with water to produce ethringite hydrate, thereby producing cement and It is known to play a role in obtaining the compressive strength of general Portland cement obtained in days or dozens of days when mixing within a few hours.
제 2 시멘트의 칼슘 설포알루미네이트 함량은 25 내지 45 중량%의 범위 내에서 조절된다. 상기 범위 내의 칼슘 설포알루미네이트의 함량을 가지는 제 2 시멘트를 이용하여야만, 본 발명에 따른 조성물은 수성 페인트와 혼화되어 상기 수성 페인트를 응고시키고, 궁극적으로 퍼티 제품으로서의 목적하는 가사시간 및 물리적 강도를 달성할 수 있다. 만약, 칼슘 설포알루미네이트의 함량이 제 2 시멘트 내에서 25 중량%에 미치지 못하는 경우 퍼티 제품으로의 사용이 곤란해질 정도의 물성을 가질 수 있고, 칼슘 설포알루미네이트의 함량이 제 2 시멘트 내에서 45 중량%를 초과하는 경우 취급 용이성이 저하되고 흙손 시공 작업성이 열악해지며 퍼티의 제작 단가가 상승하는 문제점을 가져올 수 있어 바람직하지 않다.The calcium sulfoaluminate content of the second cement is adjusted within the range of 25 to 45% by weight. Only by using a second cement having a content of calcium sulfoaluminate within the above range, the composition according to the present invention is mixed with a water-based paint to solidify the water-based paint, and ultimately achieve the desired pot life and physical strength as a putty product. can do. If the content of calcium sulfoaluminate is less than 25% by weight in the second cement, it may have properties such that it becomes difficult to use as a putty product, and the content of calcium sulfoaluminate is 45 in the second cement. If it exceeds the weight %, handling ease is lowered, the trowel construction workability is poor, and the production cost of putty may increase, which is not preferable.
다른 예시에서, 상기 제 2 시멘트는 칼슘 설포알루미네이트를 30 내지 40 중량% 또는 32 내지 의 38 중량%의 범위 내로 포함할 수 있다.In another example, the second cement may contain calcium sulfoaluminate in the range of 30 to 40% by weight or 32 to 38% by weight.
상기 시멘트 성분은 전술한 포틀랜드 시멘트, 제 1 시멘트 및 제 2 시멘트 중 적어도 2종의 시멘트를 포함한다.The cement component includes at least two of the aforementioned Portland cement, the first cement and the second cement.
하나의 예시에서, 상기 시멘트 성분은 포틀랜드 시멘트와 제 1 시멘트 또는 제 2 시멘트를 포함할 수 있고, 다른 예시에서, 상기 시멘트 성분은 포틀랜드 시멘트, 제 1 시멘트 및 제 2 시멘트 모두를 포함할 수 있으며, 포틀랜드 시멘트, 제 1 시멘트 및 제 2 시멘트를 모두 포함하는 것이 퍼티 제품의 목적하는 가사시간 및 압축 강도 등을 확보하면서, 흙손 작업성 및 백화 현상 저항성을 향상시킴에 있어 바람직하다.In one example, the cement component may include Portland cement and the first cement or the second cement, and in another example, the cement component may include both Portland cement, the first cement and the second cement, It is preferable to include Portland cement, the first cement, and the second cement in order to improve the trowel workability and whitening resistance while securing the desired pot life and compressive strength of the putty product.
구체적으로, 상기 시멘트 성분은 상기 포틀랜드 시멘트, 상기 제 1 시멘트 및 상기 제 2 시멘트를 포함할 수 있고, 이 경우 퍼티용 시멘트 조성물은 SiO2를 주성분으로 함유하는 규사를 주성분으로 포함할 수 있다.Specifically, the cement component may include the Portland cement, the first cement, and the second cement, and in this case, the cement composition for putty may include silica sand containing SiO 2 as a main component as a main component.
구체적인 예시에서, 본 발명에 따른 퍼티용 시멘트 조성물은 SiO2를 주성분으로 함유하는 규사 50 내지 70 중량부; 포틀랜드 시멘트 5 내지 20 중량부; 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 5 내지 15 중량부; 및 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트 5 내지 15 중량부를 포함할 수 있다.In a specific example, the cement composition for putty according to the present invention comprises 50 to 70 parts by weight of silica sand containing SiO 2 as a main component; 5 to 20 parts by weight of Portland cement; 5 to 15 parts by weight of the first cement containing aluminum oxide in the range of 30 to 70% by weight; And 5 to 15 parts by weight of a second cement containing calcium sulfoaluminate in the range of 25 to 45% by weight.
한편, 상기 규사는 전술한 제 1 인조 규사 및 제 2 인조 규사를 포함할 수 있다. 따라서, 상기 퍼티용 시멘트 조성물은 60 내지 80 메쉬 범위 내의 입도를 가지는 제 1 인조 규사 20 내지 45 중량부; 80 내지 120 메쉬 범위 내의 입도를 가지는 제 2 인조 규사 30 내지 45 중량부; 포틀랜드 시멘트 10 내지 20 중량부; 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 5 내지 15 중량부; 및 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트 5 내지 15 중량부를 포함할 수 있다. 이 경우, 퍼티용 시멘트 조성물은 하기 수식 2를 만족할 수 있다.Meanwhile, the silica sand may include the first artificial silica sand and the second artificial silica sand described above. Accordingly, the cement composition for putty may include 20 to 45 parts by weight of the first artificial silica sand having a particle size in the range of 60 to 80 mesh; 30 to 45 parts by weight of the second artificial silica sand having a particle size in the range of 80 to 120 mesh; Portland cement 10 to 20 parts by weight; 5 to 15 parts by weight of the first cement containing aluminum oxide in the range of 30 to 70% by weight; And 5 to 15 parts by weight of a second cement containing calcium sulfoaluminate in the range of 25 to 45% by weight. In this case, the cement composition for putty may satisfy Equation 2 below.
[수식 2][Equation 2]
A<B<CA<B<C
상기 수식 2에서 A는 상기 제 1 시멘트 혹은 상기 제 2 시멘트의 조성물 내 함량(g)이고, B는 상기 포틀랜드 시멘트의 조성물 내 함량(g)이며, C는 제 1 시멘트 및 제 2 시멘트의 조성물 내 함량(g)의 합이다.In Equation 2, A is the content (g) in the composition of the first cement or the second cement, B is the content (g) in the composition of the Portland cement, and C is the composition of the first cement and the second cement. It is the sum of the content (g).
상기 수식 2는, 시멘트 성분의 베이스 시멘트인 포틀랜드 시멘트의 조성물 내 함량이 제 1 시멘트 및 제 2 시멘트 각각의 조성물 내 함량보다 많아야 하고, 제 1 및 제 2 시멘트의 조성물 내 함량의 합보다는 적은 비율로 조성물 내에 포함되어야 함을 의미한다.In Equation 2, the content in the composition of Portland cement, which is the base cement of the cement component, must be greater than the content in the composition of each of the first cement and the second cement, and in a ratio less than the sum of the content in the composition of the first and second cements. It means to be included in the composition.
포틀랜드 시멘트 함량 대비 제 1 시멘트 또는 제 2 시멘트의 함량을 조성물 내에 더 많이 포함시킬 경우 최종 퍼티 제품의 목적하는 가사시간 및 압축 강도를 달성하기 곤란할 수 있고 또한 흙손 시공 작업성이 열악해질 수 있고, 포틀랜드 시멘트 함량을 제 1 및 제 2 시멘트 함량의 합보다 더 많이 포함시킬 경우 흙손 시공 작업성이 열악에 해짐과 동시에 백화 현상 억제능이 저하되는 문제가 유발될 수 있어 바람직하지 않다.When the content of the first cement or the second cement is included in the composition more than the Portland cement content, it may be difficult to achieve the desired pot life and compressive strength of the final putty product, and the trowel construction workability may be poor. If the cement content is more than the sum of the first and second cement content, it is not preferable that the trowel construction workability is deteriorated and the ability to suppress whitening phenomenon may be deteriorated.
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 상기 수식 2를 만족함과 동시에 하기 수식 3을 만족할 수 있다.The cement composition for putty according to the present invention may also satisfy Equation 3 below while satisfying Equation 2 above.
[수식 3][Equation 3]
D<E<FD<E<F
상기 수식 3에서 D는 상기 제 1 시멘트의 조성물 내 함량(g)이고, E는 상기 제 2 시멘트의 조성물 내 함량(g)이며, F는 상기 포틀랜드 시멘트의 조성물 내 함량(g)이다.In Equation 3, D is the content in the composition of the first cement (g), E is the content in the composition of the second cement (g), and F is the content in the composition of Portland cement (g).
상기 수식 3은 시멘트 성분에 포함되는 포틀랜드 시멘트, 제 1 시멘트 및 제 2 시멘트의 조성물 내 함량이 포틀랜드 시멘트, 제 2 시멘트 및 제 1 시멘트 순으로 높아야 함을 의미한다. Equation 3 means that the content of Portland cement, the first cement, and the second cement contained in the cement component should be higher in the order of Portland cement, the second cement, and the first cement.
즉, 본 발명에 따른 퍼티용 시멘트 조성물에 포함되는 시멘트 성분은 포틀랜드 시멘트, 제 1 시멘트 및 제 2 시멘트를 포함하되, 포틀랜드 시멘트를 가장 많은 함량으로 포함하고, 제 2 시멘트를 그 다음 많은 함량으로 포함하며, 제 1 시멘트를 가장 적은 함량으로 포함할 수 있다. That is, the cement component included in the cement composition for putty according to the present invention includes Portland cement, the first cement, and the second cement, but includes Portland cement in the highest content, and the second cement in the next highest content. And, it may contain the lowest amount of the first cement.
본 발명에 따른 퍼티용 시멘트 조성물은 수성 페인트와 혼화되어 형성된 퍼티 제품의 적정 물성 확보와 퍼티의 백화 현상을 효과적으로 방지하고 흙손 시공 작업성의 우수성을 확보하기 위해 포틀랜드 시멘트, 제 1 시멘트 및 제 2 시멘트를 포함하는 시멘트 성분을 적정 비율로 포함하는데, 상기 조성물 내에서 포틀랜드 시멘트, 제 2 시멘트 및 제 1 시멘트 순으로 함량을 조절하는 것이 전술한 목적 및 효과를 모두 달성하는데 있어 바람직하다. 즉, 상기 수식 3을 만족하는 퍼티용 시멘트 조성물의 수성 페인트과의 혼화 및 응고물인 퍼티는 백화 현상 방지와 흙손 시공 작업성의 우수성을 가질 수 있고 동시에 적정 가사시간 및 압축 강도 등 적정 물성을 효과적으로 확보할 수 있다.The cement composition for putty according to the present invention uses Portland cement, first cement and second cement in order to secure proper physical properties of putty products formed by mixing with water-based paint, effectively prevent whitening of putty, and secure excellence in trowel construction. The cement component to be included is included in an appropriate ratio, and it is preferable to control the content in the order of Portland cement, the second cement, and the first cement in the composition to achieve all of the above-described objects and effects. That is, the putty, which is a mixture and coagulation of the cement composition for putty satisfying Equation 3, with water-based paint can prevent whitening and have excellent trowel construction workability, and at the same time, can effectively secure appropriate physical properties such as appropriate pot life and compressive strength. have.
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 석고 5 내지 10 중량부를 더 포함할 수 있다. 상기 석고는 퍼티에 적정 강성을 부여하거나 수성 페인트와 퍼티 용 시멘트 조성물과의 혼화에 따른 응결 혹은 응고 속도 및 강도를 조절하는 역할을 수행할 수 있다.The cement composition for putty according to the present invention may further include 5 to 10 parts by weight of gypsum. The gypsum may play a role of imparting appropriate rigidity to the putty or controlling a setting or solidification rate and strength according to mixing of a water-based paint and a cement composition for putty.
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 전술한 성분 이외에 소포제, 산화 방지제, 섬유사, 리? 카보네이트, 점증제, 메틸 셀룰로오즈 또는 분말 방수제 등의 각종 첨가제를 더 포함할 수 있다.Cement composition for putty according to the present invention is also, in addition to the above-described components, defoaming agent, antioxidant, fiber yarn, li? It may further contain various additives such as carbonate, thickener, methyl cellulose or powder waterproofing agent.
하나의 예시에서, 본 발명에 따른 퍼티용 시멘트 조성물은 타타르산, 말산, 락트산, 시트르산 및 숙신산으로 이루어진 군에서 선택되는 어느 하나의 유기산을 포함하는 산화 방지제 0.01 내지 0.5 중량부를 더 포함할 수 있다.In one example, the cement composition for putty according to the present invention may further include 0.01 to 0.5 parts by weight of an antioxidant containing any one organic acid selected from the group consisting of tartaric acid, malic acid, lactic acid, citric acid and succinic acid.
본 발명에 따른 퍼티용 시멘트 조성물은, 또한 소포제 0.001 내지 0.1 중량부를 더 포함할 수 있다.The cement composition for putty according to the present invention may further include 0.001 to 0.1 parts by weight of an antifoaming agent.
본 발명에 따른 퍼티용 시멘트 조성물은, 또한 Li2CO3 0.01 내지 0.1 중량부를 더 포함할 수 있다.The cement composition for putty according to the present invention may further include 0.01 to 0.1 parts by weight of Li 2 CO 3 .
본 발명에 따른 퍼티용 시멘트 조성물은 또한, 면사, 아크릴사, 유리섬유사 또는 탄소섬유사 0.1 내지 0.5 중량부를 더 포함할 수 있다.The cement composition for putty according to the present invention may further include 0.1 to 0.5 parts by weight of cotton yarn, acrylic yarn, glass fiber yarn, or carbon fiber yarn.
본 발명에 따른 퍼티용 시멘트 조성물은, 예를 들면 분말상 또는 입자상 일 수 있다.The cement composition for putty according to the present invention may be in the form of powder or particles, for example.
본 발명에 따른 퍼티용 시멘트 조성물은 전술한 성분들의 조합을 통해, 내외부 퍼티 및 에폭시 퍼티와 유사한 물리적 강도 및 가사시간을 가지면서 흙손 시공 작업성이 우수하고 백화 현상에 대한 저항성이 뛰어나며, 동시에 폐기 예정인 수성 폐페인트를 활용함으로써 제품 단가 절감을 유도할 수 있는 퍼티를 제조하는데 이용될 수 있다.The cement composition for putty according to the present invention has a physical strength and pot life similar to that of internal and external putty and epoxy putty through the combination of the above-described components, has excellent trowel construction workability, excellent resistance to whitening, and is scheduled to be discarded at the same time. It can be used to manufacture putty that can induce product cost reduction by using water-based waste paint.
본 발명은 또한, 상기 퍼티용 시멘트 조성물을 포함하는 퍼티에 대한 것이다.The present invention also relates to a putty comprising the cement composition for putty.
본 발명에 따른 퍼티는 수성 페인트와 퍼티용 시멘트 조성물을 필수 성분으로 포함하되, 두 성분의 함량을 각각 40 내지 60 중량부의 범위 내로 조절한다. 즉, 본 발명에 따른 퍼티는 퍼티용 시멘트 조성물 40 내지 60 중량부; 및 수성 페인트 40 내지 60 중량부로 이루어진다. The putty according to the present invention includes a water-based paint and a cement composition for putty as essential components, and the contents of the two components are adjusted within the range of 40 to 60 parts by weight, respectively. That is, the putty according to the present invention is 40 to 60 parts by weight of a cement composition for putty; And 40 to 60 parts by weight of a water-based paint.
상기 수성 페인트와 퍼티용 시멘트 조성물의 퍼티 내 함량은, 최종 혼화되어 형성된 퍼티의 물리적 강도를 결정하고, 궁극적으로 퍼티 제품으로 적합한 물성을 가지는지 여부를 결정할 수 있다. The content of the water-based paint and the cement composition for putty in the putty may determine the physical strength of the putty formed by final mixing, and ultimately, whether or not it has suitable physical properties as a putty product.
즉, 본 발명에 따른 퍼티 내 수성 페인트를 40 중량부 미만으로 포함하는 경우 가사시간이 지나치게 짧아서 취급이 곤란하거나 흙손 시공 작업성이 저하될 수 있고, 퍼티 내 수성 페인트를 60 중량부를 초과하여 포함하는 경우 압축 강도가 저하되어 퍼티 제품으로 이용하는 것 자체가 곤란해질 수 있어 바람직하지 않다. That is, if the water-based paint in the putty according to the present invention is included in an amount of less than 40 parts by weight, the pot life is too short, so handling may be difficult or the trowel construction workability may be deteriorated. In this case, the compressive strength is lowered, making it difficult to use as a putty product, which is not preferable.
마찬가지로, 본 발명에 따른 퍼티가 퍼티용 시멘트 조성물을 40 중량부 미만으로 포함하는 경우 퍼티 제품으로의 사용이 곤란해질 정도의 물성을 가질 수 있고, 퍼티가 퍼티용 시멘트 조성물을 60 중량부를 초과하여 포함하는 경우 취급 용이성이 저하되고 흙손 시공 작업성이 열악해질 수 있어 바람직하지 않다.Similarly, when the putty according to the present invention contains less than 40 parts by weight of the cement composition for putty, it may have physical properties such that it becomes difficult to use as a putty product, and the putty contains more than 60 parts by weight of the cement composition for putty. In this case, it is not preferable because the ease of handling may decrease and the workability of trowel construction may be poor.
본 발명에 따른 퍼티는 또한, 하기 수식 4 및 5를 만족한다.The putty according to the present invention also satisfies the following equations 4 and 5.
[수식 4][Equation 4]
3 N/mm2 ≤ Cs ≤ 10 N/mm2 3 N/mm 2 ≤ Cs ≤ 10 N/mm 2
[수식 5][Equation 5]
20 min ≤ Pf ≤ 40 min20 min ≤ P f ≤ 40 min
상기 수식 4에서, Cs는 KS L ISO 679법에 의해 측정한 상기 퍼티의 1일 양생 후 압축 강도(N/mm2)를 의미하고, 상기 수식 5에서 Pf는 퍼티의 가사시간(min)을 의미한다.In Equation 4, Cs refers to the compressive strength (N/mm 2 ) of the putty measured by the KS L ISO 679 method after 1 day curing, and in Equation 5, P f is the pot life (min) of the putty. it means.
본 발명에 따른 퍼티가 상기 수식 4를 만족한다는 것은, KS L ISO 679법에 의해 측정한 1일 양생 후 측정한 퍼티의 압축 강도를 3 내지 10N/mm2의 범위 내로 유지한다는 것을 의미한다.That the putty according to the present invention satisfies Equation 4 means that the compressive strength of the putty measured after 1 day curing measured by the KS L ISO 679 method is maintained within the range of 3 to 10 N/mm 2 .
다른 예시에서, 본 발명에 따른 퍼티는 KS L ISO 679법에 의해 측정한 1일 양생 후 압축 강도가 3 내지 8N/mm2 또는 3 내지 6N/mm2의 범위 내에 있을 수 있다.In another example, the putty according to the present invention has a compressive strength of 3 to 8 N/mm 2 after 1 day curing measured by the KS L ISO 679 method or It may be in the range of 3 to 6N/mm 2 .
또한, 본 발명에 따른 퍼티가 상기 수식 5를 만족한다는 것은, 퍼티의 가사시간을 20분 내지 40분의 범위 내로 조절한다는 것을 의미한다. Further, that the putty according to the present invention satisfies Equation 5 means that the pot life of the putty is adjusted within the range of 20 minutes to 40 minutes.
다른 예시에서, 본 발명에 따른 퍼티는 가사 시간이 25 내지 40분 또는 30 내지 40분의 범위 내에 있을 수 있다.In another example, the putty according to the present invention may have a pot life in the range of 25 to 40 minutes or 30 to 40 minutes.
본 발명에 따른 퍼티는, 또한, 하기 수식 6을 만족할 수 있다.The putty according to the present invention may also satisfy Equation 6 below.
[수식 6][Equation 6]
90g ≤ G ≤ 130g90g ≤ G ≤ 130g
상기 수식 6에서, G는 퍼티에 포함되는 퍼티 분말 100g 대비 수성 페인트의 중량(g)을 의미한다. In Equation 6, G means the weight (g) of the water-based paint relative to 100 g of putty powder included in the putty.
본 발명에 따른 퍼티가 상기 수식 6을 만족한다는 것은 퍼티용 시멘트 조성물 100 중량부 기준 수성 페인트를 90 내지 130 중량부 범위 내로 포함할 수 있음을 의미하고, 구체적으로 본 발명에 따른 퍼티가 수성 페인트 47.3 중량% 내지 56.5 중량% 및 퍼티용 시멘트 조성물 43.4 중량% 내지 52.6 중량%로 이루어질 수 있음을 의미한다.That the putty according to the present invention satisfies Equation 6 means that the putty can contain a water-based paint in the range of 90 to 130 parts by weight based on 100 parts by weight of the cement composition, and specifically, the putty according to the present invention is water-based paint 47.3 It means that it may consist of a weight% to 56.5% by weight and a cement composition for putty 43.4% to 52.6% by weight.
퍼티용 시멘트 조성물 100g 대비 수성 페인트 함량이 90g에 미치지 못하는 경우 흙손 시공 작업성이 열악해지거나 가사시간이 지나치게 짧아지는 등의 문제가 발생할 수 있고, 퍼티용 시멘트 조성물 100g 대비 수성 페인트 함량이 130g을 초과하는 경우 흙손 시공 작업성이 열악해지거나 압축강도가 퍼티 제품의 기준 스펙을 충족하지 못할 수 있어 바람직하지 아니하다.If the amount of water-based paint compared to 100 g of putty cement composition is less than 90 g, problems such as poor trowel construction workability or too short pot life may occur, and the content of water-based paint compared to 100 g of putty cement composition exceeds 130 g In this case, the trowel construction workability may be poor or the compressive strength may not meet the standard specifications of the putty product, which is not desirable.
본 발명에 따른 퍼티는 특히, 상기 수식 6의 G가 120g일 경우, 구체적으로 퍼티용 시멘트 조성물 100g 대비 수성 페인트 120g이 첨가될 경우에 흙손 시공 작업성이 가장 양호할 수 있고, 적정 압축 강도 및 가사시간을 확보할 수 있으며, 백화 현상 억제 효과 또한 유지될 수 있다.The putty according to the present invention may have the best trowel construction workability, particularly when the G of Formula 6 is 120 g, and specifically, when 120 g of water-based paint is added compared to 100 g of the cement composition for putty, and appropriate compressive strength and housework Time can be secured, and the effect of suppressing whitening can also be maintained.
이하, 본 발명에 따른 퍼티용 시멘트 조성물 및 이를 포함하는 퍼티에 대해 실시예 및 비교예를 들어 보다 구체적으로 설명하나, 하기 예시들은 본 발명에 따른 일례에 불과할 뿐 하기 예시들이 본 발명에 따른 퍼티용 시멘트 조성물 및 퍼티의 권리범위나 기술적 사상을 제한하는 것인 아님은 이 기술분야의 통상의 지식을 가진 사람에게 자명하다.Hereinafter, the cement composition for putty according to the present invention and the putty including the same are described in more detail with examples and comparative examples, but the following examples are only examples according to the present invention, and the following examples are for putty according to the present invention. It is obvious to those of ordinary skill in the art that it is not to limit the scope or technical idea of the cement composition and putty.
[실시예 1 내지 3] - 퍼티용 시멘트 조성물(A1 내지 A3) 제조
하기 표 1에 도시되어 있는 조성을 혼합, 교반하여 퍼티용 시멘트 조성물(A1 내지 A3)을 각각 제조하였다.
[비교예 1 및 4] - 퍼티용 시멘트 조성물(B1 내지 B4) 제조
하기 표 1에 도시되어 있는 조성을 혼합, 교반하여 퍼티용 시멘트 조성물(B1 내지 B4)을 각각 제조하였다.
[실험예] - 퍼티의 흙손 시공성, 가사시간 및 압축 강도 측정
실시예 및 비교예에 따른 퍼티용 시멘트 조성물 100g과 수성 페인트(삼화페인트공업(주) 社, 아이생각 수성외부프로)를 적정 비율로 혼합 교반하고 시간에 지남에 따른 응고 상태 및 최종 응고물이 퍼티 제품으로 적합한지 여부를 판단하기 위해 가사시간를 측정하였고, 최종 응고물을 이용하여 흙손 시공을 실시하였다 (도 1 및 2 참조). 또한, KS L ISO 679법에 의해 1일 양생 후 압축 강도를 측정하였고, 최종 응고물을 수분에 노출시켜 백화 현상이 발생하는지를 측정하였으며, 그 결과를 아래 표 3에 나타내었다.
(분)
(N/mm2)
상기 표 3에 나타난 바와 같이, 본 발명에 따른 퍼티용 시멘트 조성물과 수성 페인트를 적정 함량비로 혼화하여 형성된 퍼티의 경우, 적정 가사시간 및 압축 강도를 가지면서, 흙손 시공성이 우수하고 백화 현상 저항성이 매우 양호함을 확인할 수 있었다. 반면에, 본 발명에 다른 퍼티용 시멘트 조성물 중 어느 하나를 포함하지 아니하거나 (실험예 4 및 5), 시멘트 성분의 함량 비율이 적정 범위 내로 조절되지 아니한 시멘트 조성물을 이용하거나 (실험예 6 및 7), 또는 수성 페인트와의 함량이 적절히 조절되지 아니한 퍼티 제품(실험예 8 및 9)의 경우, 적정 가사시간 및 압축 강도를 가지지 못하거나, 흙손 시공성 또는 백화 현상 저항성이 열악한 것으로 확인되었다.[Examples 1 to 3]-Preparation of cement compositions for putty (A1 to A3)
The compositions shown in Table 1 were mixed and stirred to prepare cement compositions (A1 to A3) for putty, respectively.
[Comparative Examples 1 and 4]-Preparation of cement compositions for putty (B1 to B4)
The compositions shown in Table 1 were mixed and stirred to prepare cement compositions for putty (B1 to B4), respectively.
[Experimental Example]-Measurement of putty trowel workability, pot life and compressive strength
100g of a cement composition for putty according to Examples and Comparative Examples and a water-based paint (Samhwa Paint Industry Co., Ltd., Isaenggak Water-based External Pro) were mixed and stirred at an appropriate ratio, and the solidified state and final solidified material over time was putty. Pot life was measured to determine whether it was suitable as a product, and trowel construction was performed using the final solidified material (see FIGS. 1 and 2). In addition, the compressive strength was measured after 1 day curing according to the KS L ISO 679 method, and it was measured whether whitening occurs by exposing the final coagulated product to moisture, and the results are shown in Table 3 below.
(minute)
(N/mm 2 )
As shown in Table 3, in the case of the putty formed by mixing the cement composition for putty and the water-based paint according to the present invention at an appropriate content ratio, it has an appropriate pot life and compressive strength, excellent trowel workability, and very whitening resistance. It was confirmed that it was good. On the other hand, the present invention does not contain any one of the other cement composition for putty (Experimental Examples 4 and 5), or a cement composition in which the content ratio of the cement component is not adjusted within an appropriate range (Experimental Examples 6 and 7 ), or in the case of the putty product (Experimental Examples 8 and 9) in which the content of the water-based paint was not properly controlled, it was confirmed that it did not have an appropriate pot life and compressive strength, or had poor trowel workability or whitening resistance.
Claims (15)
포틀랜드 시멘트, 산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 및 칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트를 포함하는 시멘트 성분을 포함하고,
상기 규사는,
60 내지 80 메쉬 범위 내의 입도를 가지는 제 1 인조 규사; 및
80 내지 120 메쉬 범위 내의 입도를 가지는 제 2 인조 규사를 포함하며,
수성 페인트와 혼화되어 상기 수성 페인트를 응고시킴으로써 상기 수성 페인트와 함께 하기 수식 1을 만족하는 퍼티를 형성하는 퍼티용 시멘트 조성물:
[수식 1]
3 N/mm2 ≤ Cs ≤ 10 N/mm2
상기 수식 1에서, Cs는 KS L ISO 679법에 의해 측정한 상기 퍼티의 1일 양생 후 압축 강도를 의미한다. Silica sand containing 80% by weight or more of SiO 2 ; And
Portland cement, comprising a cement component comprising a first cement comprising aluminum oxide in the range of 30 to 70% by weight, and a second cement comprising calcium sulfoaluminate in the range of 25 to 45% by weight,
The silica sand,
A first artificial silica sand having a particle size in the range of 60 to 80 mesh; And
It includes a second artificial silica sand having a particle size in the range of 80 to 120 mesh,
A cement composition for putty that is mixed with a water-based paint to solidify the water-based paint to form a putty that satisfies the following formula 1 with the water-based paint:
[Equation 1]
3 N/mm 2 ≤ Cs ≤ 10 N/mm 2
In Equation 1, Cs refers to the compressive strength of the putty measured by the KS L ISO 679 method after 1 day curing.
60 내지 80 메쉬 범위 내의 입도를 가지는 제 1 인조 규사 20 내지 45 중량부;
80 내지 120 메쉬 범위 내의 입도를 가지는 제 2 인조 규사 30 내지 45 중량부;
포틀랜드 시멘트 10 내지 20 중량부;
산화알루미늄을 30 내지 70 중량%의 범위 내로 포함하는 제 1 시멘트 5 내지 15 중량부; 및
칼슘 설포알루미네이트를 25 내지 45 중량%의 범위 내로 포함하는 제 2 시멘트 5 내지 15 중량부를 포함하고,
하기 수식 2를 만족하는 퍼티용 시멘트 조성물:
[수식 2]
A<B<C
상기 수식 2에서 A는 상기 제 1 시멘트 혹은 상기 제 2 시멘트의 조성물 내 함량(g)이고, B는 상기 포틀랜드 시멘트의 조성물 내 함량(g)이며, C는 제 1 시멘트 및 제 2 시멘트의 조성물 내 함량(g)의 합이다.The method of claim 1,
20 to 45 parts by weight of the first artificial silica sand having a particle size in the range of 60 to 80 mesh;
30 to 45 parts by weight of the second artificial silica sand having a particle size in the range of 80 to 120 mesh;
Portland cement 10 to 20 parts by weight;
5 to 15 parts by weight of the first cement containing aluminum oxide in the range of 30 to 70% by weight; And
Including 5 to 15 parts by weight of a second cement containing calcium sulfoaluminate in the range of 25 to 45% by weight,
Cement composition for putty satisfying the following Formula 2:
[Equation 2]
A<B<C
In Equation 2, A is the content (g) in the composition of the first cement or the second cement, B is the content (g) in the composition of the Portland cement, and C is the composition of the first cement and the second cement. It is the sum of the content (g).
하기 수식 3을 만족하는 퍼티용 시멘트 조성물:
[수식 3]
D<E<F
상기 수식 3에서 D는 상기 제 1 시멘트의 조성물 내 함량(g)이고, E는 상기 제 2 시멘트의 조성물 내 함량(g)이며, F는 상기 포틀랜드 시멘트의 조성물 내 함량(g)이다.The method of claim 2,
Cement composition for putty satisfying the following Formula 3:
[Equation 3]
D<E<F
In Equation 3, D is the content in the composition of the first cement (g), E is the content in the composition of the second cement (g), and F is the content in the composition of Portland cement (g).
석고 5 내지 10 중량부를 더 포함하는 퍼티용 시멘트 조성물.The method of claim 1,
Cement composition for putty further comprising 5 to 10 parts by weight of gypsum.
타타르산, 말산, 락트산, 시트르산 및 숙신산으로 이루어진 군에서 선택되는 어느 하나의 유기산을 포함하는 산화 방지제 0.01 내지 0.5 중량부를 더 포함하는 퍼티용 시멘트 조성물.The method of claim 1,
A cement composition for putty further comprising 0.01 to 0.5 parts by weight of an antioxidant containing any one organic acid selected from the group consisting of tartaric acid, malic acid, lactic acid, citric acid and succinic acid.
소포제 0.001 내지 0.1 중량부를 더 포함하는 퍼티용 시멘트 조성물.The method of claim 1,
A cement composition for putty further comprising 0.001 to 0.1 parts by weight of an antifoam.
Li2CO3 0.01 내지 0.1 중량부를 더 포함하는 퍼티용 시멘트 조성물.The method of claim 1,
Cement composition for putty further comprising 0.01 to 0.1 parts by weight of Li 2 CO 3 .
면사, 아크릴사, 유리섬유사 또는 탄소섬유사 0.1 내지 0.5 중량부를 더 포함하는 퍼티용 시멘트 조성물.The method of claim 1,
Cement composition for putty further comprising 0.1 to 0.5 parts by weight of cotton yarn, acrylic yarn, glass fiber yarn or carbon fiber yarn.
수성 페인트 40 내지 60 중량부로 이루어지고,
하기 수식 4 및 5를 만족하는 퍼티:
[수식 4]
3 N/mm2 ≤ Cs ≤ 10 N/mm2
[수식 5]
20 min ≤ Pf ≤ 40 min
상기 수식 4에서, Cs는 KS L ISO 679법에 의해 측정한 상기 퍼티의 1일 양생 후 압축 강도(N/mm2)를 의미하고, 상기 수식 5에서 Pf는 퍼티의 가사시간(min)을 의미한다.40 to 60 parts by weight of the cement composition for putty according to claim 1; And
It consists of 40 to 60 parts by weight of water-based paint,
Putty satisfying the following formulas 4 and 5:
[Equation 4]
3 N/mm 2 ≤ Cs ≤ 10 N/mm 2
[Equation 5]
20 min ≤ P f ≤ 40 min
In Equation 4, Cs refers to the compressive strength (N/mm 2 ) of the putty measured by the KS L ISO 679 method after 1 day curing, and in Equation 5, P f is the pot life (min) of the putty. it means.
하기 수식 6을 만족하는 퍼티:
[수식 6]
90g ≤ G ≤ 130g
상기 수식 6에서, G는 퍼티에 포함되는 퍼티 분말 100g 대비 수성 페인트의 중량(g)을 의미한다. The method of claim 9,
Putty satisfying the following formula 6:
[Equation 6]
90g ≤ G ≤ 130g
In Equation 6, G means the weight (g) of the water-based paint relative to 100 g of putty powder included in the putty.
상기 수식 6에서 G가 120g인 퍼티.The method of claim 10,
In Equation 6, G is 120g.