CN105777022A - Ardealite concrete extrusion partition board and preparation method thereof - Google Patents
Ardealite concrete extrusion partition board and preparation method thereof Download PDFInfo
- Publication number
- CN105777022A CN105777022A CN201610242266.6A CN201610242266A CN105777022A CN 105777022 A CN105777022 A CN 105777022A CN 201610242266 A CN201610242266 A CN 201610242266A CN 105777022 A CN105777022 A CN 105777022A
- Authority
- CN
- China
- Prior art keywords
- parts
- ardealite
- partition plate
- cement
- tap water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an ardealite concrete extrusion partition board and a preparation method thereof. The ardealite concrete extrusion partition board is prepared from, by weight, 350-450 parts of cement, 350-450 parts of modified ardealite, 150-300 parts of river sand, 2-4 parts of polypropylene fiber, 3-5 parts of plant fiber, 8-10 parts of a water retaining agent and 230-250 parts of tap water. In this way, the ardealite concrete extrusion partition board has the advantages that energy is saved, no pollution is caused, different wastes can be brought into full play, utilization of wastes is improved, a large number of natural mineral resources are saved, environment is protected, waste materials are recycled, and the nation and the people are benefited.
Description
Technical field
The present invention relates to building material technical field, especially relate to a kind of Ardealite concrete extrusion partition plate and preparation method thereof.
Background technology
At present, the kind of the partition plate used on the market is varied, has a disadvantage in that according to investigation
1, concrete partition and clear-water concrete partition plate through exposing to the weather for a long time, drenching with rain, under the impact of the factor of natural environment such as freeze thawing, large area metope the whiting accumulation of salt in the surface soil, contraction fissure will occur, the phenomenon such as go mouldy.
2, after partition plate is installed, the surface of plate body can generate layer oxide film, after plate body is stuccoed, and rendering layer local yellowing and easy to fall off；
3, the expansion and contraction of partition plate is big, after installation, there will be crack between partition plate and partition plate, makes installation not up to standard；
4, general partition plate needs a large amount of situ wet operations to plaster, difficulty of construction is big, metope is easily generated the phenomenon such as crackle, infiltration；
5, produce concrete partition, need a large amount of natural mineral resources, and numerous rubbish and garbage, serious environment pollution can be produced.
Summary of the invention
The technical problem to be solved is: a kind of Ardealite concrete extrusion partition plate and preparation method thereof, the energy can be saved, pollution-free, capture a difficult problem in the building industry of the easy accumulation of salt in the surface soil of cement products, improved product strength, be effectively improved the weather resistance of partition plate, anti-accumulation of salt in the surface soil performance.
In order to solve above-mentioned technical problem, the technical solution used in the present invention is: providing a kind of Ardealite concrete extrusion partition plate, it includes following component and makes according to ratio of weight and number:
Cement 350～450 parts；
Modified ardealite 350～450 parts；
Fluvial sand 150～300 parts；
Polypropylene fibre 2～4 parts；
Plant fiber 3～5 parts；
Water-retaining agent 8～10 parts；
230～250 parts of tap water.
For solving the problems referred to above, the preparation method that the present invention also provides for a kind of Ardealite concrete extrusion partition plate, comprise the steps:
S1: prepare raw material；Wherein raw material includes the following component of ratio of weight and number:
Cement 350～450 parts；
Modified ardealite 350～450 parts；
Fluvial sand 150～300 parts；
Polypropylene fibre 2～4 parts；
Plant fiber 3～5 parts；
Water-retaining agent 8～10 parts；
230～250 parts of tap water；
S2: after being added sequentially to other raw materials beyond outside tap water to stir in blender, add tap water and be stirred, it is thus achieved that compound, and be discharged into feed group machine；
S3: use high pressure vacuum extruder extrusion compound, and after embossing, survey length and cutting, enter steam kiln ordinary pressure curing then kiln discharge, it is thus achieved that semi-finished product；
S4: after Surface Machining and essence cut semi-finished product, sends into sizing autoclave kiln maintenance, is finished product after kiln discharge.
The beneficial effects of the present invention is: be different from prior art, the present invention, by preparing the component of said ratio, being sufficiently stirred for by component, can prepare Ardealite concrete extrusion partition plate.By the way; Ardealite concrete of the present invention extrusion partition plate; there is the saving energy, pollution-free, the effect of different garbage can be given full play to, improve waste utilization, save a large amount of natural mineral resources, protection environment, turn waste into wealth, benefit the nation and the people.
Detailed description of the invention
By describing the technology contents of the present invention in detail, being realized purpose and effect, it is explained below in conjunction with embodiment.
The design of most critical of the present invention is in that: prepare the component of certain proportioning, makes Ardealite concrete extrusion partition plate, improves intensity, strengthen alkali resistance.
The present invention provides a kind of Ardealite concrete extrusion partition plate, and it includes following component and makes according to ratio of weight and number:
Cement 350～450 parts；
Modified ardealite 350～450 parts；
Fluvial sand 150～300 parts；
Polypropylene fibre 2～4 parts；
Plant fiber 3～5 parts；
Water-retaining agent 8～10 parts；
230～250 parts of tap water.
Specifically, except tap water, said components is added sequentially in the forced mixer of duty, compound is after stirring, stand-by tap water is added in forced mixer, stir 8～10 minutes, then the compound mixed and stirred is discharged into a constant feed group machine, stand-by；
Then, stand-by compound is extruded through high pressure vacuum extruder, after embossing, survey length and cutting technique, transports mounting plate, enters steam kiln ordinary pressure curing, and curing temperature is 60～65 degree, and curing time is 12～16 hours, then kiln discharge；
Finally, through steam press maintenance product through Surface Machining and essence cutting after, piling storehouse dress send into sizing autoclave kiln maintenance, the pressure of sizing maintenance is 0.8～1.0Mpa, and the temperature of sizing maintenance is 140～160 degree, and the time of sizing maintenance is 6～8 hours, then kiln discharge, is finished product.
Wherein, described cement is the portland cement of label 42.5R；
Described fluvial sand is natural coarse sand；
Described Plant fiber is wood fibre；
Described polypropylene fibre is mortar anti-crack fiber；
Described water-retaining agent is HPMC hydroxypropyl methyl cellulose, and viscosity is 200,000 units；
Described modified ardealite is made up according to percentage by weight of following component:
Calcium sulphate dihydrate ardealite 87.8%；
Composite exciting agent 22%, wherein waste glass powder 10%, soda 2%, rare earth chloride 0.2%；
Said components is added sequentially in pressure type blender, stirring mixing 10～15 minutes, carries out mass-and heat-transfer and excites catalytic treatment, modifiies voluntarily and makes modified ardealite.By modified ardealite, common ardealite included Organic substance and emblem amount radioelement excites catalytic treatment, reaches country's cement based regrown material environmental safety testing result.
Accordingly, the preparation method that the present invention also provides for a kind of Ardealite concrete extrusion partition plate, comprise the steps:
S1: prepare raw material；Wherein raw material includes the following component of ratio of weight and number:
Cement 350～450 parts；
Modified ardealite 350～450 parts；
Fluvial sand 150～300 parts；
Polypropylene fibre 2～4 parts；
Plant fiber 3～5 parts；
Water-retaining agent 8～10 parts；
230～250 parts of tap water；
S2: after being added sequentially to other raw materials beyond outside tap water to stir in pressure type blender, add tap water and be stirred 8～10 minutes, it is thus achieved that compound, and be discharged into feed group machine；
S3: use high pressure vacuum extruder extrusion compound, and after embossing, survey length and cutting, enter steam kiln ordinary pressure curing then kiln discharge, it is thus achieved that semi-finished product；
S4: after Surface Machining and essence cut semi-finished product, sends into sizing autoclave kiln maintenance, is finished product after kiln discharge.
Wherein, steam kiln ordinary pressure curing temperature is 60～65 degree, and curing time is 12～16 hours.
The pressure of sizing maintenance is 0.8～1.0Mpa, and the temperature of sizing maintenance is 140～160 degree, and the time of sizing maintenance is 6～8 hours.
It is described in detail below by way of specific embodiment, and the effect of concrete extrusion partition plate that the present invention makes is described.
Embodiment one:
The technical process of the present embodiment as hereinbefore, pressed row ratio of weight and number by following component and make by this enforcement median septum wall:
Cement 390 parts；
Modified ardealite 380 parts；
Fluvial sand 150 parts；
Polypropylene fibre 2 parts；
Plant fiber 3 parts；
Water-retaining agent 10 parts；
230 parts of tap water.
Embodiment two:
The technical process of the present embodiment as hereinbefore, pressed row ratio of weight and number by following component and make by this enforcement median septum wall:
Cement 380 parts；
Modified ardealite 420 parts；
Fluvial sand 150 parts；
Polypropylene fibre 2 parts；
Plant fiber 3 parts；
Water-retaining agent 10 parts；
245 parts of tap water.
Embodiment three:
The technical process of the present embodiment as hereinbefore, pressed row ratio of weight and number by following component and make by this enforcement median septum wall:
Cement 390 parts；
Modified ardealite 380 parts；
Fluvial sand 170 parts；
Polypropylene fibre 2 parts；
Plant fiber 4.5 parts；
Water-retaining agent 8.5 parts；
230 parts of tap water.
Embodiment four:
The technical process of the present embodiment as hereinbefore, pressed row ratio of weight and number by following component and make by this enforcement median septum wall:
Cement 410 parts；
Modified ardealite 360 parts；
Fluvial sand 180 parts；
Polypropylene fibre 2.5 parts；
Plant fiber 3.5 parts；
Water-retaining agent 9 parts；
235 parts of tap water.
Embodiment five:
The technical process of the present embodiment as hereinbefore, pressed row ratio of weight and number by following component and make by this enforcement median septum wall:
Cement 380 parts；
Modified ardealite 390 parts；
Fluvial sand 160 parts；
Polypropylene fibre 3 parts；
Plant fiber 4 parts；
Water-retaining agent 7.5 parts；
240 parts of tap water.
In above-mentioned 5 embodiments, except tap water, raw material is added sequentially in the forced mixer of duty, compound is after stirring, the tap water that step one is stand-by is added in forced mixer, stir 8～10 minutes, then the compound mixed and stirred is discharged into a constant feed group machine, stand-by；
Then, stand-by compound is extruded through high pressure vacuum extruder, after embossing, survey length and cutting technique, transports mounting plate, enters steam kiln ordinary pressure curing, and curing temperature is 60～65 degree, and curing time is 12～16 hours, then kiln discharge；
Finally, through steam press maintenance product through Surface Machining and essence cutting after, piling storehouse dress send into sizing autoclave kiln maintenance, the pressure of sizing maintenance is 0.8～1.0Mpa, and the temperature of sizing maintenance is 140～160 degree, and the time of sizing maintenance is 6～8 hours, then kiln discharge, is finished product.
The Ardealite concrete extrusion partition plate of the present invention, picks up that to test result as shown in the table:
Properties of product pick up survey result (detection foundation: GB/T23451-2009):
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalents utilizing description of the present invention to make, or directly or indirectly it is used in relevant technical field, all in like manner include in the scope of patent protection of the present invention.
Claims (10)
1. an Ardealite concrete extrusion partition plate, it is characterised in that it includes following component and makes according to ratio of weight and number:
Cement 350～450 parts；
Modified ardealite 350～450 parts；
Fluvial sand 150～300 parts；
Polypropylene fibre 2～4 parts；
Plant fiber 3～5 parts；
Water-retaining agent 8～10 parts；
230～250 parts of tap water.
2. Ardealite concrete according to claim 1 extrusion partition plate, it is characterised in that it includes following component and makes according to ratio of weight and number:
Cement 390 parts；
Modified ardealite 380 parts；
Fluvial sand 150 parts；
Polypropylene fibre 2 parts；
Plant fiber 3 parts；
Water-retaining agent 10 parts；
230 parts of tap water.
3. Ardealite concrete according to claim 1 extrusion partition plate, it is characterised in that it includes following component and makes according to ratio of weight and number:
Cement 380 parts；
Modified ardealite 420 parts；
Fluvial sand 150 parts；
Polypropylene fibre 2 parts；
Plant fiber 3 parts；
Water-retaining agent 10 parts；
245 parts of tap water.
4. Ardealite concrete according to claim 1 extrusion partition plate, it is characterised in that it includes following component and makes according to ratio of weight and number:
Cement 390 parts；
Modified ardealite 380 parts；
Fluvial sand 170 parts；
Polypropylene fibre 2 parts；
Plant fiber 4.5 parts；
Water-retaining agent 8.5 parts；
230 parts of tap water.
5. Ardealite concrete according to claim 1 extrusion partition plate, it is characterised in that it includes following component and makes according to ratio of weight and number:
Cement 410 parts；
Modified ardealite 360 parts；
Fluvial sand 180 parts；
Polypropylene fibre 2.5 parts；
Plant fiber 3.5 parts；
Water-retaining agent 9 parts；
235 parts of tap water.
6. Ardealite concrete according to claim 1 extrusion partition plate, it is characterised in that it includes following component and makes according to ratio of weight and number:
Cement 380 parts；
Modified ardealite 390 parts；
Fluvial sand 160 parts；
Polypropylene fibre 3 parts；
Plant fiber 4 parts；
Water-retaining agent 7.5 parts；
240 parts of tap water.
7. the Ardealite concrete extrusion partition plate according to any one of claim 1～6, it is characterised in that
Described cement is the portland cement of label 42.5R；
Described fluvial sand is natural coarse sand；
Described Plant fiber is wood fibre；
Described polypropylene fibre is mortar anti-crack fiber；
Described water-retaining agent is HPMC hydroxypropyl methyl cellulose, and viscosity is 200,000 units.
8. the Ardealite concrete extrusion partition plate according to any one of claim 1～6, it is characterised in that described modified ardealite is made up according to percentage by weight of following component:
Calcium sulphate dihydrate ardealite 87.8%；
Composite exciting agent 22%, wherein glass dust 10%, soda 2%, rare earth chloride 0.2%；
Said components is added sequentially in pressure type blender, stirring mixing 10～15 minutes, carries out mass-and heat-transfer and excites catalytic treatment, modifiies voluntarily and makes described modified ardealite.
9. the preparation method of an Ardealite concrete extrusion partition plate, it is characterised in that including:
S1: prepare raw material；Wherein raw material includes the following component of ratio of weight and number:
Cement 350～450 parts；
Modified ardealite 350～450 parts；
Fluvial sand 150～300 parts；
Polypropylene fibre 2～4 parts；
Plant fiber 3～5 parts；
Water-retaining agent 8～10 parts；
230～250 parts of tap water；
S2: after being added sequentially to other raw materials beyond tap water to stir in blender, add tap water and be stirred, it is thus achieved that compound, and be discharged into feed group machine；
S3: use high pressure vacuum extruder extrusion compound, and after embossing, survey length and cutting, enter steam kiln ordinary pressure curing then kiln discharge, it is thus achieved that semi-finished product；
S4: after Surface Machining and essence cut semi-finished product, sends into sizing autoclave kiln maintenance, is finished product after kiln discharge.
10. the preparation method that Ardealite concrete extrudes partition plate according to claim 9, it is characterised in that stir 8～10 minutes after adding tap water, it is thus achieved that compound；Steam kiln ordinary pressure curing temperature is 60～65 degree, and curing time is 12～16 hours；The pressure of sizing maintenance is 0.8～1.0Mpa, and the temperature of sizing maintenance is 140～160 degree, and the time of sizing maintenance is 6～8 hours.