CN105777022B - Ardealite concrete squeezes out partition plate and preparation method thereof - Google Patents
Ardealite concrete squeezes out partition plate and preparation method thereof Download PDFInfo
- Publication number
- CN105777022B CN105777022B CN201610242266.6A CN201610242266A CN105777022B CN 105777022 B CN105777022 B CN 105777022B CN 201610242266 A CN201610242266 A CN 201610242266A CN 105777022 B CN105777022 B CN 105777022B
- Authority
- CN
- China
- Prior art keywords
- parts
- ardealite
- partition plate
- water
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of Ardealite concretes to squeeze out partition plate and preparation method thereof, it is made including following component according to ratio of weight and number：350~450 parts of cement；350~450 parts of modified ardealite；150~300 parts of river sand；2~4 parts of polypropylene fibre；3~5 parts of plant fiber；8~10 parts of water-retaining agent；230~250 parts of tap water.Through the above way; Ardealite concrete of the present invention squeezes out partition plate; it is pollution-free with energy saving, the effect of different wastes can be given full play to, waste utilization is improved, saves a large amount of natural mineral resources, environmental protection, turn waste into wealth, benefit the nation and the people.
Description
Technical field
The present invention relates to building material technical fields, and partition plate and its system are squeezed out more particularly, to a kind of Ardealite concrete
Preparation Method.
Background technology
At present, the kind of the partition plate used on the market is varied, is had the disadvantage that according to investigation：
1st, concrete partition and clear-water concrete partition plate through a long time expose to the weather, drench with rain, the natural environments such as freeze thawing
Under the influence of factor, the whiting of large area the metope accumulation of salt in the surface soil, contraction fissure, phenomena such as going mouldy will occur.
2nd, after partition plate installation, the surface of plate body can generate layer oxide film, after plate body is stuccoed, the yellowing of rendering layer part
It is and easy to fall off；
3rd, the expansion and contraction of partition plate is big, and after installation, crack is will appear between partition plate and partition plate, makes installation not up to standard；
4th, it is existing that general partition plate needs a large amount of situ wet operations to plaster, difficulty of construction is big, metope is also easy to produce crackle, infiltration etc.
As；
5th, it produces concrete partition, need a large amount of natural mineral resources, and numerous rubbish and waste can be generated, seriously
Pollute environment.
Invention content
The technical problems to be solved by the invention are：A kind of Ardealite concrete squeezes out partition plate and preparation method thereof, can
It is energy saving, it is pollution-free, captured problem in the construction industry of the easy accumulation of salt in the surface soil of cement products, improve product strength, be effectively improved every
The weather resistance of wallboard, anti-accumulation of salt in the surface soil performance.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is：A kind of Ardealite concrete is provided to squeeze out
Partition plate, it is made including following component according to ratio of weight and number：
350~450 parts of cement；
350~450 parts of modified ardealite；
150~300 parts of river sand；
2~4 parts of polypropylene fibre；
3~5 parts of plant fiber；
8~10 parts of water-retaining agent；
230~250 parts of tap water.
To solve the above problems, the present invention also provides the preparation method that a kind of Ardealite concrete squeezes out partition plate, including
Following steps：
S1：Prepare raw material；Wherein raw material include the following component of ratio of weight and number：
350~450 parts of cement；
350~450 parts of modified ardealite；
150~300 parts of river sand；
2~4 parts of polypropylene fibre；
3~5 parts of plant fiber；
8~10 parts of water-retaining agent；
230~250 parts of tap water；
S2：Other raw material other than outside tap water are added sequentially to after being stirred evenly in blender, are added originally
Water is stirred, and obtains mixture, and be discharged into feed group machine；
S3：Using high pressure vacuum extruder extrusion mixing material, and after being embossed, surveying long and cutting, supported into steam kiln normal pressure
Shield, then kiln discharge obtain semi-finished product；
S4：After semi-finished product are cut in surface processing and fine cut, the kiln maintenance of sizing autoclave is sent into, is finished product after kiln discharge.
The beneficial effects of the present invention are：The prior art is different from, the component of the invention by preparing said ratio passes through
Component is sufficiently stirred, you can is prepared Ardealite concrete and is squeezed out partition plate.By the above-mentioned means, phosphorus stone of the present invention
Cream concrete extrusion partition plate, have it is energy saving, it is pollution-free, can give full play to different wastes effect, improve waste
Using, save a large amount of natural mineral resources, environmental protection, turn waste into wealth, benefit the nation and the people.
Specific embodiment
For the technology contents that the present invention will be described in detail, the objects and the effects, it is explained below in conjunction with embodiment.
The design of most critical of the present invention is：The component centainly matched is prepared, Ardealite concrete is made and squeezes out partition plate,
Intensity is improved, enhances alkali resistance.
The present invention provides a kind of Ardealite concrete and squeezes out partition plate, it includes following component according to ratio of weight and number system
Into：
350~450 parts of cement；
350~450 parts of modified ardealite；
150~300 parts of river sand；
2~4 parts of polypropylene fibre；
3~5 parts of plant fiber；
8~10 parts of water-retaining agent；
230~250 parts of tap water.
Specifically, in addition to tap water, said components are added sequentially in the forced mixer of working condition, mixture
After stirring, for use tap water is added into forced mixer, stirs 8~10 minutes, then will
The mixture mixed and stirred is discharged into a constant feed group machine, for use；
Then, for use mixture is squeezed out through high pressure vacuum extruder, after embossing, survey length and cutting technique, in transhipment
Supporting plate enters steam kiln ordinary pressure curing, and curing temperature is 60~65 degree, and curing time is 12~16 hours, then kiln discharge；
Finally, through the product of steam press maintenance after surface processing and fine cut are cut, stacking binning is sent into sizing autoclave kiln and is supported
Shield, the pressure of maintenance of shaping are 0.8~1.0Mpa, and the temperature for maintenance of shaping is 140~160 degree, time of maintenance of shaping is 6~
8 hours, then kiln discharge, as finished product.
Wherein, the cement is the portland cement of label 42.5R；
The river sand is natural coarse sand；
The plant fiber is wood fibre；
The polypropylene fibre is mortar anti-crack fiber；
The water-retaining agent is HPMC hydroxypropyl methyl celluloses, and viscosity is 200,000 units；
The modified ardealite is made of following component according to weight percent：
Calcium sulphate dihydrate ardealite 87.8%；
Composite exciting agent 22%, wherein waste glass powder 10%, soda ash 2%, rare earth chloride 0.2%；
Said components are added sequentially in pressure type blender, are stirred 10~15 minutes, carry out mass-and heat-transfer excitation
Modified ardealite is made in catalytic treatment, voluntarily modification.Common ardealite is included by organic matter by modified ardealite and emblem amount is put
Penetrating property element excitation catalytic treatment reaches national cement base regrown material environmental safety testing result.
Accordingly, the present invention also provides the preparation method that a kind of Ardealite concrete squeezes out partition plate, include the following steps：
S1：Prepare raw material；Wherein raw material include the following component of ratio of weight and number：
350~450 parts of cement；
350~450 parts of modified ardealite；
150~300 parts of river sand；
2~4 parts of polypropylene fibre；
3~5 parts of plant fiber；
8~10 parts of water-retaining agent；
230~250 parts of tap water；
S2：Other raw material other than outside tap water are added sequentially to after being stirred evenly in pressure type blender, then are added
Enter tap water to be stirred 8~10 minutes, obtain mixture, and be discharged into feed group machine；
S3：Using high pressure vacuum extruder extrusion mixing material, and after being embossed, surveying long and cutting, supported into steam kiln normal pressure
Shield, then kiln discharge obtain semi-finished product；
S4：After semi-finished product are cut in surface processing and fine cut, the kiln maintenance of sizing autoclave is sent into, is finished product after kiln discharge.
Wherein, steam kiln ordinary pressure curing temperature is 60~65 degree, and curing time is 12~16 hours.
The pressure of sizing maintenance is 0.8~1.0Mpa, and the temperature for maintenance of shaping is 140~160 degree, the time for maintenance of shaping
It is 6~8 hours.
It is described in detail below by way of specific embodiment, and illustrates the effect of concrete extrusion partition plate made of the present invention.
Embodiment one：
As hereinbefore, partition presses following ratio of weight and number to the technical process of the present embodiment by following component in this implementation
It is made：
390 parts of cement；
380 parts of modified ardealite；
150 parts of river sand；
2 parts of polypropylene fibre；
3 parts of plant fiber；
10 parts of water-retaining agent；
230 parts of tap water.
Embodiment two：
As hereinbefore, partition presses following ratio of weight and number to the technical process of the present embodiment by following component in this implementation
It is made：
380 parts of cement；
420 parts of modified ardealite；
150 parts of river sand；
2 parts of polypropylene fibre；
3 parts of plant fiber；
10 parts of water-retaining agent；
245 parts of tap water.
Embodiment three：
As hereinbefore, partition presses following ratio of weight and number to the technical process of the present embodiment by following component in this implementation
It is made：
390 parts of cement；
380 parts of modified ardealite；
170 parts of river sand；
2 parts of polypropylene fibre；
4.5 parts of plant fiber；
8.5 parts of water-retaining agent；
230 parts of tap water.
Example IV：
As hereinbefore, partition presses following ratio of weight and number to the technical process of the present embodiment by following component in this implementation
It is made：
410 parts of cement；
360 parts of modified ardealite；
180 parts of river sand；
2.5 parts of polypropylene fibre；
3.5 parts of plant fiber；
9 parts of water-retaining agent；
235 parts of tap water.
Embodiment five：
As hereinbefore, partition presses following ratio of weight and number to the technical process of the present embodiment by following component in this implementation
It is made：
380 parts of cement；
390 parts of modified ardealite；
160 parts of river sand；
3 parts of polypropylene fibre；
4 parts of plant fiber；
7.5 parts of water-retaining agent；
240 parts of tap water.
In above-mentioned 5 embodiments, in addition to tap water, raw material are added sequentially to the forced mixer of working condition
Interior, mixture into forced mixer by after stirring, adding for use tap water of step 1, stirring 8
~10 minutes, the mixture mixed and stirred is then discharged into a constant feed group machine, for use；
Then, for use mixture is squeezed out through high pressure vacuum extruder, after embossing, survey length and cutting technique, in transhipment
Supporting plate enters steam kiln ordinary pressure curing, and curing temperature is 60~65 degree, and curing time is 12~16 hours, then kiln discharge；
Finally, through the product of steam press maintenance after surface processing and fine cut are cut, stacking binning is sent into sizing autoclave kiln and is supported
Shield, the pressure of maintenance of shaping are 0.8~1.0Mpa, and the temperature for maintenance of shaping is 140~160 degree, time of maintenance of shaping is 6~
8 hours, then kiln discharge, as finished product.
The Ardealite concrete of the present invention squeezes out partition plate, picks up and tests that the results are shown in table below：
Properties of product, which are picked up, surveys result (detection foundation：GB/T23451-2009)：
The foregoing is merely the embodiment of the present invention, are not intended to limit the scope of the invention, every to utilize this hair
The equivalents that bright description is made directly or indirectly are used in relevant technical field, are similarly included in this hair
In bright scope of patent protection.
Claims (9)
1. a kind of Ardealite concrete squeezes out partition plate, which is characterized in that it is made including following component according to ratio of weight and number：
350~450 parts of cement；
350~450 parts of modified ardealite；
150~300 parts of river sand；
2~4 parts of polypropylene fibre；
3~5 parts of plant fiber；
8~10 parts of water-retaining agent；
230~250 parts of tap water；
The modified ardealite is made of following component according to weight percent：
Calcium sulphate dihydrate ardealite 87.8%；
Composite exciting agent 12.2%, wherein glass dust 10%, soda ash 2%, rare earth chloride 0.2%；
Said components are added sequentially in pressure type blender, are stirred 10~15 minutes, carry out mass-and heat-transfer excitation catalysis
The modified ardealite is made in processing, voluntarily modification.
2. Ardealite concrete according to claim 1 squeezes out partition plate, which is characterized in that it include following component according to
Ratio of weight and number is made：
390 parts of cement；
380 parts of modified ardealite；
150 parts of river sand；
2 parts of polypropylene fibre；
3 parts of plant fiber；
10 parts of water-retaining agent；
230 parts of tap water.
3. Ardealite concrete according to claim 1 squeezes out partition plate, which is characterized in that it include following component according to
Ratio of weight and number is made：
380 parts of cement；
420 parts of modified ardealite；
150 parts of river sand；
2 parts of polypropylene fibre；
3 parts of plant fiber；
10 parts of water-retaining agent；
245 parts of tap water.
4. Ardealite concrete according to claim 1 squeezes out partition plate, which is characterized in that it include following component according to
Ratio of weight and number is made：
390 parts of cement；
380 parts of modified ardealite；
170 parts of river sand；
2 parts of polypropylene fibre；
4.5 parts of plant fiber；
8.5 parts of water-retaining agent；
230 parts of tap water.
5. Ardealite concrete according to claim 1 squeezes out partition plate, which is characterized in that it include following component according to
Ratio of weight and number is made：
410 parts of cement；
360 parts of modified ardealite；
180 parts of river sand；
2.5 parts of polypropylene fibre；
3.5 parts of plant fiber；
9 parts of water-retaining agent；
235 parts of tap water.
6. Ardealite concrete according to claim 1 squeezes out partition plate, which is characterized in that it include following component according to
Ratio of weight and number is made：
380 parts of cement；
390 parts of modified ardealite；
160 parts of river sand；
3 parts of polypropylene fibre；
4 parts of plant fiber；
7.5 parts of water-retaining agent；
240 parts of tap water.
7. partition plate is squeezed out according to claim 1~6 any one of them Ardealite concrete, which is characterized in that
The cement is the portland cement of label 42.5R；
The river sand is natural coarse sand；
The plant fiber is wood fibre；
The polypropylene fibre is mortar anti-crack fiber；
The water-retaining agent is HPMC hydroxypropyl methyl celluloses, and viscosity is 200,000 units.
8. a kind of Ardealite concrete squeezes out the preparation method of partition plate, which is characterized in that including：
S1：Prepare raw material；Wherein raw material include the following component of ratio of weight and number：
350~450 parts of cement；
350~450 parts of modified ardealite；
150~300 parts of river sand；
2~4 parts of polypropylene fibre；
3~5 parts of plant fiber；
8~10 parts of water-retaining agent；
230~250 parts of tap water；
The modified ardealite is made of following component according to weight percent：
Calcium sulphate dihydrate ardealite 87.8%；
Composite exciting agent 12.2%, wherein glass dust 10%, soda ash 2%, rare earth chloride 0.2%；
Said components are added sequentially in pressure type blender, are stirred 10~15 minutes, carry out mass-and heat-transfer excitation catalysis
The modified ardealite is made in processing, voluntarily modification；
S2：Other raw material other than tap water are added sequentially to after being stirred evenly in blender, add tap water progress
Stirring obtains mixture, and is discharged into feed group machine；
S3：Using high pressure vacuum extruder extrusion mixing material, and after being embossed, surveying long and cutting, into steam kiln ordinary pressure curing, then
Kiln discharge obtains semi-finished product；
S4：After semi-finished product are cut in surface processing and fine cut, the kiln maintenance of sizing autoclave is sent into, is finished product after kiln discharge.
9. Ardealite concrete squeezes out the preparation method of partition plate according to claim 8, which is characterized in that adds in tap water
It stirs 8~10 minutes afterwards, obtains mixture；Steam kiln ordinary pressure curing temperature is 60~65 degree, and curing time is 12~16 hours；
The pressure of sizing maintenance is 0.8~1.0Mpa, and the temperature for maintenance of shaping is 140~160 degree, and the time for maintenance of shaping is small for 6~8
When.