CN102051084A - Putty powder - Google Patents
Putty powder Download PDFInfo
- Publication number
- CN102051084A CN102051084A CN2009102078781A CN200910207878A CN102051084A CN 102051084 A CN102051084 A CN 102051084A CN 2009102078781 A CN2009102078781 A CN 2009102078781A CN 200910207878 A CN200910207878 A CN 200910207878A CN 102051084 A CN102051084 A CN 102051084A
- Authority
- CN
- China
- Prior art keywords
- percent
- river sand
- white cement
- putty powder
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to putty powder, and belongs to the technology of building coatings. The putty powder comprises calcium carbonate stone powder, sierozem, white cement, river sand and cellulose serving as raw materials. The putty powder is prepared by the following steps of: proportioning the raw materials by weight: 76 to 85 percent of 300-mesh calcium carbonate stone powder, 6 to 9 percent of 300 to 400-mesh sierozem, 6 to 9 percent of white cement, 2.8 to 4.8 percent of 100 to 200-mesh river sand and 0.2 to 1.2 percent of cellulose; and stirring the raw materials uniformly, and packing the mixture according to 20 kilograms per bag to obtain a finished product. The invention provides a product with simple production process and low manufacturing cost; the product has good close bonding property, strong viscosity resistance, good abrasion resistance and good washing resistant effect; and the product also has the advantages of cracking resistance, no corrosion, no layer separation, no injury to hand, environmental friendliness, no smell, no toxicity or harm to the human body and the like.
Description
Technical field
The invention belongs to the building decoration technology field, be specifically related to a kind of putty powder that is applicable to the special use of indoor and outdoor metope.
Background technology
The plastering material of indoor and outdoor metope decoration use under construction is a lot of at present, standard practice is: with gypsum, lime putty, white cement, talcum powder, chalk powder, 107 glue, Resin adhesive, preparation of raw material such as Mierocrystalline cellulose become finishing material, also need be at the material of interior wall face with bottoming, as use talcum powder, the peace stone flour, exterior wall bottoming in the material that benzene emulsion is made carries out, the defective that above material carries out the decorating inner and external walls existence is the weather wetness for a long time, cause long blackspot trace easily on the interior outside, and peeling appears, shedding, obscission, the work-ing life of metope effect is short, also has the construction technology complexity, the difficulty of construction height, particularly use 107 glue in the material, contain formaldehyde materials, harmful.
Summary of the invention
The objective of the invention is at the deficiencies in the prior art, provide a kind of binding property of nonpoisonous and tasteless environment-friendly type good, the safe effect of human body toxicological harmless is reached easy working a kind of putty powder well.
Invent described a kind of putty powder, comprise charcoal acid calcium stone flour, grey calcium, white cement, river sand and Mierocrystalline cellulose; The raw material weight ratio is: charcoal acid calcium stone flour 760-850 ‰, grey calcium 60-90 ‰, white cement 60-90 ‰, river sand 28-48 ‰, Mierocrystalline cellulose 2-12 ‰;
It is realized by being prepared as follows step:
With 300 order charcoal acid calcium stone flours, 300-400 order ash calcium, white cement, 100-200 order river sand, Mierocrystalline cellulose by the raw material weight ratio is: charcoal acid calcium stone flour 760-850 ‰, grey calcium 60-90 ‰, white cement 60-90 ‰, river sand 28-48 ‰, Mierocrystalline cellulose 2-12 ‰; The raw material weight ratio is stirred, pack finished product for 20 kilograms with every bag.
The invention has the beneficial effects as follows: provide a kind of production process simple, cost of goods manifactured is low, product close adhesion performance is good, anti-viscosity is strong, wear resistance is good, washing-resistant effect, this product also has cracking resistance line, the not delamination of no burn into, does not hinder hand, environmental protection, tasteless, to advantages such as human body toxicological harmlesss.
Embodiment
Embodiment 1
Below in conjunction with specific embodiment, the present invention will be further described.
A kind of putty powder comprises charcoal acid calcium stone flour, grey calcium, white cement, river sand and Mierocrystalline cellulose; Feed proportioning weight permillage is: charcoal acid calcium stone flour 850, grey calcium 60, white cement 60, river sand 28, Mierocrystalline cellulose 2;
It is realized by being prepared as follows step: with 300 order charcoal acid calcium stone flours, and 300-400 order ash calcium, white cement, 100-200 order river sand, Mierocrystalline cellulose by the raw material weight permillage is: charcoal acid calcium stone flour 850, grey calcium 60, white cement 60, river sand 28, Mierocrystalline cellulose 2;
Stir by raw material weight proportion, by 20 kilograms of packings of every bag, finished product
Embodiment 2
A kind of putty powder comprises charcoal acid calcium stone flour, grey calcium, white cement, river sand and Mierocrystalline cellulose; Proportioning raw materials weight permillage is: charcoal acid calcium stone flour 760, grey calcium 90, white cement 90, river sand 48, Mierocrystalline cellulose 12;
It is realized by being prepared as follows step: with 300 order charcoal acid calcium stone flours, and 300-400 order ash calcium, white cement, 100-200 order river sand, Mierocrystalline cellulose by the raw material weight permillage is: charcoal acid calcium stone flour 760, grey calcium 90, white cement 90, river sand 48, Mierocrystalline cellulose 12; Stir by the raw material weight ratio, pack finished product for 20 kilograms with every bag.
Embodiment 3
A kind of putty powder comprises charcoal acid calcium stone flour, grey calcium, white cement, river sand and Mierocrystalline cellulose; The raw material weight permillage is: charcoal acid calcium stone flour 800, grey calcium 75, white cement 75, river sand 46, Mierocrystalline cellulose 4;
It is realized by being prepared as follows step: with 300 order charcoal acid calcium stone flours, and 300-400 order ash calcium, white cement, 100-200 order river sand, Mierocrystalline cellulose by the raw material weight permillage is: charcoal acid calcium stone flour 800, grey calcium 75, white cement 75, river sand 46, Mierocrystalline cellulose 4; Stir by the raw material weight ratio, pack finished product for 20 kilograms with every bag.
The present invention is not limited to above-mentioned preferred forms, and other any identical with the present invention or akin products that anyone draws under enlightenment of the present invention all drop within protection scope of the present invention.
Claims (2)
1. a putty powder comprises charcoal acid calcium stone flour, grey calcium, white cement, river sand and Mierocrystalline cellulose; It is characterized in that: putty powder raw material weight ratio be: charcoal acid calcium stone flour 760-850 ‰, grey calcium 60-90 ‰, white cement 60-90 ‰, river sand 28-48 ‰, Mierocrystalline cellulose 2-12 ‰.
2. a kind of putty powder according to claim 1, it is characterized in that: it is realized by being prepared as follows step: with 300 order charcoal acid calcium stone flours, and 300-400 order ash calcium, white cement, 100-200 order river sand, Mierocrystalline cellulose by the raw material weight ratio is: charcoal acid calcium stone flour 760-850 ‰, grey calcium 60-90 ‰, white cement 60-90 ‰, river sand 28-48 ‰, Mierocrystalline cellulose 2-12 ‰, stir, by 20 kilograms of packings of every bag, finished product.